CN108118346A - High tenacity gold article fabrication methods - Google Patents
High tenacity gold article fabrication methods Download PDFInfo
- Publication number
- CN108118346A CN108118346A CN201711433637.XA CN201711433637A CN108118346A CN 108118346 A CN108118346 A CN 108118346A CN 201711433637 A CN201711433637 A CN 201711433637A CN 108118346 A CN108118346 A CN 108118346A
- Authority
- CN
- China
- Prior art keywords
- gold
- semi
- finished product
- bracelet
- acid solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses high tenacity gold article fabrication methods.The high tenacity gold article fabrication methods include the following steps:The second acid solution containing nitrate ion and the gold bracelet semi-finished product that the first acid solution containing sulfate ion, concentration that concentration is 95% 99% are 95% 99% are provided;By first acid solution and second acid solution with volume ratio 8.5 9:1 1.5 mix, and form pickling solution;The pickling solution is heated up to 70 DEG C 90 DEG C, gold bracelet semi-finished product are placed in the pickling solution and soak 2 5s, are then taken out;The gold bracelet semi-finished product are placed in 30 DEG C of 60 DEG C of water and are washed, are then taken out;The gold bracelet semi-finished product in 40 DEG C of 60 DEG C of environment are dried, obtain gold bracelet.High tenacity gold article fabrication methods of the present invention, can improve gold jewellery toughness, gold jewellery is prevented to be cracked, and extend gold jewellery service life.
Description
Technical field
The present invention relates to gold manufacture technology fields, and in particular to high tenacity gold article fabrication methods.
Background technology
Gold as beautiful golden yellow non-ferrous metal, have it is rare it is valuable, density is big, hardness is low, good ductility and can
Oxidation, and pure gold face do not occur at any temperature with oxygen for the characteristics of plasticity and quite high chemical stability
Color becomes clear but very soft in golden yellow, gloss, therefore, is usually used in making jewellery.More importantly in Chinese mind, gold
Exactly worship and rich and honour symbol, and the characteristics of the exclusive cultural connotation of gold and value preserving and appreciation so that everybody goes after like a flock of ducks.
The method that gold bracelet shaping of the prior art uses manual processing mostly had also been introduced some machineries and had been added in recent years
Construction equipment.But either manual processing is still machined, and after long-time is worn, mostly tortoise not enough can occur due to toughness
It splits, affects the normal wearing of jewellery.
The content of the invention
Based on this, the present invention, which provides one kind, can improve gold jewellery toughness, prevent its high tenacity gold product making side being cracked
Method.
In order to achieve the object of the present invention, the present invention uses following technical scheme:
A kind of high tenacity gold article fabrication methods, include the following steps:
It is containing for 95%-99% to provide the first acid solution containing sulfate ion, concentration that concentration is 95%-99%
Second acid solution of nitrate ion and gold bracelet semi-finished product;
By first acid solution and second acid solution with volume ratio 8.5-9:1-1.5 is mixed, and forms acid
Dilution;
The pickling solution is heated up to 70 DEG C -90 DEG C, gold bracelet semi-finished product are placed in the pickling solution and soak 2-
5s then takes out;
The gold bracelet semi-finished product are placed in 30 DEG C of -60 DEG C of water and are washed, are then taken out;
The gold bracelet semi-finished product in 40 DEG C of -60 DEG C of environment are dried, obtain gold bracelet.
Above-mentioned high tenacity gold article fabrication methods, by the gold bracelet semi-finished product tentatively to complete be placed in sulfate radical with
In the pickling solution that nitrate anion is made into, after mixing pickling, test finds that the toughness of golden product greatly improves, and finds cracking
Probability substantially reduces, and extends the service life of gold ornaments.
In a wherein embodiment, first acid solution is sulfuric acid solution.Sulfuric acid solution can provide purer sulfate radical from
Son, the pickling solution concentration being made into are more accurate.
In a wherein embodiment, the concentration of the sulfuric acid solution is 98%.
In a wherein embodiment, second acid solution is salpeter solution.Salpeter solution can provide purer nitrate anion from
Son, the pickling solution concentration being made into are more accurate.
In a wherein embodiment, the concentration of the salpeter solution is 98%.
In a wherein embodiment, the volume ratio of first acid solution and second acid solution is 8.5:1.
In a wherein embodiment, the pickling solution is heated up to 75 DEG C -85 DEG C.
In a wherein embodiment, the gold bracelet semi-finished product are placed in 40 DEG C of water and are washed.
In a wherein embodiment, the gold bracelet semi-finished product are dried in 50 DEG C of environment.
