CN108034198A - A kind of motorcycle brake friction plate and its preparation process - Google Patents
A kind of motorcycle brake friction plate and its preparation process Download PDFInfo
- Publication number
- CN108034198A CN108034198A CN201711497749.1A CN201711497749A CN108034198A CN 108034198 A CN108034198 A CN 108034198A CN 201711497749 A CN201711497749 A CN 201711497749A CN 108034198 A CN108034198 A CN 108034198A
- Authority
- CN
- China
- Prior art keywords
- parts
- friction plate
- powder
- motorcycle brake
- brake friction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of motorcycle brake friction plate, the formula of its raw material by weight are as follows：35 55 parts of epoxy resin, 10 20 parts of natural rubber, 10 20 parts of neoprene, 15 25 parts of superfine fibre powder, 8 12 parts of graphite powder, 8 12 parts of nickel powder, 6 10 parts of iron sulfide, 6 10 parts of silica, 6 10 parts of calcium sulfide, 46 parts of grinding agent of increasing, 46 parts of activating agent, 46 parts of antioxidant.The invention also discloses a kind of preparation process of motorcycle brake friction plate.The present invention can effectively strengthen the wearability and heat-resisting quantity of friction plate, and activating agent can strengthen the tight ness rating between each element, effectively improve its service life, meet the demand developed now.
Description
Technical field
The present invention relates to motorcycle parts preparing technical field, more particularly to a kind of motorcycle brake friction plate and its system
Standby technique.
Background technology
Motorcycle, is driven by gasoline engine, fast by the two-wheeled or tricycle of bar handle front-wheel steer, light and flexible, traveling
Speed, is widely used in patrol, passenger and freight transportation etc., also serves as sports movement apparatus.Generally, motorcycle is divided into street
Car, racing cycle motorcycle, off-road motorcycle, cruise car, station wagon etc..When clutch of motorcycle works, temperature can be due to rubbing
Wiping is improved to more than 300 DEG C quickly, and the friction coefficient of friction plate can reduce quickly, in the case where temperature is higher so that friction
The friction coefficient meeting rapid decrease of piece, wear rate can be improved quickly, and in the prior art, friction plate usually can be excessive because of temperature,
So as to cause to damage, its service life is reduced.For this reason, we have proposed a kind of motorcycle brake friction plate and its preparation
Technique.
The content of the invention
The present invention proposes a kind of motorcycle brake friction plate and its preparation process, to solve to carry in above-mentioned background technology
The problem of going out.
The present invention proposes a kind of motorcycle brake friction plate, and the formula of its raw material by weight is as follows：Epoxy resin 35-
55 parts, 10-20 parts of natural rubber, 10-20 parts of neoprene, 15-25 parts of superfine fibre powder, 8-12 parts of graphite powder, nickel powder 8-12
Part, 6-10 parts of iron sulfide, 6-10 parts of silica, 6-10 parts of calcium sulfide, increase 4-6 parts of grinding agent, 4-6 parts of activating agent, antioxidant 4-6
Part.
Preferably, epoxy resin, natural rubber, the weight ratio of neoprene are 40-50: 13-17：13-17.
Preferably, superfine fibre powder, graphite powder, the weight ratio of nickel powder are 18-22: 9-11：9-11.
Preferably, iron sulfide, silica, the weight ratio of calcium sulfide are 7-9: 7-9：7-9.
Preferably, it is 4.5-5.5 to increase grinding agent, activating agent, the weight ratio of antioxidant：4.5-5.5：4.5-5.5.
Preferably, the formula of its raw material by weight is as follows：
40-50 parts of epoxy resin, 13-17 parts of natural rubber, 13-17 parts of neoprene, 18-22 parts of superfine fibre powder, stone
9-11 parts of ink powder, 9-11 parts of nickel powder, 7-9 parts of iron sulfide, 7-9 parts of silica, 7-9 parts of calcium sulfide, increase 4.5-5.5 parts of grinding agent,
4.5-5.5 parts of activating agent, 4.5-5.5 parts of antioxidant.
Preferably, the optimization formula of its raw material by weight is as follows：
45 parts of epoxy resin, 15 parts of natural rubber, 15 parts of neoprene, 20 parts of superfine fibre powder, 10 parts of graphite powder, nickel powder
10 parts, 8 parts of iron sulfide, 8 parts of silica, 8 parts of calcium sulfide, increase 5 parts of grinding agent, 5 parts of activating agent, 5 parts of antioxidant.
