CN108024586B - Full head wig - Google Patents
Full head wig Download PDFInfo
- Publication number
- CN108024586B CN108024586B CN201680056191.0A CN201680056191A CN108024586B CN 108024586 B CN108024586 B CN 108024586B CN 201680056191 A CN201680056191 A CN 201680056191A CN 108024586 B CN108024586 B CN 108024586B
- Authority
- CN
- China
- Prior art keywords
- mass
- hair
- fiber
- polyester fiber
- wig
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of full head wigs, it includes the wig matrixes (10) for being wearing on head and plantation in the hair (20) on wig matrix (10), wherein, wig matrix (10) is by being wearing on the part 1 (11) of poll region, the third portion (13) for being wearing on the part 2 (12) in occiput region and being wearing near neck is constituted, it plants the hair (21) in part 1 (11) and contains 20~40 mass % of 60~80 mass % of polyester fiber A and artificial proteins fiber, it plants the hair (22) in part 2 (12) and contains 20~90 mass % of artificial proteins fiber, 0~70 mass % of polyester fiber B 10~80 mass % and polyester fiber A, the hair (23) in third portion (13) is planted by selecting The fiber of one or more of the group that autopolyester series fiber A and polyester fiber B are constituted is constituted.Thus, it is possible to provide a kind of full head wig with natural appearance, good combing property and heat setting and Reusability durability.
Description
Technical field
Plantation is arranged to the full head of at least two kinds different compositions in the hair on wig matrix the present invention relates to a kind of
Wig.
Background technique
Usually, when congenitally hair is less, due to round baldness hair disappear when, due tos anti-cancer agent therapy etc.
When alopecia, the full head wig for covering entire head is used.For example, disclosing one kind in patent document 1 has wig main body
With the full head wig of local wig.In addition, also using full head wig sometimes to improve the aesthetics of hair style.Such as special
A kind of following wig is proposed in sharp document 2: decorating its 2nd with hairline part is worn over by the 1st wig on cladding head
Wig is constituted, and each wig can link up use individually or by clamp, thus can freely carry out to hair style varied
Design.
On the other hand, if full head wig is made of the hair of people, not only it is difficult to obtain the hair of people, but also exist
Problem at high cost, therefore use artificial hair.When being made of full head wig artificial hair, in general, in wig matrix
The upper whole artificial hair for planting single composition.
Existing technical literature
Patent document
Patent document 1: Japanese Unexamined Patent Publication 2014-91870 bulletin
Patent document 2: Japanese Unexamined Patent Publication 2004-91972 bulletin
Summary of the invention
Problems to be solved by the invention
For full head wig, it is desirable that there is natural appearance, good combing property and the heat setting obtained by hair iron,
Reusability durability is required simultaneously, it is but if planting the artificial hair of single composition on entire wig matrix, then difficult
To meet above-mentioned quality requirements.
In order to solve preceding above-mentioned conventional problem, provide one kind has natural appearance, good combing property and scalds the present invention
Send out the heat setting of device and the full head wig of Reusability durability.
The means used to solve the problem
The present invention relates to a kind of full head wig, the full head wig include be wearing on head wig matrix and plantation in
Hair on the wig matrix, which is characterized in that the wig matrix is by being wearing on the part 1 of poll region, filling and wear
It is constituted in the part 2 in occiput region and the third portion that is wearing near neck, when the entirety in part 1 will be planted
The quality settings of hair be 100 mass % when, plant in part 1 hair contain 60~80 mass % of polyester fiber A,
It is 100 matter when the quality settings in all hairs of part 2 will be planted with 20~40 mass % of artificial proteins fiber
When measuring %, the hair planted in part 2 contains 20~90 mass % of artificial proteins fiber, 10~80 matter of polyester fiber B
% and 0~70 mass % of polyester fiber A is measured, plants the hair in third portion by fine selected from polyester fiber A and Polyester
The fiber of one or more of the group that dimension B is constituted is constituted, and polyester fiber A contains brominated epoxy flame retardant and three oxidations
Antimony, polyester fiber B are free of antimony trioxide.
