CN108047901A - Enhance metal powder coating of decorative effect and preparation method thereof - Google Patents
Enhance metal powder coating of decorative effect and preparation method thereof Download PDFInfo
- Publication number
- CN108047901A CN108047901A CN201711483380.9A CN201711483380A CN108047901A CN 108047901 A CN108047901 A CN 108047901A CN 201711483380 A CN201711483380 A CN 201711483380A CN 108047901 A CN108047901 A CN 108047901A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal powder
- powder coating
- decorative effect
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides the metal powder coating of enhancing decorative effect, in units of parts by weight, including following raw material:15 20 parts of modified poly ester compound, 13 parts of bentonite, 0.5 1 parts of growth agent, 1.5 4.5 parts of metallic pigments, 0.5 1 parts of degasser, 0.2 0.5 parts of dispersant, 0.5 1 parts of toughener, 0.2 0.5 parts of optical brightener, 0.1 0.5 parts of wetting agent, 0.1 0.3 parts of preservative, 0.1 0.3 parts of antioxidant, 0.2 0.5 parts of light stabilizer, the growth agent is β hydroxyalkyl amides, degasser is stearic acid, dispersant is sulphur zinc, toughener is pvc toughener, the wetting agent is heptadecyl imidazole quinoline, and the preservative is 5 chlorine, 2 methyl, 4 isothiazoline, 3 ketone.Above-mentioned raw materials are after broken mixing, squeeze out again through double screw extruder, tabletting, shear and pulverize and sieve after, obtain the coating, metal powder coating of the present invention, by preparing modified modified poly ester compound, antioxidant, light stabilizer are added in, significantly improves the weatherability and impact resistance of metal powder coating.
Description
Technical field
The invention belongs to house ornamentation furnishing fields, are specifically related to metal powder coating and its preparation of enhancing decorative effect
Method.
Background technology
Nearly metal powder coating refers to containing metallic pigments (such as:Cu-Zn alloy powder, silver-colored aluminium powder etc.) various powdery paints.Due to
Metal powder coating can show a kind of bright, luxurious decorative effect, and it is inside and outside to be very suitable for the families such as furniture, ornaments and automobile
The spraying of object.In manufacturing process, domestic market mainly using dry pigmentation (Dry-Blending), also uses in the world
Method (Bonding) is adhesively fixed.
Metal powder end coating is without using volatile solvents such as organic solvent, water, therefore powdery paints is inorganic solvent type
Coating greatly reduces the security risk generated due to solvent, as because organic molten containing operating personnel caused by organic solvent
Agent poisoning or because fire that organic solvent is brought etc..Metal powder coating film metal luster has splendid more
The defencive function of chromatic effect and protrusion provides bright and colourful appearance for the high-grade industrial goods such as automobile, household electrical appliances, instrument and meter
Decoration.It is as long as toasted to can obtain performance directly by powder paint in the iron material Jing Guo suitable pre-treatment or aluminium etc.
Excellent film coated surface, such as the persistence of film, including:Abrasion resistance, impact, adherence, toughness, corrosion resistance and resistance to
Chemicals performance etc., but its humidity resistance and impact resistance still need to further improve, while there is also powder on corner
The shortcomings of paint film defect is difficult to conceal, condition of cure is high after inhomogenous, curing.
The content of the invention
Metal powder coating the present invention provides enhancing decorative effect and preparation method thereof, by the way that modified change will be prepared
Property petchem, add in antioxidant, light stabilizer, significantly improve the weatherability and impact resistance of metal powder coating.
The present invention is achieved by the following technical programs.
Enhance the metal powder coating of decorative effect, in units of parts by weight, including following raw material:Modified poly ester compound
15-20 parts, 1-3 parts of bentonite, 0.5-1 parts of growth agent, 1.5-4.5 parts of metallic pigments, 0.5-1 parts of degasser, dispersant 0.2-
0.5 part, 0.5-1 parts of toughener, 0.2-0.5 parts of optical brightener, 0.1-0.5 parts of wetting agent, 0.1-0.3 parts of preservative, antioxidant
0.1-0.3 parts, 0.2-0.5 parts of light stabilizer, the growth agent are beta-hydroxy alkylamide, and degasser is stearic acid, and dispersant is
Sulphur zinc, toughener are pvc toughener, and the wetting agent is heptadecyl imidazole quinoline, and the preservative is 5- chloro-2-methyls -4
Isothiazoline -3- ketone.
