CN108126602A - Utilize the method and mixing arrangement of red mud production cement - Google Patents
Utilize the method and mixing arrangement of red mud production cement Download PDFInfo
- Publication number
- CN108126602A CN108126602A CN201711430253.2A CN201711430253A CN108126602A CN 108126602 A CN108126602 A CN 108126602A CN 201711430253 A CN201711430253 A CN 201711430253A CN 108126602 A CN108126602 A CN 108126602A
- Authority
- CN
- China
- Prior art keywords
- raw material
- red mud
- coal ash
- production cement
- mixing arrangement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of methods and mixing arrangement using red mud production cement, are related to technical field of desulfurization.A kind of mixing arrangement, including ontology, several grid items and vibrating device, grid item and vibrating device are set to ontology, and vibrating device is connect with grid item.The apparatus structure is simple, and operation is flexible, good mixing effect.A kind of method using red mud production cement, including:Using above-mentioned mixing arrangement mixed raw material, by raw material and coal ash mixing calcination, then with desulfurated plaster combined grinding.This method controllability is strong, using red mud as raw material, environmental protection, and refuse reclamation.
Description
Technical field
The present invention relates to technical field of desulfurization, in particular to a kind of method using red mud production cement and mixing
Device.
Background technology
Red mud is that the industrial residue discharged after aluminium oxide is refined from bauxite, and average often produces 1 ton of aluminium oxide, attached
Band generates 1.0~2.0 tons of red muds.As the 4th big alumina producing state of the world, the red mud discharged every year is up to millions of for China
Ton.Red mud typically contains more iron oxide, and appearance is similar to redness of the skin or complexion soil, thus gains the name.Some red muds because containing iron oxide compared with
Less and in brown or even canescence.Distinguished in a manner of refining aluminium oxide, red mud be divided into Bayer process red mud, red mud from sintering process,
Combination method red mud.
Since the chemical bases that red mud combines are difficult to remove and content is big, and containing reasons such as fluorine, aluminium and other plurality of impurities,
The innoxious use of red mud is difficult to always.Countries in the world expert has carried out a large amount of science to the comprehensive utilization of red mud
Research, but such progress is little.Therefore, waste red mud residues processing and comprehensive utilization become a global hang-up.
And receive that mainly take is method that disposition is stacked on seabed or land, but with the development of aluminum i ndustry, produce oxygen to the pin of red mud
Changing the red mud amount of aluminium discharge also increasingly increases, and a series of problems caused by stockpiling disposition goes out therewith, causes serious ring
Border problem.
Invention content
The purpose of the present invention is to provide a kind of mixing arrangements, and the apparatus structure is simple, and operation is flexible, good mixing effect.
Another object of the present invention is to provide a kind of method using red mud production cement, this method controllability is strong, with
Red mud is raw material, environmental protection, refuse reclamation.
What the embodiment of the present invention was realized in:
A kind of mixing arrangement, including ontology, several grid items and vibrating device, grid item and vibrating device are set to this
Body, vibrating device are connect with grid item.
Further, in preferred embodiments of the present invention, elastic component is equipped between grid item and ontology.
A kind of method using red mud production cement, including:
Using above-mentioned mixing arrangement mixed raw material,
By raw material and coal ash mixing calcination, then with desulfurated plaster combined grinding.
Further, in preferred embodiments of the present invention, raw material include lime stone, sandstone, shale and red mud.
Further, in preferred embodiments of the present invention, by weight percentage, raw material include:Lime stone 80~
85%, sandstone 3~10%, shale 0.5~4.5%, red mud 0.5~12%.
Further, in preferred embodiments of the present invention, by weight percentage, raw material include:Lime stone 80~
85%, sandstone 5~10%, shale 5~4%, red mud 4~8%.
Further, in preferred embodiments of the present invention, raw material further include before being mixed with coal ash:By raw material and coal ash
Sieving, the fineness after sieving are 0.05~0.1mm.
Further, in preferred embodiments of the present invention, the weight percent of coal ash is the 3.6~3.9% of raw material.
