CN108046695A - Glass bead insulation plate and its processing method - Google Patents
Glass bead insulation plate and its processing method Download PDFInfo
- Publication number
- CN108046695A CN108046695A CN201711319220.0A CN201711319220A CN108046695A CN 108046695 A CN108046695 A CN 108046695A CN 201711319220 A CN201711319220 A CN 201711319220A CN 108046695 A CN108046695 A CN 108046695A
- Authority
- CN
- China
- Prior art keywords
- glass bead
- parts
- insulation plate
- rubber powder
- portland cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of glass bead insulation plate and its processing method.The glass bead insulation plate of the present invention includes glass bead particle, rubber powder, portland cement, plant fiber, felt, and the parts by weight of each component are:25 36 parts of glass bead particle, 38 parts of rubber powder, 18 23 parts of portland cement, 15 20 parts of plant fiber, 36 parts of felt.Fire-protection rating of the present invention can reach A grades, and soundproof effect is good, and service life is long.
Description
Technical field:
The present invention relates to a kind of glass bead insulation plate and its processing methods, belong to thermal insulation board production technical field.
Background technology:
It is to add other supplementary materials and poly- inclusion by raw material of polystyrene resin to thermal insulation board, is noted simultaneously by heating mixing
Enter catalyst, then extrusion molding extrusion molding and the rigid foam plate that manufactures, there is moisture-proof, water resistance, reduction can be built
Beyond the region of objective existence building enclosure thickness is built, so as to increase indoor usable floor area.
Existing thermal insulation board is mainly using EPS particles, by the expandable polystyrene pearl containing volatile fluid foaming agent
Grain, the white solid with fine hole-closing structure of hot briquetting in a mold after heated pre- hair.Benzene plate is inflammable, heat preservation
Effect is good, but easily water suction, and weight is caused to increase deformation, and waterproof measure has to handle properly, and otherwise can directly affect makes
With the service life along with fire protecting performance is low, complicated construction technique is, it is necessary to add grid cloth, therefore cannot meet the need of market development
It will.
To solve the above-mentioned problems, it is micro- to include inorganic vitreous for 201410155631.0 glass bead insulation plate of Chinese patent
Pearl, rubber powder, cellulose, portland cement, chlorine oxygen magnesium, the parts by weight of each component are:Inorganic glass bead 38-55 parts, rubber powder
7-16 parts, 23-33 parts of cellulose, 25-30 parts of cement, 15-23 parts of chlorine oxygen magnesium.Processing method includes(1)To portland cement into
The inorganic foamed processing of row;(2)Portland cement, inorganic glass bead, cellulose, chlorine oxygen magnesium after foaming is mixed in parts by weight
It closes, stirs 3-7 minutes;(3)It prepares rubber powder and the rubber powder made is added in into step(2)Product in stir 15-20 minutes;(4)
By step(3)Product pour into mold, room temperature conserve 3-5 days after stripping and slicing, then 260-320 DEG C conserve 8-12 it is small when.The party
The glass bead insulation plate fire protecting performance of method production is good, but its soundproof effect is bad.
The content of the invention:
The purpose of the present invention is provide a kind of glass bead insulation plate and its processing method, fire prevention etc. in view of the above problems
Grade can reach A grades, and soundproof effect is good, and service life is long.
Above-mentioned purpose is realized by following technical scheme:
Glass bead insulation plate, including glass bead particle, rubber powder, portland cement, plant fiber, felt, the weight of each component
Measuring number is:25-36 parts of glass bead particle, 3-8 parts of rubber powder, 18-23 parts of portland cement, 15-20 parts of plant fiber, felt
3-6 parts.
The glass bead insulation plate, the rubber powder is by the waterglass of weight percent 50~70%, the phosphoric acid of 1-4%
Salt powder, the magnesium oxide powder of 4-8%, the hydrophober of 1-4%, the water composition of the magnesium sulfate of 5-7% and surplus.
The processing method of above-mentioned glass bead insulation plate, this method comprises the following steps:
(1)Inorganic foamed processing is carried out to portland cement;
(2)Portland cement, inorganic glass bead, cellulose after foaming is mixed in parts by weight, is stirred 3-7 minutes;
(3)It prepares rubber powder and the rubber powder made is added in into step(2)Stirring 15-20 minutes after in product obtained;
(4)By step(3)Product pour into mold, the thickness of addition is 1/3rd of mold thickness, is smoothed out with instrument, then
Layer overlay felt finally goes up step again(3)Product until equal with mold thickness, room temperature conserve 3-5 days after stripping and slicing, so
When 260-320 DEG C of maintenance 8-12 is small afterwards.
