CN108046623A - A kind of portland cement - Google Patents
A kind of portland cement Download PDFInfo
- Publication number
- CN108046623A CN108046623A CN201711433313.6A CN201711433313A CN108046623A CN 108046623 A CN108046623 A CN 108046623A CN 201711433313 A CN201711433313 A CN 201711433313A CN 108046623 A CN108046623 A CN 108046623A
- Authority
- CN
- China
- Prior art keywords
- parts
- clinker
- cement
- present
- portland
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to building material technical fields, and in particular to a kind of portland cement.Include the ingredient of following parts by weight:Portland clinker:85 95 parts;Gypsum:48 parts;Coagulant:12 parts;Water-reducing agent:23 parts.The present invention improves the early strength of cement, the intensity of particularly three hours or four hours by adding in coagulant and water-reducing agent.Shorten the demoulding time of cement, improve architecture production efficiency.In clinker suitable alkalinity is brought by adding in sodium hydroxide, accelerate the early hydration speed of clinker, further improve the early strength of cement, a small amount of iron ion is brought by adding in iron oxide in clinker, so that clinker burning temperature is relatively low, the heat consumption during clinker burning is reduced.
Description
Technical field
The present invention relates to building material technical fields, and in particular to a kind of portland cement.
Background technology
Cement is powdery hydraulicity inorganic coagulation material.Add water stir after into slurry, can in air harden or in water
In preferably harden, and can the materials such as sand, stone are cemented together securely.
The mixture of early stage lime and volcanic ash and modern lime pozzolanic cement are much like, are made of its cementing rubble
Concrete, not only intensity is higher after hardening, and can also resist the erosion of fresh water or brackish water.For a long time, it is as one
The important cementitious material of kind, is widely used in the engineerings such as civil construction, water conservancy, national defence.
Portland cement is a kind of important construction material, the early strength of cement it is higher, more contribute to shorten demoulding
Time improves production efficiency.
The content of the invention
The mesh of the present invention is, for problems of the prior art, proposes a kind of portland cement, improves cement
Early strength.
To achieve these goals, the technical solution adopted by the present invention is:
A kind of portland cement includes the ingredient of following parts by weight:
Portland clinker:85-95 parts;
Gypsum:4-8 parts;
Coagulant:1-2 parts;
Water-reducing agent:2-3 parts.
The Portland clinker includes the ingredient of following parts by weight:
Lime stone:50-60 parts;
Clay:20-30 parts;
Gypsum:10-15 parts;
Additive:2-5 parts;
The additive is sodium hydroxide.
Further, the Portland clinker includes the ingredient of following parts by weight:
Lime stone:55 parts;
Clay:25 parts;
Gypsum:12 parts;
Additive:4 parts;
The additive is sodium hydroxide.
Further, the additive further includes iron oxide.
Further, the weight ratio of the sodium hydroxide and iron oxide is 5:1.
By adopting the above-described technical solution, the beneficial effects of the invention are as follows:
The present invention improves the early strength of cement by adding in coagulant and water-reducing agent, particularly three hours or four hours strong
Degree.Shorten the demoulding time of cement, improve architecture production efficiency.In clinker by add in sodium hydroxide bring into it is suitable
Alkalinity accelerates the early hydration speed of clinker, the early strength of cement is further improved, by being added in clinker
Iron oxide brings a small amount of iron ion into so that clinker burning temperature is relatively low, reduces the heat consumption during clinker burning.
Specific embodiment
The present invention is described in detail below.
It, below will be in the embodiment of the present invention to make the purpose, technical scheme and advantage of the embodiment of the present invention clearer
Technical solution be clearly and completely described, it is clear that described embodiment be part of the embodiment of the present invention rather than
Whole embodiments.
