CN108049243A - A kind of color fixing agent of high water resistant and its preparation method and application - Google Patents

A kind of color fixing agent of high water resistant and its preparation method and application Download PDF

Info

Publication number
CN108049243A
CN108049243A CN201711316279.4A CN201711316279A CN108049243A CN 108049243 A CN108049243 A CN 108049243A CN 201711316279 A CN201711316279 A CN 201711316279A CN 108049243 A CN108049243 A CN 108049243A
Authority
CN
China
Prior art keywords
parts
fixing agent
color fixing
high water
water resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711316279.4A
Other languages
Chinese (zh)
Inventor
张迪明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ningbo High Tech Zone Austen Environmental Technology Co Ltd
Original Assignee
Ningbo High Tech Zone Austen Environmental Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo High Tech Zone Austen Environmental Technology Co Ltd filed Critical Ningbo High Tech Zone Austen Environmental Technology Co Ltd
Priority to CN201711316279.4A priority Critical patent/CN108049243A/en
Publication of CN108049243A publication Critical patent/CN108049243A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of color fixing agent of high water resistant and its preparation method and application, which includes according to the raw material of following parts by weight:31 39 parts of aqueous polyurethane, 13 21 parts of methyl-silicone oil, 18 26 parts of dimethylethanolamine, 37 parts of thioacetic acid, 15 parts of penta-BDE.Aqueous polyurethane is mixed with dimethylethanolaminesolution solution, it is warming up to 71 73 DEG C and at such a temperature 0.5 0.7h of stir process, then methyl-silicone oil, mercaptoacetic acid solution are added in and is ultrasonically treated 20 25min, it then heats to 92 95 DEG C and adds in penta-BDE, then 55 60min of stir process is sealed at such a temperature, stop heating and being ultrasonically treated 35min again to get color fixing agent.The present invention can significantly improve printing paper surface nature, improve print quality, particularly greatly improve into the water-resistance of paper.The present invention greatly improves into paper and meets color density value after water, and raw material is simple, materials are extensive, and environmentally protective, pollution-free, simple production process, properties of product are stablized, suitable for industrialized production.

