CN108164139A - Parian sheen brick overglaze, parian sheen brick and preparation method thereof - Google Patents
Parian sheen brick overglaze, parian sheen brick and preparation method thereof Download PDFInfo
- Publication number
- CN108164139A CN108164139A CN201711337719.4A CN201711337719A CN108164139A CN 108164139 A CN108164139 A CN 108164139A CN 201711337719 A CN201711337719 A CN 201711337719A CN 108164139 A CN108164139 A CN 108164139A
- Authority
- CN
- China
- Prior art keywords
- parts
- parian
- sheen
- brick
- overglaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of parian sheen brick overglaze, including following component based on parts by weight of raw materials：40~60 parts of albite, 5~10 parts of zinc oxide, 10~20 parts of barium carbonate, burns 5~15 parts of talcum, 5~10 parts of calcined kaolin, 10~20 parts of zirconium silicate, 2~10 parts of corundum at 10~20 parts of dolomite.The present invention is by optimizing and adjusting overglaze component and proportioning, its glaze hair color effect is uniform, glaze paint stable glossiness, so as to assign artificial marble ceramic tiles surface more fine and smooth soft light effect, so that parian texture decoration still maintains excellent fidelity after being combined with soft light effect, while glaze paint has excellent antifouling and wear-resisting property after firing.The invention also discloses parian sheen bricks for applying the overglaze and preparation method thereof.
Description
Technical field
The present invention relates to decorative building material fields, more particularly to sheen brick field.
Background technology
Artificial marble ceramic tiles refer to there is a kind of tile product of natural marble texture true to nature, color and texture, tool
There is the superior function of decorative effect that natural marble is true to nature and ceramic tile, abandon the various natural defects of natural marble, it is
The epoch-making innovator of architectural ceramic industry and the masterpiece of modern top ceramic tile manufacturing process are after tile, polished bricks, modelled after an antique
The new category of another ceramic tile after brick, crystallite stone ceramic tile.
Sheen brick is a kind of ceramic tile of the brick face reflection between strong light and dim light, and the lofty tone of existing light class ceramic tile is bright
Gorgeous, the low-key for also having dumb light class ceramic tile is containing.As a kind of new product category, sheen brick is most particularly reflective by reducing
Rate reaches the comfort level of human visual impression and the decorative effect without light pollution.
It is existing soft on the market in the prior art for the research of sheen brick combination imitation marble effect and improvement and few
The light brick overwhelming majority is decorated for planar grains, and reflecting rate is excessively high, particularly under LED lamplight or sunlight, visually looks over
Can still feel dazzling, and when its with parian texture decoration be combined when, ceramic tile fidelity can be caused to be greatly reduced.The opposing party
Face, existing sheen brick is antifouling and wear-resisting property is poor so that its large-area applications is restricted when public place.
Invention content
It is an object of the invention in view of the above shortcomings of the prior art, provide a kind of parian sheen brick overglaze,
The advantages of artificial marble ceramic tiles surface can be made to have both light and dumb light, while assign brick face excellent wear-resisting and antifouling property.This
Invention also provides a kind of parian sheen brick for applying the overglaze and preparation method thereof.
The technical solution used in the present invention is：A kind of parian sheen brick overglaze, based on parts by weight of raw materials including
Following component：
A kind of parian sheen brick, surface charity have parian sheen brick overglaze as described above.
A kind of preparation method of parian sheen brick as described above, comprises the technical steps that：
1) adobe surface is cleaned, is dried；
2) charity ground-coat enamel；
3) inkjet printing parian texture decorative pattern；
4) parian sheen brick overglaze is applied；
5) it is burnt into through kiln, obtains parian sheen brick finished product.
As being further improved for said program, the ground-coat enamel described in step 2) is based on parts by weight of raw materials including such as the following group
Point：It is 35~45 parts of albite, 10~20 parts of quartz, 15~25 parts of aluminium oxide, 10~20 parts of potassium feldspar, 3~10 parts of air knife soil, white
2~8 parts of marble, 2~6 parts of nepheline, 0~5 part of calcined kaolin, 10~15 parts of zirconium silicate.
As being further improved for said program, kiln firing described in step 5) is first through 800~970 DEG C of middle warm area
Oxidation 20~40min of tape handling, by 1150 DEG C of high-temperature region processing 30min.
The beneficial effects of the invention are as follows：
(1) present invention is by optimizing and adjusting overglaze component and proportioning, and glaze hair color effect is uniform, glaze paint glossiness is steady
It is fixed, so as to assign artificial marble ceramic tiles surface more fine and smooth soft light effect so that parian texture is decorated and soft light effect
Excellent fidelity is still maintained with reference to after, while glaze paint has excellent antifouling and wear-resisting property after firing.
