CN108048722A - A kind of body-building hanging runner and its Wear-resistant Treatment technique - Google Patents
A kind of body-building hanging runner and its Wear-resistant Treatment technique Download PDFInfo
- Publication number
- CN108048722A CN108048722A CN201711357431.3A CN201711357431A CN108048722A CN 108048722 A CN108048722 A CN 108048722A CN 201711357431 A CN201711357431 A CN 201711357431A CN 108048722 A CN108048722 A CN 108048722A
- Authority
- CN
- China
- Prior art keywords
- parts
- runner
- hanging
- hanging runner
- wear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of body-building with hanging runner, and runner includes following components by mass percentage：Al：4 7%, C：0.12 0.13%, Mn：3 6%, Zn：10 13%, Ni：1 3%, Cu：1 3%, Sc：2 3%, P：0.005 0.008%, S：0.01 0.02%, Zr：1 3%, Ca：2 5%, Nb：0.01 0.05%, B：0.2 0.4%, Sr：2 5%, Co：2 4%, V：0.01 0.03%, Ti：0.15 0.17%, Na：0.01 0.02%, Be：0.02 0.03%, rare earth element：0.1 0.3%, remaining is Mg and the sum of trace impurity, the above components is 100%；A kind of Wear-resistant Treatment technique of the hanging runner of body-building, body-building that the treatment process is simple and practicable, and treated have good performance with hanging runner, can prolong the service life, reduce cost.
Description
Technical field
The invention belongs to field of exercise equipment, are related to a kind of hanging runner, and in particular to a kind of body-building with hanging runner and
Its Wear-resistant Treatment technique.
Background technology
How much fitness equipment is often divided into two major class of single function and integrated multi with training function, common to row the boat
Device, bodybuilder, fitness climber, treadmill, beauty belt massage etc., wherein hanging runner is one of which；
The hanging runner sold currently on the market since installation settings is in outdoor, is influenced variation greatly, easily corruption by outdoor environment
Erosion, easy to fall off, service life is short.
The content of the invention
The technical problems to be solved by the invention are, for above shortcoming existing in the prior art, to propose that a kind of body-building is used
Hanging runner and its Wear-resistant Treatment technique, the hanging runner of body-building that the treatment process is simple and practicable, and treated have good
Performance can prolong the service life, reduce cost.
The present invention solve more than technical problem technical solution be：
A kind of hanging runner of body-building, runner include following components by mass percentage：
Al：4-7%, C：0.12-0.13%, Mn：3-6%, Zn：10-13%, Ni：1-3%, Cu：1-3%, Sc：2-3%, P：0.005-
0.008%, S：0.01-0.02%, Zr：1-3%, Ca：2-5%, Nb：0.01-0.05%, B：0.2-0.4%, Sr：2-5%, Co：2-4%,
V：0.01-0.03%, Ti：0.15-0.17%, Na：0.01-0.02%, Be：0.02-0.03%, rare earth element：0.1-0.3%, remaining
For Mg and trace impurity, the sum of the above components are 100%；
The rare earth element includes following components by weight percentage： Nd：10-13%, Gd：7-9%, Pr：11-13%, Yb：
3-5%, remaining is that the sum of La, the above components is 100%.
The technical solution that further limits of the present invention as：
Foregoing hanging runner, runner include following components by mass percentage：
Al：4%, C：0.12%, Mn：3%, Zn：10%, Ni：1%, Cu：1%, Sc：2%, P：0.005%, S：0.01%, Zr：1%, Ca：
2%, Nb：0.01%, B：0.2%, Sr：2%, Co：2%, V：0.01%, Ti：0.15%, Na：0.01%, Be：0.02%, rare earth element：
0.1%, remaining is Mg and the sum of trace impurity, the above components is 100%；
The rare earth element includes following components by weight percentage： Nd：10%, Gd：7%, Pr：11%, Yb：3%, remaining
For La, the sum of the above components are 100%.
Foregoing hanging runner, runner include following components by mass percentage：
Al：7%, C：0.13%, Mn：6%, Zn：13%, Ni：3%, Cu：3%, Sc：3%, P：0.008%, S：0.02%, Zr：3%, Ca：
5%, Nb：0.05%, B：0.4%, Sr：5%, Co：4%, V：0.03%, Ti：0.15-0.17%, Na：0.02%, Be：0.03%, rare earth member
Element：0.3%, remaining is Mg and the sum of trace impurity, the above components is 100%；
Rare earth element includes following components by weight percentage： Nd：13%, Gd：9%, Pr：13%, Yb：5%, remaining is La, with
The sum of upper each component is 100%.