Further, the modified poly ester compound, in units of parts by weight, including following raw material:Poly terephthalic acid
10.5-13 parts of glycol ester, 2-3 parts of 6- hexylene glycols, 2-3 parts of maleic anhydride, 0.5-1 parts of lauryl sodium sulfate.
Further, the preparation method of the modified poly ester compound, comprises the following steps:By poly terephthalic acid second two
Alcohol ester, 6- hexylene glycols are added in reaction kettle, and 200-220 DEG C, insulation reaction 2-4h is warming up under nitrogen protection, sampling it is transparent and
After acid value reaches 15-25mgKOH/g, maleic anhydride is added at 220 DEG C, insulation reaction 1-2h samples transparent and acid value
After reaching 35-45mgKOH/g, lauryl sodium sulfate is added in, heat preservation 1-2h obtains modified poly ester compound.
Further, the metallic pigments, in units of parts by weight, including following raw material:0.5-1.5 parts of titanium dioxide, oxygen
Change 0.5-1.5 parts of iron oxide red, 0.5-1.5 parts of pearl powder.
Further, the optical brightener, in units of parts by weight, including following raw material:Butyl acrylate copolymer 0.1-
0.25 part, 0.1-0.25 parts of methylmethacrylate copolymer.
Further, the antioxidant is phosphite ester.
Further, the light stabilizer is hindered amine light stabilizer.
Meanwhile the system of the metal powder coating present invention provides the enhancing decorative effect as described in claim 1-7
Preparation Method, it is characterised in that:Comprise the following steps:
S1, modified poly ester compound, bentonite, growth agent, metallic pigments, degasser, dispersant part, increasing are weighed in proportion
Tough dose, optical brightener, wetting agent, preservative, antioxidant, light stabilizer, be placed in compounding jar, be sufficiently mixed and crush, premixed
Material;Material after premixing enters double screw extruder extrusion, and in compression section, temperature is 140-160 DEG C, in homogenizing zone temperature
Control is at 120-140 DEG C;Material after extrusion is made sheet body, then is sheared with cutter, system by crusher film-making after cooling
Obtain pelletizing;Pelletizing is finally smashed it through into 400-600 mesh sieve, obtains the metal powder coating.
Further, described in compression section, leading portion I areas temperature is 150-160 DEG C, and back segment II areas temperature is 80-85 DEG C;
Further, the screw speed of the double screw extruder is 110-150r/min.
The beneficial effects of the present invention are:
1. the present invention can be carried by using the modified modified poly ester compound of the preparation that alcoholysis and acidolysis come to prepare metal
The high significant impact for improving low-temperature flexibility and humidity resistance, improving coating, folding test and weatherability.
2. hindered amine light stabilizer can prevent the photochemical degradating of polymer molecule by closing activity center, by
Hindered amine light stabilizer is a kind of free agent capturing agent, by capturing free radical, hydroperoxide decomposition, quenching excited state energy
It measures to reach age inhibiting purpose, with reference to the use of phosphite antioxidant, the two plays synergistic effect, can provide for coating
Such as anti-gloss reduction, anti-decomposition, anti-dropout, Anti- tarnishing are preferably protected.
3. the metal powder coating of enhancing decorative effect of the present invention, nontoxic, pollution-free, environmental protection can be applied once
Film is dressed up, construction cost is low, good decorating effect.
Specific embodiment
Be described further below technical scheme, but claimed scope be not limited to it is described.
Embodiment 1
Enhance the metal powder coating of decorative effect, it is characterised in that:In units of parts by weight, including following raw material:Change
15 parts of petchem of property, 1 part of bentonite, 0.5 part of growth agent, 1.5 parts of metallic pigments, 0.5 part of degasser, 0.2 part of dispersant,
0.5 part of toughener, 0.2 part of optical brightener, 0.1 part of wetting agent, 0.1 part of preservative, 0.1 part of antioxidant, 0.2 part of light stabilizer, institute
Growth agent is stated as beta-hydroxy alkylamide, degasser is stearic acid, and dispersant is sulphur zinc, and toughener is pvc toughener, the profit
Humectant is heptadecyl imidazole quinoline, and the preservative is -4 isothiazoline -3- ketone of 5- chloro-2-methyls, and the antioxidant is phosphorous
Acid esters, the light stabilizer are hindered amine light stabilizer.
