CN108165123A - A kind of residence outer wall thermal acoustic insulation coating and preparation method thereof - Google Patents
A kind of residence outer wall thermal acoustic insulation coating and preparation method thereof Download PDFInfo
- Publication number
- CN108165123A CN108165123A CN201711262509.3A CN201711262509A CN108165123A CN 108165123 A CN108165123 A CN 108165123A CN 201711262509 A CN201711262509 A CN 201711262509A CN 108165123 A CN108165123 A CN 108165123A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulation coating
- acoustic insulation
- silicon oxide
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of residence outer wall thermal acoustic insulation coating and preparation method thereof, coating therein is made from the following raw materials in parts by weight:10 15 parts of polymer emulsion, 5 10 parts of ethyl cellulose, 5 13 parts of water-compatible amino resin, 69 parts of benzoyl peroxide fire retardant, 47 parts of isocyanates, 59 parts of land plaster, 9 12 parts of basalt fibre, 13 18 parts of inorganic thermal insulation filler, 69 parts of dispersant, 58 parts of adhesive, 47 parts of polyvinyl alcohol, 79 parts of toughener, hollow 58 parts of nano silicon oxide, 6 10 parts of toluene di-isocyanate(TDI), 69 parts of swelling agent, 26 39 parts of ionized water.The present invention combines the preferable styrene block copolymer resin of physical property, Corvic, basalt fibre and hollow nano silicon oxide etc. and is compounded, so that the heat-insulating property of thermal acoustic insulation coating and damping are preferable after the performance of the recipe ingredient, sound insulation value is high simultaneously, and with purification air, the effect of humidity is adjusted, the toxic and harmful gas in air can also be adsorbed.
Description
Technical field
The present invention relates to a kind of residence outer wall thermal acoustic insulation coating and preparation method thereof.
Background technology
At present, the existing ornamental acoustic material of traditional residence outer wall be all based on glass fibre, it the shortcomings that
It is poor to low-frequency sound-absorbing effect in glass fiber material, without fire retardation, it is impossible to mosquito proof, and not only substance in itself to human body
It is harmful, it can also generate pernicious gas in burning.
The noise pollution that modern society occurs, especially room noise are polluted is gradually to the harm of health and daily life
People are paid attention to, and therefore, many Modern Residence exterior walls need to consider the soundproof effect inside it in design.Acoustic material is not only
Indoor sound quality environment can be improved, and very important effect is also functioned to noise abatement.Traditional residence outer wall sound insulation
The various types of material, common mainly has gypsum decorative acoustic board, mineral wool decoration acoustic absorption, the decoration sound absorption of rock (ore deposit) cotton
Plate, pearlite decorative acoustic board, polystyrene foam plastics decoration acoustic absorption, metal finishing acoustic board, perforated microstructure sound absorption
Plate etc..These acoustic boards are not easy to store, transport, is assembled, some material surfaces also need to supplementary protection due to restricted by size
And decorative layer.Moreover, rock (ore deposit) cotton material is harmful, if improper use has carcinogenic danger;Polystyrene foam is moulded
Expect that acoustic board gas permeability and heat resistance are bad, harmful gas can be released by meeting fire;And porous metal plate sound absorption material
Material and perforated microstructure acoustic board, cost is excessively high, and there are no be widely used.
However, there are following several problems for the patented technology announced at present:NRC is not high, and soundproof effect is limited;Product
Flame retardant property is not good enough;Irritant pernicious gas releasing of gluing lotion etc. in drying process.Patent CN1425720A (application numbers
03118445.6) a kind of sound-absorbing environment protection paint is disclosed, which makees lightweight aggregate using flyash pearl of floaing, to improve sound insulation effect
Fruit, but due to flyash float pearl stomata closing, it is not penetrating so that the coating soundproof effect is undesirable.Patent CN1429869A (Shens
Number a kind of special flashing and sound-absorbent coating for music hall please 01145015.0) be disclosed, which is added to light pearl stone and foam
Granules of polystyrene generates certain sound-absorbing soundproof effect;But its heat insulation is poor.
