CN108041100A - A kind of mildew resistant slice - Google Patents

A kind of mildew resistant slice Download PDF

Info

Publication number
CN108041100A
CN108041100A CN201711282884.4A CN201711282884A CN108041100A CN 108041100 A CN108041100 A CN 108041100A CN 201711282884 A CN201711282884 A CN 201711282884A CN 108041100 A CN108041100 A CN 108041100A
Authority
CN
China
Prior art keywords
parts
mildew resistant
resistant slice
filler
drier
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711282884.4A
Other languages
Chinese (zh)
Inventor
梁宗贵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chengdu Shunfa Disinfectant and Washing Technology Co Ltd
Original Assignee
Chengdu Shunfa Disinfectant and Washing Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chengdu Shunfa Disinfectant and Washing Technology Co Ltd filed Critical Chengdu Shunfa Disinfectant and Washing Technology Co Ltd
Priority to CN201711282884.4A priority Critical patent/CN108041100A/en
Publication of CN108041100A publication Critical patent/CN108041100A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of mildew resistant slices, belong to Prevention of Mould Development field.The invention discloses a kind of mildew resistant slice, including the following components according to weight meter：1 20 parts of solid chlorine dioxide, 5 10 parts of essence and flavoring agent, 20 60 parts of polyolefin particles, 5 20 parts of cyclodextrin, 5 20 parts of filler, 2 20 parts of drier receive him mould 18 parts, 1 10 parts of plants essential oil, 1 20 parts of EVA colloidal sols, 15 parts of sorbic acid.The present invention for it is mould proof the main reason for one of be that humidity is excessive, drier will be added in mould proof ingredient, it would be desirable to which mould proof environment has carried out drying process, reduces humidity, and auxiliary has carried out mould proof processing.By adding readily volatilized plants essential oil in mildew resistant slice of the present invention active ingredient therein, it is achieved thereby that efficient mould proof processing.

