CN108065463A - A kind of production method with rose scent silica gel breast pad - Google Patents
A kind of production method with rose scent silica gel breast pad Download PDFInfo
- Publication number
- CN108065463A CN108065463A CN201611016964.0A CN201611016964A CN108065463A CN 108065463 A CN108065463 A CN 108065463A CN 201611016964 A CN201611016964 A CN 201611016964A CN 108065463 A CN108065463 A CN 108065463A
- Authority
- CN
- China
- Prior art keywords
- silica
- silica gel
- rose
- breast pad
- master batch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production methods with rose scent silica gel breast pad, are that first liquid organosilicon glue, silane coupling agent, rose flavoring particle master batch, catalyst, inhibitor are mixed evenly according to list of ingredients, obtain silica-gel mixture as raw material；Then obtained silica-gel mixture is vacuumized under vacuum, deaeration；Again by the silica-gel mixture injection moulding mold after deaeration, then with curing molding under the conditions of 110 DEG C~135 DEG C；Then silica gel breast pad after shaping is removed from the molds, carries out whole deburring processing, remove and sizing material is remained at injection gate；Finally make its surface smooth to get finished product the outer surface coating processing agent of refurbished silica gel breast pad.The present invention allows chest pad to distribute rose scent naturally, not only can cover stink with perspiration in summer, fine fragrance can be more given out instead of perfume, attracts liking for customer women by adding rose flavoring particle in silica gel materials.
Description
Technical field
The present invention relates to a kind of production method of silica gel breast pad, particularly a kind made from rose scent silica gel breast pad
Method.
Background technology
Brassiere is one of underwear that women uses, also known as bust, brassiere, brassiere or brassiere, sometimes also with general term " underwear "
It replacing or laudatory title " inner beauty ", function is to cover and support breast, and general accessory of the chest pad as brassiere,
It plays a very important role to the plasticity tool of female breast.As the improvement of people's living standards, requirement of the people to daily necessities
Not only limitation and its normal function, and more delights of life are required, therefore for chest pad, if it can give out naturally
Fragrance, will be more welcome for the women for pursuing fine smell.Invention describes the fragrant silica gel breast pads of kind of hair, lead to
The addition flavoring particle in silica gel materials is crossed, allows chest pad naturally fragrant, not only stink with perspiration can be covered in summer, more may be used
To give out fine fragrance instead of perfume, attract liking for customer women.
The content of the invention
It is an object of the present invention to provide a kind of production methods with rose scent silica gel breast pad.
Technical scheme：A kind of production method with rose scent silica gel breast pad, includes the following steps：
（1）Liquid organosilicon glue, silane coupling agent, rose flavoring particle master batch, catalyst, inhibitor are mixed according to list of ingredients
It stirs evenly, obtains silica-gel mixture as raw material；
（2）By step（1）Obtained silica-gel mixture vacuumizes under vacuum, deaeration；
（3）By in the silica-gel mixture injection moulding mold after deaeration, then with curing molding under the conditions of 110 DEG C~135 DEG C；
（4）Silica gel breast pad after shaping is removed from the molds, whole deburring processing is carried out, removes and sizing material is remained at injection gate；
（5）Make its surface smooth to get finished product the outer surface coating processing agent of refurbished silica gel breast pad.
The foregoing production method with rose scent silica gel breast pad, includes the following steps：
（1）Liquid organosilicon glue, silane coupling agent, rose flavoring particle master batch, catalyst, inhibitor are mixed according to list of ingredients
It stirs evenly, obtains density as 0.4-0.8g/ml, viscosity is the silica-gel mixture of 5500~6800mpas as raw material；
（2）By step（1）Obtained silica-gel mixture vacuumizes under conditions of vacuum degree is negative 0.08-0.1Mpa, deaeration；
（3）Will in the silica-gel mixture injection moulding mold after deaeration, then under the conditions of 110 DEG C~135 DEG C keep 30min~
40min, with curing molding；
（4）Silica gel breast pad after shaping is removed from the molds, whole deburring processing is carried out, removes and sizing material is remained at injection gate；
（5）Make its surface smooth to get finished product the outer surface coating processing agent of refurbished silica gel breast pad.
The foregoing production method with rose scent silica gel breast pad, by weight, the silica-gel mixture includes
There are 120-130 parts of organic silica gel, 4-7 parts of silane coupling agent, 6-9 parts of rose flavoring particle master batch, 0.6-0.8 parts of catalyst, suppression
0.02-0.04 parts of preparation.
The foregoing production method with rose scent silica gel breast pad, the matrix resin of the rose flavoring particle master batch are
Polyurethanes, the rose fumet in rose flavoring particle master batch account for the 5% of master batch total weight.
Beneficial effects of the present invention：The present invention allows chest pad certainly by adding rose flavoring particle in silica gel materials
Rose scent so is distributed, not only stink with perspiration can be covered in summer, fine fragrance can be more given out instead of perfume, attracts women
Customer's likes.