Therefore, the detailed description of the embodiment of the present invention presented below is not intended to limit claimed invention
Scope, but it is merely representative of the selected embodiment of the present invention.Based on the embodiments of the present invention, those of ordinary skill in the art exist
All other embodiments obtained under the premise of creative work are not made, belong to the scope of protection of the invention.
In the description of the present invention, it is also necessary to explanation, unless otherwise clearly defined and limited, term " setting ",
" installation ", " connection " should be interpreted broadly, for example, it may be being fixedly connected or being detachably connected or integrally connect
It connects;Can be mechanical connection or electrical connection;It can be directly connected, can also be indirectly connected by intermediary, it can
To be the connection inside two elements.For the ordinary skill in the art, can above-mentioned term be understood with concrete condition
Concrete meaning in the present invention.
Embodiment 1
As a kind of preferred embodiment of the present invention, present embodiment discloses a kind of portland cement, the present embodiment includes:
A kind of portland cement includes the ingredient of following parts by weight:
Portland clinker:85 parts;
Gypsum:4 parts;
Coagulant:1 part;
Water-reducing agent:2 parts.
The Portland clinker includes the ingredient of following parts by weight:
Lime stone:50 parts;
Clay:20 parts;
Gypsum:10 parts;
Additive:2 parts;
The additive is sodium hydroxide.
The additive further includes iron oxide.
The weight ratio of the sodium hydroxide and iron oxide is 5:1.
Embodiment 2
As a kind of preferred embodiment of the present invention, present embodiment discloses a kind of portland cement, the present embodiment includes:
A kind of portland cement includes the ingredient of following parts by weight:
Portland clinker:90 parts;
Gypsum:6 parts;
Coagulant:1 part;
Water-reducing agent:2 parts.
The Portland clinker includes the ingredient of following parts by weight:
Lime stone:55 parts;
Clay:25 parts;
Gypsum:12 parts;
Additive:4 parts;
The additive is sodium hydroxide.
The additive further includes iron oxide.
The weight ratio of the sodium hydroxide and iron oxide is 5:1.
Embodiment 3
As a kind of preferred embodiment of the present invention, present embodiment discloses a kind of portland cement, the present embodiment includes:
A kind of portland cement includes the ingredient of following parts by weight:
Portland clinker:95 parts;
Gypsum:8 parts;
Coagulant:2 parts;
Water-reducing agent:3 parts.
The Portland clinker includes the ingredient of following parts by weight:
Lime stone:60 parts;
Clay:30 parts;
Gypsum:15 parts;
Additive:5 parts;
The additive is sodium hydroxide.
Further, the additive further includes iron oxide.
Further, the weight ratio of the sodium hydroxide and iron oxide is 5:1.
Embodiment 4
As a kind of preferred embodiment of the present invention, present embodiment discloses a kind of portland cement, the present embodiment includes:
A kind of portland cement includes the ingredient of following parts by weight:
Portland clinker:85 parts;
Gypsum:4 parts;
Coagulant:1 part;
Water-reducing agent:2 parts.
Claims (5)
1. a kind of portland cement, which is characterized in that include the ingredient of following parts by weight:
Portland clinker:85-95 parts;
Gypsum:4-8 parts;
Coagulant:1-2 parts;
Water-reducing agent:2-3 parts.
2. portland cement according to claim 1, which is characterized in that the Portland clinker includes following weight
The ingredient of part:
Lime stone:50-60 parts;
Clay:20-30 parts;
Gypsum:10-15 parts;
Additive:2-5 parts;
The additive is sodium hydroxide.
3. portland cement according to claim 1, which is characterized in that the Portland clinker includes following weight
The ingredient of part:
Lime stone:55 parts;
Clay:25 parts;
Gypsum:12 parts;
Additive:4 parts;
The additive is sodium hydroxide.
4. the portland cement according to Claims 2 or 3, it is characterised in that:The additive further includes iron oxide.
5. portland cement according to claim 4, it is characterised in that:The weight ratio of the sodium hydroxide and iron oxide is
5:1.