CN108067408A - A kind of preparation method of resistant container bag - Google Patents
A kind of preparation method of resistant container bag Download PDFInfo
- Publication number
- CN108067408A CN108067408A CN201711264719.6A CN201711264719A CN108067408A CN 108067408 A CN108067408 A CN 108067408A CN 201711264719 A CN201711264719 A CN 201711264719A CN 108067408 A CN108067408 A CN 108067408A
- Authority
- CN
- China
- Prior art keywords
- parts
- container bag
- preparation
- liquid
- resistant container
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of resistant container bag, including following operating procedure：（1）The container bag of knitting forming is added in modification liquid, when abundant immersion treatment 23 is small, wherein modification liquid is made of the component of following parts by weight：37 parts of sodium vanadate, 69 parts of hexamethonium bromide, 11 16 parts of Sodium Allyl Sulfonate, 280 300 parts of water；（2）Step will be passed through（1）The container bag of processing is put into anti-dirtying liquid, when immersion treatment 23 is small after, take out, finished product after drying.A kind of preparation method of resistant container bag provided by the invention, it is easy to operate, it is of low cost, the green safe environmental protection of operating process, container bag obtained, without every excellent in mechanical performance, intensity is high, and with extremely excellent anti-pollution characteristic, surface is not easy residual splendid attire substance, is effectively reduced the number of container bag cleaning.
Description
Technical field
The invention belongs to container bag preparing technical fields, and in particular to a kind of resistant container bag preparation method.
Background technology
Container bag is also known as flexible container bag, ton pack, space bag etc., is one kind of contained implement utensil, is equipped with crane
Or fork truck, it is possible to realize that contained unitization transports, it is suitable for shipping large bulk powder and granule shape material.Container bag is a kind of soft
Property transportation package holds are widely used in the transport bag of the powderies such as food, Cereals, medicine, chemical industry, mineral products, particle, block article
Dress, flourishing country generally use packaging product of the container bag as transport, storage.Container bag is during use, easily
The article pollution being contained, in the prior art, container bag seldom has antifouling property.
The content of the invention
In order to solve the above technical problem, the present invention provides a kind of preparation methods of resistant container bag.
The present invention is achieved by the following technical solutions.
A kind of preparation method of resistant container bag, including following operating procedure：
（1）The container bag of knitting forming is added in modification liquid, when abundant immersion treatment 2-3 is small, wherein modification liquid is by following heavy
The component of amount part is made：3-7 parts of sodium vanadate, 6-9 parts of hexamethonium bromide, 11-16 parts of Sodium Allyl Sulfonate, 280-300 parts of water；
（2）Step will be passed through（1）The container bag of processing is put into anti-dirtying liquid, when immersion treatment 2-3 is small after, take out, made after drying
Finished product is obtained, wherein anti-dirtying liquid is made of the component of following parts by weight：11-18 parts of sodium trifluoroacetate, N- butyl-N- hydroxyethylanilines
10-16 parts, 10-16 parts of tetrabutyl ammonium fluoride, 4-9 parts of m-trifluoromethylbenzoic acid methyl esters, 80-85 parts of polyacrylate emulsion, nothing
68-72 parts of water-ethanol, 120-140 parts of water.
Specifically, above-mentioned steps（1）In, the temperature of modification liquid is 45-55 DEG C.
Specifically, above-mentioned steps（2）Anti-dirtying liquid preparation method include following operating procedure：By N- butyl-N- hydroxyl second
Base aniline, tetrabutyl ammonium fluoride, m-trifluoromethylbenzoic acid methyl esters are added in into absolute ethyl alcohol, after mixing, successively to it
Middle addition water and sodium trifluoroacetate, continue after being uniformly mixed, mixed liquor are added in into polyacrylate emulsion, use
After the rotating speed of 400r/min persistently stirs 60min, anti-dirtying liquid is made.
Specifically, above-mentioned steps（2）In, the temperature of drying is 65-70 DEG C.
