CN108058317A - The production method of metallic high temperature gas assisted molding combination plastic cement - Google Patents
The production method of metallic high temperature gas assisted molding combination plastic cement Download PDFInfo
- Publication number
- CN108058317A CN108058317A CN201610981434.3A CN201610981434A CN108058317A CN 108058317 A CN108058317 A CN 108058317A CN 201610981434 A CN201610981434 A CN 201610981434A CN 108058317 A CN108058317 A CN 108058317A
- Authority
- CN
- China
- Prior art keywords
- plastic cement
- hardware
- high temperature
- temperature gas
- hole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The production method that a kind of metallic high temperature gas assisted molding is combined with plastic cement, especially refer to and metal sheet is placed in mold, and it presses on the metal sheet, metal sheet softening transform is made to mold heating using heating unit, gases at high pressure are inputted again by the metal sheet blow pressure of softening into die cavity, and the hardware to get high temperature gas assisted molding is taken out after to be formed, hardware and plastic cement element are combined into one again, are its characteristic person.
Description
Technical field
The production method of metallic high temperature gas assisted molding combination plastic cement of the present invention, mainly applied to mobile phone, tablet computer, pen
Note type computer, glasses, cosmetic container, automobile-used decoration with lamp decoration etc., have the high temperature gas assisted molding of metal and two kinds of elements of plastic cement with
On forming technique with reference to plastic cement.
Background technology
It presses, mobile phone is received to be needed to rely on antenna with transferring signal, and mobile phone is set there are two types of the modes of antenna, and one kind is tradition
Old-fashioned external antenna, another kind are built-in aerial common at present, and external antenna is removed due to being to protrude from outside handset shell
Outside more unsightly, protrude the external antenna outside handset shell and easily bend or fracture because of collision.So often at present
The mobile phone seen all is to use built-in aerial.
Only, when mobile phone using all-metal material (such as:Aluminium alloy) be used as housing when, since metal material has mask signal
Effect, so can influence built-in aerial receives function with transferring signal, therefore generally in the handset shell of all-metal material
On all can setting unit plastic cement element, while at plastic cement element install built-in aerial, can penetrate plastic cement using electromagnetic field
Built-in aerial still can swimmingly be received with transferring signal for the characteristic of element.
The metal shell of conventional mobile phone and the combination of plastic cement element, one way in which is first by the thick embryo of metal shell
It first passes through CNC and processes the line of rabbet joint, handle and complete using anode, not only cost of manufacture is high, and when process tool passes through one section
Between after, i.e., can generate abrasion, the tolerance in machining accuracy is caused to increase, and cause the generation of faulty materials;Meanwhile at anode
Chemical agent after reason also can attack metal and plastics, processing and then metal-back is taken away jet-out plastic, using shoot mode
, since metal shell is not whole plane, some places have radian, some places are textured, so noting
Plastics are easily run chaotically during material, and the situation for having flash occurs, and plastics are easily higher by the groove of metal-back very in material feeding
It is more, it is touched up with hand, sense of touch is bad, also seems in appearance unsightly, had both been deposited for it and has waited to overcome the problems, such as solution and missing.
Another mode is in a manner that plastics and metal shell are combined into one by adhesive agent, using adhesive means
Metal shell and plastic cement element between combine that power is poor and not wear-resisting, not acid and alkali-resistance, both deposited for it and waited to overcome solution
Problem and missing.
In addition to mobile phone shell, also many products on the market, such as:Tablet computer, glasses, cosmetic container, automobile-used dress
Decorations and lamp decoration etc. are mostly to use aluminium extruded type or the metal of aluminium punching press when making all with metal and two kinds of elements of plastic cement
Element recycles the mode of plastic cement fitting or fitting plastic cement, hardware and plastic cement element is combined into one.
It is above-mentioned general common by extrusion molding or stamping forming hardware, the appearance of hardware still need
The daraf(reciprocal of farad) silk made after recycling or the processing technologys such as sandblasting or polishing or grinding could produce complexity in the appearance of hardware
Lines or embossment or totem, after the complicated processing program of multiple tracks, the appearance of hardware can just show roughness
Different mirror effects or different lines or different embossment totems, not only take a lot of work time-consuming, cost of manufacture is high, and process tool
After a while, i.e., abrasion can be generated, the tolerance in machining accuracy is caused to increase, and causes the generation of faulty materials,
It had both been deposited for it and has waited to overcome the problems, such as solution and missing.