Present invention also offers a kind of preparation process of motorcycle brake friction plate, include the following steps：
S1, in proportion insert epoxy resin, natural rubber and neoprene in smelting furnace, at 800-1000 degrees Celsius
Under conditions of melted, after its completion is melted, and nickel powder, iron sulfide and silica are added into smelting furnace at the same time,
After stirring 10-15min, the solution formed is filtered, so as to remove the impurity in solution, is added thereto again ultra-fine
Fiber powder, graphite powder and nickel powder, are mixed under conditions of 500-700 degrees Celsius, after its completion mixing, finally again to it
Middle addition increases grinding agent, activating agent and antioxidant, after 20-30min is mixed, takes out, and forms mixed liquor, spare；
S2, choose friction sheet mold, and friction sheet mold is carried out preheating 10- under conditions of 150-200 degrees Celsius
14min, then pours into a mould mixed liquor to friction plate mould inside, and teeming rate is 10-20ml/s, after casting complete, is put
In 40-50 degrees Celsius of environment, Temperature fall shaping, after its shaping, is drawn off, and naturally cool to using manipulator
Room temperature, and its surface is machined, is polished and burr removing, it is motorcycle brake friction plate.
Preferably, then the smelting furnace in S1 is dried, at 300-400 before use, its inside need to be cleaned multiple times
Into preheating 10-20min under conditions of degree Celsius.
In the present invention, rational proportion is carried out by the addition of plurality of raw materials, and to it, can effectively strengthen the resistance to of friction plate
Mill property and heat-resisting quantity, activating agent can strengthen the tight ness rating between each element, and antioxidant can then prevent friction plate aging,
So as to effectively improve its service life, meet the demand developed now.
Embodiment
With reference to specific embodiment, the present invention will be further described.
Embodiment 1
The present invention proposes a kind of motorcycle brake friction plate, and the formula of its raw material by weight is as follows：Epoxy resin 35
Part, 10 parts of natural rubber, 10 parts of neoprene, 15 parts of superfine fibre powder, 8 parts of graphite powder, 8 parts of nickel powder, 6 parts of iron sulfide, dioxy
6 parts of SiClx, 6 parts of calcium sulfide, increase 4 parts of grinding agent, 4 parts of activating agent, 4 parts of antioxidant.
Present invention also offers a kind of preparation process of motorcycle brake friction plate, include the following steps：
S1, in proportion insert epoxy resin, natural rubber and neoprene in smelting furnace, in 800 degrees Celsius of bar
Melted under part, after its completion is melted, and add nickel powder, iron sulfide and silica into smelting furnace at the same time, stirring
After 10min, the solution formed is filtered, so as to remove the impurity in solution, add thereto again superfine fibre powder,
Graphite powder and nickel powder, are mixed under conditions of 500 degrees Celsius, and after its completion mixing, finally addition increases mill thereto again
Agent, activating agent and antioxidant, after 20min is mixed, take out, and form mixed liquor, spare；
S2, choose friction sheet mold, and friction sheet mold is carried out preheating 10min under conditions of 150 degrees Celsius, then
Mixed liquor is poured into a mould to friction plate mould inside, and teeming rate is 10ml/s, after casting complete, is placed on 40 degrees Celsius of ring
In border, Temperature fall shaping, after its shaping, is drawn off, and naturally cool to room temperature using manipulator, and to its surface into
Row mechanical processing, polishing and burr removing, are motorcycle brake friction plate.
Then smelting furnace in S1 is dried, in 300 degrees Celsius of bar before use, its inside need to be cleaned multiple times
Into preheating 10min under part.
Embodiment 2
The present invention proposes a kind of motorcycle brake friction plate, and the formula of its raw material by weight is as follows：Epoxy resin 40
Part, 13 parts of natural rubber, 13 parts of neoprene, 18 parts of superfine fibre powder, 9 parts of graphite powder, 9 parts of nickel powder, 7 parts of iron sulfide, dioxy
7 parts of SiClx, 7 parts of calcium sulfide, increase 4.5 parts of grinding agent, 4.5 parts of activating agent, 4.5 parts of antioxidant.
Present invention also offers a kind of preparation process of motorcycle brake friction plate, include the following steps：
S1, in proportion insert epoxy resin, natural rubber and neoprene in smelting furnace, in 850 degrees Celsius of bar
Melted under part, after its completion is melted, and add nickel powder, iron sulfide and silica into smelting furnace at the same time, stirring
After 12min, the solution formed is filtered, so as to remove the impurity in solution, add thereto again superfine fibre powder,
Graphite powder and nickel powder, are mixed under conditions of 550 degrees Celsius, and after its completion mixing, finally addition increases mill thereto again
Agent, activating agent and antioxidant, after 23min is mixed, take out, and form mixed liquor, spare；
S2, choose friction sheet mold, and friction sheet mold is carried out preheating 11min under conditions of 160 degrees Celsius, then
Mixed liquor is poured into a mould to friction plate mould inside, and teeming rate is 13ml/s, after casting complete, is placed on 43 degrees Celsius of ring
In border, Temperature fall shaping, after its shaping, is drawn off, and naturally cool to room temperature using manipulator, and to its surface into
Row mechanical processing, polishing and burr removing, are motorcycle brake friction plate.