Description

A kind of mildew resistant slice
Technical field
The invention belongs to Prevention of Mould Development fields, and in particular to a kind of mildew resistant slice.
Background technology
At present, on the market there are no applied to leather and fur products such as leather shoes, suitcase, the fur clothings in daily home life and Mould proof, antibacterial, antibacterial the solid product of textile, Wood craft and painting and calligraphy collection product is one in chemical industry sterilizes industry Item blank.Mildew resistant slice on the market is completely used for the mould proof of product shoes and bag, and effectively sterilizing time can only reach 1-3 Month.Secondly, whether the ingredient to volatilize in mildew resistant slice volatilizees away, and whether mildew resistant slice fails, and there is no apparent instructions, use one User is difficult to remember the time that the mildew resistant slice has used after the section time, and the mildew resistant slice that also resulting in still has service life is discarded It and is mistaken as still effectively using mildew resistant slice totally already so that clothing etc. does not obtain effective mould proof protection.
State Intellectual Property Office discloses Application No. CN201010262133.8 on February 09th, 2011, and entitled one The patent of invention of kind environmental protection, sustained-release mildew-proof tablet and preparation method thereof, technical solution are：It is related to mildew resistant slice more particularly to one Kind of environmental protection, sustained-release mildew-proof tablet and preparation method thereof, the environmental protection, sustained-release mildew-proof tablet include the original of following weight percent Material：Chlorine dioxide 2-10%, essence and flavoring agent 2-10%, polyolefin particles 40-85%, cyclodextrin 2-10%.Pass through the environmental protection, sustained release Type mildew resistant slice Preparation Method makes above-mentioned mould proof mixture between two layers of degradation plastic or scraps of paper layer and presses into a piece of, Mould proof mixture is made slowly to be discharged from mildew resistant slice periphery, as long as drug effect is up to half a year, so as to the effect of effectively having played mildew resistant slice.
The above-mentioned prior art has the following problems：Mildew is mainly moist environment, and above-mentioned mildew resistant slice is slow-release, no It is suitble to use in moist environment, it is impossible to reach optimal anti-mold effect.
The content of the invention
In order to solve above-mentioned problems of the prior art, the present invention proposes a kind of mildew resistant slice, discharges active principle Content it is high, it is with obvious effects.
Present invention employs following technical schemes：
A kind of mildew resistant slice, including the following components according to weight meter：
1-20 parts of solid chlorine dioxide,
5-10 parts of essence and flavoring agent,
20-60 parts of polyolefin particles,
5-20 parts of cyclodextrin,
5-20 parts of filler,
2-20 parts of drier,
1-8 parts of natamycin,
1-10 parts of plants essential oil,
1-20 parts of EVA colloidal sols,
1-5 parts of sorbic acid.
Preferably, plants essential oil of the present invention is mustard oil, in tea oil, litsea citrate oil, sassafras oil, lemongrass oil One of which or its any combination.
Preferably, EVA colloidal sols of the present invention, sorbic acid and filler first form substrate, the quality of filler in the substrate At least account for more than 20%.
Preferably, the ratio of drier and plants essential oil of the present invention is 2:1.
Preferably, drier of the present invention is silica-gel desiccant.
Preferably, the mesh number of filler of the present invention is 40-120 mesh.
Preferably, the quality of natamycin of the present invention is at least 2 times of sorbic acid.
The preparation method of mildew resistant slice of the present invention, comprises the following steps：
A. substrate processed
Substrate is first made in EVA colloidal sols, sorbic acid and filler；
B. hybrid solid layer processed
It is solid that polyolefin particles, drier, essence and flavoring agent, solid chlorine dioxide and natamycin progress high temperature are mixed and made into mixing Body layer, temperature are 200-250 DEG C, heating time 100-120min；
C. tabletting
With extruder, by high temperature high pressure process, lower end is pressed into substrate to manufactured solid layer on it after mixing, and mildew resistant slice is made；
D. essential oil coating
Plants essential oil reaction kettle is penetrated into the form of hyperbaric heating in the functional layer of mildew resistant slice.
Preferably, the ratio of EVA colloidal sols, sorbic acid and filler is 2 in step A of the present invention:1:2.
Preferably, in step B of the present invention, the powder that mesh number is 80-120 is first made in polyolefin particles and cyclodextrin, then It is mixed with other raw materials.
Preferably, in step A of the present invention, the half of EVA colloidal sols, sorbic acid and filler gross mass is added in Deionized water.
Preferably, in step C of the present invention, the operating temperature of extruder is 200-300 DEG C, pressure 20-45Mpa.
Preferably, in step D of the present invention, 60-90 DEG C of the heating temperature of essential oil coating presses 15-20Mpa.
What the present invention was brought has the beneficial effect that：
（One）The present invention will add drier in mould proof ingredient, it would be desirable to which mould proof environment has carried out drying process, reduces Humidity, auxiliary have carried out mould proof processing.It is readily volatilized by being added in mildew resistant slice of the present invention active ingredient therein Plants essential oil, it is achieved thereby that efficient mould proof processing.
（Two）EVA colloidal sols, sorbic acid and filler are first formed substrate by the present invention, and the quality of filler at least accounts in the substrate More than 20%.Active ingredient is loaded wherein with substrate, the ingredient of filler at least accounts for more than 20% in substrate, can ensure to prevent The shaping of mould, it is non-breakable.
Specific embodiment
Embodiment 1
A kind of mildew resistant slice, including the following components according to weight meter：
20 parts of solid chlorine dioxide,
10 parts of essence and flavoring agent,
60 parts of polyolefin particles,
20 parts of cyclodextrin,
20 parts of filler,
20 parts of drier,
8 parts of natamycin,
10 parts of plants essential oil,
20 parts of EVA colloidal sols,
5 parts of sorbic acid.
Embodiment 2
A kind of mildew resistant slice, including the following components according to weight meter：
1 part of solid chlorine dioxide,
5 parts of essence and flavoring agent,
20 parts of polyolefin particles,
5 parts of cyclodextrin,
5 parts of filler,
2 parts of drier,
1 part of natamycin,
1 part of plants essential oil,
1 part of EVA colloidal sols,
1 part of sorbic acid.
Embodiment 3
A kind of mildew resistant slice, including the following components according to weight meter：
10 parts of solid chlorine dioxide,
8 parts of essence and flavoring agent,
30 parts of polyolefin particles,
15 parts of cyclodextrin,
15 parts of filler,
10 parts of drier,
5 parts of natamycin,
5 parts of plants essential oil,
5 parts of EVA colloidal sols,
4 parts of sorbic acid.
Preferably, plants essential oil of the present invention is mustard oil, in tea oil, litsea citrate oil, sassafras oil, lemongrass oil One of which or its any combination.
Embodiment 4
A kind of mildew resistant slice, including the following components according to weight meter：
1-20 parts of solid chlorine dioxide,
5-10 parts of essence and flavoring agent,
20-60 parts of polyolefin particles,
5-20 parts of cyclodextrin,
5-20 parts of filler,
2-20 parts of drier,
1-8 parts of natamycin,
1-10 parts of plants essential oil,
1-20 parts of EVA colloidal sols,
1-5 parts of sorbic acid.
Preferably, EVA colloidal sols of the present invention, sorbic acid and filler first form substrate, the quality of filler in the substrate At least account for more than 20%.
Preferably, the ratio of drier and plants essential oil of the present invention is 2:1.
Preferably, drier of the present invention is silica-gel desiccant.
Preferably, the mesh number of filler of the present invention is 40-120 mesh.
Preferably, the quality of natamycin of the present invention is at least 2 times of sorbic acid.
Embodiment 5
The preparation method of mildew resistant slice of the present invention, comprises the following steps：
A. substrate processed
Substrate is first made in EVA colloidal sols, sorbic acid and filler；
B. hybrid solid layer processed
It is solid that polyolefin particles, drier, essence and flavoring agent, solid chlorine dioxide and natamycin progress high temperature are mixed and made into mixing Body layer, temperature are 200-250 DEG C, heating time 100-120min；
C. tabletting
With extruder, by high temperature high pressure process, lower end is pressed into substrate to manufactured solid layer on it after mixing, and is made mould proof Piece；
D. essential oil coating
Plants essential oil reaction kettle is penetrated into the form of hyperbaric heating in the functional layer of mildew resistant slice.
Embodiment 6
The preparation method of mildew resistant slice of the present invention, comprises the following steps：
A. substrate processed
Substrate is first made in EVA colloidal sols, sorbic acid and filler；
B. hybrid solid layer processed
It is solid that polyolefin particles, drier, essence and flavoring agent, solid chlorine dioxide and natamycin progress high temperature are mixed and made into mixing Body layer, temperature are 200-250 DEG C, heating time 100-120min；
C. tabletting
With extruder, by high temperature high pressure process, lower end is pressed into substrate to manufactured solid layer on it after mixing, and is made mould proof Piece；
D. essential oil coating
Plants essential oil reaction kettle is penetrated into the form of hyperbaric heating in the functional layer of mildew resistant slice.
Preferably, the ratio of EVA colloidal sols, sorbic acid and filler is 2 in step A of the present invention:1:2.
Preferably, in step B of the present invention, the powder that mesh number is 80-120 is first made in polyolefin particles and cyclodextrin, then It is mixed with other raw materials.
Preferably, in step A of the present invention, the half of EVA colloidal sols, sorbic acid and filler gross mass is added in Deionized water.
Preferably, in step C of the present invention, the operating temperature of extruder is 200-300 DEG C, pressure 20-45Mpa.
Preferably, in step D of the present invention, 60-90 DEG C of the heating temperature of essential oil coating presses 15-20Mpa.