Description

A kind of color fixing agent of high water resistant and its preparation method and application
Technical field
The present invention relates to color fixing agent technical fields, are specifically a kind of color fixing agent of high water resistant and its preparation method and application.
Background technology
Color fixing agent is the auxiliary agent of common fixation colorant in color spray paper and coating, and general character is cation and high molecular weight.Ion Intensity is high, with strong in dichroic dye molecule active force, can capture rapidly and fix electronegative colorant, play the role of fixation.It is high Molecular weight cationic polymer, such as polyethyleneimine, polyvinylamine, polydimethyl diallyl ammonium chloride and polystyrene methyl The polyamine class strong cation polymer such as trimethylamine chloride, is used equally for fixation, but these common color fixing agent often water-resistance It is bad.Aqueous polyurethane is using water organic solvent to be replaced to be also referred to as moisture as the new polyurethane system of decentralized medium and dissipate poly- ammonia Ester, aqueous polyurethane or water-based polyurethane.Aqueous polyurethane using water as solvent, pollution-free, safe and reliable, good mechanical performance, The advantages that compatibility is good, easily modified.But since it is dissolved in water, make it few, it is necessary to at it in the application of color fixing agent field It manages to improve the performances such as its water-resistance difference.
The content of the invention
It is an object of the invention to provide a kind of color fixing agent of high water resistant and its preparation method and application, to solve the above-mentioned back of the body The problem of being proposed in scape technology.
To achieve the above object, the present invention provides following technical solution:
A kind of color fixing agent of high water resistant, includes according to the raw material of following parts by weight:31-39 parts of aqueous polyurethane, methyl silicon 13-21 parts oily, 18-26 parts of dimethylethanolamine, 3-7 parts of thioacetic acid, 1-5 parts of penta-BDE.
As further embodiment of the present invention:The color fixing agent of the high water resistant, includes according to the raw material of following parts by weight:Water 33-37 parts of polyurethane of property, 15-19 parts of methyl-silicone oil, 20-24 parts of dimethylethanolamine, 4-6 parts of thioacetic acid, penta-BDE 2-4 parts.
As further embodiment of the present invention:The color fixing agent of the high water resistant, includes according to the raw material of following parts by weight:Water 35 parts of polyurethane of property, 17 parts of methyl-silicone oil, 22 parts of dimethylethanolamine, 5 parts of thioacetic acid, 3 parts of penta-BDE.
A kind of preparation method of the color fixing agent of high water resistant, comprises the following steps:
1) deionized water of 4-5 times of dimethylethanolamine and its quality is mixed, dimethylethanolaminesolution solution is made;By mercapto 35% ethanol solution of 2-3 times of guanidine-acetic acid and its quality mixes, and mercaptoacetic acid solution is made;
2) aqueous polyurethane with dimethylethanolaminesolution solution is mixed, be warming up at 71-73 DEG C and at such a temperature stirring 0.5-0.7h is managed, then add in methyl-silicone oil, mercaptoacetic acid solution and is ultrasonically treated 20-25min, then heats to 92-95 DEG C And penta-BDE is added in, stir process 55-60min is then sealed at such a temperature, then is stopped heating and be ultrasonically treated 35min is to get color fixing agent.
As further embodiment of the present invention:In step 2), first time ultrasonic power is 500W.
As further embodiment of the present invention:In step 2), mixing speed 180-200r/min.
As further embodiment of the present invention:In step 2), second of ultrasonic power is 900W.
Another object of the present invention is to provide application of the color fixing agent in paper processing.
Compared with prior art, the beneficial effects of the invention are as follows:
The present invention carries out aqueous polyurethane processing by dimethylethanolamine, thioacetic acid etc. and is mixed to prepare color fixing agent, Printing paper surface nature can be significantly improved, improves print quality, particularly greatly improves into the water-resistance of paper, solves aqueous poly- ammonia Ester is seldom applied on color fixing agent and the problems such as it is poor there are water-resistance, and a kind of new product is provided for color fixing agent field.This Invention greatly improves into paper and meets color density value after water, and raw material is simple, materials are extensive, environmentally protective, pollution-free, production technology letter Single, properties of product are stablized, suitable for industrialized production.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical solution in the embodiment of the present invention is clearly and completely described, Obviously, described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.Based in the present invention Embodiment, those of ordinary skill in the art's all other embodiments obtained without making creative work, all Belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of color fixing agent of high water resistant, including following raw material:31 parts of aqueous polyurethane, methyl silicon Oily 13kg, dimethylethanolamine 18kg, thioacetic acid 3kg, penta-BDE 1kg.
4 times of deionized water of dimethylethanolamine and its quality is mixed, dimethylethanolaminesolution solution is made;By sulfydryl second Acid is mixed with 35% ethanol solution of 2 times of its quality, obtained mercaptoacetic acid solution.Aqueous polyurethane is molten with dimethylethanolamine Liquid mixes, and is warming up to 71 DEG C and at such a temperature stir process 0.5h, then mixing speed 180r/min adds in methyl silicon Oil, mercaptoacetic acid solution are simultaneously ultrasonically treated 20min, ultrasonic power 500W.It then heats to 92 DEG C and adds in penta-BDE, Then stir process 55min, mixing speed 180r/min are sealed at such a temperature, then stop heating and being ultrasonically treated 35min, Ultrasonic power is 900W to get color fixing agent.
