CN108102440A - A kind of aluminum alloy doors and windows coating - Google Patents
A kind of aluminum alloy doors and windows coating Download PDFInfo
- Publication number
- CN108102440A CN108102440A CN201711277393.0A CN201711277393A CN108102440A CN 108102440 A CN108102440 A CN 108102440A CN 201711277393 A CN201711277393 A CN 201711277393A CN 108102440 A CN108102440 A CN 108102440A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminum alloy
- alloy doors
- coating
- isopropanol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of aluminum alloy doors and windows coating, including phenyltrimethoxysila,e, fluorosilicone, hexafluorobutyl acrylate, isopropanol, phosphite, diglycidyl ether, different dehydro-α-curcumene, silicon nitride, trimethylolpropane, graphite powder.Coating protecting performance of the present invention is good, can improve the wear-resisting property of door and window.
Description
Technical field
The present invention relates to a kind of aluminum alloy doors and windows coating, belong to technical field of coatings.
Background technology
Coating, in the entitled paint of Chinese tradition.So-called coating is to be coated in the body surface protected or decorated, and
The continuous film of firm attachment can be formed with coated article.And aluminum alloy doors and windows coating requires higher, it is necessary to coating than traditional coating
Aluminum alloy doors and windows can be effectively protected.
The content of the invention
To overcome above-mentioned deficiency, the object of the invention provides a kind of aluminum alloy doors and windows coating.
The solution of the present invention is as follows：A kind of aluminum alloy doors and windows coating, is made of following raw material according to parts by weight：Phenyl three
60 ~ 100 parts of methoxy silane, 10 ~ 30 parts of fluorosilicone, 20 ~ 40 parts of hexafluorobutyl acrylate, 10 ~ 20 parts of isopropanol, phosphorous acid
5 ~ 10 parts of fat, 2 ~ 5 parts of diglycidyl ether, 5 ~ 10 parts of silicon nitride, 3 ~ 8 parts of trimethylolpropane, 0.5 ~ 1.5 part of graphite powder.
Further, it is made of following raw material according to parts by weight：60 parts of phenyltrimethoxysila,e, 15 parts of fluorosilicone,
30 parts of hexafluorobutyl acrylate, 15 parts of isopropanol, 5 parts of phosphite, 3 parts of diglycidyl ether, 7 parts of silicon nitride, trihydroxy methyl
4 parts of propane, 0.5 part of graphite powder.
Further, it is made of following raw material according to parts by weight：70 parts of phenyltrimethoxysila,e, 20 parts of fluorosilicone,
25 parts of hexafluorobutyl acrylate, 16 parts of isopropanol, 7 parts of phosphite, 3 parts of diglycidyl ether, 8 parts of silicon nitride, trihydroxy methyl
5 parts of propane, 1 part of graphite powder.
Further, it is made of following raw material according to parts by weight：90 parts of phenyltrimethoxysila,e, 25 parts of fluorosilicone,
35 parts of hexafluorobutyl acrylate, 17 parts of isopropanol, 6 parts of phosphite, 4 parts of diglycidyl ether, 6 parts of silicon nitride, trihydroxy methyl
6 parts of propane, 1.2 parts of graphite powder.
Beneficial effects of the present invention：Coating protecting performance of the present invention is good, can improve the wear-resisting property of door and window.
Specific embodiment
Embodiment 1
A kind of aluminum alloy doors and windows coating, is made of following raw material according to parts by weight：60 parts of phenyltrimethoxysila,e, fluorine silica
15 parts of alkane, 30 parts of hexafluorobutyl acrylate, 15 parts of isopropanol, 5 parts of phosphite, 3 parts of diglycidyl ether, 7 parts of silicon nitride, three
4 parts of hydroxymethyl-propane, 0.5 part of graphite powder.
Embodiment 2
A kind of aluminum alloy doors and windows coating, is made of following raw material according to parts by weight：70 parts of phenyltrimethoxysila,e, fluorine silica
20 parts of alkane, 25 parts of hexafluorobutyl acrylate, 16 parts of isopropanol, 7 parts of phosphite, 3 parts of diglycidyl ether, 8 parts of silicon nitride, three
5 parts of hydroxymethyl-propane, 1 part of graphite powder.
Embodiment 3
A kind of aluminum alloy doors and windows coating, is made of following raw material according to parts by weight：90 parts of phenyltrimethoxysila,e, fluorine silica
25 parts of alkane, 35 parts of hexafluorobutyl acrylate, 17 parts of isopropanol, 6 parts of phosphite, 4 parts of diglycidyl ether, 6 parts of silicon nitride, three
6 parts of hydroxymethyl-propane, 1.2 parts of graphite powder.
Although giving detailed description and explanation to the specific embodiment of the present invention above, it should be noted that
We according to the invention can conceive to carry out the above embodiment various equivalent changes and modification, and generated function is made
It, should all be within protection scope of the present invention during with the spirit still covered without departing from specification.
Claims (4)
1. a kind of aluminum alloy doors and windows coating, which is characterized in that be made of following raw material according to parts by weight：Phenyl trimethoxy silicon
60 ~ 100 parts of alkane, 10 ~ 30 parts of fluorosilicone, 20 ~ 40 parts of hexafluorobutyl acrylate, 10 ~ 20 parts of isopropanol, phosphite 5 ~ 10
Part, 2 ~ 5 parts of diglycidyl ether, 5 ~ 10 parts of silicon nitride, 3 ~ 8 parts of trimethylolpropane, 0.5 ~ 1.5 part of graphite powder.
2. a kind of aluminum alloy doors and windows coating according to claim 1, which is characterized in that according to parts by weight by following raw material group
Into：60 parts of phenyltrimethoxysila,e, 15 parts of fluorosilicone, 30 parts of hexafluorobutyl acrylate, 15 parts of isopropanol, phosphite 5
Part, 3 parts of diglycidyl ether, 7 parts of silicon nitride, 4 parts of trimethylolpropane, 0.8 part of graphite powder.
3. a kind of aluminum alloy doors and windows coating according to claim 1, which is characterized in that according to parts by weight by following raw material group
Into：70 parts of phenyltrimethoxysila,e, 20 parts of fluorosilicone, 25 parts of hexafluorobutyl acrylate, 16 parts of isopropanol, phosphite 7
Part, 3 parts of diglycidyl ether, 8 parts of silicon nitride, 5 parts of trimethylolpropane, 1 part of graphite powder.
4. a kind of aluminum alloy doors and windows coating according to claim 1, which is characterized in that according to parts by weight by following raw material group
Into：90 parts of phenyltrimethoxysila,e, 25 parts of fluorosilicone, 35 parts of hexafluorobutyl acrylate, 17 parts of isopropanol, phosphite 6
Part, 4 parts of diglycidyl ether, 6 parts of silicon nitride, 6 parts of trimethylolpropane, 1.2 parts of graphite powder.