The processing method of the glass bead insulation plate, step(1)Described in inorganic hair is carried out to portland cement
Steeping the method for processing is:By cement and water according to 1:The ratio of 12-13 is sent into foaming machine and carries out physical blowing.
The processing method of the glass bead insulation plate, step(3)Described in the rubber powder for preparing be according to weight percent
Than by magnesium oxide powder part, hydrophober part of 1-4%, 5-7% of phosphate powder part of 50~70% waterglass, 1-4%, 4-8%
Magnesium sulfate and the water of surplus be thoroughly mixed.
Advantageous effect:
1. the present invention adds one layer of felt among glass bead insulation plate, not only high insulating effect, and its sound insulation is imitated
Fruit greatly improves, and due to the supporting role of felt, intensity is more preferable, and service life is long.
2. the present invention is without using inflammable rubber powder, fire-protection rating is high, good environmental protection.
Specific embodiment:
Embodiment 1:
Glass bead insulation plate, including glass bead particle, rubber powder, portland cement, plant fiber, felt, the weight of each component
Measuring number is:25 parts of glass bead particle, 8 parts of rubber powder, 18 parts of portland cement, 20 parts of plant fiber, 3 parts of felt.
The glass bead insulation plate, waterglass of the rubber powder by weight percent 70%, 1% phosphoric acid salt fines
End, 8% magnesium oxide powder, 1% hydrophober, the water composition of 7% magnesium sulfate and surplus.
The processing method of above-mentioned glass bead insulation plate, this method comprises the following steps:
(1)Inorganic foamed processing is carried out to portland cement;
(2)Portland cement, inorganic glass bead, cellulose after foaming is mixed in parts by weight, is stirred 7 minutes;
(3)It prepares rubber powder and the rubber powder made is added in into step(2)Stirring 15 minutes after in product obtained;
(4)By step(3)Product pour into mold, the thickness of addition is 1/3rd of mold thickness, is smoothed out with instrument, then
Layer overlay felt finally goes up step again(3)Product until equal with mold thickness, room temperature conserve 5 days after stripping and slicing, then
When 320 DEG C of maintenances 8 are small.
The processing method of the glass bead insulation plate, step(1)Described in inorganic hair is carried out to portland cement
Steeping the method for processing is:By cement and water according to 1:13 ratio is sent into foaming machine and carries out physical blowing.
The processing method of the glass bead insulation plate, step(3)Described in the rubber powder for preparing be according to weight percent
Than by the water of the magnesium sulfate of the hydrophober of the magnesium oxide powder of the phosphate powder of 70% waterglass, 1%, 8%, 1%, 7% and surplus
It is thoroughly mixed.
Embodiment 2:
Glass bead insulation plate, including glass bead particle, rubber powder, portland cement, plant fiber, felt, the weight of each component
Measuring number is:36 parts of glass bead particle, 3 parts of rubber powder, 23 parts of portland cement, 15 parts of plant fiber, 6 parts of felt.
The glass bead insulation plate, waterglass of the rubber powder by weight percent 50%, 4% phosphoric acid salt fines
End, 4% magnesium oxide powder, 4% hydrophober, the water composition of 5% magnesium sulfate and surplus.
The processing method of above-mentioned glass bead insulation plate, this method comprises the following steps:
(1)Inorganic foamed processing is carried out to portland cement;
(2)Portland cement, inorganic glass bead, cellulose after foaming is mixed in parts by weight, is stirred 3 minutes;
(3)It prepares rubber powder and the rubber powder made is added in into step(2)Stirring 20 minutes after in product obtained;
(4)By step(3)Product pour into mold, the thickness of addition is 1/3rd of mold thickness, is smoothed out with instrument, then
Layer overlay felt finally goes up step again(3)Product until equal with mold thickness, room temperature conserve 3 days after stripping and slicing, then
When 260 DEG C of maintenances 12 are small.
The processing method of the glass bead insulation plate, step(1)Described in inorganic hair is carried out to portland cement
Steeping the method for processing is:By cement and water according to 1:13 ratio is sent into foaming machine and carries out physical blowing.