From the above technical scheme, it can be seen that the beneficial effects of the invention are as follows：
A kind of preparation method of resistant container bag provided by the invention, easy to operate, of low cost, the green safe ring of operating process
It protects, container bag obtained, without every excellent in mechanical performance, intensity is high, and with extremely excellent anti-pollution characteristic, surface
It is not easy residual and contains substance, be effectively reduced the number of container bag cleaning.Wherein, step（1）In, modification liquid can be carried effectively
The surface energy of container bag is risen, and then the effective surface energy for improving container bag, and then enhance the effect of anti-dirtying liquid；Step
Suddenly（2）In anti-dirtying liquid, the surface of the reduction container bag that can be imitated can, the water contact angle on increase container bag surface, and then effective
Improve the antifouling property of container bag.
Specific embodiment
Following embodiment cannot be used for limiting the scope of the invention for illustrating the present invention.The reality used in embodiment
The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
A kind of preparation method of resistant container bag, including following operating procedure：
（1）The container bag of knitting forming is added in modification liquid, when abundant immersion treatment 2 is small, wherein modification liquid is by following weight
The component of part is made：3 parts of sodium vanadate, 6 parts of hexamethonium bromide, 11 parts of Sodium Allyl Sulfonate, 280 parts of water；
（2）Step will be passed through（1）The container bag of processing is put into anti-dirtying liquid, when immersion treatment 2 is small after, take out, after drying be made
Finished product, wherein anti-dirtying liquid are made of the component of following parts by weight：11 parts of sodium trifluoroacetate, 10 parts of N- butyl-N- hydroxyethylanilines,
10 parts of tetrabutyl ammonium fluoride, 4 parts of m-trifluoromethylbenzoic acid methyl esters, 80 parts of polyacrylate emulsion, 68 parts of absolute ethyl alcohol, water 120
Part.
Specifically, above-mentioned steps（1）In, the temperature of modification liquid is 45 DEG C.
Specifically, above-mentioned steps（2）Anti-dirtying liquid preparation method include following operating procedure：By N- butyl-N- hydroxyl second
Base aniline, tetrabutyl ammonium fluoride, m-trifluoromethylbenzoic acid methyl esters are added in into absolute ethyl alcohol, after mixing, successively to it
Middle addition water and sodium trifluoroacetate, continue after being uniformly mixed, mixed liquor are added in into polyacrylate emulsion, use
After the rotating speed of 400r/min persistently stirs 60min, anti-dirtying liquid is made.
Specifically, above-mentioned steps（2）In, the temperature of drying is 65 DEG C.
Embodiment 2
A kind of preparation method of resistant container bag, including following operating procedure：
（1）The container bag of knitting forming is added in modification liquid, when abundant immersion treatment 2.5 is small, wherein modification liquid is by following heavy
The component of amount part is made：5 parts of sodium vanadate, 8 parts of hexamethonium bromide, 13 parts of Sodium Allyl Sulfonate, 290 parts of water；
（2）Step will be passed through（1）The container bag of processing is put into anti-dirtying liquid, when immersion treatment 2.5 is small after, take out, made after drying
Finished product is obtained, wherein anti-dirtying liquid is made of the component of following parts by weight：15 parts of sodium trifluoroacetate, N- butyl-N- hydroxyethylanilines 14
Part, 14 parts of tetrabutyl ammonium fluoride, 5 parts of m-trifluoromethylbenzoic acid methyl esters, 83 parts of polyacrylate emulsion, 70 parts of absolute ethyl alcohol, water
130 parts.
Specifically, above-mentioned steps（1）In, the temperature of modification liquid is 50 DEG C.
Specifically, above-mentioned steps（2）Anti-dirtying liquid preparation method include following operating procedure：By N- butyl-N- hydroxyl second
Base aniline, tetrabutyl ammonium fluoride, m-trifluoromethylbenzoic acid methyl esters are added in into absolute ethyl alcohol, after mixing, successively to it
Middle addition water and sodium trifluoroacetate, continue after being uniformly mixed, mixed liquor are added in into polyacrylate emulsion, use
After the rotating speed of 400r/min persistently stirs 60min, anti-dirtying liquid is made.
