CN108130481A - A kind of excellent cold-rolled steel sheet of stretch flange - Google Patents
A kind of excellent cold-rolled steel sheet of stretch flange Download PDFInfo
- Publication number
- CN108130481A CN108130481A CN201711285861.9A CN201711285861A CN108130481A CN 108130481 A CN108130481 A CN 108130481A CN 201711285861 A CN201711285861 A CN 201711285861A CN 108130481 A CN108130481 A CN 108130481A
- Authority
- CN
- China
- Prior art keywords
- rolled steel
- steel sheet
- stretch flange
- cold
- excellent cold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses the cold-rolled steel sheet that a kind of stretch flange is excellent, with following chemical compositions:Contain C in terms of quality %:0.1%~0.5%, Mn:0.05%~0.3%, Si:0.01%~0.2%, AL:0.03%~0.15%, Ni:0.005%~0.01%, Mo:0.003%~0.05%, Cu:0.05%~0.12%, Ca:0.005%~0.2%, Su:0.001%~0.05%, Nb:0.001%~0.005%, P:0.003%~0.04%, S:0.006%~0.015%, surplus is made of iron and inevitable impurity.The cold-rolled steel sheet ductility of the present invention, processing hardening, stretch flange is excellent, tensile strength is high, tension is high and toughness is high.
Description
Technical field
The present invention relates to the cold-rolled steel sheets that a kind of stretch flange is excellent.
Background technology
Today that height is segmented in industrial technology field, there have to the material requirements used in each technical field to be special and high
The performance of degree.For example, for the cold-rolled steel sheet used after compression moulding, with the diversification of compacting shape, it is also desirable to more excellent
Mouldability.Furthermore, it desired to there is high intensity, the application of high tensile strength cold-rolled steel sheet is had studied.Especially for automobile cold-rolled steel
Plate, the considerations of to earth environment, in order to which body lightening is improved fuel consumption efficiency, to thin-walled high-mouldability
The demand of high tensile strength cold-rolled steel sheet significantly increases.In compression moulding, the thickness of used cold-rolled steel sheet is thinner, easier hair
Raw crackle, gauffer, it is therefore desirable to the superior cold-rolled steel sheet of ductility, stretch flange.However, this compression moulding and cold rolling
The high intensity of steel plate is the anti-characteristic of the back of the body, it is difficult to while meet these characteristics.
Invention content
The purpose of the present invention is that solve the above-mentioned problems and provides a kind of ductility, processing hardening, stretch flange
The excellent cold-rolled steel sheet of property.
To achieve these goals, the present invention is achieved by the following technical solutions:A kind of excellent cold of stretch flange
Rolled steel plate, with following chemical compositions:Contain C in terms of quality %:0.1%~0.5%, Mn:0.05%~0.3%, Si:0.01%
~0.2%, AL:0.03%~0.15%, Ni:0.005%~0.01%, Mo:0.003%~0.05%, Cu:0.05%~0.12%,
Ca:0.005%~0.2%, Su:0.001%~0.05%, Nb:0.001%~0.005%, P:0.003%~0.04%, S:
0.006%~0.015%, surplus is made of iron and inevitable impurity.
Further, the excellent cold-rolled steel sheet of a kind of stretch flange, with following chemical compositions:Contained in terms of quality %
C:0.1%~0.35%, Mn:0.05%~0.15%, Si:0.01%~0.15%, AL:0.03%~0.1%, Ni:0.005%~
0.008%、Mo:0.003%~0.02%, Cu:0.05%~0.1%, Ca:0.005%~0.15%, Su:0.001%~0.02%,
Nb:0.001%~0.003%, P:0.003%~0.02%, S:0.006%~0.01%, surplus is by iron and inevitable impurity
It forms.
