CN108126878A - The color plating laser carving of mobile phone shell imitates glass, ceramic processing method and mobile phone shell appearance member - Google Patents
The color plating laser carving of mobile phone shell imitates glass, ceramic processing method and mobile phone shell appearance member Download PDFInfo
- Publication number
- CN108126878A CN108126878A CN201810131017.9A CN201810131017A CN108126878A CN 108126878 A CN108126878 A CN 108126878A CN 201810131017 A CN201810131017 A CN 201810131017A CN 108126878 A CN108126878 A CN 108126878A
- Authority
- CN
- China
- Prior art keywords
- plating
- vacuum coating
- transparent
- mobile phone
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the processing methods that a kind of Mobile phone plastic appearance coloured silk plating laser carving bloom imitates glass, ceramics, include the following steps:One plastic rubber substrate is provided;UV colored paint layers are formed on the surface of the plastic rubber substrate;The first vacuum coating is formed on the surface of first clear primer layer;Transparent protective layer is formed on the surface of first vacuum coating;The vacuum coating for showing the region of first prime coat is needed to be removed by laser laser carving on the vacuum coating;Plastic rubber substrate after laser carving is complete is cleaned;The transparent plating bottoms of UV are formed in the plastic surface cleaned;The second vacuum coating is formed on the surface of the second colored paint layer;Enamelled coating in being formed on the surface of second vacuum coating;Top coat layer is formed on the surface of the middle enamelled coating;The present invention can realize that PC plastic cement plating DE Specular Lighting, imitative glass technology can replace ceramics to a certain extent;Glass appearance effect also has the selections such as more colors, and is also equipped with shatter-resistant function.
Description
Technical field
The present invention relates to plating laser carving and Vacuum Deposition spraying field, more particularly to a kind of effect infinite approach ceramics, glass
The technology of glass.
Background technology
At present, the material of the phone housing in market is varied, from makrolon to all kinds of alloy shells again to carbon fibre
Peacekeeping glass shell even wooden, ceramic shell ... is as the material at most being applied to phone housing, traditional poly- carbonic acid
Ester plasticity is strong, impact resistance, has certain suppleness, and that its color is had is more for the high grade of transparency and free dyeability
Kind selection.Antenna interference degree is weaker, and weight was light so that the shell of makrolon was once pursued by masses.It is however traditional
Makrolon also have that texture is poor, not wear-resisting grade insoluble pain spot always.
Invention content
Based on this, it is necessary to for prior art problem, provide a kind of Mobile phone plastic appearance coloured silk plating laser carving bloom imitate glass,
The processing method of ceramics, with reference to present invention process, shows stereo decoration lines, and appearance color effect is infinitely close to pottery
Porcelain, glass;And PC plastic cement two-way mirror will not completely cut off signal;It significantly improves using metal signal is bad and ceramic, glass
The problem of easily breaking into pieces.
To solve prior art problem, the invention discloses:
A kind of Mobile phone plastic appearance coloured silk plating laser carving bloom imitates the processing method of glass, ceramics, includes the following steps:
(1) plastic rubber substrate is provided;
(2) UV colored paint layers are formed on the surface of the plastic rubber substrate;
(3) the first vacuum coating is formed on the surface of the UV colored paints layer;
(4) transparent protective layer is formed on the surface of first vacuum coating;
(5) by the vacuum coating for needing to show the region of first prime coat on first vacuum coating by swashing
Light laser carving removes;
(6) plastic rubber substrate of the laser carving after complete is cleaned;
(7) the transparent plating bottoms of UV are formed in the transparency protected layer surface cleaned;
(8) the second vacuum coating is formed on the surface of the transparent plating bottoms of the UV;
(9) enamelled coating in being formed on the surface of second vacuum coating;
(10) top coat layer is formed on the surface of the middle enamelled coating;
Further, the thickness of the first UV colored paint layers is 20~35um, and the first UV colored paint layers are transparent by UV
Base oil paint, UV solvents is electroplated in the reconciliation of mill base ratio, the paint reconciled paints to plastic rubber substrate, is dried using oven
After roasting levelling, cured according to UV lamp light.