For full head wig of the invention, it is preferred that when the quality by plantation in all hairs of part 1 is set
When being set to 100 mass %, the hair planted in part 1 contains 70~80 mass % of polyester fiber A fiber and artificial protein
20~30 mass % of matter fiber, when will plant in all hairs of part 2 quality settings be 100 mass % when, plantation in
The hair of part 2 contains 20~30 mass % of artificial proteins fiber, 20~30 mass % of polyester fiber B and Polyester
40~60 mass % of fiber A, when will plant in all hairs of third portion quality settings be 100 mass % when, plantation in
The hair of third portion is made of 30~50 mass % of polyester fiber A 50~70 mass % and polyester fiber B.
Aforementioned artificial proteins fiber is preferably collagenous fibres.In addition, polyester fiber B preferably comprises the resistance of brominated epoxy system
Fire agent.
Invention effect
The present invention can provide it is a kind of with natural appearance, good combing property and hair iron heat setting and
The full head wig of Reusability durability.
Detailed description of the invention
Fig. 1 is to penetrate hair to show that dress has worn the schematic of the state of the full head wig of an implementation form of the invention
Side view.
The A of Fig. 2 is the schematic side elevational view for showing the back side of full head wig of an implementation form of the invention, Fig. 2's
B is its schematic facial figure.
Fig. 3 is the schematic side elevational view for illustrating each position on head.
A-the C of Fig. 4 is that fluffy measuring machine schematically illustrates figure.
Fig. 5 is the schematic diagram being illustrated to curly form.
Specific embodiment
Present inventors etc. are for the wig matrix comprising being wearing on head and plantation in the artificial hair on aforementioned wig matrix
The full head wig (also referred to as full head emulation hair (full wig), full wig) of hair, for meeting natural appearance, good comb
The case where all qualities of the heat setting (being also only denoted as heat setting below) and Reusability durability of property and hair iron
Research has been repeated.As a result, discovery, on wig matrix, by will be wearing on the part 1 of poll region, dress is worn
In occiput region part 2 and be wearing on the artificial hair planted respectively in the third portion near neck and be set to special
Different composition (fibre furnish), it will be able to meet natural appearance, good combing property and heat setting and Reusability is resistance to
These all qualities of long property, so as to complete the present invention.
In an implementation form of the invention, as wig matrix, it is not particularly limited, can be used for example netted
Object, fabric etc. are typically used as the material of wig matrix.Aforementioned wig matrix divide into be wearing on poll region part 1,
The third portion for being wearing on the part 2 in occiput region and being wearing near neck.Usually, as shown in Figure 3, head
Portion 30 divides for fringe part 31, overhead 32, lateral parts 33, pileum part 34, middle section 35 and neck neck portion 36.This
In one implementation form of invention, it is preferred that the part 1 of wig matrix is wearing on fringe part 31, overhead 32, side
In a part and pileum part 34 of face part 33, the part 2 of wig matrix is wearing on a part of lateral parts 33 in
Between on part 35, the third portion of wig matrix is wearing on neck neck portion 36.
When that will plant when the quality settings of all hairs of part 1 are 100 mass %, plant in the hair of part 1
Hair contains 20~40 mass % of 60~80 mass % of polyester fiber A and artificial proteins fiber.Preferably, containing polyester
20~30 mass % of 70~80 mass % of series fiber A and artificial proteins fiber.It is further preferred that containing polyester fiber A
20~25 mass % of 75~80 mass % and artificial proteins fiber.The gloss of hair is low, has natural appearance, while heat
Constancy is also excellent.In full head wig, gloss is mainly driven by the gloss of the hair of overhead, therefore is wearing on overhead
If containing brominated epoxy flame retardant and three oxidations containing 60 mass % or more in the hair planted in the part 1 in region
The polyester fiber A of antimony, then be able to suppress gloss, and wig entirety has natural appearance.
In the range of not hindering the purpose of the present invention, plantation is in the hair of part 1 in addition to containing polyester fiber A
Other than artificial proteins fiber, other fiber for artificial hair can also be contained.As other fiber for artificial hair,
Polyester fiber, polyvinyl chloride fiber, the modified acrylic fibre other than polyester fiber A can be used
(modacrylic fiber), polyolefin series fiber etc..Although being not particularly limited, work as the entirety that will be planted in part 1
When the quality settings of hair are 100 mass %, the content of other fibers is for example, it can be set to be 20 mass % or less.