Further, in preferred embodiments of the present invention, the weight percent of desulfurated plaster is the 4~6% of raw material.
Further, in preferred embodiments of the present invention, the granularity of coal ash and desulfurated plaster is less than 30mm.
The advantageous effect of the embodiment of the present invention:
The present invention provides a kind of mixing arrangement, including ontology, several grid items and vibrating device, vibrating device and grid
Item connects, for the item vibration of band dynamic mesh.Since red mud moisture is big and viscosity is big, can be mixed to machine with general batch mixer
With larger damage, mixed effect is bad.Vibration and gravity of the structure using grid item so that raw material mixes, and
And raw material good mixing effect big for moisture and big viscosity.
A kind of method using red mud production cement provided by the invention, cement, water obtained are prepared by raw material of red mud
Mud complies with standard, and realizes refuse reclamation, development cycle warp, environmental pollution and security risk asks caused by solving red mud pilling
Topic.
Description of the drawings
It in order to illustrate the technical solution of the embodiments of the present invention more clearly, below will be to needed in the embodiment attached
Figure is briefly described, it should be understood that the following drawings illustrates only certain embodiments of the present invention, therefore is not construed as pair
The restriction of range, for those of ordinary skill in the art, without creative efforts, can also be according to this
A little attached drawings obtain other relevant attached drawings.
Fig. 1 is the structure diagram at the first visual angle of mixing arrangement that the embodiment of the present invention 1 provides;
Fig. 2 is the structure diagram at the second visual angle of mixing arrangement that the embodiment of the present invention 1 provides.
Icon:100- mixing arrangements;110- ontologies;111- support columns;120- grid items;130- vibrating devices;140- bullets
Property part.
Specific embodiment
Purpose, technical scheme and advantage to make the embodiment of the present invention are clearer, below in conjunction with the embodiment of the present invention
In attached drawing, the technical solution in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is
Part of the embodiment of the present invention, instead of all the embodiments.The present invention being usually described and illustrated herein in the accompanying drawings is implemented
The component of example can be configured to arrange and design with a variety of different.The person that is not specified actual conditions in embodiment, according to conventional strip
The condition that part or manufacturer suggest carries out.Reagents or instruments used without specified manufacturer, being can be by commercially available purchase
The conventional products of acquisition.
Therefore, below the detailed description of the embodiment of the present invention to providing in the accompanying drawings be not intended to limit it is claimed
The scope of the present invention, but be merely representative of the present invention selected embodiment.Based on the embodiments of the present invention, this field is common
Technical staff's all other embodiments obtained without creative efforts belong to the model that the present invention protects
It encloses.
Below in conjunction with the accompanying drawings, it elaborates to some embodiments of the present invention.In the present invention, in not contradiction or punching
In the case of prominent, all embodiments, embodiment and feature of the invention can be combined with each other.In the present invention, it is conventional
Unit, component etc., both can be commercially available, can also make by oneself according to the present disclosure.In the present invention, in order to prominent
Go out the emphasis of the present invention, the omission or be only briefly described that operations and unit, component to some routines carry out.
Embodiment 1
Referring to Fig.1 and 2, the present embodiment provides a kind of mixing arrangement 100, including ontology 110, several grid items 120
And vibrating device 130, grid item 120 and vibrating device 130 are set to ontology 110, vibrating device 130 connects with grid item 120
It connects.Mixing arrangement 100 is applied to the mixing of red mud and other raw materials, since red mud moisture is big and viscosity is big, is mixed with general
Expect that chance mixing has larger damage to machine, mixed effect is bad.
In the present embodiment, ontology 110 includes support column 111, is used to support several grid items 120.Several grid items 120
Relative level, which is obliquely installed between ontology 110, several grid items 120 and ontology 110, is equipped with elastic component 140.Vibrating device
130 connect with grid item 120, are vibrated for band dynamic mesh item 120.Elastic component 140 causes grid item 120 while vibration not
The stability of ontology 110 is influenced, reduces abrasion of the vibration to ontology 110.Elastic component 140 is spring in the present embodiment, at this
In the other embodiment of invention, elastic component 140 can be elastic, and the present invention does not limit it.When raw material is in grid item 120
When upper, due to vibration and gravity so that raw material mixes, and raw material good mixing effect big for moisture and big viscosity.
