CN108102245A - A kind of environment-friendly PVC leaching modeling liquid - Google Patents
A kind of environment-friendly PVC leaching modeling liquid Download PDFInfo
- Publication number
- CN108102245A CN108102245A CN201711222719.XA CN201711222719A CN108102245A CN 108102245 A CN108102245 A CN 108102245A CN 201711222719 A CN201711222719 A CN 201711222719A CN 108102245 A CN108102245 A CN 108102245A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- modeling liquid
- leaching modeling
- friendly pvc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of environment-friendly PVCs to soak modeling liquid, and the environment-friendly PVC leaching modeling liquid includes following raw material：37~42 parts of PVC resin powder, 23~32 parts of PVC paste resin, 25~34 parts of pigment, 15~23 parts of butyl rubber powder, 12~18 parts of rubber oil, 11~15 parts of silicon virgin rubber, 9~13 parts of vinyl silica gel oil, 8~15 parts of lightweight nano-calcium carbonate, 5~9 parts of nano zine oxide, newborn 7~14 parts of virgin rubber, 7~18 parts of three palm ester of citric acid, 30~46 parts of 3~5 parts of organic stabilizer and ionic liquid, and add new material on this base-material, environment-friendly PVC leaching modeling liquid is obtained after scattered grinding, environment-friendly PVC leaching modeling liquid security of the present invention is good, environment-friendly and green is pollution-free, uniform coloring, it is easy to use, good economy performance, it manufactures at low cost, with good potentiality, leaching modeling effect is good, it is good to soak plasticity matter.
Description
Technical field
The present invention relates to polyvinyl chloride environment-friendly materials technical fields, and in particular to a kind of environment-friendly PVC leaching modeling liquid.
Background technology
PVC (polyvinyl chloride) leaching modeling liquid can be widely used in physical fitness equipment, labour protection PVC glove, hardware tool handle,
Handle, iron wire clothes hanger, hook, electrical insulating material, soft rubber cover glue beans, craftwork, valve handle, automobile (motorcycle) theftproof lock
In the coating of the products such as sheath.
Existing PVC paste resin or PVC leaching modeling liquid production equipments are in whipping process is produced, because stirrer paddle and material
Friction process can generate heat, and when material reaches certain temperature (being more than 60 DEG C), it is existing that PVC will generate caking due to plasticizing
As processing is difficult, has seriously affected production efficiency；(it is less than 0 DEG C) when environment temperature is very low, one of raw material of PVC leaching modeling liquid
Plasticizer viscosity becomes larger, and can increase motor load in whipping process, motor is even burnt when serious.In addition, the modeling liquid of PVC leachings at present
Color matching kettle is generally a kettle polychrome or more kettle polychromes, the former can increase cleaning difficulty when switching color, time-consuming, laborious, useless
Material, and the latter then needs to increase equipment investment, increases cost, human and material resources is caused to waste.
The content of the invention
To solve the above problems, a kind of the present invention is intended to provide environment-friendly PVC leaching modeling liquid.
Purpose to realize the present invention, the technical solution adopted is that：A kind of environment-friendly PVC leaching modeling liquid, the environment-friendly PVC leaching modeling liquid
Include following raw material：37~42 parts of PVC resin powder, 23~32 parts of PVC paste resin, 25~34 parts of pigment, butyl rubber powder
15~23 parts, 12~18 parts of rubber oil, 11~15 parts of silicon virgin rubber, 9~13 parts of vinyl silica gel oil, lightweight nano-calcium carbonate 8~
15 parts, 5~9 parts of nano zine oxide, newborn 7~14 parts of virgin rubber, 7~18 parts of three palm ester of citric acid, 3~5 parts of organic stabilizer and
30~46 parts of ionic liquid.
Preferably, 1~2 part of γ-FeO (OH), ZnCO are also added in the environment-friendly PVC leaching modeling liquid3And FeTiO3-
MgTiO3Mixture, wherein, γ-FeO (OH), ZnCO3And FeTiO3-MgTiO3Adding proportion be 2~3:1~2:1~3.
Preferably, 2~4 parts of thinner is also added in the environment-friendly PVC leaching modeling liquid, wherein, thinner is Porous deproteinized bone
Hydrocarbon thinner.
Preferably, 8~11 parts of pearly-lustre mill base is also added in the environment-friendly PVC leaching modeling liquid.