Further, the thickness of first vacuum coating is 1um, and first vacuum coating is described carrying out
The plastic rubber substrate of first UV colored paint layers is placed in vacuum plating furnace, places into target indium metal, is extracted the air in stove, is reached pre-
If target evaporation plating is carried out after vacuum values.
Further, the thickness of the transparent protective layer be 3~8um, the transparent protective layer be by it is transparency protected paint, it is molten
Agent forms transparent protective layer paint after paint viscosity is scaled, and is painted with the transparent protective layer in first Vacuum Deposition
It paints on the basis of film layer, after oven cooking cycle levelling, is cured according to UV lamp light.
Further, the plastic cement cleaning is dirty for the artificial wiping residual that carries out, then is carried out clearly with non-dust cloth or ultrasonic wave
It washes.
Further, the thickness of the transparent plating bottoms of the UV is 25~35um, and the transparent plating bottoms of UV are by saturating
Bright plating bottom UV paint, UV open grease, mill base, reconcile to form the transparent plating roughstuffs of UV according to color matching ratio, with the UV
Transparent plating roughstuff paints on the basis of the transparent protective layer after the cleaning, after oven cooking cycle levelling,
According to UV lamp photocuring.
Further, the thickness of second vacuum coating is 0.5um, and second vacuum coating is that handle carries out institute
The plastic rubber substrate for stating the transparent plating bottoms of UV is placed in vacuum plating furnace, is placed into target indium metal, is extracted the air in stove, reach
Target evaporation plating is carried out after to predetermined vacuum value.
Further, the thickness of the middle enamelled coating is 3~8um, and the middle enamelled coating is by transparent middle urushoil paint, solvent, color
It starches enamelled coating in reconciliation formation in proportion to paint, be painted on the basis of second vacuum coating with the middle enamelled coating paint,
After oven cooking cycle, cured according to UV lamp light.
Further,:The thickness of the top coat layer be 15~35um, the top coat layer be painted by clear finish, solvent,
It reconciles in proportion and forms top coat layer paint, painted on the basis of the middle enamelled coating with top coat layer paint, oven dries
After roasting levelling, according to UV lamp photocuring.
Further, the surface of the plastic rubber substrate is sequentially formed with UV colored paints layer, the first vacuum coating, transparent outward
The transparent plating bottom of protective layer, UV, the second vacuum coating, middle enamelled coating, top coat layer.
Beneficial effects of the present invention are:
1st, the shielding that metalwork easily brings signal is solved;
2nd, solution shows the appearance color of more options
3rd, it solves glass and ceramics is easily broken into pieces, mounted inside structure is single
4th, under the premise of appearance infinite approach ceramics and glass, cost is lower.
Description of the drawings
Fig. 1 is the structure diagram of mobile phone shell plastic outer part of the present invention.
Specific embodiment
For that can further appreciate that the feature, technological means and the specific purposes reached, function of the present invention, figure is please referred to
1, a kind of Mobile phone plastic appearance member is shown in figure, including plastic rubber substrate, which is characterized in that the surface of the plastic rubber substrate 1 to
It is outer to be sequentially formed with the transparent plating bottom 5 of UV colored paints layer 2, the first vacuum coating 3, transparent protective layer 4, UV, the second Vacuum Deposition
Film layer 6, middle enamelled coating 7, top coat layer 8.
Wherein, UV colored paints layer 2 have the function of cover 1 flaw of plastic rubber substrate and enhance adhesive force, have rich colors and
The effect as 3 carrier of the first vacuum coating simultaneously of texture effect;First vacuum coating 3 has metal-like, can play
Bloom bright border effect;Transparent protective layer 4 has the function of to protect the first vacuum coating 3;The transparent plating bottoms 5 of UV are used as second
The carrier function of vacuum coating 6,6 metal-like of the second vacuum coating can play bloom bright border effect, enrich metal-like
With color, middle enamelled coating 7 has the function of to improve test performance;Top coat layer 8 has the function of protection coating below.
The surface treatment method of Mobile phone plastic appearance member is explained in detail below, includes the following steps:
(1) plastic rubber substrate 1 is provided;
(2) UV colored paints layer 2 is formed on the surface of the plastic rubber substrate 1;
In embodiment, the thickness of the UV colored paints layer 2 is 20~35um, and the UV colored paints layer 2 is by the transparent plating of UV
Base oil paint, UV solvents reconcile to form UV colored paints layer paint in mill base ratio, and UV colored paints layer paint carries out plastic rubber substrate
Spray painting, after oven cooking cycle levelling, is cured according to UV lamp light.
