CN108083409A - A kind of waste water treating agent and preparation method thereof - Google Patents
A kind of waste water treating agent and preparation method thereof Download PDFInfo
- Publication number
- CN108083409A CN108083409A CN201711448143.9A CN201711448143A CN108083409A CN 108083409 A CN108083409 A CN 108083409A CN 201711448143 A CN201711448143 A CN 201711448143A CN 108083409 A CN108083409 A CN 108083409A
- Authority
- CN
- China
- Prior art keywords
- parts
- waste water
- treating agent
- water treating
- diopside
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of waste water treating agent, include the raw material of following parts by weight：11 25 parts of sepiolite powder, 59 parts of sodium metaaluminate, 10 16 parts of ginger extract, 4 10 parts of waterglass, 5 10 parts of ball strepaster ball algae, 25 parts of edible seaweed powder, 36 parts of animal skin glue, 48 parts of white fused alumina micro mist, 36 parts of the herb mixtures tea dregs of rice, 26 parts of multi-vitamins, 25 parts of borax, 36 parts of erythrina bark, 48 parts of diopside, 25 parts of carbon black.The waste water treating agent of the present invention is to the Zn in heavy metal wastewater thereby2+、Cu2+、Pd2+、Cd2+, chromium, manganese have good removal effect, and have the advantages that it is environmentally friendly, energy saving, non-toxic, on operator without influence, handle after water non-secondary pollution；Preparation method is simple simultaneously, and raw material is easy to get, and cost is lower.
Description
Technical field
The present invention relates to wastewater treating technology fields, are specifically a kind of waste water treating agent and preparation method thereof.
Background technology
Water is Source of life, water pollution and the shortage of water resource, and people is forced to focus more on the protection of water resource, with
And the improvement to waste water.How waste water to be made to reach discharging standards, be current urgent problem to be solved.
What heavy metal wastewater thereby referred to discharge in the industrial processes such as mining and metallurgy, machine-building, chemical industry, electronics, instrument contains weight
The waste water of metal, heavy metal (such as containing cadmium, nickel, mercury, zinc) waste water are to an environmental pollution most serious and the mankind are endangered maximum
One of industrial wastewater, water quality and quantity is related with production technology, and the heavy metal in waste water cannot generally decompose destruction, Zhi Nengzhuan
It moves its existence position and changes its Material Form.
The processing method of heavy metal wastewater thereby is to reform production technology first at this stage, uses no or little the big huge sum of money of toxicity
Belong to, in production site, treatment in situ (if do not discharged workshop) is handled frequently with chemical precipitation method, ion-exchange etc.,
Heavy metal can discharge or reuse less than discharge standard in treated water, form new heavy metal enriched product and recycle profit as far as possible
With or be subject to harmless treatment.But the huge sum of money wastewater processing technology hysteresis in China at present, use common technique and traditional
Heavy metal containing wastewater treatment means can not effectively reduce the heavy metal ion content in waste water, and causing that treated, water cannot be sharp again
With, and cost for wastewater treatment is high.Therefore, the present invention provides a kind of waste water treating agent and preparation method thereof.
The content of the invention
It is an object of the invention to provide a kind of waste water treating agent and preparation method thereof, to solve to carry in above-mentioned background technology
The problem of going out.
To achieve the above object, the present invention provides following technical solution：
A kind of waste water treating agent includes the raw material of following parts by weight：11-25 parts of sepiolite powder, 5-9 parts of sodium metaaluminate, life
10-16 parts of ginger extracting solution, 4-10 parts of waterglass, 5-10 parts of ball strepaster ball algae, 2-5 parts of edible seaweed powder, 3-6 parts of animal skin glue, Bai Gang
Beautiful micro mist 4-8 parts, 3-6 parts of the herb mixtures tea dregs of rice, 2-6 parts of multi-vitamins, 2-5 parts of borax, 3-6 parts of erythrina bark, 4-8 parts of diopside, charcoal
It is 2-5 parts black.