Preferably, the pigment that environment-friendly PVC leaching modeling liquid uses is phthalocyanine is red, phthalocyanine basket, phthalocyanine green, everbright fast red, big
Molecule is red, macromolecular is yellow, the one or several kinds in permanent bordeaux and azophloxine.
Preferably, the organic stabilizer is the mixed of the organic calcium-zinc composite stabilizing agent of paste and organotin antimony compound stabilizer
Close object.
Preferably, 2~5 parts of antifoaming agent is also added in the environment-friendly PVC leaching modeling liquid.
Preferably, 2~3 parts of fungicide is also added in the environment-friendly PVC leaching modeling liquid.
Preferably, the manufacturing process of the environment-friendly PVC leaching modeling liquid comprises the following steps：
1) is just mixed：By rubber oil, silicon virgin rubber, vinyl silica gel oil, newborn virgin rubber, three palm ester of citric acid, organic stabilizers
Agent, ionic liquid and antifoaming agent are added in stirred tank together, with rotating speed 1~3h of high-speed stirred of 2000~3000r/min, until object
Material all merges and is uniformly mixed completely, keep 0.01~0.1MPa vacuum degree continue 2~5h of stirring obtain leaching mould liquid it is white
Material；
2) mixes colours：By the dissolving of pigment, 45~60% glycerine, PVC environmental protection mill base and pearl powder in deionized water, exist
Material is stirred at a temperature of 120~150 DEG C to be uniformly mixed to thick, adds remaining glycerine, then with 1500~2500r/
Rotating speed moderate-speed mixer to the material of min is uniformly mixed；
3) bis- mixing of：Thinner, γ-FeO will be added in the dispersed material mixed in step 1 while stirring
(OH)、ZnCO3、FeTiO3-MgTiO3The pigment that step 2 mixes up is added in after being uniformly dispersed with fungicide, then with 2500~3000r/
The rotating speed of min is stirred 3~6h, then is transferred in three-roll grinder；
4) is ground：Scattered material is transferred in three-roll grinder, is at the uniform velocity ground 2~3 times, into uniform cream
Shape carries out 2~4 times sand millings to fine and smooth paste putting into sand mill, environmental protection is made after high-speed stirred is uniformly mixed and refilters
PVC leaching modeling liquid.
Beneficial effects of the present invention are：Environment-friendly PVC leaching modeling liquid of the present invention is carried out scientific and reasonable using Novel environment-friendlymaterial material
The raw material of conventional Environmental Safety is used in formula by proportioning, and environment-friendly PVC leaching modeling liquid security obtained is good, and uniform coloring uses
Convenient, good economy performance manufactures at low cost, the potentiality having had, and environmentally protective few harm meets polycyclic aromatic hydrocarbons (PAH) inspection specification,
Polycyclic aromatic hydrocarbons (PAH) is not detected, meets environmental requirement, and environment-friendly PVC leaching modeling liquid of the present invention can be widely used for medical treatment, health and food etc.
Field.
Description of the drawings
Fig. 1 is the raw material proportioning table of environment-friendly PVC leaching modeling liquid of the present invention.
Specific embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work
Embodiment belongs to the scope of protection of the invention.
Embodiment 1
Refering to Figure 1, the technical solution adopted by the present invention is：A kind of environment-friendly PVC leaching modeling liquid, the environment-friendly PVC leaching
Modeling liquid includes following raw material：42 parts of PVC resin powder, 23 parts of PVC paste resin, 34 parts of pigment, 15 parts of butyl rubber powder, rubber
18 parts of oil, 11 parts of silicon virgin rubber, 13 parts of vinyl silica gel oil, 8 parts of lightweight nano-calcium carbonate, 9 parts of nano zine oxide, newborn 7 parts of virgin rubber,
46 parts of 18 parts of three palm ester of citric acid, 3 parts of organic stabilizer and ionic liquid.
Wherein, 1 part of γ-FeO (OH), ZnCO are also added in the environment-friendly PVC leaching modeling liquid3And FeTiO3-MgTiO3's
Mixture, wherein, γ-FeO (OH), ZnCO3And FeTiO3-MgTiO3Adding proportion be 3:2:1.
Wherein, 2 parts of thinner is also added in the environment-friendly PVC leaching modeling liquid, wherein, thinner is the hydrocarbon drop of Porous deproteinized bone
Stick.
Wherein, 11 parts of pearly-lustre mill base is also added in the environment-friendly PVC leaching modeling liquid.