(2) preparation process of the invention by adjusting full sized brick so that green body is vented in time during the reaction with glaze, instead
Should be abundant, occur the defects of pin hole, small salient point etc. in glaze paint after firing so as to further avoid full sized brick.
Specific embodiment
The present invention is specifically described with reference to embodiment, in order to technical field personnel to the present invention
Understand.It is necessary to it is emphasized that embodiment is only intended to, the present invention will be further described herein, it is impossible to be interpreted as to this
The limitation of invention protection domain, fields person skilled in the art, the non-intrinsically safe made according to foregoing invention content to the present invention
The modifications and adaptations of property, should still fall within protection scope of the present invention.Mentioned raw materials following simultaneously are unspecified, are
Commercial product；The processing step or preparation method not referred in detail be processing step known to a person skilled in the art or
Preparation method.
A kind of parian sheen brick overglaze, including following component based on parts by weight of raw materials：
A kind of parian sheen brick, surface charity have parian sheen brick overglaze as described above.
A kind of preparation method of parian sheen brick as described above, comprises the technical steps that：
1) adobe surface is cleaned, is dried；
2) charity ground-coat enamel；
3) inkjet printing parian texture decorative pattern；
4) parian sheen brick overglaze is applied；
5) it is burnt into through kiln, obtains parian sheen brick finished product.
Preferred embodiment is further used as, the ground-coat enamel described in step 2) is based on parts by weight of raw materials including such as the following group
Point：It is 35~45 parts of albite, 10~20 parts of quartz, 15~25 parts of aluminium oxide, 10~20 parts of potassium feldspar, 3~10 parts of air knife soil, white
2~8 parts of marble, 2~6 parts of nepheline, 0~5 part of calcined kaolin, 10~15 parts of zirconium silicate.
Preferred embodiment is further used as, the firing of kiln described in step 5) is first through 800~970 DEG C of middle warm area
Oxidation 20~40min of tape handling, by 1150 DEG C of high-temperature region processing 30min.
The key technical indexes such as product inherent quality and presentation quality that the present invention is burnt into reach company internal standard Q/
JPTC1-2011《Dry-pressing Ceramic Tiles》Appendix A, national standard GB/T 4100-2006《Ceramic Tiles》Annex G, national standard GB6566-2010
《Radioactive material radionuclides limitation》、HJ/T 297-2006《Environmental labelling product technology requires Ceramic Tiles》、EN 101：
1992《The assay method of ceramic floor brick and walltile surface Mohs scratch hardness》Technical requirement, glossiness for 15~
55.Which part performance is as follows：
1st, surface quality without collide with, crackle and slag, without other obvious shortcomings, high-class product；
2nd, water absorption rate：0.02%, breakdown strength：2502N；
3rd, the modulus of rupture：42Mpa；
4th, soluble lead content：﹤ 0.78mg/kg, (standard≤20) are qualified；
5th, solubility is every cadmium content：﹤ 0.05mg/kg, (standard≤5) are qualified；
6th, Mohs intensity：6 grades.
Above-described embodiment is the preferred embodiment of the present invention, all with similar technique of the invention and the equivalence changes made,
The protection category of the present invention should all be belonged to.
Claims (5)
1. a kind of parian sheen brick overglaze, which is characterized in that including following component based on parts by weight of raw materials：
2. a kind of parian sheen brick, it is characterised in that：Its surface charity has parian sheen as described in claim 1
Brick overglaze.
3. a kind of preparation method of parian sheen brick as claimed in claim 2, which is characterized in that walked including following technique
Suddenly：
1) adobe surface is cleaned, is dried；
2) charity ground-coat enamel；
3) inkjet printing parian texture decorative pattern；
4) parian sheen brick overglaze is applied；
5) it is burnt into through kiln, obtains parian sheen brick finished product.
4. a kind of preparation method of parian sheen brick according to claim 3, it is characterised in that：Described in step 2)
Ground-coat enamel based on parts by weight of raw materials including following component：35~45 parts of albite, quartz 10~20 parts, 15~25 parts of aluminium oxide,
10~20 parts of potassium feldspar, 3~10 parts of air knife soil, 2~8 parts of dolomite, 2~6 parts of nepheline, 0~5 part of calcined kaolin, zirconium silicate
10~15 parts.
5. a kind of preparation method of parian sheen brick according to claim 3, it is characterised in that：Described in step 5)
Kiln firing be oxidation 20~40min of tape handling first through 800~970 DEG C of middle warm area, by the processing of 1150 DEG C of high-temperature region
30min。