CN108147688A - A kind of preparation method of Portland clinker - Google Patents
A kind of preparation method of Portland clinker Download PDFInfo
- Publication number
- CN108147688A CN108147688A CN201711433295.1A CN201711433295A CN108147688A CN 108147688 A CN108147688 A CN 108147688A CN 201711433295 A CN201711433295 A CN 201711433295A CN 108147688 A CN108147688 A CN 108147688A
- Authority
- CN
- China
- Prior art keywords
- parts
- additive
- portland clinker
- preparation
- gypsum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to building material technical fields, and in particular to a kind of preparation method of Portland clinker.Include the following steps:It is crushed Step 1: lime stone, clay and gypsum are added in crusher;Step 2: by additive is added in broken mixture, it is then fed into grinder and grinds, raw material are made;It calcines, cools down Step 3: raw material are put into rotary kiln, Portland clinker is made.The present invention brings suitable alkalinity by adding in sodium hydroxide, accelerates the early hydration speed of clinker, improves the early strength of cement, shortens demoulding time, and the durability of cement later strength and cement is also secure.A small amount of iron ion is brought by adding in iron oxide so that clinker burning temperature is relatively low, reduces the heat consumption during clinker burning.
Description
Technical field
The present invention relates to building material technical fields, and in particular to a kind of preparation method of Portland clinker.
Background technology
Cement is powdery hydraulicity inorganic coagulation material.Add water stir after into slurry, can in air harden or in water
In preferably harden, and can the materials such as sand, stone are cemented together securely.
The mixture of early stage lime and volcanic ash and modern lime pozzolanic cement are much like, are made of its cementing rubble
Concrete, not only intensity is higher after hardening, and can also resist the erosion of fresh water or brackish water.For a long time, it is as one
The important cementitious material of kind, is widely used in the engineerings such as civil construction, water conservancy, national defence.
Portland clinker is the important materials for producing portland cement, and the performance of Portland clinker determines silicon
The performance of acid salt cement.The raising of cement early strength helps to shorten demoulding time, improves production efficiency.
Invention content
The mesh of the present invention is, for problems of the prior art, proposes a kind of preparation of Portland clinker
Method improves the early strength of cement.
To achieve these goals, the technical solution adopted by the present invention is:
A kind of preparation method of Portland clinker, including such as step:
It is crushed Step 1: lime stone, clay and gypsum are added in crusher;
Step 2: by additive is added in broken mixture, it is then fed into grinder and grinds, raw material are made;
It calcines, cools down Step 3: raw material are put into rotary kiln, Portland clinker is made.
The lime stone, clay, gypsum and additive parts by weight be:
Lime stone:50-60 parts;
Clay:20-30 parts;
Gypsum:10-15 parts;
Additive:2-5 parts;
The additive is sodium hydroxide.
Further, the parts by weight of the lime stone, clay, gypsum and additive are:
Lime stone:55 parts;
Clay:25 parts;
Gypsum:12 parts;
Additive:4 parts;
The additive is sodium hydroxide.
Further, the additive further includes iron oxide.
Further, the weight ratio of the sodium hydroxide and iron oxide is 5:1.
The temperature of the calcining is 900-1400 DEG C.
The time of the calcining is 50-100min.
By adopting the above-described technical solution, the beneficial effects of the invention are as follows:
The present invention brings suitable alkalinity by adding in sodium hydroxide, accelerates the early hydration speed of clinker, improves cement
Early strength, shorten demoulding time, the durability of cement later strength and cement is also secure.It is brought by adding in iron oxide
A small amount of iron ion so that clinker burning temperature is relatively low, reduces the heat consumption during clinker burning.
Specific embodiment
The present invention is described in detail below.
Purpose, technical scheme and advantage to make the embodiment of the present invention are clearer, below will be in the embodiment of the present invention
Technical solution be clearly and completely described, it is clear that described embodiment be part of the embodiment of the present invention rather than
Whole embodiments.
Therefore, the detailed description of the embodiment of the present invention presented below is not intended to limit claimed invention
Range, but it is merely representative of the selected embodiment of the present invention.Based on the embodiments of the present invention, those of ordinary skill in the art exist
All other embodiments obtained under the premise of creative work are not made, shall fall within the protection scope of the present invention.
In the description of the present invention, it is also necessary to which explanation is unless specifically defined or limited otherwise, term " setting ",
" installation ", " connection " should be interpreted broadly, for example, it may be being fixedly connected or being detachably connected or integrally connect
It connects;Can be mechanical connection or electrical connection;It can be directly connected, can also be indirectly connected by intermediary, it can
To be the connection inside two elements.For the ordinary skill in the art, can above-mentioned term be understood with concrete condition
Concrete meaning in the present invention.