The present invention designs a kind of Wear-resistant Treatment technique of hanging runner, specific as follows
（1）It is polished with sand paper the hanging runner of selection, then the surface after polishing is cleaned with acetone, then certainly
It so dries, sandblasting roughening treatment is carried out to hanging wheel surface after drying, hanging runner is sprayed with compressed air after sandblasting
Processing is blown, then cleans the surface of hanging runner with acetone again, is heated to 80-95 DEG C after naturally dry to hanging runner, is protected
Warm 5-10min is for use；
（2）Wear-resistant paint is prepared, the wear-resistant paint includes following components according to the mass fraction：
Crystal whisker of hexa potassium titanate：7-9 parts, dispersant：5-10 parts, zinc oxide：1-5 parts, delustering agent：2-6 parts, glue crosslinking agent：1-3 parts；
Methyl phenyl silicone resin：11-13 parts, thickener：5-10 parts, binding agent：2-4 parts, suspending agent：3-5 parts, surfactant：1-3
Part, catalyst：1-3 parts, n-butanol：4-7 parts, silane coupling agent；8-12 parts, curing agent：8-11 parts；
（3）By step（1）In the hanging runner handled well send 200-300 DEG C be preheated into heating furnace, set subsequently into spraying
In putting, first with spray gun to the tiny grains of sand of valve surface even application, spray distance 110-150mm, spray angle is 80-90 °,
Then it is heating and curing rapidly, it is 0.04-0.08mm to repeat above-mentioned spraying process to coating materials thickness；
（4）The hanging runner for being coated with wear-resistant paint is cooled down, after being cooled to room temperature, is examined, storage.
The beneficial effects of the invention are as follows：
Adding Ti in the present invention in ingredient can be with crystal grain thinning, and dendrite can equally be refined by quickly solidifying, and make the extruding of alloy
Performance is improved.
Cu is added in the present invention, except hardening constituent CuAl can be formed2It outside, can also be strong with the formation high temperature of the Mg in alloy
Change phase CuMgAl2, crystal grain thinning prevents the formation in hole, inhibits the precipitation of Si, so as to improve the toughness of alloy；In addition, it adds in
Cu can be in refining alloy Mg2Low-alloyed quenching sensitivity drops in Si precipitated phases, without reducing the anti-cut change ability of alloy.
Zr, Mn, Cr are added in the present invention can improve the quenching sensitivity of alloy, and Zr meetings are added in while Mn is added in
Fibr tissue in alloy is made to maintain a high level, a kind of the reached effect being significantly larger than individually added into the two
Fruit；Add in Cr can also crystal grain thinning, retain fibr tissue, so as to improve the wilfulness of alloy；Fe is also added into the present invention can
To refine Mg2Si particles and crystal grain, Si atoms is made to leave crystal boundary, improve the toughness of alloy.
Radius is big and rare earth has higher activity, it is easy to fill up the gap of storeroom, meanwhile, rare earth element easily and
The high compound of the element compounds such as oxygen, sulphur generation fusing point, the addition of compound rare-earth improves to a certain extent prepares coating
Dispersiveness and compatibility, make product mix uniformly also improve the anti-flammability of coating.
The aminomethyl phenyl resin prepared in the present invention has good heat resistance, is suitable as the base-material of high-temperature resistant coating,
In addition the methyl phenyl silicone resin resinoid containing methyl silica structure unit and phenyl silica structure unit simultaneously, due to benzene
The introducing of base effectively raises it in thermoelasticity, the phase to the cohesivenesses of various base materials, with the substances such as organic resin and pigment
The performance of capacitive etc..
The crystal whisker of hexa potassium titanate used in the present invention, wherein potassium ion are occupied among tunnel, have higher stability, so as to
Make crystal whisker of hexa potassium titanate that there is chemical stability, insulating properties, reflection infrared ray, excellent antiseptic property etc..