The content of the invention
The present inventor is currently undertaken by the manufacture of Related product, design, practical experience and gains in depth of comprehension for many years is accumulated, for tradition
The problem of existing metal casing forming with reference to plastic cement technology with both depositing and missing energetically put into the spirit of innovation and improvement, institute
The production method of the metallic high temperature gas assisted molding combination plastic cement of completion.
Invention solve the problems, such as applied technological means tie up in:The production method of the hardware of high temperature gas assisted molding,
Metal sheet is placed in mold by system, and is pressed on the metal sheet, makes gold to mold heating using heating unit
Belong to plate softening transform, then input gases at high pressure by the metal sheet blow pressure of softening into die cavity, taken out after to be formed to get height
The hardware of wet shaping.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, wherein:The hardware of high temperature gas assisted molding
With the associated methods of plastic cement element, including:Material feeding mode, the first hardware in high temperature gas assisted molding are equipped with inwardly or outwardly convex
Going out and not perforative slot, shape and the size of the slot are regardless of, the depth of the slot is more than the thickness of hardware, and by plastic cement material feeding
Mold penetrates molded plastic cement element in slot, then the excess metal material that hardware thickness is protruded in slot is cut off with plastic rubber material,
Hardware is allowed to be combined into one with plastic cement element.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, wherein:The hardware of high temperature gas assisted molding
With the associated methods of plastic cement element, including:Material feeding mode is first equipped with perforative hole in the hardware of high temperature gas assisted molding, should
The shape in hole is regardless of with size, and is penetrated in appearance cladding one film of fitting of hardware, then by plastic cement material feeding mold in hole
Molded plastic cement element waits the shaping of plastic cement element afterwards again to remove film, hardware is allowed to be combined into one with plastic cement element.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, wherein:The hardware of high temperature gas assisted molding
With the associated methods of plastic cement element, including:Material feeding mode is first equipped with perforative hole in the hardware of high temperature gas assisted molding, should
The shape in hole is regardless of with size, and is existed in the appearance printing of hardware or one protective layer of application, then by plastic cement material feeding mold
Molded plastic cement element is penetrated in hole, waits and again removes protective layer after the shaping of plastic cement element, allows hardware and plastic cement element knot
Integrator.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, wherein:The hardware of high temperature gas assisted molding
With the associated methods of plastic cement element, including:Material feeding mode is first equipped with perforative hole in the hardware of high temperature gas assisted molding, should
The shape in hole is regardless of with size, and molded plastic cement element is directly penetrated in hole by plastic cement material feeding mold, allows hardware with moulding
Glue element is combined into one.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, wherein:The hardware of high temperature gas assisted molding
With the associated methods of plastic cement element, including:Laminating type first goes out plastic cement element by plastic cement material feeding Mold Making, and in High Temperature Gas
The hardware patch of shaping, spray or apply last layer glue (such as:Double faced adhesive tape or liquid glue), then plastic cement element is fitted in into metal
Element allows hardware to be combined into one with plastic cement element.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, wherein:The hardware of high temperature gas assisted molding
With the associated methods of plastic cement element, including:Laminating type is first equipped with perforative hole in the hardware of high temperature gas assisted molding, should
The shape in hole is regardless of with size, and goes out plastic cement element by plastic cement material feeding Mold Making, and plastic cement element can be embedded into hole, then
Paste, spray or apply around hole last layer glue (such as:Double faced adhesive tape or liquid glue), then plastic cement element is fitted in into hardware,
Hardware is allowed to be combined into one with plastic cement element.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, wherein:The hardware of high temperature gas assisted molding
With the associated methods of plastic cement element, including:Dispensing mode is first equipped with perforative hole in the hardware of high temperature gas assisted molding, should
The shape in hole is regardless of with size, and goes out plastic cement element by plastic cement material feeding Mold Making, is clicked and entered in hole identical with plastic cement element
Material is in the plastic rubber material of molten condition, etc. after the plastic rubber material coagulation forming of molten conditions, hardware is allowed to be combined with plastic cement element
Integrally.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, wherein:The hardware of high temperature gas assisted molding
With the associated methods of plastic cement element, including:Reperfusion mode is first equipped with perforative hole in the hardware of high temperature gas assisted molding, should
The shape in hole is regardless of with size, and goes out plastic cement element by plastic cement material feeding Mold Making, is perfused in hole identical with plastic cement element
Material is in the plastic rubber material of molten condition, etc. after the plastic rubber material coagulation forming of molten conditions, hardware is allowed to be combined with plastic cement element
Integrally.