A kind of method using red mud production cement provided in an embodiment of the present invention, including:
To raw material progress chemical composition analysis, the ingredient of the red mud in the present embodiment is as follows:
1 red mud component list of table
The raw material of raw material is weighed, using the raw material for the mixing arrangement mixed raw material that embodiment 1 provides, is uniformly mixed it.
In the present invention, raw material include lime stone, sandstone, shale and red mud.Lime stone main component is calcium carbonate, is largely used to build
Material, the raw material of industry.Sandstone main component is silica, is the main component to form silicate mineral.Shale contains viscous
Native mineral, as active material.Lime stone, shale, shale are mixed with red mud prepares cement as raw material so that cement have compared with
Good intensity and heat resisting corrosion-proof corrosion.
By the experimental study of inventor, by weight percentage, when raw material include:Lime stone 80~85%, sandstone 3~
10%, shale 0.5~4.5%, during red mud 0.5~12%, the processing performance of raw material is preferable.Further, it is more excellent in the present invention
Embodiment in, by weight percentage, raw material include:Lime stone 80~85%, sandstone 5~10%, shale 2~4%, red mud
4~8%.
Raw material and coal ash are weighed for the 3.6~3.9% of raw material by the weight percent of coal ash, are sieved, it is 0.05 to take fineness
The screenings of~0.1mm.Wherein, coal ash is the product by coal dust firing.Calcination obtains silicic acid after coal ash is mixed with raw material
Salt cement clinker.In order to be uniformly mixed, the granularity of coal ash is less than 30mm.
After obtained clinker is mixed milling with desulfurated plaster, ordinary cement is made.Wherein, the weight percent of desulfurated plaster
Than 4~6% for raw material, in order to mix milling uniformly, the granularity of desulfurated plaster is less than 30mm.
Embodiment 2
A kind of cement is present embodiments provided, is mainly made by following methods:
The raw material of raw material is weighed, the mixing arrangement mixed raw material provided using embodiment 1 is uniformly mixed it.Raw material packet
It includes:Lime stone 80%, sandstone 10%, shale 4.5%, red mud 5.5%.
3.6% weigh raw material and coal ash for raw material by the weight percent of coal ash, be sieved, take fineness for 0.05~
The screenings of 0.1mm.Wherein, the granularity of coal ash is less than 30mm.It is ripe to obtain portland cement for calcination after coal ash is mixed with raw material
Material.
After obtained clinker is mixed milling with desulfurated plaster, ordinary cement is made.Wherein, the weight percent of desulfurated plaster
Than 4% for raw material, the granularity of desulfurated plaster is less than 30mm.
Embodiment 3
The raw material of raw material is weighed, the mixing arrangement mixed raw material provided using embodiment 1 is uniformly mixed it.Raw material packet
It includes:Lime stone 85%, sandstone 5%, shale 3.5%, red mud 6.5%.
3.9% weigh raw material and coal ash for raw material by the weight percent of coal ash, be sieved, take fineness for 0.05~
The screenings of 0.1mm.Wherein, the granularity of coal ash is less than 30mm.It is ripe to obtain portland cement for calcination after coal ash is mixed with raw material
Material.
After obtained clinker is mixed milling with desulfurated plaster, ordinary cement is made.Wherein, the weight percent of desulfurated plaster
Than 6% for raw material, the granularity of desulfurated plaster is less than 30mm.
Embodiment 4
The raw material of raw material is weighed, the mixing arrangement mixed raw material provided using embodiment 1 is uniformly mixed it.Raw material packet
It includes:Lime stone 83%, sandstone 8%, shale 3%, red mud 6%.
