CN108016155A - A kind of novel touch screen low temperature manufacturing process - Google Patents

A kind of novel touch screen low temperature manufacturing process Download PDF

Info

Publication number
CN108016155A
CN108016155A CN201610976599.1A CN201610976599A CN108016155A CN 108016155 A CN108016155 A CN 108016155A CN 201610976599 A CN201610976599 A CN 201610976599A CN 108016155 A CN108016155 A CN 108016155A
Authority
CN
China
Prior art keywords
silver paste
conductive film
conductive
manufacturing process
conductive silver
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610976599.1A
Other languages
Chinese (zh)
Inventor
刘元哲
闫锦爽
刘兰兰
徐亮
刘旭
顾潇飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANO TOP ELECTRONIC TECHNOLOGY Co Ltd
Original Assignee
NANO TOP ELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANO TOP ELECTRONIC TECHNOLOGY Co Ltd filed Critical NANO TOP ELECTRONIC TECHNOLOGY Co Ltd
Priority to CN201610976599.1A priority Critical patent/CN108016155A/en
Publication of CN108016155A publication Critical patent/CN108016155A/en
Pending legal-status Critical Current

Abstract

The present invention is a kind of novel touch screen low temperature manufacturing process, the technique prints " cryogenic curing conductive silver paste " to touch-screen dedicated substrate membrane material, using 80 110 DEG C of low-temperature settings, it is abnormal to can effectively avoid base material contraction, fold and deformation etc. caused by 130 DEG C of hot settings of conductive silver paste.The technique can be saved in conventional touch screen manufacturing process to the burin-in process process of substrate membrane material, achieve the purpose that to save activity time, improve prouctiveness, reduce manufacture energy consumption and shorten processing procedure process.