Embodiment 2
In the embodiment of the present invention, a kind of color fixing agent of high water resistant, including following raw material:39 parts of aqueous polyurethane, methyl silicon Oily 21kg, dimethylethanolamine 26kg, thioacetic acid 7kg, penta-BDE 5kg.
5 times of deionized water of dimethylethanolamine and its quality is mixed, dimethylethanolaminesolution solution is made;By sulfydryl second Acid is mixed with 35% ethanol solution of 3 times of its quality, obtained mercaptoacetic acid solution.Aqueous polyurethane is molten with dimethylethanolamine Liquid mixes, and is warming up to 73 DEG C and at such a temperature stir process 0.7h, then mixing speed 200r/min adds in methyl silicon Oil, mercaptoacetic acid solution are simultaneously ultrasonically treated 25min, ultrasonic power 500W.It then heats to 95 DEG C and adds in penta-BDE, Then stir process 60min, mixing speed 200r/min are sealed at such a temperature, then stop heating and being ultrasonically treated 35min, Ultrasonic power is 900W to get color fixing agent.
Embodiment 3
In the embodiment of the present invention, a kind of color fixing agent of high water resistant, including following raw material:Aqueous polyurethane 33kg, methyl silicon Oily 15kg, dimethylethanolamine 20kg, thioacetic acid 4kg, penta-BDE 2kg.
4.5 times of deionized water of dimethylethanolamine and its quality is mixed, dimethylethanolaminesolution solution is made;By sulfydryl 35% ethanol solution of 3 times of acetic acid and its quality mixes, and mercaptoacetic acid solution is made.By aqueous polyurethane and dimethylethanolamine Solution mixes, and is warming up to 72 DEG C and at such a temperature stir process 0.6h, then mixing speed 200r/min adds in methyl silicon Oil, mercaptoacetic acid solution are simultaneously ultrasonically treated 25min, ultrasonic power 500W.It then heats to 95 DEG C and adds in penta-BDE, Then stir process 60min, mixing speed 200r/min are sealed at such a temperature, then stop heating and being ultrasonically treated 35min, Ultrasonic power is 900W to get color fixing agent.
Embodiment 4
In the embodiment of the present invention, a kind of color fixing agent of high water resistant, including following raw material:Aqueous polyurethane 37kg, methyl silicon Oily 19kg, dimethylethanolamine 24kg, thioacetic acid 6kg, penta-BDE 4kg.
4.5 times of deionized water of dimethylethanolamine and its quality is mixed, dimethylethanolaminesolution solution is made;By sulfydryl 35% ethanol solution of 3 times of acetic acid and its quality mixes, and mercaptoacetic acid solution is made.By aqueous polyurethane and dimethylethanolamine Solution mixes, and is warming up to 72 DEG C and at such a temperature stir process 0.6h, then mixing speed 200r/min adds in methyl silicon Oil, mercaptoacetic acid solution are simultaneously ultrasonically treated 25min, ultrasonic power 500W.It then heats to 95 DEG C and adds in penta-BDE, Then stir process 60min, mixing speed 200r/min are sealed at such a temperature, then stop heating and being ultrasonically treated 35min, Ultrasonic power is 900W to get color fixing agent.
Embodiment 5
In the embodiment of the present invention, a kind of color fixing agent of high water resistant, including following raw material:Aqueous polyurethane 35kg, methyl silicon Oily 17kg, dimethylethanolamine 22kg, thioacetic acid 5kg, penta-BDE 3kg.
4.5 times of deionized water of dimethylethanolamine and its quality is mixed, dimethylethanolaminesolution solution is made;By sulfydryl 35% ethanol solution of 3 times of acetic acid and its quality mixes, and mercaptoacetic acid solution is made.By aqueous polyurethane and dimethylethanolamine Solution mixes, and is warming up to 72 DEG C and at such a temperature stir process 0.6h, then mixing speed 200r/min adds in methyl silicon Oil, mercaptoacetic acid solution are simultaneously ultrasonically treated 25min, ultrasonic power 500W.It then heats to 95 DEG C and adds in penta-BDE, Then stir process 60min, mixing speed 200r/min are sealed at such a temperature, then stop heating and being ultrasonically treated 35min, Ultrasonic power is 900W to get color fixing agent.
Comparative example 1
It is other consistent with embodiment 5 in addition to no dimethylethanolamine.
Comparative example 2
It is other consistent with embodiment 5 in addition to no thioacetic acid.
Comparative example 3
It is other consistent with embodiment 5 in addition to no dimethylethanolamine, thioacetic acid.
Color fixing agent obtained by above-described embodiment 1-5 and comparative example 1-3 is applied over ink-jet paper surface respectively, printing color is close Degree is measured using X-Rite color densitometers, and four color densities are measured after washing by water 1 minute to color lump, and the high explanation of four color densities is anti-after bath Aqueous good, four color densities are C (indigo plant), M (fuchsin), Y (Huang), K (black).It measures color density value and is shown in Table 1.
Table 1
After lacking dimethylethanolamine or thioacetic acid, wash by water to color lump after 1min, the color density value of four colors has very It is big to decline, and color fixing agent prepared by 1-5 of the embodiment of the present invention, after color lump bath 1min, the color density value detected declines Very little.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned exemplary embodiment, Er Qie In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power Profit requirement rather than above description limit, it is intended that all by what is fallen within the meaning and scope of the equivalent requirements of the claims Variation is included within the present invention.
Moreover, it will be appreciated that although this specification is described in terms of embodiments, but not each embodiment is only wrapped Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should Using specification as an entirety, the technical solutions in each embodiment can also be properly combined, forms those skilled in the art It is appreciated that other embodiment.

