CN108003622A - A kind of oil well dedicated elas-tic rubber packing and preparation method thereof - Google Patents
A kind of oil well dedicated elas-tic rubber packing and preparation method thereof Download PDFInfo
- Publication number
- CN108003622A CN108003622A CN201711281329.XA CN201711281329A CN108003622A CN 108003622 A CN108003622 A CN 108003622A CN 201711281329 A CN201711281329 A CN 201711281329A CN 108003622 A CN108003622 A CN 108003622A
- Authority
- CN
- China
- Prior art keywords
- rubber
- parts
- carbon black
- oil well
- packing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of oil well dedicated elas-tic rubber packing.Mainly solve the problems, such as that existing oil pumping unit seal material serious wear must be replaced repeatedly.It is characterized in that:Its component and the parts by weight of each component are:100 200 parts of dimethyl silicone rubber, 30 40 parts of White Carbon black, 40 45 parts of high abrasion carbon black, 20 25 parts of di-iron trioxide, crosslinking agent are 35 parts, accelerating agent is 24 parts, antioxidant is 12 parts;Its preparation method comprises the following steps:(1)Dimethyl silicone rubber is put into rubber mixing machine and is plasticated, Bao Tongsan is parked stand-by all over bottom sheet;(2)Above-mentioned film is put into rubber mixing machine again and starts to be kneaded, after film bag roller, input rubber chemicals White Carbon black, high abrasion carbon black, di-iron trioxide, crosslinking agent, accelerating agent, antioxidant, are made rubber compound;(3)By rubber compound slice, weigh, be put into mould, then vulcanized, product packing is made.The rubber packing, has higher elasticity and wear resistance, can lift the sealing performance of mouth of pumped oil well polished rod.
Description
Technical field
The present invention relates to a kind of seal in oil extraction in oil field technical field, especially a kind of oil well dedicated elas-tic rubber packing
And preparation method thereof.
Background technology
At present, oil pumping polish rod pumps in mouth of pumped oil well in oil exploitation, sealing between the two mainly by
Inner sealing packing is completed, but due to the aqueous high, factors such as impurity is big, temperature is high in underground, due to original oil pumping
Sealing material poor lubrication, the function of wellhead polish rod are low, cause oil pumping unit seal material serious wear, and oil dripping phenomenon of dripping is tight
Weight, it is therefore necessary to sealed packing is replaced repeatedly, not only increases the labor intensity of worker, causes crude oil to waste, pollution environment, and
And it have impact on the yield of oil pumping.
The content of the invention
It must be replaced repeatedly the invention reside in existing oil pumping unit seal material serious wear present in background technology is overcome
The problem of packing, and a kind of oil well dedicated elas-tic rubber packing is provided.The oil well dedicated elas-tic rubber packing, has higher bullet
Property, abrasion resistance properties are strong, can lift the sealing performance and oil pumping well yield of mouth of pumped oil well polished rod.Present invention also offers one
The preparation method of kind oil well dedicated elas-tic rubber packing.
The present invention solves the problems, such as that it can reach by following technical solution:A kind of oil well dedicated elas-tic rubber packing, its
Component and the parts by weight of each component are:100-200 parts of dimethyl silicone rubber, 30-40 parts of White Carbon black, 40-45 parts of high abrasion carbon black,
20-25 parts of di-iron trioxide, crosslink agent DCP are 3-5 parts, diphenylguanidine PG is 2-4 parts, antioxidant MB is 1-2 parts.
The crosslinking agent is DCP crosslinking agents, and accelerating agent is DPG accelerating agents, and antioxidant is MB antioxidants.
The present invention also provides a kind of preparation method of oil well dedicated elas-tic rubber packing, comprise the following steps:
(1)Dimethyl silicone rubber is weighed up in proportion, is put into rubber mixing machine, the control of rubber mixing machine roller temperature is moulded at 30-50 °C
Refining, time of plasticating at 20-25 minute, when viscosity reaches 10-12, are kneaded uniform, Bao Tongsan times bottom sheet, park 12 it is small when it is stand-by;
(2)The above-mentioned film parked is put into rubber mixing machine again, roller temperature starts to be kneaded between 20-50 °C, treats film bag
After roller, rubber chemicals White Carbon black, high abrasion carbon black, di-iron trioxide, crosslinking agent, accelerating agent, antioxidant are put into proportion, is made
Rubber compound;
(3)By step(2)The rubber compound slice of preparation, weigh, and is put into mould, is then heated on 160 tons of vulcanizers
150-160 °C, pressurization 4kg/cm2 is vulcanized, and vulcanization time determines 20-25 minutes, and product packing is made.
In the oil field oil sludge cleaning agent in each component:Dimethyl silicone rubber has the low temperature resistant superior function of high temperature resistant,
Di-iron trioxide plays the role of increasing weight, and White Carbon black and high abrasion carbon black play the role of reinforcing agent, crosslinking agent and promotion
Agent effect is to promote the vulcanization of rubber, and antioxidant improves the packing service life.
It is of the invention to be had the advantages that compared with above-mentioned background technology:The oil well dedicated elas-tic rubber packing,
Manufacturing process is simple, and material is easy to get, and can all be produced using General Purpose Rubber processing equipment for product, production cost is low.Make
Oil well dedicated elas-tic rubber packing there is higher elasticity, cold-resistant, heat-resisting, oil resistant, acid-alkali-resistant degree and abrasion resistance properties are strong, carry
The sealing performance of mouth of pumped oil well polished rod has been risen, has improved oil pumping well yield.