When that will plant when the quality settings of all hairs of part 2 are 100 mass %, plant in the hair of part 2
Hair contains 20~90 mass % of artificial proteins fiber, polyester fiber B 10~80 mass % and polyester fiber A 0~70
Quality %.Preferably, containing 20~50 mass % of artificial proteins fiber, 10~40 mass % of polyester fiber B and polyester
40~70 mass % of series fiber A.It is further preferred that containing 20~40 mass % of artificial proteins fiber, polyester fiber B 20
40~60 mass % of~40 mass % and polyester fiber A.It may further be preferable that containing artificial proteins fiber 20~30
Quality %, 40~60 mass % of polyester fiber B 20~30 mass % and polyester fiber A.Heat setting is excellent and combs
The general character is excellent.In full head wig, combing property is mainly influenced by occipital hair.By be wearing on occiput region
Polyester fiber B in the hair planted on 2 parts containing 20 mass % of artificial proteins fiber or more and without antimony trioxide
10 mass % or more, combing property becomes good.
In the range of not hindering the purpose of the present invention, plantation is in the hair of part 2 in addition to containing polyester fiber
A, other than polyester fiber B and artificial proteins fiber, other fiber for artificial hair can also be contained.As other people
Polyvinyl chloride fiber, modified acrylic fibre, polyolefin series fiber etc. can be used in work fiber for hair use.Although no
It is particularly limited to, but when that will plant when the quality settings of all hairs of part 2 are 100 mass %, other fibers contain
Amount is for example, it can be set to be 20 mass % or less.
In full head wig, the heat setting of hair iron is mainly influenced by overhead and occipital hair.By
It is wearing on the part 1 of poll region and is wearing in the hair planted in the part 2 in occiput region and contain artificial egg
20 mass % of white matter fiber or more, heat setting becomes good.
The hair planted in third portion is made of polyester fiber A and/or polyester fiber B.When will plant in the 3rd
It is preferably fine by 30~70 mass % of polyester fiber B and Polyester when the quality settings of all hairs divided are 100 mass %
It ties up 30~70 mass % of A to constitute, more preferably by 30~50 mass % of polyester fiber B and 50~70 matter of polyester fiber A
% is measured to constitute.It is easy to repair damage by hair iron.In full head wig, Reusability durability mainly passes through raising and is easy
The injury repair of hair near the neck of cumulative damage improves.By making to plant in the third portion being wearing near neck
The hair of plant is made of polyester fiber A and/or polyester fiber B, then is easy to repair damage by hair iron, wig
Useful life longevity becomes good.
As aforementioned artificial proteins fiber, as long as the fiber of the protein of manual manufacture, is not particularly limited,
Collagenous fibres, keratin fiber etc. can be used for example using protein as the fiber of principal component.As aforementioned collagenous fibres, do not have
It is particularly limited to, well known collagenous fibres can be used.Regenerated collagen fiber can be used for example.Aforementioned regenerated collagen fiber is for example
Can by the way that collage raw material is carried out dissolution process, and will be solubilized obtained from solubilized collagen solution carry out spinning to obtain
?.Specifically, commercially available regenerated collagen fiber, the regeneration recorded in Japanese Unexamined Patent Publication 2007-169806 bulletin can be used
Collagenous fibres etc..It as commercially available regenerated collagen fiber, is not particularly limited, Co., Ltd.'s Kaneka system can be used for example
Regenerated collagen fiber Ultima (registered trademark) etc..
From the viewpoint of being suitable for hair, the filament denier of aforementioned artificial proteins fiber is preferably 10~
100dtex, more preferably 20~90dtex, further preferably 35~80dtex.
Polyester fiber A is preferably comprised: selected from by polyalkylene terephthalate and with poly terephthalic acid alkane glycol
Polyester resin, brominated epoxy flame retardant and the antimony trioxide of one or more of the group that copolyester based on ester is constituted.