Description

A kind of novel touch screen low temperature manufacturing process
Technical field
The present invention relates to touch screen technology field, more particularly to a kind of novel touch screen low temperature manufacturing process.
Background technology
Touch-screen is a kind of input equipment for significantly improving man machine operation interface, is had the advantages that directly perceived, simple, quick. Touch-screen has been obtained for being widely applied in many electronic products, for example smart mobile phone, PDA, multimedia, public information are looked into Inquiry system etc..
In traditional process for manufacturing touch panel, conductive silver paste solidification temperature used can just be fully cured more than 130 DEG C. Therefore need substrate membrane material by least 150 DEG C, 1 it is small when more than burin-in process process, can ensure in follow-up silver paste In curing process, substrate membrane material is not in that deformation, fold, harmomegathus etc. are abnormal.
And time-consuming for burin-in process process, more than the 30% of whole touch-screen manufacturing time is accounted for;Efficiency is low, easily because of waiting Substrate membrane material carries out burin-in process and causes the idle material of producing line, shut-down, high energy consumption, adds the energy loss in production process;Process Numerous and diverse, easily the scuffing of base substrate, folding line etc. are abnormal caused by operating reason in operation.
Therefore, if burin-in process process can be reduced, the production efficiency of touch-screen can be greatly improved, reduce production energy Consumption, shortens manufacturing step, improves product yield.
The content of the invention
The purpose of the present invention is exactly to improve many deficiencies in existing handset touch panel production technology, there is provided a kind of Novel touch screen low temperature manufacturing process, has great advantage in terms of processing procedure process is shortened.
The technical solution adopted by the present invention to solve the technical problems is:To be " ultralow in touch-screen dedicated substrate membrane material Warm curing conductive silver paste " forms silver paste leads with " direct silk-screened conductive silver paste, 80-110 DEG C of low-temperature setting after ", or " whole Body prints conductive silver paste, and after 80-110 DEG C of low-temperature setting, laser-induced thermal etching is carried out to conductive silver paste " to form silver paste leads, Avoid conventional conductive silver paste and cure required hot conditions.And conductive silver paste low-temperature setting under the conditions of 80-110 DEG C, will not Deformation, fold and harmomegathus etc. is caused to influence on touch-screen dedicated substrate membrane material, therefore substrate membrane material need not carry out burin-in process.Contracting Substrate membrane material burin-in process process is subtracted, has shortened in whole touch-screen manufacturing process 30% manufacture duration, improve production Ability;The idle material of producing line, shut-down caused by avoiding when waiting substrate membrane material and carrying out burin-in process, improve production efficiency;Nothing Substrate membrane material high temperature ageing need to be handled and conductive silver paste solidification temperature is low, greatly reduce the energy in process of factory production Loss, has saved the energy;Reduce one of manufacturing process, it is possible to reduce the damage such as substrate membrane material scuffing caused by manual operation Consumption, improves product yield, reduces waste, reduce cost.
To achieve these goals, the present invention adopts the following technical scheme that:
A kind of novel touch screen low temperature manufacturing process, including following process:
A, conductive film sensor production process, comprises the following steps:
Step A1:In touch-screen dedicated substrate membrane material, by " cryogenic curing conductive silver paste " with " direct silk-screened conductive silver Starch, after 80-110 DEG C of low-temperature setting " form silver paste leads, or " overall printing conductive silver paste, 80-110 DEG C of low-temperature setting Afterwards, laser-induced thermal etching is carried out to conductive silver paste " to form silver paste leads.The conductive film opened greatly;
Step A2:The conductive film opened greatly is cut, obtains conductive film sensor;
B, process is bound, is comprised the following steps:
Step B1:After conductive film sensor test passes, there are conductive silver paste leads in conductive film sensor The side is bonded optical cement OCA, and conductive film sensor and glass cover-plate are carried out fitting assembling by optical cement, then taken off Bubble.
Step B2:Conducting resinl ACF is fitted on FPC flexible PCBs;
Step B3;Finally FPC is bound on film sensor, obtains touch-screen.
Preferably, the novel touch screen low temperature manufacturing process, " cryogenic curing conductive silver paste " is north in step A1 Kona leads to the model NT-TL40 series of conductive silver pastes of Electron Technology Co., Ltd in capital.
Preferably, the novel touch screen low temperature manufacturing process, the silver paste leads line width line formed in step A1 Away from 20-150 μm.
Preferably, the novel touch screen low temperature manufacturing process, the baking of " cryogenic curing conductive silver paste " in step A1 Roasting temperature is 80-110 DEG C, baking time 10-60min.