Wherein, the pigment that environment-friendly PVC leaching modeling liquid uses for phthalocyanine is red, phthalocyanine basket, phthalocyanine green, everbright fast red, big point
Son is red, macromolecular is yellow, the one or several kinds in permanent bordeaux and azophloxine.
Wherein, the organic stabilizer is the mixing of the organic calcium-zinc composite stabilizing agent of paste and organotin antimony compound stabilizer
Object.
Wherein, 2 parts of antifoaming agent is also added in the environment-friendly PVC leaching modeling liquid.
Wherein, 3 parts of fungicide is also added in the environment-friendly PVC leaching modeling liquid.
Embodiment 2
Refering to Figure 1, the technical solution adopted by the present invention is：A kind of environment-friendly PVC leaching modeling liquid, the environment-friendly PVC leaching
Modeling liquid includes following raw material：37 parts of PVC resin powder, 32 parts of PVC paste resin, 25 parts of pigment, 23 parts of butyl rubber powder, rubber
12 parts of oil, 15 parts of silicon virgin rubber, 9 parts of vinyl silica gel oil, 15 parts of lightweight nano-calcium carbonate, 5 parts of nano zine oxide, newborn virgin rubber 14
Part, 7 parts of three palm ester of citric acid, 5 parts of organic stabilizer and 30 parts of ionic liquid.
Wherein, 2 parts of γ-FeO (OH), ZnCO are also added in the environment-friendly PVC leaching modeling liquid3And FeTiO3-MgTiO3's
Mixture, wherein, γ-FeO (OH), ZnCO3And FeTiO3-MgTiO3Adding proportion be 2:2:1.
Wherein, 4 parts of thinner is also added in the environment-friendly PVC leaching modeling liquid, wherein, thinner is the hydrocarbon drop of Porous deproteinized bone
Stick.
Wherein, 8 parts of pearly-lustre mill base is also added in the environment-friendly PVC leaching modeling liquid.
Wherein, the pigment that environment-friendly PVC leaching modeling liquid uses for phthalocyanine is red, phthalocyanine basket, phthalocyanine green, everbright fast red, big point
Son is red, macromolecular is yellow, the one or several kinds in permanent bordeaux and azophloxine.
Wherein, the organic stabilizer is the mixing of the organic calcium-zinc composite stabilizing agent of paste and organotin antimony compound stabilizer
Object.
Wherein, 5 parts of antifoaming agent is also added in the environment-friendly PVC leaching modeling liquid.
Wherein, 2 parts of fungicide is also added in the environment-friendly PVC leaching modeling liquid.
Embodiment 3
Refering to Figure 1, the technical solution adopted by the present invention is：A kind of environment-friendly PVC leaching modeling liquid, the environment-friendly PVC leaching
Modeling liquid includes following raw material：42 parts of PVC resin powder, 32 parts of PVC paste resin, 34 parts of pigment, 23 parts of butyl rubber powder, rubber
18 parts of oil, 5 parts of silicon virgin rubber, 13 parts of vinyl silica gel oil, 15 parts of lightweight nano-calcium carbonate, 9 parts of nano zine oxide, newborn virgin rubber 14
Part, 18 parts of three palm ester of citric acid, 5 parts of organic stabilizer and 46 parts of ionic liquid.
Wherein, 2 parts of γ-FeO (OH), ZnCO are also added in the environment-friendly PVC leaching modeling liquid3And FeTiO3-MgTiO3's
Mixture, wherein, γ-FeO (OH), ZnCO3And FeTiO3-MgTiO3Adding proportion be 3:2:3.
Wherein, 4 parts of thinner is also added in the environment-friendly PVC leaching modeling liquid, wherein, thinner is the hydrocarbon drop of Porous deproteinized bone
Stick.
Wherein, 11 parts of pearly-lustre mill base is also added in the environment-friendly PVC leaching modeling liquid.
Wherein, the pigment that environment-friendly PVC leaching modeling liquid uses for phthalocyanine is red, phthalocyanine basket, phthalocyanine green, everbright fast red, big point
Son is red, macromolecular is yellow, the one or several kinds in permanent bordeaux and azophloxine.
Wherein, the organic stabilizer is the mixing of the organic calcium-zinc composite stabilizing agent of paste and organotin antimony compound stabilizer
Object.