The modified poly ester compound, in units of parts by weight, including following raw material:Polyethylene terephthalate
10.5 parts, 2 parts of 6- hexylene glycols, 2 parts of maleic anhydride, 0.5 part of lauryl sodium sulfate.
The preparation method of the modified poly ester compound, comprises the following steps:By polyethylene terephthalate, 6-
Glycol is added in reaction kettle, and 200 DEG C, insulation reaction 2h are warming up under nitrogen protection, is sampled transparent and acid value and is reached
After 15mgKOH/g, maleic anhydride is added at 220 DEG C, insulation reaction 1h samples transparent and acid value and reaches 35mgKOH/g
Afterwards, lauryl sodium sulfate is added in, heat preservation 1h obtains modified poly ester compound.
The metallic pigments, in units of parts by weight, including following raw material:0.5 part of dibutyl tin laurate, titanium dioxide
0.5 part, 0.5 part of iron oxide red, 0.5 part of pearl powder.
The optical brightener, in units of parts by weight, including following raw material:0.1 part of butyl acrylate copolymer, metering system
Sour 0.1 part of methyl terpolymer.
The preparation method of the metal powder coating of the enhancing decorative effect, it is characterised in that:Comprise the following steps:
S1, modified poly ester compound, bentonite, growth agent, metallic pigments, degasser, dispersant part, increasing are weighed in proportion
Tough dose, optical brightener, wetting agent, preservative, antioxidant, light stabilizer, be placed in compounding jar, be sufficiently mixed and crush, premixed
Material;Material after premixing enters double screw extruder extrusion, and in compression section, temperature is 140-160 DEG C, in homogenizing zone temperature
Control is at 120 DEG C;Material after extrusion is by crusher film-making, obtained sheet body after cooling, then is sheared with cutter, is made and cuts
Grain;Pelletizing is finally smashed it through into 400-600 mesh sieve, obtains the metal powder coating.
Described in compression section, leading portion I areas temperature is 150-160 DEG C, and back segment II areas temperature is 150-140 DEG C;It is described double
The screw speed of screw extruder is 110r/min.
Embodiment 2
Enhance the metal powder coating of decorative effect, it is characterised in that:In units of parts by weight, including following raw material:Change
20 parts of petchem of property, 3 parts of bentonite, 1 part of growth agent, 4.5 parts of metallic pigments, 1 part of degasser, 0.5 part of dispersant, toughening
1 part of agent, 0.5 part of optical brightener, 0.5 part of wetting agent, 0.3 part of preservative, 0.3 part of antioxidant, 0.5 part of light stabilizer, it is described to increase electricity
Agent is beta-hydroxy alkylamide, and degasser is stearic acid, and dispersant is sulphur zinc, and toughener is pvc toughener, and the wetting agent is
Heptadecyl imidazole quinoline, the preservative be -4 isothiazoline -3- ketone of 5- chloro-2-methyls, the antioxidant be phosphite ester, institute
Light stabilizer is stated as hindered amine light stabilizer.
The modified poly ester compound, in units of parts by weight, including following raw material:Polyethylene terephthalate 13
Part, 3 parts of 6- hexylene glycols, 3 parts of maleic anhydride, 1 part of lauryl sodium sulfate.
The preparation method of the modified poly ester compound, comprises the following steps:By polyethylene terephthalate, 6-
Glycol is added in reaction kettle, and 220 DEG C, insulation reaction 4h are warming up under nitrogen protection, is sampled transparent and acid value and is reached
After 25mgKOH/g, maleic anhydride is added at 220 DEG C, insulation reaction 2h samples transparent and acid value and reaches 45mgKOH/g
Afterwards, lauryl sodium sulfate is added in, heat preservation 2h obtains modified poly ester compound.
The metallic pigments, in units of parts by weight, including following raw material:1.5 parts of titanium dioxide, 1.5 parts of iron oxide red, pearl
1.5 parts of light powder.
The optical brightener, in units of parts by weight, including following raw material:0.25 part of butyl acrylate copolymer, methyl-prop
0.25 part of e pioic acid methyl ester copolymer.
The preparation method of the metal powder coating of the enhancing decorative effect, it is characterised in that:Comprise the following steps:
S1, modified poly ester compound, bentonite, growth agent, metallic pigments, degasser, dispersant part, increasing are weighed in proportion
Tough dose, optical brightener, wetting agent, preservative, antioxidant, light stabilizer, be placed in compounding jar, be sufficiently mixed and crush, premixed
Material;Material after premixing enters double screw extruder extrusion, and in compression section, temperature is 140-160 DEG C, in homogenizing zone temperature
Control is at 140 DEG C;Material after extrusion is by crusher film-making, obtained sheet body after cooling, then is sheared with cutter, is made and cuts
Grain;Pelletizing is finally smashed it through into 600 mesh sieve, obtains the metal powder coating.