(3) the first vacuum coating 3 is formed on the surface of the UV colored paints layer 2;
In embodiment, the thickness of first vacuum coating 3 is 1um, and first vacuum coating 3 is that handle is carried out
The plastic rubber substrate of the UV colored paints layer 2 is placed in vacuum plating furnace, places into target indium metal, is extracted the air in stove, is reached
Target evaporation plating is carried out after predetermined vacuum value.
(4) transparent protective layer 4 is formed on the surface of first vacuum coating 3;
In embodiment, the thickness of the transparent protective layer 4 is 3~8um, and the transparent protective layer 4 is by transparency protected
Paint, solvent form transparent protective layer paint after paint viscosity is scaled, and are painted with the transparent protective layer described first
It paints on the basis of vacuum coating, after oven cooking cycle levelling, is cured according to UV lamp light.
(5) vacuum coating in the region for showing the UV colored paints layer 2 will be needed on first vacuum coating 3 by swashing
Light laser carving removes;
In embodiment, large area laser carving is carried out by infrared laser carving machine, stays LOGO and C angles Liang Mian positions.
(6) plastic rubber substrate of the laser carving after complete is cleaned;
In embodiment, wiping dust is manually carried out after product laser carving and residual is dirty, then with non-dust cloth or ultrasound
Wave is cleaned.
(7) the transparent plating bottoms 5 of UV are formed on 4 surface of transparent protective layer cleaned;
In embodiment, the thickness of the transparent plating bottoms 5 of the UV is 25~35um, and the transparent plating bottoms 5 of UV are
Grease, mill base are opened by transparent plating bottom UV paint, UV, reconciles to form the transparent plating roughstuffs of UV according to color matching ratio, uses institute
It states and paints on the basis of transparent transparent protective layers of the plating roughstuff after the cleaning of UV, by oven cooking cycle levelling
Afterwards, according to UV lamp photocuring.
(8) the second vacuum coating 6 is formed on the surface of the transparent plating bottoms 5 of the UV;
In embodiment, the thickness of second vacuum coating 6 is 0.5um, and second vacuum coating 6 is that handle is done
The plastic rubber substrate of the good transparent plating bottoms of the UV is placed in vacuum plating furnace, is placed into target indium metal, is extracted the sky in stove
Gas carries out target evaporation plating after reaching predetermined vacuum value.
(9) enamelled coating 7 in being formed on the surface of second vacuum coating 6;
In embodiment, the thickness of the middle enamelled coating 7 is 3~8um, and the middle enamelled coating 7 is by transparent middle urushoil paint, molten
Agent, mill base reconcile in proportion to be formed in enamelled coating paint, with the middle enamelled coating paint on the basis of second vacuum coating
Spray painting, after oven cooking cycle, is cured according to UV lamp light.
(10) top coat layer 8 is formed on the surface of the middle enamelled coating 7;
In embodiment, the thickness of the top coat layer 8 is 15~35um, and the top coat layer 8 is to be painted by clear finish, is molten
Agent, in proportion reconciliation form top coat layer paint, are painted on the basis of the middle enamelled coating with top coat layer paint, oven
After toasting levelling, according to UV lamp photocuring.
Embodiment described above only expresses the several embodiments of the present invention, and description is more specific and detailed, but simultaneously
Cannot the limitation to the scope of the claims of the present invention therefore be interpreted as.It should be pointed out that for those of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect range.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (10)
1. a kind of Mobile phone plastic appearance coloured silk plating laser carving bloom imitates the processing method of glass, ceramics, which is characterized in that including following step
Suddenly:
(1) plastic rubber substrate is provided;
(2) UV colored paint layers are formed on the surface of the plastic rubber substrate;
(3) the first vacuum coating is formed on the surface of the UV colored paints layer;
(4) transparent protective layer is formed on the surface of first vacuum coating;
(5) vacuum coating that the region for showing the UV colored paints layer is needed on the vacuum coating is gone by laser laser carving
It removes;
(6) plastic rubber substrate of the laser carving after complete is cleaned;
(7) the transparent plating bottoms of UV are formed in the transparency protected layer surface cleaned;
(8) the second vacuum coating is formed on the surface of the transparent plating bottoms of the UV;
(9) enamelled coating in being formed on the surface of second vacuum coating;
(10) top coat layer is formed on the surface of the middle enamelled coating.