Wherein, 5 parts of antifoaming agent is also added in the environment-friendly PVC leaching modeling liquid.
Wherein, 3 parts of fungicide is also added in the environment-friendly PVC leaching modeling liquid.
Embodiment 4
Refering to Figure 1, the technical solution adopted by the present invention is：A kind of environment-friendly PVC leaching modeling liquid, the environment-friendly PVC leaching
Modeling liquid includes following raw material：37 parts of PVC resin powder, 23 parts of PVC paste resin, 25 parts of pigment, 15 parts of butyl rubber powder, rubber
12 parts of oil, 11 parts of silicon virgin rubber, 9 parts of vinyl silica gel oil, 8 parts of lightweight nano-calcium carbonate, 5 parts of nano zine oxide, newborn 7 parts of virgin rubber,
30 parts of 7 parts of three palm ester of citric acid, 3 parts of organic stabilizer and ionic liquid.
Wherein, 1 part of γ-FeO (OH), ZnCO are also added in the environment-friendly PVC leaching modeling liquid3And FeTiO3-MgTiO3's
Mixture, wherein, γ-FeO (OH), ZnCO3And FeTiO3-MgTiO3Adding proportion be 2:1:1.
Wherein, 2 parts of thinner is also added in the environment-friendly PVC leaching modeling liquid, wherein, thinner is the hydrocarbon drop of Porous deproteinized bone
Stick.
Wherein, 8 parts of pearly-lustre mill base is also added in the environment-friendly PVC leaching modeling liquid.
Wherein, the pigment that environment-friendly PVC leaching modeling liquid uses for phthalocyanine is red, phthalocyanine basket, phthalocyanine green, everbright fast red, big point
Son is red, macromolecular is yellow, the one or several kinds in permanent bordeaux and azophloxine.
Wherein, the organic stabilizer is the mixing of the organic calcium-zinc composite stabilizing agent of paste and organotin antimony compound stabilizer
Object.
Wherein, 2 parts of antifoaming agent is also added in the environment-friendly PVC leaching modeling liquid.
Wherein, 2 parts of fungicide is also added in the environment-friendly PVC leaching modeling liquid.
Refering to Figure 1, the technical solution adopted by the present invention is：A kind of environment-friendly PVC leaching modeling liquid, the environment-friendly PVC leaching
The manufacturing process of modeling liquid comprises the following steps：
1) is just mixed：By rubber oil, silicon virgin rubber, vinyl silica gel oil, newborn virgin rubber, three palm ester of citric acid, organic stabilizers
Agent, ionic liquid and antifoaming agent are added in stirred tank together, with the rotating speed high-speed stirred 3h of 3000r/min, until material is all complete
Merge and be uniformly mixed entirely, keep 0.01MPa vacuum degree continue stir 5h obtain leaching mould liquid expect in vain；
2) mixes colours：By the dissolving of pigment, 60% glycerine, PVC environmental protection mill base and pearl powder in deionized water, at 150 DEG C
At a temperature of stir material and be uniformly mixed to thick, add remaining glycerine, then the rotating speed moderate-speed mixer with 2500r/min
It is uniformly mixed to material；
3) bis- mixing of：Thinner, γ-FeO will be added in the dispersed material mixed in step 1 while stirring
(OH)、ZnCO3、FeTiO3-MgTiO3The pigment that step 2 mixes up is added in after being uniformly dispersed with fungicide, then with 3000r/min's
Rotating speed is stirred 6h, then is transferred in three-roll grinder；
4) is ground：Scattered material is transferred in three-roll grinder, is at the uniform velocity ground 3 times, into uniform paste,
4 times sand millings are carried out to fine and smooth paste putting into sand mill, and environment-friendly PVC leaching modeling is made after high-speed stirred is uniformly mixed and refilters
Liquid.