Claims (7)

1. a kind of mildew resistant slice, including the following components according to weight meter：
1-20 parts of solid chlorine dioxide,
5-10 parts of essence and flavoring agent,
20-60 parts of polyolefin particles,
5-20 parts of cyclodextrin,
5-20 parts of filler,
2-20 parts of drier,
1-8 parts of natamycin,
1-10 parts of plants essential oil,
1-20 parts of EVA colloidal sols,
1-5 parts of sorbic acid.
2. mildew resistant slice as described in claim 1, it is characterised in that：The plants essential oil is mustard oil, tea oil, the fruit of a cubeb litsea tree One of which or its any combination in oil, sassafras oil, lemongrass oil.
3. mildew resistant slice as claimed in claim 1 or 2, it is characterised in that：The EVA colloidal sols, sorbic acid and filler first form base Piece, the quality of filler at least accounts for more than 20% in the substrate.
4. mildew resistant slice as claimed in claim 1 or 2, it is characterised in that：The ratio of the drier and plants essential oil is 2:1.
5. mildew resistant slice as claimed in claim 3, it is characterised in that：The drier is silica-gel desiccant.
6. mildew resistant slice as described in claim 1, it is characterised in that：The mesh number of the filler is 40-120 mesh.
7. mildew resistant slice as described in claim 1, it is characterised in that：The quality of the natamycin is at least 2 times of sorbic acid.
CN201711282884.4A 2017-12-07 2017-12-07 A kind of mildew resistant slice Pending CN108041100A (en)