CN104108892B - A kind of method of producing light partition board with industrial slags and construction refuse regenerated utilization - Google Patents
A kind of method of producing light partition board with industrial slags and construction refuse regenerated utilization Download PDFInfo
- Publication number
- CN104108892B CN104108892B CN201410289985.4A CN201410289985A CN104108892B CN 104108892 B CN104108892 B CN 104108892B CN 201410289985 A CN201410289985 A CN 201410289985A CN 104108892 B CN104108892 B CN 104108892B
- Authority
- CN
- China
- Prior art keywords
- industrial slags
- partition board
- light partition
- millimeters
- construction refuse
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of manufacture method of light partition board, especially relate to a kind of method of producing light partition board with industrial slags and construction refuse regenerated utilization. It is mainly to solve raw material that the existing partition wall batten manufacture method of prior art adopts some is bulky grain more than 5mm, therefore in process, easily lump, water absorption rate is poor, drying shrinkage value and the value of creeping are less, anti-strong and extensibility is poor, cause product easily to produce the technical problem of be full of cracks etc. The present invention to industrial slags, building waste sort, Screening Treatment, selecting particle diameter is that 5 millimeters of following fineves are as regenerative raw materials, again industrial slags regenerated granule, construction refuse regenerated particle, Industry Waste sand, haydite are put into mixer together and carry out mix and blend, putting into successively mass percent is that cement, flyash carry out mix and blend for the second time again, fully after mix and blend, add water and stir for the third time more for the second time, finally obtain producing the compound of light partition board.
Description
Technical field
The present invention relates to a kind of manufacture method of light partition board, especially relate to a kind of method of producing light partition board with industrial slags and construction refuse regenerated utilization.
Background technology
Along with the change of China's building material industry, and the attention of country to environmental protection, following construction material is by the green ecotypical building materials that are low pollution, low energy consumption, the feature such as renewable, and novel environment friendly light cellular partition board is exactly wherein well a kind of. So-called light cellular partition board refers to member frivolous (thickness is generally 90mm and 120mm), and apparent density is low, non-bearing, heat insulation, sound insulation, the building wall board that flameproof effect is good. According to regeneration concrete feature, be used for preparing light wall plate, can form mutual supplement with each other's advantages, have and have higher value and environmental benefit. Chinese patent discloses a kind of building refuse concrete perforated brick and manufacture method (publication number: CN101148340A) thereof, and the weight percentages of components of this brick is that coarse aggregate is 20~25%, fine aggregate 50~55%, cement 15~18%, slightly wet ash discharge 1O~12%, water-solid ratio 13~l5%; Slightly, fine aggregate obtains for building useless brick, concrete or other refuse dressing sieves, coarse aggregate size is 5~lOmm, fine aggregate particle diameter is O.15~5mm; Cement is Portland cement (GB175) or the portland slag cement (GBl344) of selecting 325 labels; Thick wet ash discharge is the wet-discharged coal ash of power plant's waste discharge; Useless bulk in building waste brick, concrete are less than to particle diameter 500mm block through manually resolving into, the sieve that shakes goes mud processing, deliver to one-level and be broken into the block below particle diameter 200mm, and then send two-stage crushing to carry out fragmentation, the following particle of particle diameter 10mm is reached more than 30%, deliver to again vibratory sieve classification screening, obtain particle diameter 5~10mm coarse aggregate, O.15~5mm fine aggregate is delivered to respectively storage bin; By aggregate in storage bin taking weight ratio as coarse aggregate 20~25%, fine aggregate is as 50~55%, by automatic blending, and metering cement be l5~18%, slightly wet ash discharge is that lO~12% is mixed into mixing center; Mixture after stirring is transported to forming machine moulding, send precuring field or curing kilns maintenance after moulding, and finished product is set to product stockyard and dispatches from the factory. But some is bulky grain more than 5mm for the raw material that this manufacture method adopts, therefore in process, easily lump, water absorption rate is poor, and drying shrinkage value and the value of creeping are less, anti-strong poor with extensibility, cause product easily to produce be full of cracks.
Summary of the invention
The present invention is to provide a kind of method of producing light partition board with industrial slags and construction refuse regenerated utilization, it is mainly to solve raw material that the existing partition wall batten manufacture method of prior art adopts some is bulky grain more than 5mm, therefore in process, easily lump, water absorption rate is poor, drying shrinkage value and the value of creeping are less, anti-strong and extensibility is poor, cause product easily to produce the technical problem of be full of cracks etc.