Then smelting furnace in S1 is dried, in 330 degrees Celsius of bar before use, its inside need to be cleaned multiple times
Into preheating 13min under part.
Embodiment 3
The present invention proposes a kind of motorcycle brake friction plate, and the formula of its raw material by weight is as follows：Epoxy resin 45
Part, 15 parts of natural rubber, 15 parts of neoprene, 20 parts of superfine fibre powder, 10 parts of graphite powder, 10 parts of nickel powder, 8 parts of iron sulfide, two
8 parts of silica, 8 parts of calcium sulfide, increase 5 parts of grinding agent, 5 parts of activating agent, 5 parts of antioxidant.
Present invention also offers a kind of preparation process of motorcycle brake friction plate, include the following steps：
S1, in proportion insert epoxy resin, natural rubber and neoprene in smelting furnace, in 900 degrees Celsius of bar
Melted under part, after its completion is melted, and add nickel powder, iron sulfide and silica into smelting furnace at the same time, stirring
After 13min, the solution formed is filtered, so as to remove the impurity in solution, add thereto again superfine fibre powder,
Graphite powder and nickel powder, are mixed under conditions of 600 degrees Celsius, and after its completion mixing, finally addition increases mill thereto again
Agent, activating agent and antioxidant, after 25min is mixed, take out, and form mixed liquor, spare；
S2, choose friction sheet mold, and friction sheet mold is carried out preheating 12min under conditions of 170 degrees Celsius, then
Mixed liquor is poured into a mould to friction plate mould inside, and teeming rate is 15ml/s, after casting complete, is placed on 45 degrees Celsius of ring
In border, Temperature fall shaping, after its shaping, is drawn off, and naturally cool to room temperature using manipulator, and to its surface into
Row mechanical processing, polishing and burr removing, are motorcycle brake friction plate.
Then smelting furnace in S1 is dried, in 350 degrees Celsius of bar before use, its inside need to be cleaned multiple times
Into preheating 15min under part.
Embodiment 4
The present invention proposes a kind of motorcycle brake friction plate, and the formula of its raw material by weight is as follows：Epoxy resin 50
Part, 17 parts of natural rubber, 17 parts of neoprene, 22 parts of superfine fibre powder, 11 parts of graphite powder, 11 parts of nickel powder, 9 parts of iron sulfide, two
9 parts of silica, 9 parts of calcium sulfide, increase 5.5 parts of grinding agent, 5.5 parts of activating agent, 5.5 parts of antioxidant.
Present invention also offers a kind of preparation process of motorcycle brake friction plate, include the following steps：
S1, in proportion insert epoxy resin, natural rubber and neoprene in smelting furnace, in 950 degrees Celsius of bar
Melted under part, after its completion is melted, and add nickel powder, iron sulfide and silica into smelting furnace at the same time, stirring
After 14min, the solution formed is filtered, so as to remove the impurity in solution, add thereto again superfine fibre powder,
Graphite powder and nickel powder, are mixed under conditions of 650 degrees Celsius, and after its completion mixing, finally addition increases mill thereto again
Agent, activating agent and antioxidant, after 27min is mixed, take out, and form mixed liquor, spare；
S2, choose friction sheet mold, and friction sheet mold is carried out preheating 13min under conditions of 190 degrees Celsius, then
Mixed liquor is poured into a mould to friction plate mould inside, and teeming rate is 17ml/s, after casting complete, is placed on 47 degrees Celsius of ring
In border, Temperature fall shaping, after its shaping, is drawn off, and naturally cool to room temperature using manipulator, and to its surface into
Row mechanical processing, polishing and burr removing, are motorcycle brake friction plate.
Then smelting furnace in S1 is dried, in 370 degrees Celsius of bar before use, its inside need to be cleaned multiple times
Into preheating 17min under part.
Embodiment 5
The present invention proposes a kind of motorcycle brake friction plate, and the formula of its raw material by weight is as follows：Epoxy resin 55
Part, 20 parts of natural rubber, 20 parts of neoprene, 25 parts of superfine fibre powder, 12 parts of graphite powder, 12 parts of nickel powder, 10 parts of iron sulfide, two
10 parts of silica, 10 parts of calcium sulfide, increase 6 parts of grinding agent, 6 parts of activating agent, 6 parts of antioxidant.