Invention content
The present invention seeks to provide in view of the defects existing in the prior art a kind of residence outer wall thermal acoustic insulation coating and its
Preparation method.
The present invention to achieve the above object, adopts the following technical scheme that:A kind of thermal acoustic insulation coating, by following parts by weight
Raw material is made:10-15 parts of polymer emulsion, 5-10 parts of ethyl cellulose, 5-13 parts of water-compatible amino resin, benzoyl peroxide resistance
Fire 6-9 parts of agent, 4-7 parts of isocyanates, 5-9 parts of land plaster, 9-12 parts of basalt fibre, 13-18 parts of inorganic thermal insulation filler, dispersion
6-9 parts of agent, 5-8 parts of adhesive, 4-7 parts of polyvinyl alcohol, 7-9 parts of toughener, hollow nano silicon oxide 5-8 parts, toluene diisocyanate
6-10 parts of acid esters, 6-9 parts of swelling agent, 26-39 parts of ionized water.
Preferably, 20 parts of the polymer emulsion, 5 parts of ethyl cellulose, 5 parts of water-compatible amino resin, benzoyl peroxide first
2 parts of acyl fire retardant, 4 parts of isocyanates, 5 parts of land plaster, 9 parts of basalt fibre, 13 parts of inorganic thermal insulation filler, 2 parts of dispersant glue
1 part of mixture, 4 parts of polyvinyl alcohol, 7 parts of toughener, hollow 5 parts of nano silicon oxide, 6 parts of toluene di-isocyanate(TDI), 2 parts of swelling agent,
26 parts of ionized water.
Preferably, 28 parts of the polymer emulsion, 8 parts of ethyl cellulose, 8 parts of water-compatible amino resin, benzoyl peroxide
4 parts of fire retardant, 6 parts of isocyanates, 6 parts of land plaster, 11 parts of basalt fibre, 13 parts of inorganic thermal insulation filler, 3 parts of dispersant glue
1 part of mixture, 4 parts of polyvinyl alcohol, 8 parts of toughener, hollow 6 parts of nano silicon oxide, 9 parts of toluene di-isocyanate(TDI), 3 parts of swelling agent,
33 parts of ionized water.
Preferably, 35 parts of polymer emulsion, 10 parts of ethyl cellulose, 13 parts of water-compatible amino resin, benzoyl peroxide resistance
Fire 5 parts of agent, 7 parts of isocyanates, 9 parts of land plaster, 12 parts of basalt fibre, 18 parts of inorganic thermal insulation filler, 5 parts of dispersant, bonding
2 parts of agent, 7 parts of polyvinyl alcohol, 9 parts of toughener, hollow 8 parts of nano silicon oxide, 10 parts of toluene di-isocyanate(TDI), 5 parts of swelling agent, from
Sub- 39 parts of water.
Preferably, 22-27 parts of diamond titanium dioxide is further included, micrometer level porous diatomite 5-10 parts, 3-8 parts of calcium oxide,
6-9 parts of pigment, 6-9 parts of ceramic powder, 10-15 parts of silicone acrylic emulsion.Preferably, the pigment is rutile type titanium white, anatase
Any one or a few in type titanium dioxide or lithopone.