As further embodiment of the present invention：Include the raw material of following parts by weight：21 parts of sepiolite powder, 7 parts of sodium metaaluminate,
13 parts of ginger extract, 8 parts of waterglass, 7 parts of ball strepaster ball algae, 4 parts of edible seaweed powder, 5 parts of animal skin glue, 6 parts of white fused alumina micro mist, hardship
5 parts of tea seed cake, 4 parts of multi-vitamins, 3 parts of borax, 4 parts of erythrina bark, 5 parts of diopside, 4 parts of carbon black.
As further embodiment of the present invention：Include the raw material of following parts by weight：14 parts of sepiolite powder, 8 parts of sodium metaaluminate,
11 parts of ginger extract, 9 parts of waterglass, 6 parts of ball strepaster ball algae, 3 parts of edible seaweed powder, 4 parts of animal skin glue, 5 parts of white fused alumina micro mist, hardship
4 parts of tea seed cake, 5 parts of multi-vitamins, 4 parts of borax, 5 parts of erythrina bark, 7 parts of diopside, 3 parts of carbon black.
As further embodiment of the present invention：The diopside, erythrina bark, carbon black, the grain size of borax are 100-250
Mesh.
A kind of preparation method of waste water treating agent, comprises the following steps：(1) according to parts by weight weigh sepiolite powder, partially
Sodium aluminate, ginger extract, waterglass, ball strepaster ball algae, edible seaweed powder, animal skin glue, white fused alumina micro mist, the herb mixtures tea dregs of rice, compound dimension
Raw element, borax, erythrina bark, diopside and carbon black, it is spare；(2) sepiolite powder, white fused alumina micro mist, diopside and carbon black are mixed,
15-35min is mixed at 100-200 DEG C；(3) multi-vitamins, ginger extract, waterglass and the herb mixtures tea dregs of rice are mixed,
After being stirred 5-10min at 30-42 DEG C, 100-125 DEG C is warming up to, stirs 10-20min, dried at 100-150 DEG C,
It is ground up, sieved 80-120 mesh；(4) sodium metaaluminate, animal skin glue, borax and step (1) gains and step (2) gains are mixed
It closes, 25-45min is stirred under 200-350r/min rotating speeds, erythrina bark, ball strepaster ball algae and edible seaweed powder are then added in, in 200-
1-2h is stirred under 350r/min rotating speeds to get finished product.
As further embodiment of the present invention：Step (2) mixes sepiolite powder, white fused alumina micro mist, diopside and carbon black,
22min is mixed at 160 DEG C.
As further embodiment of the present invention：Step (3) is by multi-vitamins, ginger extract, waterglass and the herb mixtures tea dregs of rice
Mixing after being stirred 7min at 38 DEG C, is warming up to 112 DEG C, stirs 16min, dried at 135 DEG C, be ground up, sieved 100
Mesh.
As further embodiment of the present invention：Step (4) is by sodium metaaluminate, animal skin glue, borax and step (1) gains
It is mixed with step (2) gains, 30min is stirred under 280r/min rotating speeds, then add in erythrina bark, ball strepaster ball algae and edible seaweed
Powder stirs 1.4h to get finished product under 285r/min rotating speeds.
Compared with prior art, the beneficial effects of the invention are as follows：
The waste water treating agent of the present invention is to the Zn in heavy metal wastewater thereby2+、Cu2+、Pd2+、Cd2+, chromium, manganese has and good goes
Except effect, and have the advantages that it is environmentally friendly, energy saving, non-toxic, on operator without influence, processing after water non-secondary pollution；Simultaneously
Preparation method is simple, and raw material is easy to get, and cost is lower.
Specific embodiment
The technical solution of this patent is described in more detail With reference to embodiment.
Embodiment 1
A kind of waste water treating agent includes the raw material of following parts by weight：11 parts of sepiolite powder, 5 parts of sodium metaaluminate, ginger extraction
10 parts of liquid, 4 parts of waterglass, 5 parts of ball strepaster ball algae, 2 parts of edible seaweed powder, 3 parts of animal skin glue, 4 parts of white fused alumina micro mist, 3 parts of the herb mixtures tea dregs of rice,
2 parts of multi-vitamins, 2 parts of borax, 3 parts of erythrina bark, 4 parts of diopside, 2 parts of carbon black.The diopside, erythrina bark, carbon black, borax
Grain size be 100 mesh.