The processing method of the glass bead insulation plate, step(3)Described in the rubber powder for preparing be according to weight percent
Than by the water of the magnesium sulfate of the hydrophober of the magnesium oxide powder of the phosphate powder of 50% waterglass, 4%, 4%, 4%, 5% and surplus
It is thoroughly mixed.
Embodiment 3:
Glass bead insulation plate, including glass bead particle, rubber powder, portland cement, plant fiber, felt, the weight of each component
Measuring number is:32 parts of glass bead particle, 5 parts of rubber powder, 21 parts of portland cement, 18 parts of plant fiber, 5 parts of felt.
The glass bead insulation plate, waterglass of the rubber powder by weight percent 60%, 3% phosphoric acid salt fines
End, 5% magnesium oxide powder, 3% hydrophober, the water composition of 6% magnesium sulfate and surplus.
The processing method of above-mentioned glass bead insulation plate, this method comprises the following steps:
(1)Inorganic foamed processing is carried out to portland cement;
(2)Portland cement, inorganic glass bead, cellulose after foaming is mixed in parts by weight, is stirred 6 minutes;
(3)It prepares rubber powder and the rubber powder made is added in into step(2)Stirring 18 minutes after in product obtained;
(4)By step(3)Product pour into mold, the thickness of addition is 1/3rd of mold thickness, is smoothed out with instrument, then
Layer overlay felt finally goes up step again(3)Product until equal with mold thickness, room temperature conserve 4 days after stripping and slicing, then
When 300 DEG C of maintenances 10 are small.
The processing method of the glass bead insulation plate, step(1)Described in inorganic hair is carried out to portland cement
Steeping the method for processing is:By cement and water according to 1:12 ratio is sent into foaming machine and carries out physical blowing.
The processing method of the glass bead insulation plate, step(3)Described in the rubber powder for preparing be according to weight percent
Than by the water of the magnesium sulfate of the hydrophober of the magnesium oxide powder of the phosphate powder of 60% waterglass, 3%, 5%, 3%, 6% and surplus
It is thoroughly mixed.
It the above is only highly preferred embodiment of the present invention, it is public that technical scheme includes but not limited to above-described embodiment institute
The technical solution opened, unaccomplished matter of the invention belong to the common knowledge of those skilled in the art.
Claims (5)
1. a kind of glass bead insulation plate, it is characterized in that:Including glass bead particle, rubber powder, portland cement, plant fiber,
Felt, the parts by weight of each component are:25-36 parts of glass bead particle, 3-8 parts of rubber powder, 18-23 parts of portland cement, plant
15-20 parts of fiber, 3-6 parts of felt.
2. glass bead insulation plate according to claim 1, it is characterized in that:The rubber powder by weight percent 50~
70% waterglass, the phosphate powder of 1-4%, the magnesium oxide powder of 4-8%, the hydrophober of 1-4%, the magnesium sulfate of 5-7% and surplus
Water composition.
3. a kind of processing method of glass bead insulation plate, it is characterized in that:This method comprises the following steps:
(1)Inorganic foamed processing is carried out to portland cement;
(2)Portland cement, inorganic glass bead, cellulose after foaming is mixed in parts by weight, is stirred 3-7 minutes;
(3)It prepares rubber powder and the rubber powder made is added in into step(2)Stirring 15-20 minutes after in product obtained;
(4)By step(3)Product pour into mold, the thickness of addition is 1/3rd of mold thickness, is smoothed out with instrument, then
Layer overlay felt finally goes up step again(3)Product until equal with mold thickness, room temperature conserve 3-5 days after stripping and slicing, so
When 260-320 DEG C of maintenance 8-12 is small afterwards.
4. the processing method of glass bead insulation plate according to claim 3, it is characterized in that:Step(1)Described in pair
The method that portland cement carries out inorganic foamed processing is:By cement and water according to 1:The ratio of 12-13 be sent into foaming machine into
Row physical blowing.
5. the processing method of glass bead insulation plate according to claim 3, it is characterized in that:Step(3)Described in system
Standby rubber powder be according to weight percent by 50~70% waterglass, phosphate powder part of 1-4%, 4-8% magnesium oxide powder
Part, hydrophober part of 1-4%, the magnesium sulfate of 5-7% and the water of surplus are thoroughly mixed.