The present invention is by touch-screen dedicated substrate membrane material, by " cryogenic curing conductive silver paste " with " direct silk-screen is led Electric silver paste, after 80-110 DEG C of low-temperature setting " forms silver paste leads, or " overall printing conductive silver paste, 80-110 DEG C of low-temperature solid After change, laser-induced thermal etching is carried out to conductive silver paste " to form silver paste leads, avoid conventional conductive silver paste and cure required height Warm condition.Conductive silver paste cures under 80-110 DEG C of cryogenic conditions, will not cause deformation, fold to touch-screen dedicated substrate membrane material Influenced with harmomegathus etc..Burin-in process is carried out so as to avoid to substrate membrane material, touch-screen manufacture duration is substantially reduced, improves Production efficiency and product yield.
Preferably, the novel touch screen low temperature manufacturing process, in step A1 touch-screen dedicated substrate membrane material be PET, One kind in ito film, nano silver wire conducting film, PI and PEEK materials.
Preferably, the novel touch screen low temperature manufacturing process, is cut the conductive film opened greatly in step A2 Before, last layer PE protective films are covered, are torn off when step B1 carries out fitting assembling.
Embodiment
With reference to embodiment, the present invention is described in detail.
Example one
A kind of new touch-screen low temperature manufacturing process, including following process:
A, conductive film sensor production process, comprises the following steps:
Step A1:In touch-screen dedicated substrate membrane material, by " cryogenic curing conductive silver paste " with " direct silk-screened conductive silver Starch, after 110 DEG C of low-temperature settings " form silver paste leads.The conductive film opened greatly;
Step A2:The conductive film opened greatly is cut, obtains conductive film sensor;
B, process is bound, is comprised the following steps:
Step B1:After conductive film sensor test passes, there are conductive silver paste leads in conductive film sensor The side is bonded optical cement OCA, and conductive film sensor and glass cover-plate are carried out fitting assembling by optical cement, then taken off Bubble.
Step B2:Conducting resinl ACF is fitted on FPC flexible PCBs;
Step B3:Finally FPC is bound on film sensor, obtains touch-screen.
Wherein, in step A1 " cryogenic curing conductive silver paste " be Nano Top Electronic Technology Co., Ltd. model For the conductive silver paste of NT-TL40A.
Wherein, the silver paste leads line width line-spacing formed in step A1 is 100 μm.
Wherein, the baking temperature of " cryogenic curing conductive silver paste " is 110 DEG C in step A1, and baking time is 30 minutes.
Wherein, touch-screen dedicated substrate membrane material is ITO conducting membrane materials in step A1.
Wherein, before the conductive film opened greatly is cut in step A2, last layer PE protective films are covered, are carried out in step B1 Torn off during fitting assembling.
Example two
A kind of novel touch screen low temperature manufacturing process, including following process:
A, conductive film sensor production process, comprises the following steps:
Step A1:In touch-screen dedicated substrate membrane material, by " cryogenic curing conductive silver paste " with " overall printing conductive silver Slurry, after 110 DEG C of low-temperature settings, laser-induced thermal etching is carried out to conductive silver paste " to form silver paste leads.The conductive thin opened greatly Film;
Step A2:The conductive film opened greatly is cut, obtains conductive film sensor;
B, process is bound, is comprised the following steps:
Step B1:After conductive film sensor test passes, there are conductive silver paste leads in conductive film sensor The side is bonded optical cement OCA, and conductive film sensor and glass cover-plate are carried out fitting assembling by optical cement, then taken off Bubble.
Step B2:Conducting resinl ACF is fitted on FPC flexible PCBs;
Step B3:Finally FPC is bound on film sensor, obtains touch-screen.
Wherein, in step A1 " cryogenic curing conductive silver paste " be Nano Top Electronic Technology Co., Ltd. model For the conductive silver paste of NT-TL40A.
Wherein, the silver paste leads line width line-spacing formed in step A1 is 30 μm.
Wherein, the baking temperature of " cryogenic curing conductive silver paste " is 110 DEG C in step A1, and baking time is 30 minutes.
Wherein, touch-screen dedicated substrate membrane material is ITO conducting membrane materials in step A1.
Wherein, before the conductive film opened greatly is cut in step A2, last layer PE protective films are covered, are carried out in step B1 Torn off during fitting assembling.
Example three
A kind of novel touch screen low temperature manufacturing process, including following process:
A, conductive film sensor production process, comprises the following steps:
Step A1:In touch-screen dedicated substrate membrane material, by " cryogenic curing conductive silver paste " with " direct silk-screened conductive silver Starch, after 90 DEG C of low-temperature settings " form silver paste leads.The conductive film opened greatly;
Step A2:The conductive film opened greatly is cut, obtains conductive film sensor;
B, process is bound, is comprised the following steps:
Step B1:After conductive film sensor test passes, there are conductive silver paste leads in conductive film sensor The side is bonded optical cement OCA, and conductive film sensor and glass cover-plate are carried out fitting assembling by optical cement, then taken off Bubble.
Step B2:Conducting resinl ACF is fitted on FPC flexible PCBs;
Step B3:Finally FPC is bound on film sensor, obtains touch-screen.
Wherein, in step A1 " cryogenic curing conductive silver paste " be Nano Top Electronic Technology Co., Ltd. model For the conductive silver paste of NT-TL40A.
Wherein, the silver paste leads line width line-spacing formed in step A1 is 120 μm.
