CN108084812A - A kind of preparation method of corrosion-resistant magnetic plant - Google Patents
A kind of preparation method of corrosion-resistant magnetic plant Download PDFInfo
- Publication number
- CN108084812A CN108084812A CN201711290800.1A CN201711290800A CN108084812A CN 108084812 A CN108084812 A CN 108084812A CN 201711290800 A CN201711290800 A CN 201711290800A CN 108084812 A CN108084812 A CN 108084812A
- Authority
- CN
- China
- Prior art keywords
- parts
- magnetic plant
- corrosion
- preparation
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of corrosion-resistant magnetic plant, including following operating procedure:(1)After the sulfuric acid solution that the surface sprinkling volume fraction of magnetic plant is 3% is carried out activation process, then wash with water clean;(2)By step(1)Liquid is adhered in the magnetic plant surface of processing on uniformly spraying;(3)23 it is small when after, in magnetic plant external coating corrosion resistant coating.The preparation method of corrosion-resistant magnetic plant provided by the invention, operating process is environmentally protective, non-hazardous to environment and human body, magnetic plant obtained, and surface has excellent resistance to oxidation, corrosion resistance, greatly extends the service life of magnetic plant.
Description
Technical field
The invention belongs to magnetic plant manufacturing technology fields, and in particular to a kind of preparation method of corrosion-resistant magnetic plant.
Background technology
Magnetic plant refers to the magnetic characteristic according to material, will contain magnetic material from other materials using magnetic apparatus
It is separated in material, the plant machinery for carrying out this operation is just magnetic plant, is typically used as the magnetic mineral products such as magnetic iron ore
Production screening.Magnetic plant often needs to contact with corrosive substance with some, the shell on surface, using common painting
Material, anticorrosion effect is poor, therefore serious corrosion phenomenon often occurs for the shell of magnetic plant.
The content of the invention
In order to solve the above technical problem, the present invention provides a kind of preparation methods of corrosion-resistant magnetic plant.
The present invention is achieved by the following technical solutions.
A kind of preparation method of corrosion-resistant magnetic plant, including following operating procedure:
(1)After the sulfuric acid solution that the surface sprinkling volume fraction of magnetic plant is 3% is carried out activation process, then wash with water
Totally;
(2)By step(1)Liquid is adhered in the magnetic plant surface of processing on uniformly spraying, wherein attachment liquid is by following weight
The component of part is made:11-17 parts of Polyethylenimine, 1-2 parts of dipotassium glycyrrhizinate, 3-6 parts of lithium chloride, 360-400 parts of water;
(3)After when 2-3 is small, in magnetic plant external coating corrosion resistant coating, wherein corrosion resistant coating by following parts by weight group
Divide and be made:45-52 parts of styrene-acrylic emulsion, 1-2 parts of triisopropanolamine, 3-6 parts of o-methyl-benzene sulfonamide, 11-15 parts of ammonium pentaborate, cunning
12-15 parts of mountain flour, 10-14 parts of titanium dioxide.
Specifically, above-mentioned steps(1)In, the fountain height of sulfuric acid solution is 150-200ml/m2。
Specifically, above-mentioned steps(2)In, adhere to the fountain height 280-310ml/m of liquid2。
Specifically, above-mentioned steps(3)In, the brushing amount of corrosion resistant coating is 300-350g/m2。
Specifically, the Average Particle Diameters of above-mentioned talcum powder and titanium dioxide are 550-600 mesh.
From the above technical scheme, it can be seen that the beneficial effects of the invention are as follows:
The preparation method of corrosion-resistant magnetic plant provided by the invention, operating process is environmentally protective, non-hazardous to environment and human body,
Magnetic plant obtained, surface have excellent resistance to oxidation, corrosion resistance, and greatly extend magnetic plant uses the longevity
Life.Wherein, first by magnetic plant using sulfuric acid activated, the effect of attachment liquid can be enhanced so that attachment liquid effect it is uniform
Property and depth are more excellent, attachment liquid provided by the invention, can effectively enhance the adhesive force of corrosion resistant coating so that it is not easy
The phenomenon that falling off and crack in the high environment of high temperature and low temperature or humidity;Corrosion resistant coating provided by the invention, tool
There is excellent corrosion resistance, surface is not susceptible to electrochemical reaction.
Specific embodiment
Following embodiment cannot be used for limiting the scope of the invention for illustrating the present invention.The reality used in embodiment
The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
A kind of preparation method of corrosion-resistant magnetic plant, including following operating procedure:
(1)After the sulfuric acid solution that the surface sprinkling volume fraction of magnetic plant is 3% is carried out activation process, then wash with water
Totally;
(2)By step(1)Liquid is adhered in the magnetic plant surface of processing on uniformly spraying, wherein attachment liquid is by following weight
The component of part is made:11 parts of Polyethylenimine, 1 part of dipotassium glycyrrhizinate, 3 parts of lithium chloride, 360 parts of water;
(3)2 it is small when after, in magnetic plant external coating corrosion resistant coating, wherein corrosion resistant coating by following parts by weight component
It is made:45 parts of styrene-acrylic emulsion, 1 part of triisopropanolamine, 3 parts of o-methyl-benzene sulfonamide, 11 parts of ammonium pentaborate, 12 parts of talcum powder, titanium
10 parts of white powder.