Embodiment:
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1
(1)Weigh in 100g dimethyl silicone rubbers input rubber mixing machine, the roller temperature control of machine is plasticated at 30 °C, is plasticated the time
At 20 minutes, when viscosity reaches 10, be kneaded it is uniform, Bao Tongsan all over bottom sheet, park 12 it is small when it is stand-by;
(2)The above-mentioned film parked is put into rubber mixing machine again, roller temperature starts to be kneaded at 30 °C, after film bag roller, throws
Enter rubber chemicals White Carbon black 40g, high abrasion carbon black 40, di-iron trioxide 20g, crosslink agent DCP 3g, diphenylguanidine PG2g, antioxidant
MB1g, is made rubber compound.
(3)By rubber compound slice, weigh, be put into designed rectangular mould, be then heated on 160 tons of vulcanizers
151 °C, pressurization 4kg/cm2 is vulcanized, and vulcanization time determines 20 minutes, prepares the sealed packing product of sulfidization molding.
Embodiment 2
(1)Weigh in 200g dimethyl silicone rubbers input rubber mixing machine, the roller temperature control of machine is plasticated at 50 °C, is plasticated the time
At 20 minutes, when viscosity reaches 10, be kneaded it is uniform, Bao Tongsan all over bottom sheet, park 12 it is small when it is stand-by;
(2)The above-mentioned film parked is put into rubber mixing machine again, roller temperature starts to be kneaded at 50 °C, after film bag roller, throws
Enter rubber chemicals White Carbon black 40g, high abrasion carbon black 45, di-iron trioxide 25g, crosslink agent DCP 5g, diphenylguanidine PG4g, antioxidant
MB2g, is made rubber compound.
(3)By rubber compound slice, weigh, be put into designed rectangular mould, be then heated on 160 tons of vulcanizers
151 °C, pressurization 4kg/cm2 is vulcanized, and vulcanization time determines 20 minutes, prepares the sealed packing product of sulfidization molding.
Embodiment 3
(1)Weigh in 150g dimethyl silicone rubbers input rubber mixing machine, the roller temperature control of machine is plasticated at 40 °C, is plasticated the time
At 20 minutes, when viscosity reaches 10, be kneaded it is uniform, Bao Tongsan all over bottom sheet, park 12 it is small when it is stand-by;
(2)The above-mentioned film parked is put into rubber mixing machine again, roller temperature starts to be kneaded at 40 °C, after film bag roller, throws
Enter rubber chemicals White Carbon black 35g, high abrasion carbon black 42, di-iron trioxide 23g, crosslink agent DCP 4g, diphenylguanidine PG3g, antioxidant
MB2g, is made rubber compound.
(3)By rubber compound slice, weigh, be put into designed rectangular mould, be then heated on 160 tons of vulcanizers
151 °C, pressurization 4kg/cm2 is vulcanized, and vulcanization time determines 20 minutes, prepares the sealed packing product of sulfidization molding.
Product packing prepared by embodiment 1-3 each performance compared with the natural rubber packing that existing oil field uses is shown in Table 1:
Table 1
By table 1 as it can be seen that rubber packing prepared by the present invention, leakproofness, service life, temperature tolerance, wearability and elasticity are all obvious
The performance of the natural rubber packing used better than current oil field, leakproofness improve 6 times, extend 4 times using service life, become
4 times of shape time lengthening.
Oil well dedicated elas-tic rubber packing face shaping of the present invention is rectangle or circle, and each sealing ring is equipped with
Spiral helicine bar mouth, easy to load and unload, sealing ring size has tens kinds, can be adjusted at any time according to oil-extractor polish-rod size, adjusts
It is convenient to be replaced after whole, and easily assembled, rational in infrastructure, wear extent is few, substantially increases product service life.
Claims (4)
- A kind of 1. oil well dedicated elas-tic rubber packing, it is characterised in that:Its component and the parts by weight of each component are:Dimethyl-silicon rubber 100-200 parts of glue, 30-40 parts of White Carbon black, 40-45 parts of high abrasion carbon black, 20-25 parts of di-iron trioxide, crosslinking agent for 3-5 parts, Accelerating agent is 2-4 parts, antioxidant is 1-2 parts.
- A kind of 2. oil well dedicated elas-tic rubber packing according to claim 1, it is characterised in that:The crosslinking agent is DCP Crosslinking agent, accelerating agent are DPG accelerating agents, and antioxidant is MB antioxidants.
- A kind of 3. preparation method of oil well dedicated elas-tic rubber packing according to claim 1, it is characterised in that:Including with Lower step:(1)Dimethyl silicone rubber is weighed up in proportion, is put into rubber mixing machine, the control of rubber mixing machine roller temperature is plasticated at 30-50 °C, The time plasticated at 20-25 minutes, when viscosity reaches 10-12, be kneaded it is uniform, Bao Tongsan all over bottom sheet, park 12 it is small when it is stand-by;(2)The above-mentioned film parked is put into rubber mixing machine again, roller temperature starts to be kneaded between 20-50 °C, treats film bag After roller, rubber chemicals White Carbon black, high abrasion carbon black, di-iron trioxide, crosslinking agent, accelerating agent, antioxidant are put into proportion, is made Rubber compound;(3)By step(2)The rubber compound slice of preparation, weigh, and is put into mould, is then heated on 160 tons of vulcanizers 150-160 °C, pressurization 4kg/cm2 is vulcanized, and vulcanization time determines 20-25 minutes, and product packing is made.
- A kind of 4. preparation method of oil field oil sludge cleaning agent according to claim 3, it is characterised in that:The mould is Circular or rectangle.