CN108004784A - A kind of dipping solution for improving Polyester Cord quality and preparation method thereof - Google Patents
A kind of dipping solution for improving Polyester Cord quality and preparation method thereof Download PDFInfo
- Publication number
- CN108004784A CN108004784A CN201711337330.XA CN201711337330A CN108004784A CN 108004784 A CN108004784 A CN 108004784A CN 201711337330 A CN201711337330 A CN 201711337330A CN 108004784 A CN108004784 A CN 108004784A
- Authority
- CN
- China
- Prior art keywords
- parts
- latex
- weight
- resin
- dipping solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of dipping solution for improving Polyester Cord quality and preparation method thereof, belongs to industrial cloth technical field.It is prepared including following each component:Resorcinol, sodium hydroxide, formaldehyde, latex, resin, the parts by weight of the resorcinol are 15 30 parts, the parts by weight of the sodium hydroxide are 3 12 parts, the parts by weight of the formaldehyde are 8 16 parts, the parts by weight of the latex are 80 180 parts, the parts by weight of the resin are 15 35 parts, and the latex is styrene-butadiene latex, Heveatex, hydroxyl latex.The present invention has the advantages that high temperature resistance, antiacid alkali, high abrasion, improves the performance of dipping solution.
Description
Technical field
The present invention relates to a kind of formula of dipping solution and preparation method thereof, especially a kind of Polyester Cord quality that improves
Dipping solution and preparation method thereof, belongs to industrial cloth technical field.
Background technology
Impregnation is fabric by glue immersion trough, makes the upper rubber cement of fabric fibre leaching, to improve the ripe knot power of fabric and sizing material.Leaching
Glue can make artificial silk, synthetic fibers and glass-fiber cord surface smooth, and the vigorous of sizing material and fiber is remarkably improved after impregnation slurry
Put forth effort.Common immersion liquid is natural emulsion and the matched aqueous emulsion of resorcinol formaldehyde resin.Use as a servant gluing equipment include labour stain groove,
Hothouse, hot secondary and devices for taking-up, can also be connected with calender, composition Supreme Being's cloth impregnation, rubberizing, rubber linkage production line.Leaching
Glue can improve rubber and the private of glass fibre is puted forth effort, and cotton cord can also significantly improve the durability of tire through soaking phenolic aldehyde latex
Energy.But existing dipping solution urgently improves in raising the heat-resisting of woven fibrous, corrosion resistant, pressure-resistant aspect of performance.
The content of the invention
The purpose of the present invention is in view of the above shortcomings of the prior art, improve a kind of impregnation for improving Polyester Cord quality
Liquid and preparation method thereof, to improve the heat-resisting of industrial cloth, corrosion resistant, pressure-resistant and fatigue performance.
Technical scheme is as follows:A kind of dipping solution for improving Polyester Cord quality, it is characterized in that, including it is following
Each component is prepared:Resorcinol, sodium hydroxide, formaldehyde, latex, resin, the parts by weight of the resorcinol are 15-30
Part, the parts by weight of the sodium hydroxide are 3-12 parts, and the parts by weight of the formaldehyde are 8-16 parts, and the parts by weight of the latex are
80-180 parts, the parts by weight of the resin are 15-35 parts, and the latex is styrene-butadiene latex, Heveatex, hydroxyl latex.
The resin includes epoxy resin, isocyanates, methacrylate and is prepared.
The parts by weight of the epoxy resin are 10-35 parts, and the parts by weight of isocyanates are 2-8 parts, methacrylate
Parts by weight are 1-6 parts.
A kind of preparation method for the dipping solution for improving Polyester Cord quality, it is characterized in that, resorcinol is first dissolved in water
In, sodium hydroxide solution is then added, is stirred evenly;After standing five minutes, formalin is added, stirs reaction solution, and make
At 25 DEG C carry out 6 it is small when be condensed;Latex is added to the water and is diluted, after adding above-mentioned reaction solution and resin, at 25 DEG C
It is lower by the mixing easily cure 16-24 it is small when.
Heveatex belongs to the thermoplastic synthetic resin of rubber, its main feature is that when high resiliency, bonding filming performance it is good,
Glued membrane is imbued with pliability, thus glued membrane is had excellent flexible resistance, shock resistance and creep resistance, suitable for dynamic lower part
Bonding between the bonding and different thermal expansion coefficient material of part.