A kind of preparation method of waste water treating agent, comprises the following steps：(1) according to parts by weight weigh sepiolite powder, partially
Sodium aluminate, ginger extract, waterglass, ball strepaster ball algae, edible seaweed powder, animal skin glue, white fused alumina micro mist, the herb mixtures tea dregs of rice, compound dimension
Raw element, borax, erythrina bark, diopside and carbon black, it is spare；(2) sepiolite powder, white fused alumina micro mist, diopside and carbon black are mixed,
15min is mixed at 100 DEG C；(3) multi-vitamins, ginger extract, waterglass and the herb mixtures tea dregs of rice are mixed, at 30 DEG C
After being stirred 5min, 100 DEG C are warming up to, 10min is stirred, is dried at 100 DEG C, is ground up, sieved 80 mesh；(4) by meta-aluminic acid
Sodium, animal skin glue, borax are mixed with step (1) gains and step (2) gains, and 25min is stirred under 200r/min rotating speeds,
Then erythrina bark, ball strepaster ball algae and edible seaweed powder are added in, 1h is stirred under 200r/min rotating speeds to get finished product.
Embodiment 2
A kind of waste water treating agent includes the raw material of following parts by weight：25 parts of sepiolite powder, 9 parts of sodium metaaluminate, ginger extraction
16 parts of liquid, 10 parts of waterglass, 10 parts of ball strepaster ball algae, 5 parts of edible seaweed powder, 6 parts of animal skin glue, 8 parts of white fused alumina micro mist, the herb mixtures tea dregs of rice 6
Part, 6 parts of multi-vitamins, 5 parts of borax, 6 parts of erythrina bark, 8 parts of diopside, 5 parts of carbon black.The diopside, erythrina bark, carbon black,
The grain size of borax is 250 mesh.
A kind of preparation method of waste water treating agent, comprises the following steps：(1) according to parts by weight weigh sepiolite powder, partially
Sodium aluminate, ginger extract, waterglass, ball strepaster ball algae, edible seaweed powder, animal skin glue, white fused alumina micro mist, the herb mixtures tea dregs of rice, compound dimension
Raw element, borax, erythrina bark, diopside and carbon black, it is spare；(2) sepiolite powder, white fused alumina micro mist, diopside and carbon black are mixed,
35min is mixed at 200 DEG C；(3) multi-vitamins, ginger extract, waterglass and the herb mixtures tea dregs of rice are mixed, at 42 DEG C
After being stirred 10min, 125 DEG C are warming up to, 20min is stirred, is dried at 150 DEG C, is ground up, sieved 120 mesh；(4) by meta-aluminic acid
Sodium, animal skin glue, borax are mixed with step (1) gains and step (2) gains, and 45min is stirred under 350r/min rotating speeds,
Then erythrina bark, ball strepaster ball algae and edible seaweed powder are added in, 2h is stirred under 350r/min rotating speeds to get finished product.
Embodiment 3
A kind of waste water treating agent includes the raw material of following parts by weight：21 parts of sepiolite powder, 7 parts of sodium metaaluminate, ginger extraction
13 parts of liquid, 8 parts of waterglass, 7 parts of ball strepaster ball algae, 4 parts of edible seaweed powder, 5 parts of animal skin glue, 6 parts of white fused alumina micro mist, 5 parts of the herb mixtures tea dregs of rice,
4 parts of multi-vitamins, 3 parts of borax, 4 parts of erythrina bark, 5 parts of diopside, 4 parts of carbon black.The diopside, erythrina bark, carbon black, borax
Grain size be 150 mesh.