A kind of residence outer wall preparation method of thermal acoustic insulation coating, is as follows:
(1) by 10-15 parts of polymer emulsion, 5-10 parts of ethyl cellulose, 5-13 parts of water-compatible amino resin and benzoyl peroxide
6-9 parts of formyl fire retardant is put into heating stirring 32-46 minutes in the reaction kettle with blender, then temperature is sent at 70-85 DEG C
Enter storage tank natural cooling 1 hour;
(2) by 4-7 parts of olefine resin, 5-9 parts of land plaster, 9-12 parts of basalt fibre, 13-18 parts of inorganic thermal insulation filler, point
5-8 parts of 6-9 parts of powder and adhesive, which are put into reaction kettle, to be stirred 22-33 minutes, and temperature is then placed in another storage at 46-55 DEG C
Slot natural cooling 1 hour is for use;
(3) mixture handled well in step (1) and step (2) is sent simultaneously with two metering pumps to there is polyethylene respectively
4-7 parts of alcohol, in 7-9 parts of toughener and hollow nano silicon oxide 5-8 parts of mixer, by remaining component:Toluene di-isocyanate(TDI)
6-10 parts, 26-39 parts of 6-9 parts of swelling agent and ionized water are sent into mixer simultaneously with another metering pump successively, through 1200-
1500r/min is stirred 60-80 minutes, and temperature is controlled at 50-60 DEG C, is then placed in incubator, the temperature control of incubator
At 30-35 DEG C, kept for 4 hours for use;
(4) 5-12 parts of heat stabilizer stirring is added in the mixture handled well in step (3), into required after final cooling
Coating.
Beneficial effects of the present invention:The present invention combines the preferable styrene block copolymer resin of physical property, gathers
Vinyl chloride resin, basalt fibre and hollow nano silicon oxide etc. are compounded, so that thermal insulation after the performance of the recipe ingredient
The heat-insulating property and damping of sound-deadening paint are preferable, while sound insulation value is high, and with purification air, adjust the work of humidity
With the toxic and harmful gas in air can also be adsorbed.
Illustrate book
Fig. 1 is the process flow chart of the present invention.
Specific embodiment
The invention discloses a kind of thermal acoustic insulation coating, are made from the following raw materials in parts by weight:Polymer emulsion 10-15
Part, 5-10 parts of ethyl cellulose, 5-13 parts of water-compatible amino resin, 6-9 parts of benzoyl peroxide fire retardant, 4-7 parts of isocyanates,
5-9 parts of land plaster, 9-12 parts of basalt fibre, 13-18 parts of inorganic thermal insulation filler, 6-9 parts of dispersant, 5-8 parts of adhesive, poly- second
4-7 parts of enol, 7-9 parts of toughener, hollow nano silicon oxide 5-8 parts, 6-10 parts of toluene di-isocyanate(TDI), 6-9 parts of swelling agent, heat
5-12 parts of stabilizer, 26-39 parts of ionized water.
Preferably, 20 parts of the polymer emulsion, 5 parts of ethyl cellulose, 5 parts of water-compatible amino resin, benzoyl peroxide first
2 parts of acyl fire retardant, 4 parts of isocyanates, 5 parts of land plaster, 9 parts of basalt fibre, 13 parts of inorganic thermal insulation filler, 2 parts of dispersant glue
1 part of mixture, 4 parts of polyvinyl alcohol, 7 parts of toughener, hollow 5 parts of nano silicon oxide, 6 parts of toluene di-isocyanate(TDI), 2 parts of swelling agent,
5 parts of heat stabilizer, 26 parts of ionized water.
Preferably, 28 parts of the polymer emulsion, 8 parts of ethyl cellulose, 8 parts of water-compatible amino resin, benzoyl peroxide
4 parts of fire retardant, 6 parts of isocyanates, 6 parts of land plaster, 11 parts of basalt fibre, 13 parts of inorganic thermal insulation filler, 3 parts of dispersant glue
1 part of mixture, 4 parts of polyvinyl alcohol, 8 parts of toughener, hollow 6 parts of nano silicon oxide, 9 parts of toluene di-isocyanate(TDI), 3 parts of swelling agent,
9 parts of heat stabilizer, 33 parts of ionized water.
Preferably, 35 parts of polymer emulsion, 10 parts of ethyl cellulose, 13 parts of water-compatible amino resin, benzoyl peroxide resistance
Fire 5 parts of agent, 7 parts of isocyanates, 9 parts of land plaster, 12 parts of basalt fibre, 18 parts of inorganic thermal insulation filler, 5 parts of dispersant, bonding
2 parts of agent, 7 parts of polyvinyl alcohol, 9 parts of toughener, hollow 8 parts of nano silicon oxide, 10 parts of toluene di-isocyanate(TDI), 5 parts of swelling agent, heat
12 parts of stabilizer, 39 parts of ionized water.