Wherein, the baking temperature of " cryogenic curing conductive silver paste " is 90 DEG C in step A1, and baking time is 40 minutes.
Wherein, touch-screen dedicated substrate membrane material is nano silver wire conducting membrane material in step A1.
Wherein, before the conductive film opened greatly is cut in step A2, last layer PE protective films are covered, are carried out in step B1 Torn off during fitting assembling.
Example four
A kind of novel touch screen low temperature manufacturing process, including following process:
A, conductive film sensor production process, comprises the following steps:
Step A1:In touch-screen dedicated substrate membrane material, by " cryogenic curing conductive silver paste " with " overall printing conductive silver Starch, after 80 DEG C of low-temperature settings, laser-induced thermal etching carried out to conductive silver paste " form silver paste leads.The conductive film opened greatly;
Step A2:The conductive film opened greatly is cut, obtains conductive film sensor;
B, process is bound, is comprised the following steps:
Step B1:After conductive film sensor test passes, there are conductive silver paste leads in conductive film sensor The side is bonded optical cement OCA, and conductive film sensor and glass cover-plate are carried out fitting assembling by optical cement, then taken off Bubble.
Step B2:Conducting resinl ACF is fitted on FPC flexible PCBs;
Step B3:Finally FPC is bound on film sensor, obtains touch-screen.
Wherein, in step A1 " cryogenic curing conductive silver paste " be Nano Top Electronic Technology Co., Ltd. model For the conductive silver paste of NT-TL40A.
Wherein, the silver paste leads line width line-spacing formed in step A1 is 40 μm.
Wherein, the baking temperature of " cryogenic curing conductive silver paste " is 80 DEG C in step A1, and baking time is 20 minutes.
Wherein, touch-screen dedicated substrate membrane material is PET material in step A1.
Wherein, before the conductive film opened greatly is cut in step A2, last layer PE protective films are covered, are carried out in step B1 Torn off during fitting assembling.
Example five
A kind of novel touch screen low temperature manufacturing process, including following process:
A, conductive film sensor production process, comprises the following steps:
Step A1:In touch-screen dedicated substrate membrane material, by " cryogenic curing conductive silver paste " with " overall printing conductive silver Starch, after 100 DEG C of low-temperature settings, laser-induced thermal etching carried out to conductive silver paste " form silver paste leads.The conductive thin opened greatly Film;
Step A2:The conductive film opened greatly is cut, obtains conductive film sensor;
B, process is bound, is comprised the following steps:
Step B1:After conductive film sensor test passes, there are conductive silver paste leads in conductive film sensor The side is bonded optical cement OCA, and conductive film sensor and glass cover-plate are carried out fitting assembling by optical cement, then taken off Bubble.
Step B2:Conducting resinl ACF is fitted on FPC flexible PCBs;
Step B3:Finally FPC is bound on film sensor, obtains touch-screen.
Wherein, in step A1 " cryogenic curing conductive silver paste " be Nano Top Electronic Technology Co., Ltd. model For the conductive silver paste of NT-TL40A.
Wherein, the silver paste leads line width line-spacing formed in step A1 is 40 μm.
Wherein, the baking temperature of " cryogenic curing conductive silver paste " is 100 DEG C in step A1, and baking time is 50 minutes.
Wherein, touch-screen dedicated substrate membrane material is PEEK materials in step A1.
Wherein, before the conductive film opened greatly is cut in step A2, last layer PE protective films are covered, are carried out in step B1 Torn off during fitting assembling.
Example six
A kind of novel touch screen low temperature manufacturing process, including following process:
A, conductive film sensor production process, comprises the following steps:
Step A1:In touch-screen dedicated substrate membrane material, by " cryogenic curing conductive silver paste " with " direct silk-screened conductive silver Starch, after 110 DEG C of low-temperature settings " form silver paste leads.The conductive film opened greatly;
Step A2:The conductive film opened greatly is cut, obtains conductive film sensor;
B, process is bound, is comprised the following steps:
Step B1:After conductive film sensor test passes, there are conductive silver paste leads in conductive film sensor The side is bonded optical cement OCA, and conductive film sensor and glass cover-plate are carried out fitting assembling by optical cement, then taken off Bubble.
Step B2:Conducting resinl ACF is fitted on FPC flexible PCBs;
Step B3:Finally FPC is bound on film sensor, obtains touch-screen.
Wherein, in step A1 " cryogenic curing conductive silver paste " be Nano Top Electronic Technology Co., Ltd. model For the conductive silver paste of NT-TL40A.
Wherein, the silver paste leads line width line-spacing formed in step A1 is 80 μm.
Wherein, the baking temperature of " cryogenic curing conductive silver paste " is 110 DEG C in step A1, and baking time is 60 minutes.
Wherein, touch-screen dedicated substrate membrane material is PI materials in step A1.
Wherein, before the conductive film opened greatly is cut in step A2, last layer PE protective films are covered, are carried out in step B1 Torn off during fitting assembling.
Touch-screen made from embodiment 1-6 is tested, test result refers to following table.
The above is presently preferred embodiments of the present invention, but the present invention should not be limited to it is interior disclosed in the example Hold.So every do not depart from the lower equivalent or modification completed of spirit disclosed in this invention, the model that the present invention protects is both fallen within Enclose.