A kind of preparation method of waste water treating agent, comprises the following steps：(1) according to parts by weight weigh sepiolite powder, partially
Sodium aluminate, ginger extract, waterglass, ball strepaster ball algae, edible seaweed powder, animal skin glue, white fused alumina micro mist, the herb mixtures tea dregs of rice, compound dimension
Raw element, borax, erythrina bark, diopside and carbon black, it is spare；(2) sepiolite powder, white fused alumina micro mist, diopside and carbon black are mixed,
22min is mixed at 160 DEG C.(3) multi-vitamins, ginger extract, waterglass and the herb mixtures tea dregs of rice are mixed, at 38 DEG C
After being stirred 7min, 112 DEG C are warming up to, 16min is stirred, is dried at 135 DEG C, is ground up, sieved 100 mesh.(4) by meta-aluminic acid
Sodium, animal skin glue, borax are mixed with step (1) gains and step (2) gains, and 30min is stirred under 280r/min rotating speeds,
Then erythrina bark, ball strepaster ball algae and edible seaweed powder are added in, 1.4h is stirred under 285r/min rotating speeds to get finished product.
Embodiment 4
A kind of waste water treating agent includes the raw material of following parts by weight：14 parts of sepiolite powder, 8 parts of sodium metaaluminate, ginger extraction
11 parts of liquid, 9 parts of waterglass, 6 parts of ball strepaster ball algae, 3 parts of edible seaweed powder, 4 parts of animal skin glue, 5 parts of white fused alumina micro mist, 4 parts of the herb mixtures tea dregs of rice,
5 parts of multi-vitamins, 4 parts of borax, 5 parts of erythrina bark, 7 parts of diopside, 3 parts of carbon black.The diopside, erythrina bark, carbon black, borax
Grain size be 220 mesh.
A kind of preparation method of waste water treating agent, comprises the following steps：(1) according to parts by weight weigh sepiolite powder, partially
Sodium aluminate, ginger extract, waterglass, ball strepaster ball algae, edible seaweed powder, animal skin glue, white fused alumina micro mist, the herb mixtures tea dregs of rice, compound dimension
Raw element, borax, erythrina bark, diopside and carbon black, it is spare；(2) sepiolite powder, white fused alumina micro mist, diopside and carbon black are mixed,
18min is mixed at 115 DEG C；(3) multi-vitamins, ginger extract, waterglass and the herb mixtures tea dregs of rice are mixed, at 32 DEG C
After being stirred 7min, 120 DEG C are warming up to, 16min is stirred, is dried at 108 DEG C, is ground up, sieved 110 mesh；(4) by meta-aluminic acid
Sodium, animal skin glue, borax are mixed with step (1) gains and step (2) gains, and 36min is stirred under 310r/min rotating speeds,
Then erythrina bark, ball strepaster ball algae and edible seaweed powder are added in, 1.5h is stirred under 280r/min rotating speeds to get finished product.
Inorganic agent finished product 100mg/L prepared by Application Example 3 carries out heavy metal containing wastewater treatment, and treatment effect is as follows, single
Position (mg/L)：
| Project | COD | SS | Zn2+ | Cu2+ | Pd2+ | Cd2+ | Chromium | Manganese | pH |
| Water sample | 285 | 201 | 76 | 95 | 7.2 | 58 | 13 | 8 | 5.5 |
| Embodiment 3 | 36 | 15.8 | 1.59 | 2.2 | 1.8 | 6.58 | 1.35 | 1.002 | 6.5 |
As can be known from the above table, waste water treating agent of the invention is to the Zn in heavy metal wastewater thereby2+、Cu2+、Pd2+、Cd2+, chromium, manganese tool
There is good removal effect；The present invention have it is environmentally friendly, energy saving, non-toxic, on operator without influence, handle after water without secondary dirt
The advantages of dye；Preparation method is simple, and raw material is easy to get, and cost is lower.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, can also be on the premise of this patent objective not be departed from the knowledge that one skilled in the relevant art possesses
It makes a variety of changes.