2. Mobile phone plastic appearance coloured silk plating laser carving bloom according to claim 1 imitates the processing method of glass, ceramics, feature
It is:The thickness of the UV colored paints layer is 20~35um, and the UV colored paints layer is by color by the transparent plating base oil paints of UV, UV solvents
Slurry ratio reconciles, and the paint reconciled paints to plastic rubber substrate, after oven cooking cycle levelling, is carried out according to UV lamp light
Curing.
3. Mobile phone plastic appearance coloured silk plating laser carving bloom according to claim 1 imitates the processing method of glass, ceramics, feature
It is:The thickness of first vacuum coating is 1um, and first vacuum coating is that handle carries out the first UV colored paint layers
Plastic rubber substrate be placed in vacuum plating furnace, place into target indium metal, extract the air in stove, it is laggard to reach predetermined vacuum value
The evaporation plating of row target.
4. Mobile phone plastic appearance coloured silk plating laser carving bloom according to claim 1 imitates the processing method of glass, ceramics, feature
It is:The thickness of the transparent protective layer is 3~8um, and the transparent protective layer is scaled by transparency protected paint, solvent
Transparent protective layer paint is formed after painting viscosity, with transparent protective layer paint on the basis of first vacuum coating
It paints, after oven cooking cycle levelling, is cured according to UV lamp light.
5. Mobile phone plastic appearance coloured silk plating laser carving bloom according to claim 1 imitates the processing method of glass, ceramics, feature
It is:The plastic cement cleaning is dirty for the artificial wiping residual that carries out, then is cleaned with non-dust cloth or ultrasonic wave.
6. Mobile phone plastic appearance coloured silk plating laser carving bloom according to claim 1 imitates the processing method of glass, ceramics, feature
It is:The thickness of the transparent plating bottoms of UV is 25~35um, and the transparent plating bottoms of UV are by transparent plating bottom UV oil
Paint, UV open grease, mill base, reconcile to form the transparent plating roughstuffs of UV according to color matching ratio, with the transparent plating bottoms of the UV
Paint paints on the basis of the transparent protective layer after the cleaning, after oven cooking cycle levelling, according to UV lamp photocuring.
7. Mobile phone plastic appearance coloured silk plating laser carving bloom according to claim 1 imitates the processing method of glass, ceramics, feature
It is:The thickness of second vacuum coating is 0.5um, and second vacuum coating is that handle carries out the transparent plating of the UV
The plastic rubber substrate of bottom is placed in vacuum plating furnace, places into target indium metal, is extracted the air in stove, is reached predetermined vacuum value
Target evaporation plating is carried out afterwards.
8. Mobile phone plastic appearance coloured silk plating laser carving bloom according to claim 1 imitates the processing method of glass, ceramics, feature
It is:The thickness of the middle enamelled coating is 3~8um, and the middle enamelled coating is reconciled in proportion by transparent middle urushoil paint, solvent, mill base
Enamelled coating paints in formation, is painted on the basis of second vacuum coating with the middle enamelled coating paint, by oven cooking cycle
Afterwards, cured according to UV lamp light.
9. Mobile phone plastic appearance coloured silk plating laser carving bloom according to claim 1 imitates the processing method of glass, ceramics, feature
It is:The thickness of the top coat layer be 15~35um, the top coat layer be painted by clear finish, solvent, the shape that reconciles in proportion
It paints, is painted on the basis of the middle enamelled coating with top coat layer paint, after oven cooking cycle levelling, according to UV into top coat layer
Light cures.
10. a kind of mobile phone shell plastic outer part, including plastic rubber substrate, which is characterized in that the surface of the plastic rubber substrate outward according to
It is secondary to be formed with the transparent plating bottom of UV colored paints layer, the first vacuum coating, transparent protective layer, UV, the second vacuum coating, middle paint
Layer, top coat layer.