Claims (6)

1. a kind of novel touch screen low temperature manufacturing process, it is characterised in that including following process:
A, conductive film sensor production process, comprises the following steps:
Step A1:In touch-screen dedicated substrate membrane material, by " cryogenic curing conductive silver paste " with " direct silk-screened conductive silver paste, After 80-110 DEG C of low-temperature setting " form silver paste leads, or " overall printing conductive silver paste, it is right after 80-110 DEG C of low-temperature setting Conductive silver paste carries out laser-induced thermal etching " to form silver paste leads, the conductive film opened greatly;
Step A2:The conductive film opened greatly is cut, obtains conductive film sensor.
B, process is bound, is comprised the following steps:
Step B1:After conductive film sensor test passes, there is the one side of conductive silver paste leads in conductive film sensor Optical cement (OCA) is bonded, conductive film sensor and glass cover-plate are carried out by fitting assembling by optical cement, then deaeration.
Step B2:Anisotropic conductive film (ACF) is fitted on flexible PCB (FPC);
Step B3:FPC is bound on film sensor, obtains touch-screen.
2. a kind of novel touch screen low temperature manufacturing process according to claim 1, it is characterised in that " ultralow in step A1 Warm curing conductive silver paste " is the conductive silver paste of the model NT-TL40 series of Nano Top Electronic Technology Co., Ltd..
3. a kind of novel touch screen low temperature manufacturing process according to claim 1, it is characterised in that formed in step A1 Silver paste leads line width line-spacing is at 20-150 μm.
4. a kind of novel touch screen low temperature manufacturing process according to claim 1, it is characterised in that " ultralow in step A1 The baking temperature of warm curing conductive silver paste " is 80-110 DEG C, baking time 10-60min.
A kind of 5. novel touch screen low temperature manufacturing process according to claim 1, it is characterised in that touch-screen in step A1 Dedicated substrate membrane material is one kind in PET, ito film, nano silver wire conducting film, PI and PEEK materials.
6. a kind of novel touch screen low temperature manufacturing process according to claim 1, it is characterised in that will be opened greatly in step A2 Conductive film cut before, cover last layer PE protective films, step B1 carry out fitting assembling when tear off.
CN201610976599.1A 2016-11-03 2016-11-03 A kind of novel touch screen low temperature manufacturing process Pending CN108016155A (en)