Specifically, above-mentioned steps(1)In, the fountain height of sulfuric acid solution is 150ml/m2。
Specifically, above-mentioned steps(2)In, adhere to the fountain height 280ml/m of liquid2。
Specifically, above-mentioned steps(3)In, the brushing amount of corrosion resistant coating is 300g/m2。
Specifically, the Average Particle Diameters of above-mentioned talcum powder and titanium dioxide are 550 mesh.
Embodiment 2
A kind of preparation method of corrosion-resistant magnetic plant, including following operating procedure:
(1)After the sulfuric acid solution that the surface sprinkling volume fraction of magnetic plant is 3% is carried out activation process, then wash with water
Totally;
(2)By step(1)Liquid is adhered in the magnetic plant surface of processing on uniformly spraying, wherein attachment liquid is by following weight
The component of part is made:13 parts of Polyethylenimine, 1 part of dipotassium glycyrrhizinate, 5 parts of lithium chloride, 380 parts of water;
(3)2.5 it is small when after, in magnetic plant external coating corrosion resistant coating, wherein corrosion resistant coating by following parts by weight group
Divide and be made:48 parts of styrene-acrylic emulsion, 1 part of triisopropanolamine, 5 parts of o-methyl-benzene sulfonamide, 13 parts of ammonium pentaborate, 14 parts of talcum powder,
12 parts of titanium dioxide.
Specifically, above-mentioned steps(1)In, the fountain height of sulfuric acid solution is 180ml/m2。
Specifically, above-mentioned steps(2)In, adhere to the fountain height 300ml/m of liquid2。
Specifically, above-mentioned steps(3)In, the brushing amount of corrosion resistant coating is 330g/m2。
Specifically, the Average Particle Diameters of above-mentioned talcum powder and titanium dioxide are 580 mesh.
Embodiment 3
A kind of preparation method of corrosion-resistant magnetic plant, including following operating procedure:
(1)After the sulfuric acid solution that the surface sprinkling volume fraction of magnetic plant is 3% is carried out activation process, then wash with water
Totally;
(2)By step(1)Liquid is adhered in the magnetic plant surface of processing on uniformly spraying, wherein attachment liquid is by following weight
The component of part is made:17 parts of Polyethylenimine, 2 parts of dipotassium glycyrrhizinate, 6 parts of lithium chloride, 400 parts of water;
(3)3 it is small when after, in magnetic plant external coating corrosion resistant coating, wherein corrosion resistant coating by following parts by weight component
It is made:52 parts of styrene-acrylic emulsion, 2 parts of triisopropanolamine, 6 parts of o-methyl-benzene sulfonamide, 15 parts of ammonium pentaborate, 15 parts of talcum powder, titanium
14 parts of white powder.
Specifically, above-mentioned steps(1)In, the fountain height of sulfuric acid solution is 200ml/m2。
Specifically, above-mentioned steps(2)In, adhere to the fountain height 310ml/m of liquid2。
Specifically, above-mentioned steps(3)In, the brushing amount of corrosion resistant coating is 350g/m2。
Specifically, the Average Particle Diameters of above-mentioned talcum powder and titanium dioxide are 600 mesh.
It should be appreciated that the application of the present invention is not limited to the above, it for those of ordinary skills, can
To be improved or converted according to the above description, all these modifications and variations should all belong to the guarantor of appended claims of the present invention
Protect scope.
Claims (5)
1. a kind of preparation method of corrosion-resistant magnetic plant, which is characterized in that including following operating procedure:
(1)After the sulfuric acid solution that the surface sprinkling volume fraction of magnetic plant is 3% is carried out activation process, then wash with water
Totally;
(2)By step(1)Liquid is adhered in the magnetic plant surface of processing on uniformly spraying, wherein attachment liquid is by following weight
The component of part is made:11-17 parts of Polyethylenimine, 1-2 parts of dipotassium glycyrrhizinate, 3-6 parts of lithium chloride, 360-400 parts of water;
(3)After when 2-3 is small, in magnetic plant external coating corrosion resistant coating, wherein corrosion resistant coating by following parts by weight group
Divide and be made:45-52 parts of styrene-acrylic emulsion, 1-2 parts of triisopropanolamine, 3-6 parts of o-methyl-benzene sulfonamide, 11-15 parts of ammonium pentaborate, cunning
12-15 parts of mountain flour, 10-14 parts of titanium dioxide.
A kind of 2. preparation method of corrosion-resistant magnetic plant according to claim 1, which is characterized in that above-mentioned steps(1)
In, the fountain height of sulfuric acid solution is 150-200ml/m2。
A kind of 3. preparation method of corrosion-resistant magnetic plant according to claim 1, which is characterized in that above-mentioned steps(2)
In, adhere to the fountain height 280-310ml/m of liquid2。
A kind of 4. preparation method of corrosion-resistant magnetic plant according to claim 1, which is characterized in that above-mentioned steps(3)
In, the brushing amount of corrosion resistant coating is 300-350g/m2。
5. a kind of preparation method of corrosion-resistant magnetic plant according to claim 1, which is characterized in that above-mentioned talcum powder and
The Average Particle Diameters of titanium dioxide are 550-600 mesh.