In polyester fiber A, relative to 100 mass parts of polyester resin, 5 mass parts of brominated epoxy flame retardant or more and 40 are preferably comprised
Below the mass with 1.5 mass parts of antimony trioxide more than or lower than 7 mass parts.Preferably, relative to above-mentioned polyester resin
100 mass parts contain 10 mass parts of brominated epoxy flame retardant~30 mass parts, further preferably 15 mass parts~25 mass
Part.As brominated epoxy flame retardant, if using resin it is flame-retarded used in fire retardant, do not limit especially
It is fixed.From the viewpoint of gloss adjustment effect is excellent, relative to 100 mass parts of polyester resin, 1.5 matter of antimony trioxide is preferably comprised
Measure part~5 mass parts, further preferably 1.5 mass parts~4 mass parts, further preferably 1.5 mass parts~3 mass parts.
It as polyester fiber A, is not particularly limited, the fire-retardant polyester series fiber of Co., Ltd. Kaneka can be used for example
The commercially available products such as Futura-NL.
As polyester fiber B, as long as being free of the polyester fiber of antimony trioxide, it is not particularly limited.From resistance
From the perspective of combustion property is excellent, brominated epoxy flame retardant is preferably comprised.In polyester fiber B, relative to selected from by gathering to benzene
One or more of the group that dioctyl phthalate alkane diol ester and the copolyester based on polyalkylene terephthalate are constituted is gathered
100 mass parts of ester resin preferably comprise 5 mass parts of brominated epoxy flame retardant~40 mass parts, further preferably 10 mass parts
~30 mass parts, further preferably 15 mass parts~25 mass parts.Polyester fiber B can also be containing other than antimony trioxide
Antimonial, such as sodium antimonate is as flame retardant.It as polyester fiber B, is not particularly limited, strain can be used for example
The cities such as the fire-retardant polyester series fiber Futura and fire-retardant polyester series fiber (trade name Futura-ST) of formula commercial firm Kaneka
Sell product.
From the viewpoint of suitable hair, the filament denier of polyester fiber A and polyester fiber B is preferably 10~
100dtex, more preferably 20~90dtex, further preferably 35~80dtex.
In the present invention, hair is also not particularly limited toward the plantation on wig matrix, and it is false that general production can be used for example
Method and apparatus used when hair etc. carry out.
Hereinafter, explaining the present invention in detail referring to attached drawing.
Fig. 1 is to penetrate hair to show that dress has worn the side of the state of the full head wig of an implementation form of the invention
Figure.The A of Fig. 2 is the schematic side elevational view for showing the back side of full head wig of an implementation form of the invention, and the B of Fig. 2 is
Its schematic facial figure.
As shown in Fig. 1~2, the full head wig 1 of the implementation form include be wearing on head wig matrix 10 and plantation in
Hair 20 on wig matrix 10.Wig matrix 10 is by being wearing on the 1st part 11 of poll region, being wearing on occiput area
The part 2 12 in domain and the third portion 13 being wearing near neck are constituted.When all hairs in part 1 will be planted
When quality settings are 100 mass %, the hair 21 planted in part 1 contains 60~80 mass % of polyester fiber A and people
20~40 mass % of work protein fibre.When will plant in all hairs of part 2 quality settings be 100 mass % when,
The hair 22 planted in part 2 12 contains 20~90 mass % of artificial proteins fiber, 10~80 matter of polyester fiber B
Measure % and 0~70 mass % of polyester fiber A.The hair 23 in third portion 13 is planted by polyester fiber A and/or polyester
Series fiber B is constituted.
By FIG. 1 to FIG. 3 it is found that the part 1 11 of the wig matrix of the implementation form is wearing on fringe part 31, overhead
Divide on 32, a part of lateral parts 33 and pileum part 34, the part 2 12 of wig matrix is wearing on lateral parts 33
In a part and middle section 35, the third portion 13 of wig matrix is wearing on neck neck portion 36.
Embodiment
Hereinafter, further illustrating the present invention by embodiment.In addition, the present invention is not limited by following embodiments.
Firstly, measuring gloss value, combing property, hair iron as described below to the hair sample of composition shown in following table 1
Heat setting and hair iron injury repair rate.The results are shown in following table 1.Polyester fiber A uses Co., Ltd.