Described in compression section, leading portion I areas temperature is 150-160 DEG C, and back segment II areas temperature is 80-85 DEG C;Double spiral shells
The screw speed of bar extruder is 150r/min.
Embodiment 3
Enhance the metal powder coating of decorative effect, it is characterised in that:In units of parts by weight, including following raw material:Change
Property 18 parts of petchem, 2 parts of bentonite, 0.8 part of growth agent, 3 parts of metallic pigments, 0.8 part of degasser, 0.4 part of dispersant, increase
Tough dose 0.7 part, 0.4 part of optical brightener, 0.3 part of wetting agent, 0.2 part of preservative, 0.14 part of antioxidant, 0.4 part of light stabilizer, it is described
Growth agent is beta-hydroxy alkylamide, and degasser is stearic acid, and dispersant is sulphur zinc, and toughener is pvc toughener, the wetting
Agent is heptadecyl imidazole quinoline, and the preservative is -4 isothiazoline -3- ketone of 5- chloro-2-methyls, and the antioxidant is phosphorous acid
Ester, the light stabilizer are hindered amine light stabilizer.
The modified poly ester compound, in units of parts by weight, including following raw material:Polyethylene terephthalate 12
Part, 2.5 parts of 6- hexylene glycols, 2.8 parts of maleic anhydride, 0.7 part of lauryl sodium sulfate.
The preparation method of the modified poly ester compound, comprises the following steps:By polyethylene terephthalate, 6-
Glycol is added in reaction kettle, and 180 DEG C, insulation reaction 3h are warming up under nitrogen protection, is sampled transparent and acid value and is reached
After 20mgKOH/g, maleic anhydride is added at 220 DEG C, insulation reaction 1.5h samples transparent and acid value and reaches 40mgKOH/
After g, lauryl sodium sulfate is added in, heat preservation 1.5h obtains modified poly ester compound.
The metallic pigments, in units of parts by weight, including following raw material:1 part of titanium dioxide, 1 part of iron oxide red, pearl powder
1 part.
The optical brightener, in units of parts by weight, including following raw material:0.2 part of butyl acrylate copolymer, metering system
Sour 0.2 part of methyl terpolymer.
The preparation method of the metal powder coating of the enhancing decorative effect, it is characterised in that:Comprise the following steps:
S1, modified poly ester compound, bentonite, growth agent, metallic pigments, degasser, dispersant part, increasing are weighed in proportion
Tough dose, optical brightener, wetting agent, preservative, antioxidant, light stabilizer, be placed in compounding jar, be sufficiently mixed and crush, premixed
Material;Material after premixing enters double screw extruder extrusion, and in compression section, temperature is 140-160 DEG C, in homogenizing zone temperature
Control is at 130 DEG C;Material after extrusion is by crusher film-making, obtained sheet body after cooling, then is sheared with cutter, is made and cuts
Grain;Pelletizing is finally smashed it through into 500 mesh sieve, obtains the metal powder coating.
Described in compression section, leading portion I areas temperature is 150-160 DEG C, and back segment II areas temperature is 80-85 DEG C;Double spiral shells
The screw speed of bar extruder is 1300r/min.
Embodiment 4
Enhance the metal powder coating of decorative effect, it is characterised in that:In units of parts by weight, including following raw material:Change
15 parts of petchem of property, 3 parts of bentonite, 0.5 part of growth agent, 4.5 parts of metallic pigments, 0.5 part of degasser, 0.2 part of dispersant,
1 part of toughener, 0.2 part of optical brightener, 0.1 part of wetting agent, 0.3 part of preservative, 0.1 part of antioxidant, 0.5 part of light stabilizer, it is described
Growth agent is beta-hydroxy alkylamide, and degasser is stearic acid, and dispersant is sulphur zinc, and toughener is pvc toughener, the wetting
Agent is heptadecyl imidazole quinoline, and the preservative is -4 isothiazoline -3- ketone of 5- chloro-2-methyls, and the antioxidant is phosphorous acid
Ester, the light stabilizer are hindered amine light stabilizer.