The present invention there is a need to another high tenacity gold article fabrication methods of offer, include the following steps:
There is provided salpeter solution that sulfuric acid solution, concentration that concentration is 95%-99% are 95%-99% and gold bracelet half into
Product;
By the sulfuric acid solution and the salpeter solution with volume ratio 8.5-9:1-1.5 is mixed, and it is molten to form pickling
Liquid;
The pickling solution is heated up to 75 DEG C -85 DEG C, gold bracelet semi-finished product are placed in the pickling solution and soak 2-
5s then takes out;
The gold bracelet semi-finished product are placed in 30 DEG C of -60 DEG C of water and are washed, are then taken out;
The gold bracelet semi-finished product are dried in 40 DEG C of -60 DEG C of environment;
The gold bracelet semi-finished product are again placed in soak 2-5s in the pickling solution, are then taken out, such period
Secondary, last gold bracelet semi-finished product are dried in 40 DEG C of -60 DEG C of environment, obtain gold bracelet.
Specific embodiment
For the ease of understanding the present invention, the present invention will be described more fully below.But the present invention can be with perhaps
Mostly different form is realized, however it is not limited to embodiment described herein.On the contrary, the purpose for providing these embodiments is to make
To the understanding more thorough and comprehensive of the disclosure.
Unless otherwise defined, all of technologies and scientific terms used here by the article is with belonging to technical field of the invention
The normally understood meaning of technical staff is identical.Term used in the description of the invention herein is intended merely to description tool
The purpose of the embodiment of body, it is not intended that in the limitation present invention.
The present invention provides a kind of high tenacity gold article fabrication methods, for processing golden product, especially gold jewelry for example
Gold bracelet improves the toughness of gold ornaments, prevents to be cracked, and extends the service life of jewellery.
In a wherein embodiment, gold bracelet semi-finished product for the gold bracelet half after being processed early period into the present invention one compared with
The high tenacity gold article fabrication methods of good embodiment, include the following steps.
First, it is 95%-99%'s to provide the first acid solution containing sulfate ion, concentration that concentration is 95%-99%
The second acid solution containing nitrate ion and gold bracelet semi-finished product.
2nd, by the first acid solution and the second acid solution with volume ratio 8.5-9:1-1.5 is mixed, and it is molten to form pickling
Liquid;
3rd, pickling solution is heated up to 70 DEG C -90 DEG C, gold bracelet semi-finished product is placed in pickling solution and soak 2-5s, so
After take out;
4th, gold bracelet semi-finished product are placed in 30 DEG C of -60 DEG C of water and washed, then taken out;
5th, gold bracelet semi-finished product in 40 DEG C of -60 DEG C of environment are dried, obtains gold bracelet.
Product.For example, it may be using gold block through tabletting, volume ring, treated this finished product such as trombone slide.Tabletting therein is
Refer to and gold is first pressed into sheet, the size of needs can also be cut into.Ring is rolled up to refer to the gold piece of sheet being rolled into ring-shaped, with
It is handled convenient for the later stage.Trombone slide refers to cricoid gold pulling into hollow annular, forms the shape of the jewellery of needs.
It is to be appreciated that in other embodiments, if processing is not bracelet, but the jewelry of other shapes, such as
Animals shaped gold bullion then will carry out die casting by mold and be formed, also be semi-finished product.
First acid solution is sulfuric acid solution, and sulfuric acid solution can provide purer sulfate ion, and the pickling solution being made into is dense
Degree is more accurate.Compared with sulfate of the others containing sulfate radical, the pickling solution purity higher being made into is more conducive to acid
Wash journey.
Similarly, the second acid solution is salpeter solution, and salpeter solution can provide purer nitrate ion, and the pickling being made into is molten
Liquid concentration is more accurate.Compared with nitrate of the others containing nitrate anion, the pickling solution purity higher being made into, advantageously
In acid cleaning process.
In a wherein embodiment, the concentration of sulfuric acid solution is 98%, and the concentration of salpeter solution is 98%.What the concentration was made into
Pickle, the golden product toughness higher of wash-off.
In a wherein embodiment, the first acid solution and the second acid solution are with volume ratio 8.5-9:1-1.5 it mixes, example
Such as with 8.5:1、8.5:1.5、9:1、9:1.5 equal proportions mix.Optionally, the volume of the first acid solution and second acid solution
Than for 8.5:1.The pickle that the ratio is made into, the golden product toughness higher of wash-off.
In a wherein embodiment, pickling solution is heated up to such as 70 DEG C, 75 DEG C, 80 DEG C, 85 DEG C, 90 DEG C.Optionally, pickling
Solution is heated up to 75 DEG C -85 DEG C, such as can be 75 DEG C, 80 DEG C, 85 DEG C.
In a wherein embodiment, gold bracelet semi-finished product are placed in 30 DEG C of -60 DEG C of water and are washed, for example, be placed in 30 DEG C,
35 DEG C, 40 DEG C, 45 DEG C, 50 DEG C, 55 DEG C, wash in 60 DEG C of water.Optionally, gold bracelet semi-finished product are placed in 40 DEG C of water and carry out
Washing.