Above-mentioned technical problem of the present invention is mainly solved by following technical proposals:
A kind of method of producing light partition board with industrial slags and the utilization of building waste garbage regeneration of the present invention, is characterized in that described method comprises:
A. industrial slags is carried out to Screening Treatment, select particle diameter be 5 millimeters of following fineves as industrial slags regenerative raw materials, send into the first feed bin through material conveyor; The rear 5 millimeters of above industrial slags of screening separation are delivered to disintegrating machine through material conveyor and pulverize, and it is stand-by that the industrial slags particle after pulverizing is sent into the first feed bin as industrial slags regenerated granule through material conveyor below 5 millimeters;
B. building waste is sorted to processing, slightly break for the first time again, building waste after thick breaking carries out thickness separation through mass transport Belt Conveying to vibratory sieve, and it is stand-by that particle below 5 millimeters is sent to the second feed bin as construction refuse regenerated raw material through material conveyor; It is more than 5 millimeters that building waste is sent to conveyer belt through vibratory sieve, being sent to impact breaker by material conveyer belt pulverizes, graininess after pulverizing is sent to cylinder sieve by conveyer belt, isolate construction refuse regenerated particle below 5 millimeters through cylinder sieve, be delivered to the second feed bin through material conveyor stand-by; Sieve isolated more than 5 millimeters building waste through cylinder and be recycled to impact breaker by conveyer belt and pulverize, after reciprocating, obtain 5 millimeters of following construction refuse regenerated particles, be delivered to the second feed bin through material conveyor stand-by;
C. the haydite of the construction refuse regenerated particle of the industrial slags regenerated granule that is 30-40% by mass percent, 20-30%, the Industry Waste sand of 8-10%, 5-10% is put into together mixer and is carried out mix and blend, after fully stirring, put into successively again the cement that mass percent is 18-22%, the flyash of 5-10% carries out mix and blend for the second time, fully after mix and blend, add water and stir for the third time more for the second time, until reach moisture content 15%-25%, finally obtain producing the compound of light partition board;
D. utilizing full-automatic partition wall batten former, is light partition board by the compound machine-shaping being stirred;
E. the light partition board after machine-shaping, utilizes steam to carry out maintenance to it, obtains finished light partition wall batten.
Replace natural stone with building castoff, can be made into Aggregate of recycled concrete. Because the physical property of the regeneration aggregate such as industrial slags or building waste is as bulk density, apparent density, water absorption rate, crush index etc. are different from natural aggregate, make regenerated aggregate concrete performance and natural aggregate concrete performance have obvious difference. The present invention tests aborning, by with normal intensity grade be the comparison of C25 concrete, explore the impact of the regeneration aggregate that adds different proportion in concrete on performance indications such as concrete crushing strengths, improve technical recipe, find best proportioning, make regeneration concrete indices can be applicable to the quality requirements of innovative panellised wall. The ratio that replaces natural rubble along with industrial slags increases, and concrete slump value reduces thereupon, and reason is that industrial slags space is large, water absorption rate is high, causes the loss of the slump. In addition, concrete apparent density is also on a declining curve, and reason is that the apparent density of industrial slags self is low, and this is of value to and alleviates concrete own wt, improves shock resistance. Wherein in the time that industrial slags is controlled in 40% scope, industrial slags is little on concrete compression strength impact, while adding in addition the building waste of 20-30%, also have more by a small margin and promote, reason is that the water absorption rate of industrial slags is much larger than natural rubble, quite a few is absorbed by industrial slags to add concrete mixing water, has objectively reduced the concrete ratio of mud.
As preferably, described step c adds water while stirring for the third time, and the first speed rising to 90 DEG C with 3 DEG C/s by temperature is incubated 20 minutes, then, with the speed rapid cooling to 40 DEG C of 5 DEG C/s, is incubated 10 minutes; With the speed rising to 70 DEG C of 3 DEG C/s, be incubated 20 minutes again, then with the speed rapid cooling to 30 DEG C of 5 DEG C/s; Finally, with the speed rising to 60 DEG C of 3 DEG C/s, be incubated 20 minutes, then naturally cool to room temperature. Heat up rapidly by three times, material fully can be mixed, Industry Waste is husky can produce because repeatedly heat up rapidly explosion with cement, thus further refinement material particles, it is mixed fully. The processing of can rapidly material being condensed of twice rapid cooling, thus can repeatedly tentatively shape.
As preferably, when described step e maintenance, carry out maintenance with the steam of 55-65 DEG C.
As preferably, the time that described step c stirs is for the first time 1 minute, and the time of stirring is for the second time 1.5 minutes.
As preferably, described material conveyor is provided with deironing apparatus, and the metallics containing in industrial slags, building waste is carried out to adsorption removal.
Therefore, water absorption rate of the present invention is higher, and drying shrinkage value and the value of creeping are larger, but anti-strong better with extensibility, apparent density is lower than standard concrete, and crushing resistance is better, and thermal technology's property is good, and thermal conductivity factor is low.