The modified poly ester compound, in units of parts by weight, including following raw material:Polyethylene terephthalate
10.5 parts, 2 parts of 6- hexylene glycols, 2 parts of maleic anhydride, 0.5 part of lauryl sodium sulfate.
The preparation method of the modified poly ester compound, comprises the following steps:By polyethylene terephthalate, 6-
Glycol is added in reaction kettle, and 205 DEG C, insulation reaction 2h are warming up under nitrogen protection, is sampled transparent and acid value and is reached
After 15mgKOH/g, maleic anhydride is added at 220 DEG C, insulation reaction 1.8h samples transparent and acid value and reaches 45mgKOH/
After g, lauryl sodium sulfate is added in, heat preservation 1.1h obtains modified poly ester compound.
The metallic pigments, in units of parts by weight, including following raw material:1.5 parts of titanium dioxide, 1.5 parts of iron oxide red, pearl
1.5 parts of light powder.
The optical brightener, in units of parts by weight, including following raw material:0.1 part of butyl acrylate copolymer, metering system
Sour 0.1 part of methyl terpolymer.
The preparation method of the metal powder coating of the enhancing decorative effect, it is characterised in that:Comprise the following steps:
S1, modified poly ester compound, bentonite, growth agent, metallic pigments, degasser, dispersant part, increasing are weighed in proportion
Tough dose, optical brightener, wetting agent, preservative, antioxidant, light stabilizer, be placed in compounding jar, be sufficiently mixed and crush, premixed
Material;Material after premixing enters double screw extruder extrusion, and in compression section, temperature is 140-160 DEG C, in homogenizing zone temperature
Control is at 125 DEG C;Material after extrusion is by crusher film-making, obtained sheet body after cooling, then is sheared with cutter, is made and cuts
Grain;Pelletizing is finally smashed it through into 400-600 mesh sieve, obtains the metal powder coating.
Described in compression section, leading portion I areas temperature is 150-160 DEG C, and back segment II areas temperature is 80-85 DEG C;Double spiral shells
The screw speed of bar extruder is 125r/min.
Comparative example 1
In the raw material composition of the metal powder coating of the enhancing decorative effect, no modified poly ester compound, and use
Conventional saturated polyester compound, other conditions are consistent with embodiment 3.
Comparative example 2
In the raw material composition of the metal powder coating of the enhancing decorative effect, antioxidant and light in no embodiment 3
Stabilizer, other conditions are consistent with embodiment 3.
Comparative example 3
In the raw material composition of the metal powder coating of the enhancing decorative effect, the light stabilizer in no embodiment 3,
His condition is consistent with embodiment 3.
Comparative example 4
In the raw material composition of the metal powder coating of the enhancing decorative effect, antioxidant in no embodiment 3, other
Part is consistent with embodiment 3.
By the powdery paints prepared by embodiment 1-4 and comparative example 1-4, applied according to a conventional method to indoor decoration
Material, then be tested for the property, test result is as in the table below:
1 the performance test results of table
It is analyzed from the result of embodiment 1- embodiments 4, the powdery paints that the present invention prepares is applied to actual production
When in journey, weatherability >=1500h, coating is more smooth than relatively thin (film thickness≤40 μm) and surface, three-dimensional sense is strong, and glossiness is good
(more than 87) have preferable impact (50cmkg) and folding test result (more than 3mm)
From embodiment 3 and the testing result of comparative example 1, it can be seen that modified petchem is as in metal powder
Important substrate, the modified petchem of the preparation that comes by using alcoholysis and acidolysis can improve preparing metal and significantly carry
High/low temperature toughness and humidity resistance improve the impact of coating, folding test and weatherability.
From embodiment 3 and the testing result of comparative example 2-4, it can be seen that when there is no hindered amine light stabilizers and Asia
During phosphate antioxidant, the performance of coating is significantly substantially reduced (gloss is reduced to 55, weatherability and is reduced to 600h), when only depositing
In hindered amine light stabilizer or phosphite antioxidant, the performance of coating has the reduction of certain amplitude, and (gloss is reduced to 73
Left and right, weatherability are reduced to 750h), when all there are when hindered amine light stabilizer and phosphite antioxidant, each side of coating
The performance in face obtains more apparent promotion, and the analysis of causes is as follows:
Hindered amine light stabilizer can prevent the photochemical degradating of polymer molecule by closing activity center, be obstructed
Amine light stabilizer is a kind of free agent capturing agent, by capturing free radical, hydroperoxide decomposition, quenching excited state energy
Reach age inhibiting purpose, with reference to the use of phosphite antioxidant, the two plays synergistic effect, can be provided for coating as
Anti- gloss reduction, anti-decomposition, anti-dropout, Anti- tarnishing etc. are preferably protected.