Invention against existing technologies the effect of tie up in:Hardware as made by high temperature gas assisted molding method out,
The appearance of the hardware no longer needs the daraf(reciprocal of farad) silk made after utilizing or sandblasting or the processing technologys such as polishing or grinding, you can in height
The when marquis of wet shaping copies the complicated lines of die cavity or embossment or totem in mold, shows the different mirror of roughness
Face effect or different lines or different embossment totems, this hardware come out as made by high temperature gas assisted molding method, then
Using laminating type (such as:Double faced adhesive tape or liquid glue) or press or temperature (hot pressing glue) is combined with plastic cement element;It or will
This hardware come out as made by high temperature gas assisted molding method, which is imbedded in plastic cement material feeding mold, injects plastic cement and plastic cement member
Part combines;Or the hardware for coming out this as made by high temperature gas assisted molding method, molten plastic is utilized to inject or instill institute
The complexity of metal appearance can be not only presented in the position needed, the structure that hardware and plastic cement element can be combined into one
Lines or totem change various and low manufacture cost, and precision improves, and is more avoided that the appearance of hardware after formation,
The technique for imposing the time consumption and energy consumptions such as daraf(reciprocal of farad) silk or sandblasting or polishing or grinding again, made product out, not only cost of manufacture
It is low, and processing precise degree improve, can effectively avoid the generation of faulty materials, have effects that on enhancement, reached for its main purpose
Winner.
Description of the drawings
Fig. 1:It is the hardware of the embodiment of the present invention one and plastic cement element combination schematic diagram.
Fig. 2:It is the hardware of the embodiment of the present invention two and plastic cement element combination schematic diagram.
Fig. 3:It is the hardware of the embodiment of the present invention three and plastic cement element combination schematic diagram.
Fig. 4:It is the hardware of the embodiment of the present invention four and plastic cement element combination schematic diagram.
Fig. 5:It is the hardware of the embodiment of the present invention five and plastic cement element combination schematic diagram.
Fig. 6:It is the hardware of the embodiment of the present invention six and plastic cement element combination schematic diagram.
Fig. 7:It is the hardware of the embodiment of the present invention seven and plastic cement element combination schematic diagram.
Wherein, the reference numerals are as follows:
1 film
2 protective layers
3 glue
10 hardwares
11 slots
12 holes
20 plastic cement elements
21 plastic rubber materials
Specific embodiment
The function and benefit understood the construction content of the present invention in depth to be easy to those skilled in the art and can reached,
Specific embodiment is hereby enumerated, and schema is coordinated to be discussed in detail and is described as follows:
A kind of production method of the hardware of high temperature gas assisted molding, is that metal sheet is placed in mold, and imposes pressure
Power makes metal sheet softening transform to mold heating using heating unit, then inputs gases at high pressure and incite somebody to action on the metal sheet
The metal sheet blow pressure of softening takes out the hardware to get high temperature gas assisted molding into die cavity after to be formed.Wherein, apply
In pressure and temperature on the metal sheet, depending on being material and thickness according to metal sheet, the gases at high pressure of the input with
The pressure limit being applied on metal sheet all can be 50kg/cm2~350kg/cm2;Heating makes metal sheet softening transform
Temperature can be 450 DEG C~1200 DEG C, for example, metal sheet be aluminium when, the temperature can be 450 DEG C~550 DEG C;Metal sheet
For stainless steel when, the temperature can be 1000 DEG C~1200 DEG C.The making side of above-mentioned metallic high temperature gas assisted molding combination plastic cement
Method, as shown in Figure 1, wherein:The hardware 10 of high temperature gas assisted molding and the associated methods of plastic cement element 20, including:Material feeding side
Formula is first equipped with inwardly or outwardly protrusion and not perforative slot 11, the shape of the slot 11 in the hardware 10 of high temperature gas assisted molding
It to be regardless of with size, the depth of the slot 11 is more than the thickness of hardware 10, and by plastic cement material feeding mold (not shown) in slot 11
In penetrate molded plastic cement element 20, then the excess metal material of 10 thickness of hardware will be protruded in slot 11 and plastic rubber material is cut off, allowed
Hardware 10 is combined into one with plastic cement element 20.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, as shown in Fig. 2, wherein:High temperature gas assisted molding
Hardware 10 and plastic cement element 20 associated methods, including:Material feeding mode, first in the hardware 10 of high temperature gas assisted molding