Brief description of the drawings
Accompanying drawing 1 is a kind of schematic flow sheet of the present invention.
Detailed description of the invention
Below by embodiment, and by reference to the accompanying drawings, technical scheme of the present invention is described in further detail.
Embodiment: a kind of method of producing light partition board with industrial slags and construction refuse regenerated utilization of this example, its step is as Fig. 1, for:
A. industrial slags is carried out to Screening Treatment, select particle diameter be 5 millimeters of following fineves as industrial slags regenerative raw materials, send into the first feed bin through material conveyor; The rear 5 millimeters of above industrial slags of screening separation are delivered to disintegrating machine through material conveyor and pulverize, it is stand-by that industrial slags particle after pulverizing is sent into the first feed bin as industrial slags regenerated granule through material conveyor below 5 millimeters, material conveyor is provided with deironing apparatus, and the metallics containing in industrial slags is carried out to adsorption removal;
B. building waste is sorted to processing, slightly break for the first time again, building waste after thick breaking carries out thickness separation through mass transport Belt Conveying to vibratory sieve, and it is stand-by that particle below 5 millimeters is sent to the second feed bin as construction refuse regenerated raw material through material conveyor; It is more than 5 millimeters that building waste is sent to conveyer belt through vibratory sieve, being sent to impact breaker by material conveyer belt pulverizes, graininess after pulverizing is sent to cylinder sieve by conveyer belt, isolate construction refuse regenerated particle below 5 millimeters through cylinder sieve, be delivered to the second feed bin through material conveyor stand-by; Sieving isolated more than 5 millimeters building waste through cylinder is recycled to impact breaker by conveyer belt and pulverizes, after reciprocating, obtain 5 millimeters of following construction refuse regenerated particles, be delivered to the second feed bin through material conveyor stand-by, material conveyor is provided with deironing apparatus, and the metallics containing in building waste is carried out to adsorption removal. ;
C. the industrial slags regenerated granule that is 38% by mass percent, 18% construction refuse regenerated particle, 9% Industry Waste sand, 8% haydite are put into together mixer and are carried out mix and blend, stirring and putting into successively mass percent after 1 minute is again that 21% cement, 6% flyash carry out mix and blend for the second time, mix and blend added water and stirs for the third time again after 1.5 minutes, when stirring, the first speed rising to 90 DEG C with 3 DEG C/s by temperature, be incubated 20 minutes, then with the speed rapid cooling to 40 DEG C of 5 DEG C/s, be incubated 10 minutes; With the speed rising to 70 DEG C of 3 DEG C/s, be incubated 20 minutes again, then with the speed rapid cooling to 30 DEG C of 5 DEG C/s; Finally, with the speed rising to 60 DEG C of 3 DEG C/s, be incubated 20 minutes, then naturally cool to room temperature; Finally reach moisture content 15%-25%, finally obtain producing the compound of light partition board;
D. utilizing full-automatic partition wall batten former, is light partition board by the compound machine-shaping being stirred;
E. the light partition board after machine-shaping, utilizes the steam of 55-65 DEG C to carry out maintenance to it, obtains finished light partition wall batten.
The present invention by with normal intensity grade be the comparison of C25 concrete, explore the impact of the regeneration aggregate that adds different proportion in concrete on performance indications such as concrete crushing strengths, improve technical recipe, find best proportioning, make regeneration concrete indices can be applicable to the quality requirements of innovative panellised wall. Test situation is as shown in the table:
The character of table 1 regeneration aggregate, natural rubble
Table 2 mix Design and mixture performance
Table 3 each numbering Concrete in Natural maintenance mechanical property of 28 days
Test explanation: regeneration aggregate adopts the waste concrete block in certain building removal, surveying particle diameter thereafter through broken, screening processing is 5-20mm, continuous grading. The test specimen that is numbered A0 is standard C 25 concrete benchmark test specimens, is numbered A20, A40, A60, A80, A100 test specimen is that regeneration aggregate replaces the concrete sample of making after natural rubble, and 20,40,60,80 is replacement rate.
Test result analysis:
Table 2 can find out, the ratio that replaces natural rubble along with regeneration aggregate increases, and concrete slump value reduces thereupon, and reason is that regeneration aggregate space is large, water absorption rate is high, causes the loss of the slump. In addition, concrete apparent density is also on a declining curve, and reason is that the apparent density of regeneration aggregate self is low, and this is of value to and alleviates concrete own wt, improves shock resistance.