The above content is combine specific/preferred embodiment further description made for the present invention, it is impossible to
Assert that the specific implementation of the present invention is confined to these explanations.Come for general technical staff of the technical field of the invention
It says, without departing from the inventive concept of the premise, some replacements or modification can also be made to the embodiment that these have been described,
And these are substituted or variant should all be considered as belonging to protection scope of the present invention.
Claims (10)
1. enhance the metal powder coating of decorative effect, it is characterised in that:In units of parts by weight, including following raw material:It is modified
15-20 parts of petchem, 1-3 parts of bentonite, 0.5-1 parts of growth agent, 1.5-4.5 parts of metallic pigments, 0.5-1 parts of degasser,
0.2-0.5 parts of dispersant, 0.5-1 parts of toughener, 0.2-0.5 parts of optical brightener, 0.1-0.5 parts of wetting agent, preservative 0.1-0.3
Part, 0.1-0.3 parts of antioxidant, 0.2-0.5 parts of light stabilizer, the growth agent are beta-hydroxy alkylamide, and degasser is stearic acid,
Dispersant is sulphur zinc, and toughener is pvc toughener, and the wetting agent is heptadecyl imidazole quinoline, and the preservative is chloro- for 5-
- 4 isothiazoline -3- ketone of 2- methyl.
2. the metal powder coating of enhancing decorative effect according to claim 1, it is characterised in that:The modified poly ester
Object is closed, in units of parts by weight, including following raw material:10.5-13 parts of polyethylene terephthalate, 2-3 parts of 6- hexylene glycols,
2-3 parts of maleic anhydride, 0.5-1 parts of lauryl sodium sulfate.
3. the metal powder coating of enhancing decorative effect according to claim 2, it is characterised in that:The modified poly ester
The preparation method of object is closed, is comprised the following steps:Polyethylene terephthalate, 6- hexylene glycols are added in reaction kettle, nitrogen
200-220 DEG C, insulation reaction 2-4h is warming up under gas shielded, after the transparent and acid value of sampling reaches 15-25mgKOH/g, at 220 DEG C
Lower addition maleic anhydride, insulation reaction 1-2h after the transparent and acid value of sampling reaches 35-45mgKOH/g, add in dodecyl
Sodium sulphate, heat preservation 1-2h obtain modified poly ester compound.
4. the metal powder coating of enhancing decorative effect according to claim 1, it is characterised in that:The metallic pigments,
In units of parts by weight, including following raw material:0.5-1.5 parts of titanium dioxide, 0.5-1.5 parts of iron oxide red, pearl powder 0.5-1.5
Part.
5. the metal powder coating of enhancing decorative effect according to claim 1, it is characterised in that:The optical brightener, with
Parts by weight are unit, including following raw material:0.1-0.25 parts of butyl acrylate copolymer, methylmethacrylate copolymer 0.1-
0.25 part.
6. the metal powder coating of enhancing decorative effect according to claim 1, it is characterised in that:The antioxidant is Asia
Phosphate.
7. the metal powder coating of enhancing decorative effect according to claim 1, it is characterised in that:The light stabilizer is
Hindered amine light stabilizer.
8. a kind of preparation method for the metal powder coating for enhancing decorative effect such as claim 1-7 any one of them, special
Sign is:Comprise the following steps:
S1, each component raw material is weighed in proportion, be placed in compounding jar, be sufficiently mixed and crushed, obtain premix material;After premixing
Material enters double screw extruder extrusion, and in compression section, temperature is 140-160 DEG C, is controlled in homogenizing zone temperature at 120-140 DEG C;
Material after extrusion is made sheet body, then is sheared with cutter, obtained pelletizing by crusher film-making after cooling;It will finally cut
Grain smashes it through 400-600 mesh sieve, obtains the metal powder coating.
9. the preparation method of the metal powder coating of enhancing decorative effect according to claim 8, it is characterised in that:It is described
In compression section, leading portion I areas temperature is 150-160 DEG C, and back segment II areas temperature is 150-140 DEG C.
10. the preparation method of the metal powder coating of enhancing decorative effect according to claim 8, it is characterised in that:Institute
The screw speed for stating double screw extruder is 110-150r/min.