Equipped with perforative hole 12, shape and the size in the hole 12 are regardless of, and in appearance cladding one film 1 of fitting of hardware 10, then
Molded plastic cement element 20 is penetrated in hole 12 by plastic cement material feeding mold (not shown), waits the shaping of plastic cement element 20 afterwards again by film
1 removes, and hardware 10 is allowed to be combined into one with plastic cement element 20.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, as shown in figure 3, wherein:High temperature gas assisted molding
Hardware 10 and plastic cement element 20 associated methods, including:Material feeding mode, first in the hardware 10 of high temperature gas assisted molding
Equipped with perforative hole 12, shape and the size in the hole 12 are regardless of, and are protected in the appearance printing or application one of hardware 10
Layer 2, then penetrates molded plastic cement element 20 by plastic cement material feeding mold (not shown) in hole 12, waits after plastic cement element 20 is molded
Protective layer 2 is removed again, hardware 10 is allowed to be combined into one with plastic cement element 20.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, as shown in figure 4, wherein:High temperature gas assisted molding
Hardware and plastic cement element associated methods, including:Material feeding mode is first equipped in the hardware 10 of high temperature gas assisted molding
Perforative hole 12, shape and the size in the hole 12 are regardless of, and pressure is directly penetrated in hole 12 by plastic cement material feeding mold (not shown)
Forming plastic cement element 20 allows hardware 10 to be combined into one with plastic cement element 20.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, wherein:The hardware of high temperature gas assisted molding
10 with the associated methods of plastic cement element 20, including:Laminating type first produces plastic cement member by plastic cement material feeding mold (not shown)
Part 20, and in high temperature gas assisted molding hardware 10 paste, spray or apply last layer glue 3 (such as:Double faced adhesive tape or liquid glue), then will
Plastic cement element 20 fits in hardware 10, and hardware 10 is allowed to be combined into one with plastic cement element 20.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, as shown in figure 5, wherein:High temperature gas assisted molding
Hardware 10 and plastic cement element 20 associated methods, including:Laminating type, first in the hardware 10 of high temperature gas assisted molding
Equipped with perforative hole 12, shape and the size in the hole 12 are regardless of, and produce plastic cement member by plastic cement material feeding mold (not shown)
Plastic cement element 20 can be embedded into hole 12 for part 20, paste, spray or apply around hole 12 last layer glue 3 (such as:It is two-sided
Glue or liquid glue), then plastic cement element 20 is fitted in into hardware 10, hardware 10 is allowed to be combined into one with plastic cement element 20
Body.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, as shown in fig. 6, wherein:High temperature gas assisted molding
Hardware 10 and plastic cement element 20 associated methods, including:Dispensing mode, first in the hardware 10 of high temperature gas assisted molding
Equipped with perforative hole 12, shape and the size in the hole 12 are regardless of, and produce plastic cement member by plastic cement material feeding mold (not shown)
Part 20, clicked and entered in hole 12 with 20 phase same material of plastic cement element be in molten condition plastic rubber material 21, etc. molten conditions plastic cement
After expecting 21 coagulation formings, hardware 10 is allowed to be combined into one with plastic cement element 20.
The production method of above-mentioned metallic high temperature gas assisted molding combination plastic cement, as shown in fig. 7, wherein:High temperature gas assisted molding
Hardware 10 and plastic cement element 20 associated methods, including:Reperfusion mode, first in the hardware 10 of high temperature gas assisted molding
Equipped with perforative hole 12, shape and the size in the hole 12 are regardless of, and produce plastic cement member by plastic cement material feeding mold (not shown)
Part 20, in hole 12 perfusion with 20 phase same material of plastic cement element in molten condition plastic rubber material 21, etc. molten conditions plastic cement
After expecting 21 coagulation formings, hardware 10 is allowed to be combined into one with plastic cement element 20.
Summary institute is old, and the present invention, which ties up to, provides a kind of production method of metallic high temperature gas assisted molding combination plastic cement, passes through
Cross the present inventor it is actual manufacture completion and repeatedly operation test after, it was demonstrated that the function desired by the present invention can be reached really
Benefit, while there is the utility value in industry, really met invention in the streets to there is no creating first for information at present again
Hence according to the regulation of Patent Law, the application of patent of invention is proposed to an ancient unit of weight office for the establishment main idea of patent practicability and progressive.