As can be seen from Table 3, when the replacement rate of regeneration aggregate in concrete is controlled in the scope of 0-40%, regeneration aggregate is little on concrete compression strength impact, while adding 20%, also have more by a small margin and promote, reason is that the water absorption rate of regeneration aggregate is much larger than natural rubble, quite a few is reproduced aggregate absorption to add concrete mixing water, objectively reduce the concrete ratio of mud, can make up to a great extent the loss because adding the compression strength that regeneration aggregate causes, in addition, because regeneration aggregate corner angle are many, rough surface, increase frictional force, while making to destroy, speed slows down, thereby also improve concrete compression strength. but after replacement rate exceedes 40%, the character of regeneration aggregate has exceeded on the impact of compressive property the impact that the ratio of mud causes, causes the remarkable reduction of compression strength. in addition, along with the increase of substitute proportion, concrete resistance to compression bullet mould is decline state, illustrates that the fragility of regeneration concrete has reduced.
From the performance characteristic of above-mentioned regeneration concrete, the production that it is applied to Light trabs is highly beneficial. As little in the apparent density of regeneration concrete, good-extensibility, thermal conductivity factor is low, can alleviate building loading, plays antidetonation, fire prevention, heat insulation texts. The problems such as, resistance to compression tension high for regeneration concrete water absorption rate is poor, need on raw material, check on the one hand, need in technical recipe and technology of preparing, further investigate on the other hand, as regulate the ratio of mud, control regeneration aggregate mixed ratio, add water reducer, increase curing time etc., some defects that exist to make up regeneration concrete.
The foregoing is only specific embodiments of the invention, but architectural feature of the present invention is not limited to this, any those skilled in the art is in the field of the invention, and the variation of doing or modification are all encompassed among the scope of the claims of the present invention.
Claims (4)
1. a method of producing light partition board with industrial slags and construction refuse regenerated utilization, is characterized in that described method comprises:
A. industrial slags is carried out to Screening Treatment, select particle diameter be 5 millimeters of following fineves as industrial slags regenerative raw materials, send into the first feed bin through material conveyor; The rear 5 millimeters of above industrial slags of screening separation are delivered to disintegrating machine through material conveyor and pulverize, and it is stand-by that the industrial slags particle after pulverizing is sent into the first feed bin as industrial slags regenerated granule through material conveyor below 5 millimeters;
B. building waste is sorted to processing, slightly break for the first time again, building waste after thick breaking carries out thickness separation through mass transport Belt Conveying to vibratory sieve, and it is stand-by that particle below 5 millimeters is sent to the second feed bin as construction refuse regenerated raw material through material conveyor; It is more than 5 millimeters that building waste is sent to conveyer belt through vibratory sieve, being sent to impact breaker by material conveyer belt pulverizes, graininess after pulverizing is sent to cylinder sieve by conveyer belt, isolate construction refuse regenerated particle below 5 millimeters through cylinder sieve, be delivered to the second feed bin through material conveyor stand-by; Sieve isolated more than 5 millimeters building waste through cylinder and be recycled to impact breaker by conveyer belt and pulverize, after reciprocating, obtain 5 millimeters of following construction refuse regenerated particles, be delivered to the second feed bin through material conveyor stand-by;
C. the haydite of the construction refuse regenerated particle of the industrial slags regenerated granule that is 30-40% by mass percent, 20-30%, the Industry Waste sand of 8-10%, 5-10% is put into together mixer and is carried out mix and blend, after fully stirring, put into successively again the cement that mass percent is 18-22%, the flyash of 5-10% carries out mix and blend for the second time, fully after mix and blend, add water and stir for the third time more for the second time, the first speed rising to 90 DEG C with 3 DEG C/s by temperature, be incubated 20 minutes, then with the speed rapid cooling to 40 DEG C of 5 DEG C/s, be incubated 10 minutes; With the speed rising to 70 DEG C of 3 DEG C/s, be incubated 20 minutes again, then with the speed rapid cooling to 30 DEG C of 5 DEG C/s; Finally, with the speed rising to 60 DEG C of 3 DEG C/s, be incubated 20 minutes, then naturally cool to room temperature, until reach moisture content 15%-25%, finally obtain producing the compound of light partition board;
D. utilizing full-automatic partition wall batten former, is light partition board by the compound machine-shaping being stirred;
E. the light partition board after machine-shaping, utilizes steam to carry out maintenance to it, obtains finished light partition wall batten.
2. a kind of method of producing light partition board with industrial slags and construction refuse regenerated utilization according to claim 1, carries out maintenance with the steam of 55-65 DEG C while it is characterized in that described step e maintenance.
3. a kind of method of producing light partition board with industrial slags and construction refuse regenerated utilization according to claim 1, is characterized in that the time that described step c stirs is for the first time 1 minute, and the time of stirring is for the second time 1.5 minutes.
4. a kind of method of producing light partition board with industrial slags and construction refuse regenerated utilization according to claim 1, it is characterized in that described material conveyor is provided with deironing apparatus, carries out adsorption removal to the metallics containing in industrial slags, building waste.