The fire-retardant polyester series fiber (trade name Futura-NL, filament denier 58dtex) of Kaneka, polyester fiber B are used
The fire-retardant polyester series fiber (trade name Futura, filament denier 65dtex) of Co., Ltd. Kaneka, collagenous fibres make
With the regenerated collagen fiber (trade name Ultima, filament denier 78dtex) of Co., Ltd. Kaneka.
<measurement of gloss value>
It is measured using gloss measurement device (Bossa Nova Technologies corporation, trade name SAMBA Hair)
Gloss value.Gloss value is that 30 or less persons are set to qualification, and it is unqualified that gloss value, which is more than 30,.
<evaluation of combing property>
Hair is hung over into dynamometer (NIDEC-SHIMPO corporation, type with sample (16 inches of fiber quality 50g, length)
Number FGC-10B) on, hair sample is sandwiched with hair brush (at into corporation, trade name WIG Block ラ シ), from top to bottom mobile hair
Brush, measures its load, as combing value.It is lower to comb value, indicates that combing property is the better.It combs value and is set to conjunction for 3kg is below
Lattice are unqualified more than 3kg.
<evaluation of heat setting>
After being fixed with the position of the upper end 2cm of sample (fiber quality 15g, length 38cm) with rubber apart from hair,
The upper end of the overhead installation hair sample of headform's (Regina corporation, trade name CUT66).With being heated to 180
DEG C hair iron (U.S.'s Belson Products corporation, GOLD N HOT Professional Ceramic Spring
Curling Iron 1-1/4inch GH2150) hair tip of hair sample is caught, volume to root of hair rides over after being kept for 5 seconds
It does not allow curly form to fold on hand, allows hand to leave within 1 second and impart curling.The hair sample of curling will be imparted from people
It is taken off on head model, measures its length.The length for imparting the hair sample of curling is smaller, then it represents that easier imparting volume
Song, heat setting are the better.The length for imparting the hair sample of curling, which is that 35cm is below, is set to qualification, more than 35cm's
It is unqualified.
<evaluation of injury repair rate>
(1) the initial stage fluffy value in the hair layering portion (4 inches) of sample (16 inches of overall length, 15g) is measured.
(2) to hair with sample with hair brush allow down in an opposite direction hair erect and tangle hair.
(3) layering portion is rubbed 10 times with hand, hair is allowed further to tangle.
(4) hair tangled comb is opened with hair brush.
(5) operation 5 times of (2)~(4) are repeated, damage is promoted.
(6) the fluffy value in the layering portion of the hair sample after measurement damage promotes, as the fluffy value after damage.
(7) hair iron for being heated to 180 DEG C is allowed to damage 5 times from the root of hair of hair sample to hair tip reparation.Hair iron makes
It is and same hair iron used in heat setting evaluation.
(8) the fluffy value in the layering portion of measurement hair iron treated hair sample, as fluffy after injury repair
Value.
(9) injury repair rate is calculated according to following numerical expressions (1).Injury repair rate is 55% or more to be set to qualification, is lower than
55% is unqualified.
Fluffy value after injury repair rate (%)=(the fluffy value after fluffy value-injury repair after damage)/damage ×
100
<measurement of fluffy value>
The fluffy value of hair sample is measured using fluffy measuring machine shown in Fig. 4.As shown in A~C of Fig. 4,
Fluffy measuring machine 100 has support table 101 and is configured at fixture 102,103 in support table 101, to clamp hair.In fixture
On 102, scale 104 has been attached with adhesive tape (not shown).Support table 101, fixture 102 and 103 are by acrylic resin
It constitutes.As shown in the C of Fig. 4, between fixture 102 and fixture 103, according to the length direction for making fixture 102 center with
The consistent mode in center in the layering portion of hair sample 40 configures hair sample 40, and measures fluffy value.