Claims (10)
1. a kind of production method of metallic high temperature gas assisted molding combination plastic cement, metal sheet is placed in mold by main system, and is applied
With pressure on the metal sheet, metal sheet softening transform is made to mold heating using heating unit, then inputs gases at high pressure
By the metal sheet blow pressure of softening into die cavity, the hardware to get high temperature gas assisted molding is taken out after to be formed, then by metal
Element is combined into one with plastic cement element.
2. the production method of metallic high temperature gas assisted molding combination plastic cement according to claim 1, wherein:It is first auxiliary in High Temperature Gas
Molding hardware is equipped with inwardly or outwardly protrusion and not perforative slot, shape and the size of the slot are regardless of, the depth of the slot
Molded plastic cement element is penetrated in slot more than the thickness of hardware, and by plastic cement material feeding mold, then metal member will be protruded in slot
The excess metal material of part thickness is cut off with plastic rubber material, and hardware is allowed to be combined into one with plastic cement element.
3. the production method of metallic high temperature gas assisted molding combination plastic cement according to claim 1, wherein:It is first auxiliary in High Temperature Gas
Molding hardware is equipped with perforative hole, and shape and the size in the hole are regardless of, and coats fitting in the appearance of hardware
One film, then molded plastic cement element is penetrated in hole by plastic cement material feeding mold is waited and again removed film after the shaping of plastic cement element, allows gold
Belong to element to be combined into one with plastic cement element.
4. the production method of metallic high temperature gas assisted molding combination plastic cement according to claim 1, wherein:It is first auxiliary in High Temperature Gas
Molding hardware is equipped with perforative hole, and shape and the size in the hole are regardless of, and in the appearance printing or painting of hardware
A protective layer is filled, then molded plastic cement element is penetrated in hole by plastic cement material feeding mold, waits the shaping of plastic cement element afterwards again will protection
Layer removes, and hardware is allowed to be combined into one with plastic cement element.
5. the production method of metallic high temperature gas assisted molding combination plastic cement according to claim 1, wherein:It is first auxiliary in High Temperature Gas
Molding hardware is equipped with perforative hole, and shape and the size in the hole are regardless of, and are directly penetrated by plastic cement material feeding mold in hole
Molded plastic cement element, allows hardware to be combined into one with plastic cement element.
6. the production method of metallic high temperature gas assisted molding combination plastic cement according to claim 1, wherein:First by plastic cement material feeding
Mold Making goes out plastic cement element, and the hardware patch in high temperature gas assisted molding, spray or painting last layer glue, then plastic cement element is pasted
Together in hardware, hardware is allowed to be combined into one with plastic cement element.
7. the production method of metallic high temperature gas assisted molding combination plastic cement according to claim 1, wherein:It is first auxiliary in High Temperature Gas
Molding hardware is equipped with perforative hole, and shape and the size in the hole are regardless of, and goes out plastic cement member by plastic cement material feeding Mold Making
Plastic cement element can be embedded into hole for part, is pasted around hole, sprays or apply last layer glue, then plastic cement element is fitted in
Hardware allows hardware to be combined into one with plastic cement element.
8. the production method of the metallic high temperature gas assisted molding combination plastic cement according to claim 6 or 7, wherein:The glue can be by
Double faced adhesive tape or liquid glue selection wherein one.
9. the production method of metallic high temperature gas assisted molding combination plastic cement according to claim 1, wherein:It is first auxiliary in High Temperature Gas
Molding hardware is equipped with perforative hole, and shape and the size in the hole are regardless of, and goes out plastic cement member by plastic cement material feeding Mold Making
Part, clicked and entered in hole with plastic cement element phase same material be in molten condition plastic rubber material, etc. the plastic rubber materials of molten conditions be frozen into
After type, hardware is allowed to be combined into one with plastic cement element.
10. the production method of metallic high temperature gas assisted molding combination plastic cement according to claim 1, wherein:First in High Temperature Gas
The hardware of shaping is equipped with perforative hole, and shape and the size in the hole are regardless of, and go out plastic cement by plastic cement material feeding Mold Making
Element, in hole perfusion with plastic cement element phase same material be in molten condition plastic rubber material, etc. molten conditions plastic rubber material solidify
After shaping, hardware is allowed to be combined into one with plastic cement element.