Present invention also offers a kind of preparation process of motorcycle brake friction plate, include the following steps：
S1, in proportion insert epoxy resin, natural rubber and neoprene in smelting furnace, in 1000 degrees Celsius of bar
Melted under part, after its completion is melted, and add nickel powder, iron sulfide and silica into smelting furnace at the same time, stirring
After 15min, the solution formed is filtered, so as to remove the impurity in solution, add thereto again superfine fibre powder,
Graphite powder and nickel powder, are mixed under conditions of 700 degrees Celsius, and after its completion mixing, finally addition increases mill thereto again
Agent, activating agent and antioxidant, after 30min is mixed, take out, and form mixed liquor, spare；
S2, choose friction sheet mold, and friction sheet mold is carried out preheating 14min under conditions of 200 degrees Celsius, then
Mixed liquor is poured into a mould to friction plate mould inside, and teeming rate is 20ml/s, after casting complete, is placed on 50 degrees Celsius of ring
In border, Temperature fall shaping, after its shaping, is drawn off, and naturally cool to room temperature using manipulator, and to its surface into
Row mechanical processing, polishing and burr removing, are motorcycle brake friction plate.
Then smelting furnace in S1 is dried, in 400 degrees Celsius of bar before use, its inside need to be cleaned multiple times
Into preheating 20min under part.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (9)
1. a kind of motorcycle brake friction plate, it is characterised in that the formula of its raw material by weight is as follows：Epoxy resin 35-55
Part, 10-20 parts of natural rubber, 10-20 parts of neoprene, 15-25 parts of superfine fibre powder, 8-12 parts of graphite powder, 8-12 parts of nickel powder,
6-10 parts of iron sulfide, 6-10 parts of silica, 6-10 parts of calcium sulfide, 4-6 parts of grinding agent of increasing, 4-6 parts of activating agent, 4-6 parts of antioxidant.
2. motorcycle brake friction plate according to claim 1, it is characterised in that epoxy resin, natural rubber, neoprene
The weight ratio of rubber is 40-50: 13-17: 13-17.
3. motorcycle brake friction plate according to claim 1, it is characterised in that superfine fibre powder, graphite powder, nickel powder
Weight ratio be 18-22: 9-11: 9-11.
4. motorcycle brake friction plate according to claim 1, it is characterised in that iron sulfide, silica, calcium sulfide
Weight ratio be 7-9: 7-9: 7-9.
5. motorcycle brake friction plate according to claim 1, it is characterised in that increase grinding agent, activating agent, antioxidant
Weight ratio is 4.5-5.5: 4.5-5.5: 4.5-5.5.
6. the motorcycle brake friction plate according to claim 2-5, it is characterised in that the formula of its raw material by weight is such as
Under：
40-50 parts of epoxy resin, 13-17 parts of natural rubber, 13-17 parts of neoprene, 18-22 parts of superfine fibre powder, graphite powder
9-11 parts, 9-11 parts of nickel powder, 7-9 parts of iron sulfide, 7-9 parts of silica, 7-9 parts of calcium sulfide, increase 4.5-5.5 part of grinding agent, be active
4.5-5.5 parts of agent, 4.5-5.5 parts of antioxidant.
7. motorcycle brake friction plate according to claim 1, it is characterised in that the optimization formula of its raw material by weight
It is as follows：
45 parts of epoxy resin, 15 parts of natural rubber, 15 parts of neoprene, 20 parts of superfine fibre powder, 10 parts of graphite powder, nickel powder 10
Part, 8 parts of iron sulfide, 8 parts of silica, 8 parts of calcium sulfide, increase 5 parts of grinding agent, 5 parts of activating agent, 5 parts of antioxidant.
8. a kind of preparation process of motorcycle brake friction plate according to claim 1, it is characterised in that including as follows
Step：
S1, in proportion insert epoxy resin, natural rubber and neoprene in smelting furnace, in 800-1000 degrees Celsius of bar
Melted under part, after its completion is melted, and add nickel powder, iron sulfide and silica into smelting furnace at the same time, stirring
After 10-15min, the solution formed is filtered, so as to remove the impurity in solution, adds superfine fibre thereto again
Powder, graphite powder and nickel powder, are mixed under conditions of 500-700 degrees Celsius, after its completion mixing, are finally added thereto again
Add and increase grinding agent, activating agent and antioxidant, after 20-30min is mixed, take out, form mixed liquor, it is spare；
S2, choose friction sheet mold, and friction sheet mold is carried out preheating 10-14min under conditions of 150-200 degrees Celsius,
Then mixed liquor is poured into a mould to friction plate mould inside, and teeming rate is 10-20ml/s, after casting complete, is placed on 40-50
Degree Celsius environment in, Temperature fall shaping, after its shaping, is drawn off, and naturally cool to room temperature using manipulator, and
Its surface is machined, is polished and burr removing, is motorcycle brake friction plate.
9. motorcycle brake friction plate according to claim 1, it is characterised in that smelting furnace in S1 before use,
Its inside need to be cleaned multiple times, then dried, into preheating 10-20min under conditions of 300-400 degrees Celsius.