Table 1
By the result of above-mentioned table 1 it is found that the hair sample 1~5 and 13 containing 20 mass % of regenerated collagen fiber or more
Impart curling after length be 35cm hereinafter, the heat setting of hair iron is good.Polyester containing 60 mass % or more
The gloss value of the hair sample 1~4,6,9,10 and 12 of fiber A is 30 hereinafter, showing natural appearance.Contain artificial hair
The hair sample 2,3,5~7 and 11 of 20 mass % of hair fiber or more and 10 mass % of polyester fiber B or more combs
Value is 3kg hereinafter, combing property is good.The hair sample 6~9,11 being made of polyester fiber A and/or polyester fiber B
Injury repair rate with 12 hair iron is 55% or more, and useful life longevity is good.
(embodiment 1)
In the part 1 11 of wig matrix 10, plantation equally constitutes fine by Polyester with above-mentioned hair sample 1
The hair 21 that 80 mass % of A and 20 mass % of regenerated collagen fiber is constituted is tieed up, in the part 2 12 of wig matrix 10, plantation
With above-mentioned hair sample 5 equally constitute by 30 mass % of polyester fiber B, 50 mass % of polyester fiber A and again
The hair 22 that 20 mass % of crude rubber original fiber is constituted, in the third portion 13 of wig matrix 10, plantation is tried with above-mentioned hair
The hair 23 being made of 40 mass % of polyester fiber B, 60 mass % of polyester fiber A that sample 6 equally constitutes makes Fig. 1
Shown in full head wig 1.
(embodiment 2)
In the part 1 11 of wig matrix 10, plantation equally constitutes fine by Polyester with above-mentioned hair sample 2
The hair 21 that 60 mass % of A, 20 mass % of polyester fiber B and 20 mass % of regenerated collagen fiber are constituted is tieed up, in wig base
In the part 2 12 of body 10, plantation and above-mentioned hair sample 2 equally constitute by 60 mass % of polyester fiber A, poly-
The hair 22 that 20 mass % of ester series fiber B and 20 mass % of regenerated collagen fiber is constituted, in the third portion 13 of wig matrix 10
On, plantation and above-mentioned hair sample 7 equally constitute by 40 mass % of polyester fiber A, 60 matter of polyester fiber B
The hair 23 that % is constituted is measured, full head wig 1 shown in FIG. 1 is made.
(embodiment 3)
In the part 1 11 of wig matrix 10, plantation equally constitutes fine by Polyester with above-mentioned hair sample 4
The hair 21 that 70 mass % of A and 30 mass % of regenerated collagen fiber is constituted is tieed up, in the part 2 12 of wig matrix 10, plantation
With above-mentioned hair sample 3 equally constitute by 70 mass % of polyester fiber A, 10 mass % of polyester fiber B and again
The hair 22 that 20 mass % of crude rubber original fiber is constituted, in the third portion 13 of wig matrix 10, plantation is tried with above-mentioned hair
The hair 23 being made of 80 mass % of polyester fiber A, 20 mass % of polyester fiber B that sample 9 equally constitutes makes Fig. 1
Shown in full head wig 1.
(comparative example 1)
It is all planted and the above-mentioned hair same structure of sample 10 in the part 1, part 2, third portion of wig matrix
At the hair being made of 90 mass % of polyester fiber A and 10 mass % of regenerated collagen fiber, in addition to this, with embodiment 1
Similarly make full head wig.
(comparative example 2)
It is all planted and the above-mentioned hair same structure of sample 6 in the part 1, part 2, third portion of wig matrix
At the hair being made of 60 mass % of polyester fiber A, 40 mass % of polyester fiber B, make similarly to Example 1
Full head wig.
(comparative example 3)
It is all planted and the above-mentioned hair same structure of sample 11 in the part 1, part 2, third portion of wig matrix
At the hair being made of 100 mass % of polyester fiber B, make full head wig similarly to Example 1.
The full head wig of Examples 1 to 3 and comparative example 1~3 is wearing on to the head of subject, as described below to light
Pool, combing property, the injury repair progress sense evaluation of the curl constancy of hair iron and hair iron.
(gloss)
Sense evaluation is carried out come the gloss of the hair to overhead according to the benchmark of 5 grades as described below.