Specific embodiment
The embodiment of the present invention
Embodiment 1, a kind of production method with rose scent silica gel breast pad, include the following steps：
（1）Liquid organosilicon glue, silane coupling agent, rose flavoring particle master batch, catalyst, inhibitor are mixed according to list of ingredients
It stirs evenly, obtains density as 0.4g/ml, viscosity is the silica-gel mixture of 5500mpas as raw material；
（2）By step（1）Obtained silica-gel mixture vacuumizes under conditions of vacuum degree is negative 0.08Mpa, deaeration；
（3）By in the silica-gel mixture injection moulding mold after deaeration, 30minmin is then kept under the conditions of 110 DEG C DEG C, with
Curing molding；
（4）Silica gel breast pad after shaping is removed from the molds, whole deburring processing is carried out, removes and sizing material is remained at injection gate；
（5）Make its surface smooth to get finished product the outer surface coating processing agent of refurbished silica gel breast pad.
By weight, 120 parts of organic silica gel, 4 parts of silane coupling agent, rose flavoring are included in the silica-gel mixture
6 parts of particle master batch, 0.6 part of catalyst, 0.02 part of inhibitor.
The matrix resin of the rose flavoring particle master batch is polyurethanes, the rose in rose flavoring particle master batch
Fumet accounts for the 5% of master batch total weight.
Embodiment 2, a kind of production method with rose scent silica gel breast pad, include the following steps：
（1）Liquid organosilicon glue, silane coupling agent, rose flavoring particle master batch, catalyst, inhibitor are mixed according to list of ingredients
It stirs evenly, obtains density as 0.8g/ml, viscosity is the silica-gel mixture of 6800mpas as raw material；
（2）By step（1）Obtained silica-gel mixture vacuumizes under conditions of vacuum degree is negative 0.1Mpa, deaeration；
（3）By in the silica-gel mixture injection moulding mold after deaeration, 40min then is kept under the conditions of 135 DEG C, to be solidified into
Type；
（4）Silica gel breast pad after shaping is removed from the molds, whole deburring processing is carried out, removes and sizing material is remained at injection gate；
（5）Make its surface smooth to get finished product the outer surface coating processing agent of refurbished silica gel breast pad.
By weight, 130 parts of organic silica gel, 7 parts of silane coupling agent, rose flavoring are included in the silica-gel mixture
9 parts of particle master batch, 0.8 part of catalyst, 0.04 part of inhibitor.
The matrix resin of the rose flavoring particle master batch is polyurethanes, the rose in rose flavoring particle master batch
Fumet accounts for the 5% of master batch total weight.
Claims (4)
1. a kind of production method with rose scent silica gel breast pad, it is characterised in that：Include the following steps：
（1）Liquid organosilicon glue, silane coupling agent, rose flavoring particle master batch, catalyst, inhibitor are mixed according to list of ingredients
It stirs evenly, obtains silica-gel mixture as raw material；
（2）By step（1）Obtained silica-gel mixture vacuumizes under vacuum, deaeration；
（3）By in the silica-gel mixture injection moulding mold after deaeration, then with curing molding under the conditions of 110 DEG C~135 DEG C；
（4）Silica gel breast pad after shaping is removed from the molds, whole deburring processing is carried out, removes and sizing material is remained at injection gate；
（5）Make its surface smooth to get finished product the outer surface coating processing agent of refurbished silica gel breast pad.
2. the production method according to claim 1 with rose scent silica gel breast pad, it is characterised in that：Including walking as follows
Suddenly：
（1）Liquid organosilicon glue, silane coupling agent, rose flavoring particle master batch, catalyst, inhibitor are mixed according to list of ingredients
It stirs evenly, obtains density as 0.4-0.8g/ml, viscosity is the silica-gel mixture of 5500~6800mpas as raw material；
（2）By step（1）Obtained silica-gel mixture vacuumizes under conditions of vacuum degree is negative 0.08-0.1Mpa, deaeration；
（3）Will in the silica-gel mixture injection moulding mold after deaeration, then under the conditions of 110 DEG C~135 DEG C keep 30min~
40min, with curing molding；
（4）Silica gel breast pad after shaping is removed from the molds, whole deburring processing is carried out, removes and sizing material is remained at injection gate；
（5）Make its surface smooth to get finished product the outer surface coating processing agent of refurbished silica gel breast pad.
3. the production method according to claim 1 or 2 with rose scent silica gel breast pad, it is characterised in that：By weight
Part is counted, and includes 120-130 parts of organic silica gel, 4-7 parts of silane coupling agent, rose flavoring particle master batch in the silica-gel mixture
6-9 parts, 0.6-0.8 parts of catalyst, 0.02-0.04 parts of inhibitor.
4. the production method according to claim 1 or 2 with rose scent silica gel breast pad, it is characterised in that：The rose
The matrix resin of rare flavoring particle master batch is polyurethanes, and it is total that the rose fumet in rose flavoring particle master batch accounts for master batch
The 5% of weight.