CN108070747A - A kind of high performance vanadium strontium alloy - Google Patents
A kind of high performance vanadium strontium alloy Download PDFInfo
- Publication number
- CN108070747A CN108070747A CN201611019623.9A CN201611019623A CN108070747A CN 108070747 A CN108070747 A CN 108070747A CN 201611019623 A CN201611019623 A CN 201611019623A CN 108070747 A CN108070747 A CN 108070747A
- Authority
- CN
- China
- Prior art keywords
- parts
- high performance
- strontium alloy
- mass fraction
- following component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of high performance vanadium strontium alloys, are mainly made of the following component counted with mass fraction:8.08 parts of V6.8,20.5 parts of Sr10.5,35.5 parts of Mg20,56 parts of Al35,0.15 part of Sc0.05,1.2 parts of Mn0.5,2.5 parts of Fe0.5,0.06 part of C0.04,0.06 part of Ce0.02,1.8 parts of Zn0.6,0.3 part of Ti0.1,3.0 parts of Cu0.5.The vanadium strontium alloy of the present invention has that smelting temperature is low, tensile property is good and high radiopaque excellent properties.
Description
Technical field
The present invention relates to strontium alloy technical field more particularly to a kind of high performance vanadium strontium alloys.
Background technology
Vanadium strontium alloy can integrate strontium metal high temperature resistance and vanadium metal be not easy to be aoxidized, acid-proof alkaline it is good
Feature so that the alloy of preparation possesses good performance.
The content of the invention
In order to solve the above-mentioned technical problem, a kind of high temperature resistant, the vanadium strontium alloy of acid and alkali-resistance are provided, the present invention provides following skill
Art scheme:
A kind of high performance vanadium strontium alloy, is made of the following component counted with mass fraction:V6.8-8.08 parts, Sr10.5-
20.5 parts, Mg20-35.5 parts, Al35-56 parts, Sc0.05-0.15 parts, Mn0.5-1.2 parts, Fe0.5-2.5 parts, C0.04-0.06
Part, Ce0.02-0.06 parts, Zn0.6-1.8 parts, Ti0.1-0.3 parts, Cu0.5-3.0 parts.
Further, it is made of the following component counted with mass fraction:V7.8 parts, Sr15.5 parts, Mg27.5 parts, Al45.5
Part, Sc0.15 parts, Mn0.85 parts, Fe1.5 parts, C0.05 parts, Ce0.04 parts, Zn1.2 parts, Ti0.2 parts, Cu1.75 parts.
Further, it is made of the following component counted with mass fraction:V6.8 parts, Sr10.5 parts, Mg20 parts, Al35 parts,
Sc0.05 parts, Mn0.5 parts, Fe0.5 parts, C0.04 parts, Ce0.02 parts, Zn0.6 parts, Ti0.1 parts, Cu0.5 parts.
Further, it is made of the following component counted with mass fraction:V8.08 parts, Sr20.5 parts, Mg35.5 parts, Al56
Part, Sc0.15 parts, Mn1.2 parts, Fe2.5 parts, C0.06 parts, Ce0.06 parts, Zn1.8 parts, Ti0.3 parts, Cu3.0 parts.
The beneficial effects of the present invention are:With smelting temperature is low, tensile property is good and high radiopaque superiority
Can, and alloy surface oxidation resistance and acid-alkali-corrosive-resisting is very competent.
Specific embodiment
Embodiment 1,
A kind of high performance vanadium strontium alloy, is made of the following component counted with mass fraction:V7.8 parts, Sr15.5 parts,
Mg27.5 parts, Al45.5 parts, Sc0.15 parts, Mn0.85 parts, Fe1.5 parts, C0.05 parts, Ce0.04 parts, Zn1.2 parts, Ti0.2 parts,
Cu1.75 parts.
Embodiment 2,
A kind of high performance vanadium strontium alloy, is made of the following component counted with mass fraction:V6.8 parts, Sr10.5 parts, Mg20
Part, Al35 parts, Sc0.05 parts, Mn0.5 parts, Fe0.5 parts, C0.04 parts, Ce0.02 parts, Zn0.6 parts, Ti0.1 parts, Cu0.5 parts.
Embodiment 3,
A kind of high performance vanadium strontium alloy, is made of the following component counted with mass fraction:V8.08 parts, Sr20.5 parts,
Mg35.5 parts, Al56 parts, Sc0.15 parts, Mn1.2 parts, Fe2.5 parts, C0.06 parts, Ce0.06 parts, Zn1.8 parts, Ti0.3 parts,
Cu3.0 parts.
Using above-mentioned foundation desirable embodiment of the present invention as enlightenment, by above-mentioned description, relevant staff is complete
Can various changes and amendments be carried out without departing from the scope of the technological thought of the present invention'.This invention it is technical
Scope is not limited to the content on specification, it is necessary to determine its technical scope according to right.
Claims (4)
1. a kind of high performance vanadium strontium alloy, which is characterized in that be made of the following component counted with mass fraction:V6.8-8.08 parts,
Sr10.5-20.5 parts, Mg20-35.5 parts, Al35-56 parts, Sc0.05-0.15 parts, Mn0.5-1.2 parts, Fe0.5-2.5 parts,
C0.04-0.06 parts, Ce0.02-0.06 parts, Zn0.6-1.8 parts, Ti0.1-0.3 parts, Cu0.5-3.0 parts.
2. a kind of high performance vanadium strontium alloy as described in claim 1, which is characterized in that by the following component in terms of mass fraction
Composition:V7.8 parts, Sr15.5 parts, Mg27.5 parts, Al45.5 parts, Sc0.15 parts, Mn0.85 parts, Fe1.5 parts, C0.05 parts,
Ce0.04 parts, Zn1.2 parts, Ti0.2 parts, Cu1.75 parts.
3. a kind of high performance vanadium strontium alloy as described in claim 1, which is characterized in that by the following component in terms of mass fraction
Composition:V6.8 parts, Sr10.5 parts, Mg20 parts, Al35 parts, Sc0.05 parts, Mn0.5 parts, Fe0.5 parts, C0.04 parts, Ce0.02 parts,
Zn0.6 parts, Ti0.1 parts, Cu0.5 parts.
4. a kind of high performance vanadium strontium alloy as claimed in claim, which is characterized in that by the following component in terms of mass fraction
Composition:V8.08 parts, Sr20.5 parts, Mg35.5 parts, Al56 parts, Sc0.15 parts, Mn1.2 parts, Fe2.5 parts, C0.06 parts, Ce0.06
Part, Zn1.8 parts, Ti0.3 parts, Cu3.0 parts.