5: with the hair substantially same gloss of the sample 12 (measured value of the gloss of hair sample 12: 21)
4: with the hair substantially same gloss of the sample 4 (measured value of the gloss of hair sample 4: 25)
3: with the hair substantially same gloss of the sample 8 (measured value of the gloss of hair sample 8: 33)
2: with the hair substantially same gloss of the sample 7 (measured value of the gloss of hair sample 7: 37)
1: with the hair substantially same gloss of the sample 11 (measured value of the gloss of hair sample 11: 48)
(combing property)
The hair for holding lateral parts sandwiches the hair with hair brush (at into corporation, trade name WIG Block ラ シ), from upper
Move down hair brush.It is repeated 5 times the operation of aforementioned (1), according to the situation of tangling of hair, as described below according to 5 grades
Benchmark evaluates combing property.
5: being tangled until to the 5th hair does not all occur for comb, hair brush can comb
4: hair occurring when comb is to the 4th~5 time and tangles, but hair brush can comb
3: hair occurring when comb is to the 2nd~3 time and tangles, but hair brush can comb
2: hair just slightly occurring at comb the 1st time and tangles, but hair brush can comb
1: hair just occurs at comb the 1st time and tangles, hair brush cannot comb
(curl constancy of hair iron)
The hair of lateral parts is divided into 3 parts according to identical pieces amount, by the pieces of a copy of it with being heated to 180
DEG C hair iron (U.S.'s Belson Products corporation, GOLD N HOT Professional Ceramic Spring
Curling Iron 1-1/4inch GH2150) it clamps, it rolls up from hair tip to root of hair, after being kept for 5 seconds, according to not allowing curl shape
The mode that shape folds removes hair iron.The shape crimped with visual confirmation, as described below according to the benchmark of 5 grades to curling
Mouldability (easiness for assigning curling) carries out sense evaluation.The typical curly form of each evaluation criteria is shown in Figure 5.
5: hair has the curling of 1.5 circles or more
4: hair has 1 circle more but less than the curling of 1.5 circles
3: hair has 0.5 circle more but less than the curling of 1 circle
2: hair has the curling less than 0.5 circle
1: not assigning curling, be substantially straight shape
(injury repair of hair iron)
(1) pieces for holding the wide 3cm of neck neck portion, with hair brush allow down in an opposite direction hair erect and tangle hair, then, with hair
Brush opens hair comb, assigns damage.
(2) with hair iron (U.S.'s Belson Products corporation, GOLD N HOT for being heated to 180 DEG C
Professional Ceramic Spring Curling Iron 1-1/4inch GH2150) it clamps and has been assigned damage
Pieces is moved to hair tip from root of hair.
(3) after passing through hair iron, 20 hairs of optionally choosing.
(4) with 20 hairs are visually confirmed respectively, damage hair will be set to there are corrugated shape in hair tip, damages the ratio of hair
It is calculated describedly under such as, according to the value of the ratio of damage hair, as described below according to the benchmark of 5 grades to injury repair
Property carry out sense evaluation.
Damage ratio (%)=(radical/20 of damage hair) × 100 of hair
5: the ratio for damaging hair is 10% or less
4: the ratio for damaging hair is more than 10% but is 30% or less
3: the ratio for damaging hair is more than 30% but is 50% or less
2: the ratio for damaging hair is more than 50% but is 70% or less
1: the ratio for damaging hair is more than 71%
Table 2
| Gloss | Combing property | The cans of hair iron | The injury repair of hair iron | |
| Embodiment 1 | 4 | 4 | 4 | 4 |
| Embodiment 2 | 4 | 3 | 4 | 4 |
| Embodiment 3 | 5 | 3 | 3 | 4 |
| Comparative example 1 | 5 | 2 | 1 | 2 |
| Comparative example 2 | 3 | 3 | 1 | 5 |
| Comparative example 3 | 1 | 5 | 1 | 5 |
By the data of table 2 it is found that the full head wig of Examples 1 to 3 is compared with the full head wig of comparative example 2~3, gloss is obtained
Inhibition has been arrived, has shown natural appearance.In addition, the full head wig of Examples 1 to 3 has more than the full head wig of comparative example 1
Good combing property.In addition, the full head wig of Examples 1 to 3 is easier to assign curling than the full head wig of comparative example 1~3.Separately
Outside, the full head wig of Examples 1 to 3 is easier to repair damage than the full head wig of comparative example 1.