Claims (8)
1. a kind of waste water treating agent, which is characterized in that include the raw material of following parts by weight：11-25 parts of sepiolite powder, sodium metaaluminate
5-9 parts, 10-16 parts of ginger extract, 4-10 parts of waterglass, 5-10 parts of ball strepaster ball algae, 2-5 parts of edible seaweed powder, animal skin glue 3-6
Part, 4-8 parts of white fused alumina micro mist, 3-6 parts of the herb mixtures tea dregs of rice, 2-6 parts of multi-vitamins, 2-5 parts of borax, 3-6 parts of erythrina bark, diopside 4-
8 parts, 2-5 parts of carbon black.
2. waste water treating agent according to claim 1, which is characterized in that include the raw material of following parts by weight：Sepiolite powder
21 parts, 7 parts of sodium metaaluminate, 13 parts of ginger extract, 8 parts of waterglass, 7 parts of ball strepaster ball algae, 4 parts of edible seaweed powder, animal skin glue 5
Part, 6 parts of white fused alumina micro mist, 5 parts of the herb mixtures tea dregs of rice, 4 parts of multi-vitamins, 3 parts of borax, 4 parts of erythrina bark, 5 parts of diopside, 4 parts of carbon black.
3. waste water treating agent according to claim 1, which is characterized in that include the raw material of following parts by weight：Sepiolite powder
14 parts, 8 parts of sodium metaaluminate, 11 parts of ginger extract, 9 parts of waterglass, 6 parts of ball strepaster ball algae, 3 parts of edible seaweed powder, animal skin glue 4
Part, 5 parts of white fused alumina micro mist, 4 parts of the herb mixtures tea dregs of rice, 5 parts of multi-vitamins, 4 parts of borax, 5 parts of erythrina bark, 7 parts of diopside, 3 parts of carbon black.
4. waste water treating agent according to claim 1, which is characterized in that the diopside, erythrina bark, carbon black, borax
Grain size is 100-250 mesh.
5. the preparation method of a kind of waste water treating agent as described in claim 1-4 is any, which is characterized in that including following step
Suddenly：（1）According to parts by weight weigh sepiolite powder, sodium metaaluminate, ginger extract, waterglass, ball strepaster ball algae, edible seaweed powder,
Animal skin glue, white fused alumina micro mist, the herb mixtures tea dregs of rice, multi-vitamins, borax, erythrina bark, diopside and carbon black, it is spare；（2）By Hai Pao
Mountain flour, white fused alumina micro mist, diopside and carbon black mixing, 15-35min is mixed at 100-200 DEG C；（3）Compound dimension is given birth to
Element, ginger extract, waterglass and the mixing of the herb mixtures tea dregs of rice, after being stirred 5-10min at 30-42 DEG C, are warming up to 100-125
DEG C, 10-20min is stirred, dried at 100-150 DEG C, be ground up, sieved 80-120 mesh；（4）By sodium metaaluminate, animal skin glue, boron
Sand and step（1）Gains and step（2）Gains mix, and 25-45min, Ran Houjia are stirred under 200-350r/min rotating speeds
Enter erythrina bark, ball strepaster ball algae and edible seaweed powder, 1-2h is stirred under 200-350r/min rotating speeds to get finished product.
6. the preparation method of waste water treating agent according to claim 5, which is characterized in that step（2）By sepiolite powder, in vain
Corundum powder, diopside and carbon black mixing, 22min is mixed at 160 DEG C.
7. the preparation method of waste water treating agent according to claim 5, which is characterized in that step（3）By multi-vitamins,
Ginger extract, waterglass and the mixing of the herb mixtures tea dregs of rice, after being stirred 7min at 38 DEG C, are warming up to 112 DEG C, stir 16min,
It dried at 135 DEG C, be ground up, sieved 100 mesh.
8. the preparation method of waste water treating agent according to claim 5, which is characterized in that step（4）By sodium metaaluminate, move
Object hide glue, borax and step（1）Gains and step（2）Gains mix, and 30min are stirred under 280r/min rotating speeds, then
Erythrina bark, ball strepaster ball algae and edible seaweed powder are added in, 1.4h is stirred under 285r/min rotating speeds to get finished product.