In a wherein embodiment, gold bracelet semi-finished product are dried in 40 DEG C of -60 DEG C of environment, for example, be placed in 40 DEG C, 45 DEG C,
50 DEG C, 55 DEG C, dry in 60 DEG C of environment.Optionally, gold bracelet semi-finished product are dried in 50 DEG C of environment.
Another embodiment provides high tenacity gold article fabrication methods, and obtained golden product toughness is obtained higher than said program
The golden product arrived, the high tenacity gold article fabrication methods include the following steps:
First, provide concentration be 95%-99% sulfuric acid solution, concentration be 95%-99% salpeter solution and gold bracelet
Semi-finished product.
2nd, by sulfuric acid solution and salpeter solution with volume ratio 8.5-9:1-1.5 is mixed, and forms pickling solution;
3rd, pickling solution is heated up to 75 DEG C -85 DEG C, gold bracelet semi-finished product is placed in the pickling solution and soak 2-
5s then takes out;
4th, gold bracelet semi-finished product are placed in 30 DEG C of -60 DEG C of water and washed, then taken out;
5th, gold bracelet semi-finished product are dried in 40 DEG C of -60 DEG C of environment;
6th, gold bracelet semi-finished product are again placed in soaking 2-5s in pickling solution, are then taken out, so cycled for several times, most
Gold bracelet semi-finished product are dried in 40 DEG C of -60 DEG C of environment afterwards, obtain gold bracelet.
Above-mentioned high tenacity gold article fabrication methods, by the gold bracelet semi-finished product tentatively to complete be placed in sulfate radical with
In the pickling solution that nitrate anion is made into, after mixing pickling, test finds that the toughness of golden product greatly improves, and finds cracking
Probability substantially reduces, and extends the service life of gold ornaments.
Embodiment one
The golden article fabrication methods of the present embodiment, include the following steps:There is provided sulfuric acid solution, concentration that concentration is 98% is
98% salpeter solution and gold bracelet semi-finished product;By sulfuric acid solution and salpeter solution with volume ratio 8.5:1 mixes, shape
Into pickling solution;Pickling solution is heated up to 80 DEG C, gold bracelet semi-finished product are placed in pickling solution and soak 3s, are then taken out;
Gold bracelet semi-finished product are placed in 45 DEG C of water and are washed, are then taken out.Gold bracelet semi-finished product are dried in 50 DEG C of environment
It is dry, gold bracelet semi-finished product are again placed in soaking 3s in pickling solution, are then taken out, are so cycled twice, last gold bracelet
Semi-finished product are dried in 50 DEG C of environment, obtain gold bracelet.
Embodiment two
The golden article fabrication methods of the present embodiment, include the following steps:There is provided sulfuric acid solution, concentration that concentration is 98% is
98% salpeter solution and gold bracelet semi-finished product;By sulfuric acid solution and salpeter solution with volume ratio 8.5:1 mixes, shape
Into pickling solution;Pickling solution is heated up to 80 DEG C, gold bracelet semi-finished product are placed in pickling solution and soak 3s, are then taken out;
Gold bracelet semi-finished product are placed in 45 DEG C of water and are washed, are then taken out.Gold bracelet semi-finished product are dried in 50 DEG C of environment
It is dry, obtain gold bracelet.
Embodiment three
The golden article fabrication methods of the present embodiment, include the following steps:The metabisulfite solution, concentration that concentration is 98% are provided
Sodium nitrate solution and gold bracelet semi-finished product for 98%;By metabisulfite solution and sodium nitrate solution with volume ratio 8.5:1 mixing
Together, pickling solution is formed;Pickling solution is heated up to 80 DEG C, gold bracelet semi-finished product are placed in pickling solution and soak 3s,
It then takes out;Gold bracelet semi-finished product are placed in 45 DEG C of water and are washed, are then taken out.By gold bracelet semi-finished product at 50 DEG C
It is dried in environment, obtains gold bracelet.
Example IV
The golden article fabrication methods of the present embodiment, include the following steps:There is provided sulfuric acid solution, concentration that concentration is 95% is
95% salpeter solution and gold bracelet semi-finished product;By sulfuric acid solution and salpeter solution with volume ratio 9:1 mixes, and is formed
Pickling solution;Pickling solution is heated up to 80 DEG C, gold bracelet semi-finished product are placed in pickling solution and soak 3s, are then taken out;It will
Gold bracelet semi-finished product are placed in 45 DEG C of water and are washed, and then take out.Gold bracelet semi-finished product are dried in 50 DEG C of environment,
Obtain gold bracelet.