In the present invention, environment-friendly PVC leaching modeling liquid of the present invention carries out scientific and reasonable proportioning using Novel environment-friendlymaterial material, will be normal
The raw material for advising Environmental Safety is used in formula, and environment-friendly PVC leaching modeling liquid security obtained is good, and uniform coloring is easy to use, economical
Property it is good, manufacture at low cost, the potentiality having had, environmentally protective few harm meets polycyclic aromatic hydrocarbons (PAH) inspection specification, do not detect polycyclic
Aromatic hydrocarbon, meets environmental requirement, and environment-friendly PVC leaching modeling liquid of the present invention can be widely used for the fields such as medical treatment, health and food.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (9)
1. a kind of environment-friendly PVC leaching modeling liquid, it is characterised in that：The environment-friendly PVC leaching modeling liquid includes following raw material：Polyvinyl chloride resin
37~42 parts of powder, 23~32 parts of PVC paste resin, 25~34 parts of pigment, 15~23 parts of butyl rubber powder, 12~18 parts of rubber oil,
11~15 parts of silicon virgin rubber, 9~13 parts of vinyl silica gel oil, 8~15 parts of lightweight nano-calcium carbonate, 5~9 parts of nano zine oxide, breast
30~46 parts of 7~14 parts of virgin rubber, 7~18 parts of three palm ester of citric acid, 3~5 parts of organic stabilizer and ionic liquid.
2. a kind of environment-friendly PVC leaching modeling liquid according to claim 1, it is characterised in that：Also add in the environment-friendly PVC leaching modeling liquid
Added with 1~2 part of γ-FeO (OH), ZnCO3And FeTiO3-MgTiO3Mixture, wherein, γ-FeO (OH), ZnCO3With
FeTiO3-MgTiO3Adding proportion be 2~3:1~2:1~3.
3. a kind of environment-friendly PVC leaching modeling liquid according to claim 1, it is characterised in that：Also add in the environment-friendly PVC leaching modeling liquid
Added with 2~4 parts of thinner, wherein, thinner is the hydrocarbon thinner of Porous deproteinized bone.
4. a kind of environment-friendly PVC leaching modeling liquid according to claim 1, it is characterised in that：Also add in the environment-friendly PVC leaching modeling liquid
Added with 8~11 parts of pearly-lustre mill base.
5. a kind of environment-friendly PVC leaching modeling liquid according to claim 1, it is characterised in that：What the environment-friendly PVC leaching modeling liquid used
Pigment is phthalocyanine is red, phthalocyanine basket, phthalocyanine green, everbright fast red, macromolecular is red, macromolecular is yellow, one kind in permanent bordeaux and azophloxine
It is or several.
6. a kind of environment-friendly PVC leaching modeling liquid according to claim 1, it is characterised in that：The organic stabilizer has for paste
The mixture of machine calcium-zinc composite stabilizing agent and organotin antimony compound stabilizer.
7. a kind of environment-friendly PVC leaching modeling liquid according to claim 1, it is characterised in that：Also add in the environment-friendly PVC leaching modeling liquid
Added with 2~5 parts of antifoaming agent.
8. a kind of environment-friendly PVC leaching modeling liquid according to claim 1, it is characterised in that：Also add in the environment-friendly PVC leaching modeling liquid
Added with 2~3 parts of fungicide.
9. a kind of environment-friendly PVC leaching modeling liquid according to claim 1, it is characterised in that：The manufacture of the environment-friendly PVC leaching modeling liquid
Technique comprises the following steps：
1) is just mixed：By rubber oil, silicon virgin rubber, vinyl silica gel oil, newborn virgin rubber, three palm ester of citric acid, organic stabilizer, from
Sub- liquid and antifoaming agent are added in stirred tank together, with rotating speed 1~3h of high-speed stirred of 2000~3000r/min, until material is complete
Portion merges and is uniformly mixed completely, keep 0.01~0.1MPa vacuum degree continue 2~5h of stirring obtain leaching mould liquid expect in vain；
2) mixes colours：By the dissolving of pigment, 45~60% glycerine, PVC environmental protection mill base and pearl powder in deionized water, 120~
Material is stirred at a temperature of 150 DEG C to be uniformly mixed to thick, adds remaining glycerine, then with 1500~2500r/min's
Rotating speed moderate-speed mixer to material is uniformly mixed；
3) bis- mixing of：To while stirring be added in the dispersed material mixed in step 1 thinner, γ-FeO (OH),
ZnCO3、FeTiO3-MgTiO3The pigment that step 2 mixes up is added in after being uniformly dispersed with fungicide, then with 2500~3000r/min's
Rotating speed is stirred 3~6h, then is transferred in three-roll grinder；
4) is ground：Scattered material is transferred in three-roll grinder, is at the uniform velocity ground 2~3 times, into uniform paste,
It puts into sand mill and carries out 2~4 times sand millings to fine and smooth paste, environment-friendly PVC leaching is made after high-speed stirred is uniformly mixed and refilters
Mould liquid.