Further, the excellent cold-rolled steel sheet of a kind of stretch flange, with following chemical compositions:Contained in terms of quality %
There is C:0.25%、Mn:0.1%、Si:0.08%、AL:0.05%、Ni:0.006%、Mo:0.01%、Cu:0.08%、Ca:0.008%、Su:
0.01%、Nb:0.002%、P:0.01%、S:0.008%, surplus is made of iron and inevitable impurity.
In summary the invention has the advantages that:The cold-rolled steel sheet ductility of the present invention, processing hardening, stretching are convex
Edge is excellent, tensile strength is high, tension is high and toughness is high.
Specific embodiment
Specific embodiment 1:The excellent cold-rolled steel sheet of a kind of stretch flange, with following chemical compositions:Contained in terms of quality %
There is C:0.1% 、Mn:0.05% 、Si:0.01% 、AL:0.03% 、Ni:0.005% 、Mo:0.003% 、Cu:0.05% 、Ca:
0.005% 、Su:0.001% 、Nb:0.001% 、P:0.003% 、S:0.006%, surplus is by iron and inevitable impurity structure
Into.
Specific embodiment 2:The excellent cold-rolled steel sheet of a kind of stretch flange, with following chemical compositions:Contained in terms of quality %
There is C:0.25%、Mn:0.1%、Si:0.08%、AL:0.05%、Ni:0.006%、Mo:0.01%、Cu:0.08%、Ca:0.008%、Su:
0.01%、Nb:0.002%、P:0.01%、S:0.008%, surplus is made of iron and inevitable impurity.
Specific embodiment 3:The excellent cold-rolled steel sheet of a kind of stretch flange, with following chemical compositions:Contained in terms of quality %
There is C:0.5%、Mn:0.3%、Si:0.2%、AL:0.15%、Ni:0.01%、Mo:0.05%、Cu:0.12%、Ca:0.2%、Su:
0.05%、Nb:0.005%、P:0.04%、S:0.015%, surplus is made of iron and inevitable impurity.
Better embodiment of the embodiment provided above for the present invention only is used for facilitating illustrating the present invention, not to this hair
The limitation of bright work in any form, any those of ordinary skill in the art, if putting forward skill not departing from the present invention
In the range of art feature, using the equivalent embodiment for locally changing or modifying made by disclosed technology contents, and
Without departing from the technical feature content of the present invention, in the range of still falling within the technology of the present invention feature.
Claims (3)
1. the excellent cold-rolled steel sheet of a kind of stretch flange, which is characterized in that there are following chemical compositions:Contain C in terms of quality %:
0.1%~0.5%, Mn:0.05%~0.3%, Si:0.01%~0.2%, AL:0.03%~0.15%, Ni:0.005%~
0.01%、Mo:0.003%~0.05%, Cu:0.05%~0.12%, Ca:0.005%~0.2%, Su:0.001%~0.05%,
Nb:0.001%~0.005%, P:0.003%~0.04%, S:0.006%~0.015%, surplus by iron and inevitably it is miscellaneous
Texture into.
2. a kind of excellent cold-rolled steel sheet of stretch flange according to claim 1, which is characterized in that have it is following chemistry into
Point:Contain C in terms of quality %:0.1%~0.35%, Mn:0.05%~0.15%, Si:0.01%~0.15%, AL:0.03%~
0.1%、Ni:0.005%~0.008%, Mo:0.003%~0.02%, Cu:0.05%~0.1%, Ca:0.005%~0.15%,
Su:0.001%~0.02%, Nb:0.001%~0.003%, P:0.003%~0.02%, S:0.006%~0.01%, surplus by
Iron and inevitable impurity are formed.
3. a kind of excellent cold-rolled steel sheet of stretch flange according to claim 1, which is characterized in that have it is following chemistry into
Point:Contain C in terms of quality %:0.25%、Mn:0.1%、Si:0.08%、AL:0.05%、Ni:0.006%、Mo:0.01%、Cu:
0.08%、Ca:0.008%、Su:0.01%、Nb:0.002%、P:0.01%、S:0.008%, surplus is by iron and inevitable impurity
It forms.