Comparative example one
The golden article fabrication methods of the present embodiment are with 8.5 by 98% sulfuric acid and water:1 volume ratio mixing, forms acid
The gold bracelet semi-finished product machined are soaked 3s in the pickling solution for being heated up to 80 DEG C, are subsequently placed in 45 DEG C by dilution
It is washed in water, is then dried, obtain gold bracelet finished product.
Comparative example two
The golden article fabrication methods of the present embodiment are with 8.5 by 98% nitric acid and water:1 volume ratio mixing, forms acid
The gold bracelet semi-finished product machined are soaked 3s in the pickling solution for being heated up to 80 DEG C, are subsequently placed in 45 DEG C by dilution
It is washed in water, is then dried, obtain gold bracelet finished product.
Comparative example three
The golden article fabrication methods of the present embodiment are that the gold bracelet semi-finished product that will be machined are placed in 80 DEG C of water and carry out
Washing, is subsequently placed in 45 DEG C of water and is washed, then dries, and obtains gold bracelet finished product.
The toughness of above several embodiments and comparative example will be tested below, data are shown in Table one.
Using the toughness of the above-mentioned golden product of following methods test:
Cricoid gold bracelet is subjected to deformation process, which observes its restorable situation including bending etc..
Table one
It restores to the original state the time | |
Embodiment one | 2min |
Embodiment two | 3min |
Embodiment three | 4min |
Example IV | 3.5min |
Comparative example one | 10min |
Comparative example two | 10min |
Comparative example three | 20min or longer |
As can be seen from Table I, golden article fabrication methods of the present invention, it is restorable compared with the prior art
Better performances are demonstrate,proved its toughness and are higher by much compared with the prior art, can be better protected from being cracked during routine use,
Extend its service life.
Embodiment described above only expresses the several embodiments of the present invention, and description is more specific and detailed, but simultaneously
Cannot the limitation to the scope of the claims of the present invention therefore be interpreted as.It should be pointed out that for those of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (10)
1. a kind of high tenacity gold article fabrication methods, which is characterized in that include the following steps:
It is that 95%-99% contains nitric acid to provide the first acid solution containing sulfate ion, concentration that concentration is 95%-99%
Second acid solution of radical ion and gold bracelet semi-finished product;
By first acid solution and second acid solution with volume ratio 8.5-9:1-1.5 is mixed, and it is molten to form pickling
Liquid;
The pickling solution is heated up to 70 DEG C -90 DEG C, gold bracelet semi-finished product are placed in the pickling solution and soak 2-5s, so
After take out;
The gold bracelet semi-finished product are placed in 30 DEG C of -60 DEG C of water and are washed, are then taken out;
The gold bracelet semi-finished product in 40 DEG C of -60 DEG C of environment are dried, obtain gold bracelet.
2. high tenacity gold article fabrication methods according to claim 1, it is characterised in that:First acid solution is sulfuric acid
Solution.
3. high tenacity gold article fabrication methods according to claim 2, it is characterised in that:The concentration of the sulfuric acid solution is
98%.
4. high tenacity gold article fabrication methods according to claim 1, it is characterised in that:Second acid solution is nitric acid
Solution.
5. high tenacity gold article fabrication methods according to claim 4, it is characterised in that:The concentration of the salpeter solution is
98%.
6. high tenacity gold article fabrication methods according to claim 1, it is characterised in that:First acid solution with it is described
The volume ratio of second acid solution is 8.5:1.
7. high tenacity gold article fabrication methods according to claim 1, it is characterised in that:The pickling solution is heated up to 75
℃-85℃。
8. high tenacity gold article fabrication methods according to claim 1, it is characterised in that:The gold bracelet semi-finished product are put
It is washed in 40 DEG C of water.
9. high tenacity gold article fabrication methods according to claim 1, it is characterised in that:The gold bracelet semi-finished product exist
It is dried in 50 DEG C of environment.
10. a kind of high tenacity gold article fabrication methods, which is characterized in that include the following steps:
There is provided concentration be 95%-99% sulfuric acid solution, concentration be 95%-99% salpeter solution and gold bracelet semi-finished product;
By the sulfuric acid solution and the salpeter solution with volume ratio 8.5-9:1-1.5 is mixed, and forms pickling solution;
The pickling solution is heated up to 75 DEG C -85 DEG C, gold bracelet semi-finished product are placed in the pickling solution and soak 2-5s, so
After take out;
The gold bracelet semi-finished product are placed in 30 DEG C of -60 DEG C of water and are washed, are then taken out;
The gold bracelet semi-finished product are dried in 40 DEG C of -60 DEG C of environment;
The gold bracelet semi-finished product are again placed in soak 2-5s in the pickling solution, are then taken out, are so cycled for several times, most
Gold bracelet semi-finished product are dried in 40 DEG C of -60 DEG C of environment afterwards, obtain gold bracelet.