Preferably, 22-27 parts of diamond titanium dioxide is further included, micrometer level porous diatomite 5-10 parts, 3-8 parts of calcium oxide,
6-9 parts of pigment, 6-9 parts of ceramic powder, 10-15 parts of silicone acrylic emulsion.Preferably, the pigment is rutile type titanium white, anatase
Any one or a few in type titanium dioxide or lithopone.
The preparation method of the thermal acoustic insulation coating of the present invention, is as follows:
(1) by 10-15 parts of polymer emulsion, 5-10 parts of ethyl cellulose, 5-13 parts of water-compatible amino resin and benzoyl peroxide
6-9 parts of formyl fire retardant is put into heating stirring 32-46 minutes in the reaction kettle with blender, then temperature is sent at 70-85 DEG C
Enter storage tank natural cooling 1 hour;
(2) by 4-7 parts of olefine resin, 5-9 parts of land plaster, 9-12 parts of basalt fibre, 13-18 parts of inorganic thermal insulation filler, point
5-8 parts of 6-9 parts of powder and adhesive, which are put into reaction kettle, to be stirred 22-33 minutes, and temperature is then placed in another storage at 46-55 DEG C
Slot natural cooling 1 hour is for use;
(3) mixture handled well in step (1) and step (2) is sent simultaneously with two metering pumps to there is polyethylene respectively
4-7 parts of alcohol, in 7-9 parts of toughener and hollow nano silicon oxide 5-8 parts of mixer, by remaining component:Toluene di-isocyanate(TDI)
6-10 parts, 26-39 parts of 6-9 parts of swelling agent and ionized water are sent into mixer simultaneously with another metering pump successively, through 1200-
1500r/min is stirred 60-80 minutes, and temperature is controlled at 50-60 DEG C, is then placed in incubator, the temperature control of incubator
At 30-35 DEG C, kept for 4 hours for use;
(4) 5-12 parts of heat stabilizer stirring is added in the mixture handled well in step (3), into required after final cooling
Coating.
According to the technique combination above example of Fig. 1 it is found that the present invention to combine the preferable polystyrene of physical property embedding
Section copolymer resin, Corvic, basalt fibre and hollow nano silicon oxide etc. are compounded, the property of the recipe ingredient
Can be later so that the heat-insulating property of thermal acoustic insulation coating and damping be preferable, while sound insulation value is high, and there is purification air,
The effect of humidity is adjusted, the toxic and harmful gas in air can also be adsorbed.It is auxiliary in heat stabilizer and fire retarding synergist be used as every
Hot upgrade materials can greatly improve the heat insulation of the thermal and sound insulating materials.
The foregoing is merely presently preferred embodiments of the present invention, is not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention.
Claims (7)
1. a kind of residence outer wall thermal acoustic insulation coating, it is characterised in that:It is made from the following raw materials in parts by weight:Polymer emulsion
10-15 parts, 5-10 parts of ethyl cellulose, 5-13 parts of water-compatible amino resin, 6-9 parts of benzoyl peroxide fire retardant, isocyanates
4-7 parts, 5-9 parts of land plaster, 9-12 parts of basalt fibre, 13-18 parts of inorganic thermal insulation filler, 6-9 parts of dispersant, adhesive 5-8
Part, 4-7 parts of polyvinyl alcohol, 7-9 parts of toughener, hollow nano silicon oxide 5-8 parts, 6-10 parts of toluene di-isocyanate(TDI), swelling agent
6-9 parts, 5-12 parts of heat stabilizer, 26-39 parts of ionized water.