Symbol description
1 complete wig
10 wig matrixes
11 part 1s
12 part 2s
13 third portions
20 hairs
21 kinds are planted in the hair of part 1
22 kinds are planted in the hair of part 2
23 kinds are planted in the hair of third portion
30 heads
31 fringe parts
32 overheads
33 lateral parts
34 pileum parts
35 middle sections
36 neck neck portions
40 hair samples
100 fluffy measuring machines
101 support table
102,103 fixture
104 scales
Claims (10)
1. a kind of full head wig, special comprising the wig matrix for being wearing on head and plantation in the hair on the wig matrix
Sign is,
The wig matrix is by being wearing on the part 1 of poll region, being wearing on the part 2 in occiput region and dress is worn
Third portion near neck is constituted,
Contain when the hair planted when the quality settings of all hairs of part 1 are 100 mass % in part 1 will be planted
There is 20~40 mass % of 60~80 mass % of polyester fiber A and artificial proteins fiber,
Contain when the hair planted when the quality settings of all hairs of part 2 are 100 mass % in part 2 will be planted
There are artificial 20~90 mass % of protein fibre, 10~80 mass % of polyester fiber B and 0~70 matter of polyester fiber A
% is measured,
Hair in third portion is planted by one or more of the group that is constituted selected from polyester fiber A and polyester fiber B
Fiber is constituted,
Polyester fiber A contains brominated epoxy flame retardant and antimony trioxide, and polyester fiber B is free of antimony trioxide.
2. full head wig according to claim 1, wherein when will plant in the quality settings of all hairs of part 1
When for 100 mass %, the hair planted in part 1 contains 70~80 mass % of polyester fiber A fiber and artificial proteins
20~30 mass % of fiber is planted when that will plant when the quality settings of all hairs of part 2 are 100 mass % in the 2nd
Partial hair contains 20~30 mass % of artificial proteins fiber, 20~30 mass % of polyester fiber B and Polyester is fine
40~60 mass % of A is tieed up, when that will plant when the quality settings of all hairs of third portion are 100 mass %, is planted in the 3rd
Partial hair is made of 30~50 mass % of polyester fiber A 50~70 mass % and polyester fiber B.
3. full head wig according to claim 1, wherein the artificial proteins fiber is collagenous fibres.
4. full head wig described in any one of claim 1 to 3, wherein polyester fiber B contains the resistance of brominated epoxy system
Fire agent.
5. full head wig described in any one of claim 1 to 3, wherein in polyester fiber A, relative to by poly- pair
One or more of the group that phthalic acid alkane diol ester and the copolyester based on polyalkylene terephthalate are constituted
100 mass parts of polyester resin, containing it is more than 5 mass parts of brominated epoxy flame retardant and 40 below the mass with antimony trioxide 1.5
Mass parts are more than or lower than 7 mass parts.
6. full head wig described in any one of claim 1 to 3, wherein in polyester fiber B, relative to selected from by
1 kind in group that polyalkylene terephthalate and the copolyester based on polyalkylene terephthalate are constituted with
On 100 mass parts of polyester resin, contain 5 mass parts of brominated epoxy flame retardant~40 mass parts.
7. full head wig described in any one of claim 1 to 3, wherein in planting the hair in part 1, when
By plantation when the quality settings of all hairs of part 1 are 100 mass %, contain 75~80 matter of polyester fiber A fiber
Measure % and 20~25 mass % of artificial proteins fiber.
8. full head wig according to claim 5, wherein in planting hair in part 1, when will plant in the 1st
When the quality settings of partial all hairs are 100 mass %, containing 75~80 mass % of polyester fiber A fiber and manually
20~25 mass % of protein fibre.
9. full head wig according to claim 6, wherein in planting hair in part 1, when will plant in the 1st
When the quality settings of partial all hairs are 100 mass %, containing 75~80 mass % of polyester fiber A fiber and manually
20~25 mass % of protein fibre.
10. full head wig according to claim 3, wherein the collagenous fibres are regenerated collagen fibers.