Embodiment 1
As a kind of preferred embodiment of the present invention, present embodiment discloses a kind of preparation method of Portland clinker, sheets
Embodiment includes:
A kind of preparation method of Portland clinker, including such as step:
It is crushed Step 1: lime stone, clay and gypsum are added in crusher;
Step 2: by additive is added in broken mixture, it is then fed into grinder and grinds, raw material are made;
It calcines, cools down Step 3: raw material are put into rotary kiln, Portland clinker is made.
The lime stone, clay, gypsum and additive parts by weight be:
Lime stone:50 parts;
Clay:30 parts;
Gypsum:15 parts;
Additive:5 parts;
The additive is sodium hydroxide.
Further, the additive further includes iron oxide.
Further, the weight ratio of the sodium hydroxide and iron oxide is 5:1.
The temperature of the calcining is 1400 DEG C.
The time of the calcining is 100min.
Embodiment 2
As a kind of preferred embodiment of the present invention, present embodiment discloses a kind of preparation method of Portland clinker, sheets
Embodiment includes:
A kind of preparation method of Portland clinker, including such as step:
It is crushed Step 1: lime stone, clay and gypsum are added in crusher;
Step 2: by additive is added in broken mixture, it is then fed into grinder and grinds, raw material are made;
It calcines, cools down Step 3: raw material are put into rotary kiln, Portland clinker is made.
Embodiment 3
As a kind of preferred embodiment of the present invention, present embodiment discloses a kind of preparation method of Portland clinker, sheets
Embodiment includes:
A kind of preparation method of Portland clinker, including such as step:
It is crushed Step 1: lime stone, clay and gypsum are added in crusher;
Step 2: by additive is added in broken mixture, it is then fed into grinder and grinds, raw material are made;
It calcines, cools down Step 3: raw material are put into rotary kiln, Portland clinker is made.
Further, the parts by weight of the lime stone, clay, gypsum and additive are:
Lime stone:55 parts;
Clay:25 parts;
Gypsum:12 parts;
Additive:4 parts;
The additive is sodium hydroxide.
Further, the additive further includes iron oxide.
Further, the weight ratio of the sodium hydroxide and iron oxide is 5:1.
The temperature of the calcining is 1200 DEG C.
The time of the calcining is 80min.
Embodiment 4
As a kind of preferred embodiment of the present invention, present embodiment discloses a kind of preparation method of Portland clinker, sheets
Embodiment includes:
A kind of preparation method of Portland clinker, including such as step:
It is crushed Step 1: lime stone, clay and gypsum are added in crusher;
Step 2: by additive is added in broken mixture, it is then fed into grinder and grinds, raw material are made;
It calcines, cools down Step 3: raw material are put into rotary kiln, Portland clinker is made.
The lime stone, clay, gypsum and additive parts by weight be:
Lime stone:60 parts;
Clay:20 parts;
Gypsum:10 parts;
Additive:2 parts;
The additive is sodium hydroxide.
Further, the additive further includes iron oxide.
Further, the weight ratio of the sodium hydroxide and iron oxide is 5:1.
The temperature of the calcining is 900 DEG C.
The time of the calcining is 50min.
Claims (7)
1. a kind of preparation method of Portland clinker, which is characterized in that including such as step:
It is crushed Step 1: lime stone, clay and gypsum are added in crusher;
Step 2: by additive is added in broken mixture, it is then fed into grinder and grinds, raw material are made;
It calcines, cools down Step 3: raw material are put into rotary kiln, Portland clinker is made.
2. the preparation method of Portland clinker according to claim 1, which is characterized in that the lime stone, clay,
The parts by weight of gypsum and additive are:
Lime stone:50-60 parts;
Clay:20-30 parts;
Gypsum:10-15 parts;
Additive:2-5 parts;
The additive is sodium hydroxide.
3. the preparation method of Portland clinker according to claim 2, which is characterized in that the lime stone, clay,
The parts by weight of gypsum and additive are:
Lime stone:55 parts;
Clay:25 parts;
Gypsum:12 parts;
Additive:4 parts;
The additive is sodium hydroxide.
4. the preparation method of the Portland clinker according to Claims 2 or 3, it is characterised in that:The additive is also
Including iron oxide.
5. the preparation method of Portland clinker according to claim 4, it is characterised in that:The sodium hydroxide and oxygen
The weight ratio for changing iron is 5:1.
6. the preparation method of Portland clinker according to claim 1, it is characterised in that:The temperature of the calcining is
900-1400℃。
7. the preparation method of Portland clinker according to claim 1, it is characterised in that:The time of the calcining is
50-100min。