Claims (8)

1. a kind of color fixing agent of high water resistant, which is characterized in that the raw material according to following parts by weight includes:Aqueous polyurethane 31-39 Part, 13-21 parts of methyl-silicone oil, 18-26 parts of dimethylethanolamine, 3-7 parts of thioacetic acid, 1-5 parts of penta-BDE.
2. the color fixing agent of high water resistant according to claim 1, which is characterized in that the raw material according to following parts by weight includes: 33-37 parts of aqueous polyurethane, 15-19 parts of methyl-silicone oil, 20-24 parts of dimethylethanolamine, 4-6 parts of thioacetic acid, pentabromo- hexichol 2-4 parts of ether.
3. the color fixing agent of high water resistant according to claim 1, which is characterized in that the raw material according to following parts by weight includes: 35 parts of aqueous polyurethane, 17 parts of methyl-silicone oil, 22 parts of dimethylethanolamine, 5 parts of thioacetic acid, 3 parts of penta-BDE.
4. the preparation method of the color fixing agent of a kind of high water resistant as described in claim 1-3 is any, which is characterized in that including following Step:
1)4-5 times of deionized water of dimethylethanolamine and its quality is mixed, dimethylethanolaminesolution solution is made;By sulfydryl second Acid is mixed with 35% ethanol solution of 2-3 times of its quality, obtained mercaptoacetic acid solution;
2)Aqueous polyurethane with dimethylethanolaminesolution solution is mixed, is warming up to 71-73 DEG C and at such a temperature stir process Then 0.5-0.7h adds in methyl-silicone oil, mercaptoacetic acid solution and is ultrasonically treated 20-25min, then heats to 92-95 DEG C simultaneously Penta-BDE is added in, then seals stir process 55-60min at such a temperature, then stops heating and being ultrasonically treated 35min, Up to color fixing agent.
5. the preparation method of the color fixing agent of high water resistant according to claim 4, which is characterized in that step 2)In, for the first time Ultrasonic power is 500W.
6. the preparation method of the color fixing agent of high water resistant according to claim 4, which is characterized in that step 2)In, stirring speed It spends for 180-200r/min.
7. the preparation method of the color fixing agent of high water resistant according to claim 4, which is characterized in that step 2)In, second Ultrasonic power is 900W.
8. application of the color fixing agent in paper processing as described in claim 1-3 is any.
CN201711316279.4A 2017-12-12 2017-12-12 A kind of color fixing agent of high water resistant and its preparation method and application Pending CN108049243A (en)