Specifically, above-mentioned steps（2）In, the temperature of drying is 68 DEG C.
Embodiment 3
A kind of preparation method of resistant container bag, including following operating procedure：
（1）The container bag of knitting forming is added in modification liquid, when abundant immersion treatment 3 is small, wherein modification liquid is by following weight
The component of part is made：7 parts of sodium vanadate, 9 parts of hexamethonium bromide, 16 parts of Sodium Allyl Sulfonate, 300 parts of water；
（2）Step will be passed through（1）The container bag of processing is put into anti-dirtying liquid, when immersion treatment 3 is small after, take out, after drying be made
Finished product, wherein anti-dirtying liquid are made of the component of following parts by weight：18 parts of sodium trifluoroacetate, 16 parts of N- butyl-N- hydroxyethylanilines,
16 parts of tetrabutyl ammonium fluoride, 9 parts of m-trifluoromethylbenzoic acid methyl esters, 85 parts of polyacrylate emulsion, 72 parts of absolute ethyl alcohol, water 140
Part.
Specifically, above-mentioned steps（1）In, the temperature of modification liquid is 55 DEG C.
Specifically, above-mentioned steps（2）Anti-dirtying liquid preparation method include following operating procedure：By N- butyl-N- hydroxyl second
Base aniline, tetrabutyl ammonium fluoride, m-trifluoromethylbenzoic acid methyl esters are added in into absolute ethyl alcohol, after mixing, successively to it
Middle addition water and sodium trifluoroacetate, continue after being uniformly mixed, mixed liquor are added in into polyacrylate emulsion, use
After the rotating speed of 400r/min persistently stirs 60min, anti-dirtying liquid is made.
Specifically, above-mentioned steps（2）In, the temperature of drying is 70 DEG C.
It should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted.Although with reference to compared with
The present invention is described in detail in good embodiment, it will be understood by those of ordinary skill in the art that, it can be to the technology of invention
Scheme is modified or replaced equivalently, and without departing from the scope of technical solution of the present invention, should all cover the power in the present invention
In sharp claimed range.
Claims (4)
1. a kind of preparation method of resistant container bag, which is characterized in that including following operating procedure：
（1）The container bag of knitting forming is added in modification liquid, when abundant immersion treatment 2-3 is small, wherein modification liquid is by following heavy
The component of amount part is made：3-7 parts of sodium vanadate, 6-9 parts of hexamethonium bromide, 11-16 parts of Sodium Allyl Sulfonate, 280-300 parts of water；
（2）Step will be passed through（1）The container bag of processing is put into anti-dirtying liquid, when immersion treatment 2-3 is small after, take out, made after drying
Finished product is obtained, wherein anti-dirtying liquid is made of the component of following parts by weight：11-18 parts of sodium trifluoroacetate, N- butyl-N- hydroxyethylanilines
10-16 parts, 10-16 parts of tetrabutyl ammonium fluoride, 4-9 parts of m-trifluoromethylbenzoic acid methyl esters, 80-85 parts of polyacrylate emulsion, nothing
68-72 parts of water-ethanol, 120-140 parts of water.
A kind of 2. preparation method of resistant container bag according to claim 1, which is characterized in that above-mentioned steps（1）In, change
Property liquid temperature be 45-55 DEG C.
A kind of 3. preparation method of resistant container bag according to claim 1, which is characterized in that above-mentioned steps（2）It is anti-
The preparation method of soiling solution includes following operating procedure：By N- butyl-N- hydroxyethylanilines, tetrabutyl ammonium fluoride, m-trifluoromethyl
Methyl benzoate is added in into absolute ethyl alcohol, after mixing, adds in water and sodium trifluoroacetate thereto successively, it is mixed to continue stirring
After closing uniformly, mixed liquor is added in into polyacrylate emulsion, after persistently stirring 60min using the rotating speed of 400r/min, is made
Anti-dirtying liquid.
A kind of 4. preparation method of resistant container bag according to claim 1, which is characterized in that above-mentioned steps（2）In, it dries
Dry temperature is 65-70 DEG C.