Styrene-butadiene latex is the stable emulsion formed with butadiene and styrene through low temperature polymerization.According to styrene-content, breast
The difference of agent and polymerization temperature etc., and have a variety of kinds, its performance and purposes are also different.Styrene-butadiene latex is butadiene and benzene second
Alkene monomer manufactured polymer emulsion through emulsion copolymerization after addition different chemical product and auxiliary agent.Styrene-butadiene latex has good
Adherence, since its particle is smaller than the particle of Heveatex, its mechanical stability is better than Heveatex, and can with Heveatex with
Any ratio mixing.Styrene-butadiene latex is most important synthetic latex, different according to styrene-content, can be divided into S/B latex(Benzene second
Alkene content is more than 45%)And SBR latex(Styrene-content is less than 45%).S/B latex is mainly used for paper coating(Art paper is given birth to
Production)And carpet backing, and SBR latex is then mainly for the manufacture of foam(Sponge)Product and synthetic fibers cord fabric thread impregnating neck
Domain.
Butadiene-vinylpyridine copylymer latex is vinylpyridine(Alpha-Methyl -5- vinylpyridines)With the bipolymer of butadiene, it is known as fourth
Pyrrole latex(butadiene vinyl-pyridine rubber latex).The manufacture method of butadiene-vinylpyridine copylymer latex and styrene-butadiene latex class
Seemingly, styrene simply is replaced with vinylpyridine, polymerization is divided into hot polymerization and cold poly- two major class.At present generally using hot polymerization
Method, polymerization temperature are 50 DEG C;Due to having introduced pyridine groups in latex, polarity is added, thus fiber can be greatly improved(It is special
It is not artificial silk, polyamide, polyester etc.)With the direct adhesive power of rubber.After generally being mixed during use with a small amount of styrene-butadiene latex,
A certain proportion of maceration extract abbreviation RFL is made into being mixed with resorcinol-formaldehyde solution.
Epoxy resin is to refer to the organic compound containing two or more epoxide groups in molecule, in addition to indivedual,
Their relative molecular mass is not high.The molecular structure of epoxy resin is to contain active epoxide group in strand as it
Feature, epoxide group can be located at the end of strand, centre or circlewise structure.Due to containing active ring in molecular structure
Oxygen groups, make them to crosslink reaction with polytype curing agent and form the insoluble height with three-dimensional net structure
Polymers.The high-molecular compound containing epoxide group is referred to as epoxy resin in all molecular structures.Epoxy resin tool after curing
There are good physics, chemical property, its surface to metal and nonmetallic materials has excellent adhesive strength, and dielectric properties are good
Good, deformation retract rate is small, and product size stability is good, and hardness is high, and pliability is preferable, to alkali and most of solvent-stable, thus
It is widely used in national defence, each department of national economy, pours into a mould, impregnates, the purposes such as lamination material, bonding agent, coating.
Resorcinol is mainly used for the interareas such as rubber adhesive, synthetic resin, dyestuff, preservative, medicine and analytical reagent,
Resorcinol has bactericidal effect, can be used as preservative, in cosmetics and dermatosis treating medicine paste and ointment etc. in adding.With formaldehyde
Condensation polymer is generated, available for viscose processed and the tire cord binding agent of nylon, wood gluing agent is prepared, for vinyl
The bonding of material and metal, resorcinol is the intermediate of many azo dyes, fur dyes, and medicine intermediate is to nitrogen base
Salicylic raw material.There is aldehyde radical to give birth to polycondensation reaction in formaldehyde molecule, phenolic resin can be obtained.
Latex in the present invention can form glued membrane in fiber surface, and adhesive effect is closed by molecular separating force and chemical bond.With
The prior art is compared, and the impregnation industrial cloth of impregnation formula production using the present invention, has the high temperature ageing performance of rubber shoe latex layer
Good, the features such as service life is long, the present invention make the dipping solution surface that is immersed on industrial cloth fast by adding latex in the feed
Speed forms thin film, which can play the role of heat-resisting, corrosion resistant, wear-resisting, ensures the viscous of dipping solution and industrial cloth surface
Close performance.The present invention has the advantages that high temperature resistance, antiacid alkali, high abrasion, improves the performance of dipping solution.
Embodiment
Embodiment 1
A kind of dipping solution for improving Polyester Cord quality, including following each component are prepared:Resorcinol, sodium hydroxide,
Formaldehyde, latex, resin, the parts by weight of the resorcinol are 15-30 parts, and the parts by weight of the sodium hydroxide are 3-12 parts, institute
The parts by weight for stating formaldehyde are 8-16 parts, and the parts by weight of the latex are 80-180 parts, and the parts by weight of the resin are 15-35 parts,
The latex is styrene-butadiene latex, Heveatex, hydroxyl latex.