Specific embodiment
Embodiment 1
The present embodiment provides a kind of body-building with hanging runner, and runner includes following components by mass percentage：
Al：4%, C：0.12%, Mn：3%, Zn：10%, Ni：1%, Cu：1%, Sc：2%, P：0.005%, S：0.01%, Zr：1%, Ca：
2%, Nb：0.01%, B：0.2%, Sr：2%, Co：2%, V：0.01%, Ti：0.15%, Na：0.01%, Be：0.02%, rare earth element：
0.1%, remaining is Mg and the sum of trace impurity, the above components is 100%；
The rare earth element includes following components by weight percentage： Nd：10%, Gd：7%, Pr：11%, Yb：3%, remaining
For La, the sum of the above components are 100%.
The Wear-resistant Treatment technique of the hanging runner of above-mentioned body-building, step are as follows：
（1）It is polished with sand paper the hanging runner of selection, then the surface after polishing is cleaned with acetone, then certainly
It so dries, sandblasting roughening treatment is carried out to hanging wheel surface after drying, hanging runner is sprayed with compressed air after sandblasting
Processing is blown, then cleans the surface of hanging runner with acetone again, is heated to 95 DEG C after naturally dry to hanging runner, heat preservation
10min is for use；
（2）Wear-resistant paint is prepared, the wear-resistant paint includes following components according to the mass fraction：
Crystal whisker of hexa potassium titanate：9 parts, dispersant：10 parts, zinc oxide：5 parts, delustering agent：6 parts, glue crosslinking agent：3 parts；Aminomethyl phenyl silicon
Resin：13 parts, thickener：10 parts, binding agent：4 parts, suspending agent：5 parts, surfactant：3 parts, catalyst：3 parts, n-butanol：
7 parts, silane coupling agent；12 parts, curing agent：11 parts；
（3）By step（1）In the hanging runner handled well send 300 DEG C be preheated into heating furnace, in being set subsequently into spraying,
First with spray gun to the tiny grains of sand of valve surface even application, spray distance 150mm, spray angle is 90 °, then rapid heating
Cure, it is 0.08mm to repeat above-mentioned spraying process to coating materials thickness；
（4）The hanging runner for being coated with wear-resistant paint is cooled down, after being cooled to room temperature, is examined, storage.
Embodiment 2
The present embodiment provides a kind of body-building with hanging runner, and runner includes following components by mass percentage：
Al：7%, C：0.13%, Mn：6%, Zn：13%, Ni：3%, Cu：3%, Sc：3%, P：0.008%, S：0.02%, Zr：3%, Ca：
5%, Nb：0.05%, B：0.4%, Sr：5%, Co：4%, V：0.03%, Ti：0.15-0.17%, Na：0.02%, Be：0.03%, rare earth member
Element：0.3%, remaining is Mg and the sum of trace impurity, the above components is 100%；
The rare earth element includes following components by weight percentage： Nd：13%, Gd：9%, Pr：13%, Yb：5%, remaining
For La, the sum of the above components are 100%.
The Wear-resistant Treatment technique of the hanging runner of above-mentioned body-building, step are as follows：
（1）It is polished with sand paper the hanging runner of selection, then the surface after polishing is cleaned with acetone, then certainly
It so dries, sandblasting roughening treatment is carried out to hanging wheel surface after drying, hanging runner is sprayed with compressed air after sandblasting
Processing is blown, then cleans the surface of hanging runner with acetone again, is heated to 80 DEG C after naturally dry to hanging runner, heat preservation
5min is for use；
（2）Wear-resistant paint is prepared, the wear-resistant paint includes following components according to the mass fraction：
Crystal whisker of hexa potassium titanate：7 parts, dispersant：5 parts, zinc oxide：1 part, delustering agent：2 parts, glue crosslinking agent：1 part；Aminomethyl phenyl silicon tree
Fat：11 parts, thickener：5 parts, binding agent：2 parts, suspending agent：3 parts, surfactant：1 part, catalyst：1 part, n-butanol：4
Part, silane coupling agent；8 parts, curing agent：8 parts；
（3）By step（1）In the hanging runner handled well send 200 DEG C be preheated into heating furnace, in being set subsequently into spraying,
First with spray gun to the tiny grains of sand of valve surface even application, spray distance 110mm, spray angle is 80 °, then rapid heating
Cure, it is 0.04mm to repeat above-mentioned spraying process to coating materials thickness；
（4）The hanging runner for being coated with wear-resistant paint is cooled down, after being cooled to room temperature, is examined, storage.