3.7% weigh raw material and coal ash for raw material by the weight percent of coal ash, be sieved, take fineness for 0.05~
The screenings of 0.1mm.Wherein, the granularity of coal ash is less than 30mm.It is ripe to obtain portland cement for calcination after coal ash is mixed with raw material
Material.
After obtained clinker is mixed milling with desulfurated plaster, ordinary cement is made.Wherein, the weight percent of desulfurated plaster
Than 5% for raw material, the granularity of desulfurated plaster is less than 30mm.
Embodiment 5
The raw material of raw material is weighed, the mixing arrangement mixed raw material provided using embodiment 1 is uniformly mixed it.Raw material packet
It includes:Lime stone 80~85%, sandstone 3~10%, shale 0.5~4.5%, red mud 0.5~12%.
Raw material include:Lime stone 83%, sandstone 8%, shale 3%, red mud 6%.
3.8% weigh raw material and coal ash for raw material by the weight percent of coal ash, be sieved, take fineness for 0.05~
The screenings of 0.1mm.Wherein, the granularity of coal ash is less than 30mm.It is ripe to obtain portland cement for calcination after coal ash is mixed with raw material
Material.
After obtained clinker is mixed milling with desulfurated plaster, ordinary cement is made.Wherein, the weight percent of desulfurated plaster
Than 5% for raw material, the granularity of desulfurated plaster is less than 30mm.
Cement made from choosing embodiment 2~5, is detected it, as a result as follows:
2 testing result of table
As shown in Table 2, the cement that embodiment 2~5 provides meets the requirement of GB175-2007 standards, illustrates offer of the present invention
The method using red mud production cement can be made performance cement up to standard, realize refuse reclamation, development cycle warp solves
The problem of environmental pollution caused by red mud pilling and security risk.
In summary, the present invention provides a kind of mixing arrangement, which is caused using the vibration and gravity of grid item
Raw material mixes, and can be applied to the big raw material mixing of the big viscosity of moisture, good mixing effect small to the damage of device.The present invention provides
It is a kind of using red mud production cement method, prepare cement by raw material of red mud, cement obtained complies with standard, realization waste
It recycles, development cycle warp, environmental pollution and security risk caused by solving the problems, such as red mud pilling.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, that is made any repaiies
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of mixing arrangement, which is characterized in that including ontology, several grid items and vibrating device, the grid item and institute
It states vibrating device and is set to the ontology, the vibrating device is connect with the grid item.
2. mixing arrangement according to claim 1, which is characterized in that elasticity is equipped between the grid item and the ontology
Part.
A kind of 3. method using red mud production cement, which is characterized in that including:
Using mixing arrangement mixed raw material as described in claim 1,
By the raw material and coal ash mixing calcination, then with desulfurated plaster combined grinding.
4. the method according to claim 3 using red mud production cement, which is characterized in that the raw material include lime
Stone, sandstone, shale and red mud.
5. the method according to claim 4 using red mud production cement, which is characterized in that by weight percentage, institute
Raw material are stated to include:The lime stone 80~85%, the sandstone 3~10%, the shale 0.5~4.5%, the red mud 0.5
~12%.
6. the method according to claim 5 using red mud production cement, which is characterized in that by weight percentage, institute
Raw material are stated to include:The lime stone 80~85%, the sandstone 5~10%, the shale 2~4%, the red mud 4~8%.
7. the method according to claim 3 using red mud production cement, which is characterized in that the raw material and the coal ash
It is further included before mixing:The raw material and the coal ash are sieved, the fineness after sieving is 0.05~0.1mm.
8. the method according to claim 3 using red mud production cement, which is characterized in that the weight percent of the coal ash
Than 3.6~3.9% for the raw material.
9. the method according to claim 8 using red mud production cement, which is characterized in that the weight of the desulfurated plaster
Percentage is the 4~6% of the raw material.
10. the method according to claim 9 using red mud production cement, which is characterized in that the coal ash takes off with described
The granularity of sulphur gypsum is less than 30mm.