Resin includes epoxy resin, isocyanates, methacrylate and is prepared.The parts by weight of epoxy resin are 10-
35 parts, the parts by weight of isocyanates are 2-8 parts, and the parts by weight of methacrylate are 1-6 parts.
A kind of preparation method for the dipping solution for improving Polyester Cord quality, it is characterized in that, resorcinol is first dissolved in water
In, sodium hydroxide solution is then added, is stirred evenly;After standing five minutes, formalin is added, stirs reaction solution, and make
At 25 DEG C carry out 6 it is small when be condensed;Latex is added to the water and is diluted, after adding above-mentioned reaction solution and resin, at 25 DEG C
It is lower by the mixing easily cure 16-24 it is small when.
Embodiment 2
A kind of dipping solution for improving Polyester Cord quality, including following each component are prepared:Resorcinol, sodium hydroxide,
Formaldehyde, latex, resin, the parts by weight of the resorcinol are 30 parts, and the parts by weight of the sodium hydroxide are 12 parts, the formaldehyde
Parts by weight be 16 parts, the parts by weight of the latex are 180 parts, and the parts by weight of the resin are 35 parts, and the latex is butylbenzene
Latex, Heveatex, hydroxyl latex.
Resin includes epoxy resin, isocyanates, methacrylate and is prepared.The parts by weight of epoxy resin are 35
Part, the parts by weight of isocyanates are 8 parts, and the parts by weight of methacrylate are 6 parts.
A kind of preparation method for the dipping solution for improving Polyester Cord quality, it is characterized in that, resorcinol is first dissolved in water
In, sodium hydroxide solution is then added, is stirred evenly;After standing five minutes, formalin is added, stirs reaction solution, and make
At 25 DEG C carry out 6 it is small when be condensed;Latex is added to the water and is diluted, after adding above-mentioned reaction solution and resin, at 25 DEG C
It is lower by the mixing easily curing 24 it is small when.
Embodiment 3
A kind of dipping solution for improving Polyester Cord quality, including following each component are prepared:Resorcinol, sodium hydroxide,
Formaldehyde, latex, resin, the parts by weight of the resorcinol are 15 parts, and the parts by weight of the sodium hydroxide are 3 parts, the formaldehyde
Parts by weight be 8 parts, the parts by weight of the latex are 80 parts, and the parts by weight of the resin are 15 parts, and the latex is butadiene-styrene rubber
Breast, Heveatex, hydroxyl latex.
Resin includes epoxy resin, isocyanates, methacrylate and is prepared.The parts by weight of epoxy resin are 10
Part, the parts by weight of isocyanates are 2 parts, and the parts by weight of methacrylate are 1 part.
A kind of preparation method for the dipping solution for improving Polyester Cord quality, it is characterized in that, resorcinol is first dissolved in water
In, sodium hydroxide solution is then added, is stirred evenly;After standing five minutes, formalin is added, stirs reaction solution, and make
At 25 DEG C carry out 6 it is small when be condensed;Latex is added to the water and is diluted, after adding above-mentioned reaction solution and resin, at 25 DEG C
It is lower by the mixing easily curing 16 it is small when.
Claims (4)
1. a kind of dipping solution for improving Polyester Cord quality, it is characterized in that, including following each component is prepared:Isophthalic two
Phenol, sodium hydroxide, formaldehyde, latex, resin, the parts by weight of the resorcinol are 15-30 parts, the parts by weight of the sodium hydroxide
For 3-12 parts, the parts by weight of the formaldehyde are 8-16 parts, and the parts by weight of the latex are 80-180 parts, the parts by weight of the resin
For 15-35 parts, the latex is styrene-butadiene latex, Heveatex, hydroxyl latex.
2. a kind of dipping solution for improving Polyester Cord quality according to claim 1, it is characterized in that, the resin includes
Epoxy resin, isocyanates, methacrylate are prepared.
3. a kind of dipping solution for improving Polyester Cord quality according to claim 2, it is characterized in that, the epoxy resin
Parts by weight be 10-35 part, the parts by weight of isocyanates are 2-8 parts, and the parts by weight of methacrylate are 1-6 parts.
4. a kind of preparation method of dipping solution for improving Polyester Cord quality according to claim 1, it is characterized in that, first
Resorcinol is dissolved in water, is then added sodium hydroxide solution, is stirred evenly;After standing five minutes, formalin is added,
Reaction solution is stirred, and is allowed to be condensed when progress 6 is small at 25 DEG C;Latex is added to the water and is diluted, adds above-mentioned reaction solution
After resin, at 25 DEG C by the mixing easily cure 16-24 it is small when.