2. residence outer wall according to claim 1 thermal acoustic insulation coating, which is characterized in that the polymer emulsion 10
Part, 5 parts of ethyl cellulose, 5 parts of water-compatible amino resin, 6 parts of benzoyl peroxide fire retardant, 4 parts of isocyanates, 5 parts of land plaster,
9 parts of basalt fibre, 13 parts of inorganic thermal insulation filler, 6 parts of dispersant, 5 parts of adhesive, 4 parts of polyvinyl alcohol, 7 parts of toughener are hollow
5 parts of nano silicon oxide, 6 parts of toluene di-isocyanate(TDI), 2 parts of swelling agent, 5 parts of heat stabilizer, 26 parts of ionized water.
3. residence outer wall according to claim 1 thermal acoustic insulation coating, which is characterized in that the polymer emulsion 12
Part, 8 parts of ethyl cellulose, 8 parts of water-compatible amino resin, 7 parts of benzoyl peroxide fire retardant, 6 parts of isocyanates, 6 parts of land plaster,
11 parts of basalt fibre, 15 parts of inorganic thermal insulation filler, 7 parts of dispersant, 6 parts of adhesive, 6 parts of polyvinyl alcohol, 8 parts of toughener, in
Empty 6 parts of nano silicon oxide, 6 parts of toluene di-isocyanate(TDI), 7 parts of swelling agent, 8 parts of heat stabilizer, 33 parts of ionized water.
4. residence outer wall according to claim 1 thermal acoustic insulation coating, which is characterized in that 15 parts of polymer emulsion, second
10 parts of base cellulose, 13 parts of water-compatible amino resin, 9 parts of benzoyl peroxide fire retardant, 7 parts of isocyanates, 9 parts of land plaster are profound
Military 12 parts of rock fiber, 18 parts of inorganic thermal insulation filler, 9 parts of dispersant, 8 parts of adhesive, 7 parts of polyvinyl alcohol, 9 parts of toughener are hollow
8 parts of nano silicon oxide, 10 parts of toluene di-isocyanate(TDI), 9 parts of swelling agent, 12 parts of heat stabilizer, 39 parts of ionized water.
5. residence outer wall according to any one of claims 1 to 4 thermal acoustic insulation coating, which is characterized in that further include gold
22-27 parts of hard rock titanium dioxide, micrometer level porous diatomite 5-10 parts, 3-8 parts of calcium oxide, 6-9 parts of pigment, 6-9 parts of ceramic powder, silicon
10-15 parts of acrylic emulsion.
6. residence outer wall according to claim 5 thermal acoustic insulation coating, which is characterized in that the pigment is rutile-type
Any one or a few in titanium dioxide, anatase titanium dioxide or lithopone.
7. a kind of residence outer wall preparation method of thermal acoustic insulation coating, which is characterized in that it is as follows:
(1) by 10-15 parts of polymer emulsion, 5-10 parts of ethyl cellulose, 5-13 parts of water-compatible amino resin and benzoyl peroxide
6-9 parts of fire retardant is put into heating stirring 32-46 minutes in the reaction kettle with blender, and temperature is then fed into storage at 70-85 DEG C
Slot natural cooling 1 hour;
(2) by 4-7 parts of olefine resin, 5-9 parts of land plaster, 9-12 parts of basalt fibre, 13-18 parts of inorganic thermal insulation filler, dispersant
6-9 parts and 5-8 part of adhesive, which are put into reaction kettle, to be stirred 22-33 minutes, temperature at 46-55 DEG C, be then placed in another storage tank oneself
So cool down 1 hour for use;
(3) mixture handled well in step (1) and step (2) is sent simultaneously with two metering pumps to there is polyvinyl alcohol 4- respectively
7 parts, in 7-9 parts of toughener and hollow nano silicon oxide 5-8 parts of mixer, by remaining component:Toluene di-isocyanate(TDI) 6-10
Part, 26-39 parts of 6-9 parts of swelling agent and ionized water are sent into mixer simultaneously with another metering pump successively, through 1200-1500r/
Min is stirred 60-80 minutes, and temperature is controlled at 50-60 DEG C, is then placed in incubator, and the temperature of incubator is controlled in 30-35
DEG C, kept for 4 hours for use;
(4) 5-12 parts of heat stabilizer stirring is added in the mixture handled well in step (3), into required painting after final cooling
Material.