In addition to the implementation, the present invention can also have other embodiment.It is all to use equivalent substitution or equivalent transformation shape
Into technical solution, all fall within the present invention claims protection domain.
Claims (4)
1. the hanging runner of a kind of body-building, which is characterized in that the runner includes following components by mass percentage：
Al：4-7%, C：0.12-0.13%, Mn：3-6%, Zn：10-13%, Ni：1-3%, Cu：1-3%, Sc：2-3%, P：0.005-
0.008%, S：0.01-0.02%, Zr：1-3%, Ca：2-5%, Nb：0.01-0.05%, B：0.2-0.4%, Sr：2-5%, Co：2-4%,
V：0.01-0.03%, Ti：0.15-0.17%, Na：0.01-0.02%, Be：0.02-0.03%, rare earth element：0.1-0.3%, remaining
For Mg and trace impurity, the sum of the above components are 100%；
The rare earth element includes following components by weight percentage： Nd：10-13%, Gd：7-9%, Pr：11-13%, Yb：
3-5%, remaining is that the sum of La, the above components is 100%.
2. the hanging runner of body-building according to claim 1, it is characterised in that：The runner includes by mass percentage
Following components：
Al：4%, C：0.12%, Mn：3%, Zn：10%, Ni：1%, Cu：1%, Sc：2%, P：0.005%, S：0.01%, Zr：1%, Ca：
2%, Nb：0.01%, B：0.2%, Sr：2%, Co：2%, V：0.01%, Ti：0.15%, Na：0.01%, Be：0.02%, rare earth element：
0.1%, remaining is Mg and the sum of trace impurity, the above components is 100%；
The rare earth element includes following components by weight percentage： Nd：10%, Gd：7%, Pr：11%, Yb：3%, remaining
For La, the sum of the above components are 100%.
3. the hanging runner of body-building according to claim 1, it is characterised in that：The runner includes by mass percentage
Following components：
Al：7%, C：0.13%, Mn：6%, Zn：13%, Ni：3%, Cu：3%, Sc：3%, P：0.008%, S：0.02%, Zr：3%, Ca：
5%, Nb：0.05%, B：0.4%, Sr：5%, Co：4%, V：0.03%, Ti：0.15-0.17%, Na：0.02%, Be：0.03%, rare earth member
Element：0.3%, remaining is Mg and the sum of trace impurity, the above components is 100%；
The rare earth element includes following components by weight percentage： Nd：13%, Gd：9%, Pr：13%, Yb：5%, remaining
For La, the sum of the above components are 100%.
4. the Wear-resistant Treatment technique of the hanging runner of body-building as described in any claim in claim 1-3, feature exist
In：
（1）It is polished with sand paper the hanging runner of selection, then the surface after polishing is cleaned with acetone, then certainly
It so dries, sandblasting roughening treatment is carried out to hanging wheel surface after drying, hanging runner is sprayed with compressed air after sandblasting
Processing is blown, then cleans the surface of hanging runner with acetone again, is heated to 80-95 DEG C after naturally dry to hanging runner, is protected
Warm 5-10min is for use；
（2）Wear-resistant paint is prepared, the wear-resistant paint includes following components according to the mass fraction：
Crystal whisker of hexa potassium titanate：7-9 parts, dispersant：5-10 parts, zinc oxide：1-5 parts, delustering agent：2-6 parts, glue crosslinking agent：1-3 parts；
Methyl phenyl silicone resin：11-13 parts, thickener：5-10 parts, binding agent：2-4 parts, suspending agent：3-5 parts, surfactant：1-3
Part, catalyst：1-3 parts, n-butanol：4-7 parts, silane coupling agent；8-12 parts, curing agent：8-11 parts；
（3）By step（1）In the hanging runner handled well send 200-300 DEG C be preheated into heating furnace, set subsequently into spraying
In putting, first with spray gun to the tiny grains of sand of valve surface even application, spray distance 110-150mm, spray angle is 80-90 °,
Then it is heating and curing rapidly, it is 0.04-0.08mm to repeat above-mentioned spraying process to coating materials thickness；
（4）The hanging runner for being coated with wear-resistant paint is cooled down, after being cooled to room temperature, is examined, storage.