CN107986620A - A kind of mobile phone screen protective glass - Google Patents
A kind of mobile phone screen protective glass Download PDFInfo
- Publication number
- CN107986620A CN107986620A CN201711043307.XA CN201711043307A CN107986620A CN 107986620 A CN107986620 A CN 107986620A CN 201711043307 A CN201711043307 A CN 201711043307A CN 107986620 A CN107986620 A CN 107986620A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- mobile phone
- phone screen
- protective glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of glass material, and in particular to a kind of mobile phone screen protective glass, belongs to electronic equipment screen glass technology field.Mobile phone screen protective glass, includes each component of following parts by weight：50 90 parts of silica, 20 40 parts of calcium oxide, 10 20 parts of barium monoxide, 19 parts of titanium oxide, 2 10 parts of vanadium oxide, 6 15 parts of manganese oxide, 3 18 parts of cobalt oxide, 25 parts of niobium oxide, 13 parts of zirconium oxide, 29 parts of tungsten oxide.The present invention passes through silica, calcium oxide, barium monoxide, titanium oxide, vanadium oxide, manganese oxide, cobalt oxide, niobium oxide, zirconium oxide, the compounding of tungsten oxide, obtained glass transmission rate is good, reflectance and glossiness are suitable, can effectively prevent user using mobile phone, TV, computer when it is big to eye injury, eyeshield is effective.
Description
Technical field
The present invention relates to a kind of glass material, and in particular to a kind of mobile phone screen protective glass, belongs to electronic equipment screen
With glass technology field.
Background technology
With constantly advancing for the mankind, present electronic equipment has become the essential use of people's daily life
Product, liquid crystal display is typically equipped with these electronic equipments.Liquid crystal display is the physical characteristic using liquid crystal, during energization
Arrangement becomes orderly, makes light prevent light from passing through easily by fall into disarray during, no power.On the surface of liquid crystal display
Be generally adopted by glass, but now electronic equipment glass in use, but meeting when the glass of electronic equipment uses now
Inverted image is produced on a display screen, and user can produce inconvenience when in use, and long-time service is also bad to eyes.
The content of the invention
The object of the present invention is to provide a kind of mobile phone screen protective glass, the present invention passes through silica, calcium oxide, oxidation
Barium, titanium oxide, vanadium oxide, manganese oxide, cobalt oxide, niobium oxide, zirconium oxide, the compounding of tungsten oxide, obtained glass transmission rate is good,
Reflectance and glossiness are suitable, can effectively prevent user's, shield big to eye injury when using mobile phone, TV, computer
Eye is effectively.
The purpose of the present invention is what is be achieved through the following technical solutions, a kind of mobile phone screen protective glass, it is characterized in that, institute
Stating mobile phone screen protective glass includes each component of following parts by weight：50-90 parts of silica, 20-40 parts of calcium oxide, oxidation
10-20 parts of barium, 1-9 parts of titanium oxide, 2-10 parts of vanadium oxide, 6-15 parts of manganese oxide, 3-18 parts of cobalt oxide, niobium oxide 2-5
Part, 1-3 parts of zirconium oxide, 2-9 parts of tungsten oxide.
Preferably, the mobile phone screen protective glass includes each component of following parts by weight：56-85 parts of silica, calcium oxide
23-37 parts, 12-18 parts of barium monoxide, 1.9-8.0 parts of titanium oxide, 2.4-9.5 parts of vanadium oxide, 6.8-14.1 parts of manganese oxide, oxygen
Change 7-13 parts of cobalt, 2.3-4.6 parts of niobium oxide, 1.3-2.6 parts of zirconium oxide, 2.4-8.7 parts of tungsten oxide.
Preferably, the mobile phone screen protective glass includes each component of following parts by weight：60-81 parts of silica, oxygen
Change 27-34 parts of calcium, 14-16 parts of barium monoxide, 2.7-7.3 parts of titanium oxide, 3.6-8.4 parts of vanadium oxide, manganese oxide 7.9-12.8
Part, 7.7-12.4 parts of cobalt oxide, 2.7-4.1 parts of niobium oxide, 1.6-2.4 parts of zirconium oxide, 3.9-7.2 parts of tungsten oxide.
Preferably, the mobile phone screen protective glass includes each component of following parts by weight：64-76 parts of silica, oxygen
Change 27.8-33.1 parts of calcium, 14.4-15.7 parts of barium monoxide, 3.6-6.4 parts of titanium oxide, 4.3-7.6 parts of vanadium oxide, manganese oxide
9.3-12.0 parts, 8.4-11.3 parts of cobalt oxide, 3.0-3.8 parts of niobium oxide, 1.9-2.2 parts of zirconium oxide, tungsten oxide 4.4-6.7
Part.
Preferably, the mobile phone screen protective glass includes each component of following parts by weight：67-72 parts of silica, oxygen
Change 29.2-31.8 parts of calcium, 14.8-15.2 parts of barium monoxide, 4.8-5.7 parts of titanium oxide, 5.6-6.9 parts of vanadium oxide, manganese oxide
10.7-11.6 parts, 9.2-10.7 parts of cobalt oxide, 3.2-3.5 parts of niobium oxide, 2.0-2.1 parts of zirconium oxide, tungsten oxide 5.1-6.2
Part.
Compared with prior art, the invention has the advantages that：The present invention passes through silica, calcium oxide, oxidation
Barium, titanium oxide, vanadium oxide, manganese oxide, cobalt oxide, niobium oxide, zirconium oxide, the compounding of tungsten oxide, obtained glass transmission rate is good,
Reflectance and glossiness are suitable, can effectively prevent user's, shield big to eye injury when using mobile phone, TV, computer
Eye is effectively.In addition, handset touch panel strength of glass of the present invention is high, there is good shatter-resistant performance and anti-aging property, be produced into
This is low, and service life length, glass density is relatively low, meets lightweight requirements, especially suitable for making touching for the mobile equipment such as mobile phone
Touch screen.Mobile phone screen of the present invention is simple with glass preparation technique method, and prepared product has more superior fire-retardant, acidproof
Alkali, water-proof antibiotic performance, are adapted to use in multiple fields, improve properties of product.
Embodiment
Embodiment 1
A kind of mobile phone screen protective glass, includes each component of following percentage by weight：50-90 parts of silica, calcium oxide
20-40 parts, 10-20 parts of barium monoxide, 1-9 parts of titanium oxide, 2-10 parts of vanadium oxide, 6-15 parts of manganese oxide, cobalt oxide 3-18
Part, 2-5 parts of niobium oxide, 1-3 parts of zirconium oxide, 2-9 parts of tungsten oxide.
Embodiment 2
A kind of mobile phone screen protective glass, includes each component of following percentage by weight：56-85 parts of silica, calcium oxide
23-37 parts, 12-18 parts of barium monoxide, 1.9-8.0 parts of titanium oxide, 2.4-9.5 parts of vanadium oxide, 6.8-14.1 parts of manganese oxide, oxygen
Change 7-13 parts of cobalt, 2.3-4.6 parts of niobium oxide, 1.3-2.6 parts of zirconium oxide, 2.4-8.7 parts of tungsten oxide.
Embodiment 3
A kind of mobile phone screen protective glass, includes each component of following percentage by weight：60-81 parts of silica, calcium oxide
27-34 parts, 14-16 parts of barium monoxide, 2.7-7.3 parts of titanium oxide, 3.6-8.4 parts of vanadium oxide, 7.9-12.8 parts of manganese oxide, oxygen
Change 7.7-12.4 parts of cobalt, 2.7-4.1 parts of niobium oxide, 1.6-2.4 parts of zirconium oxide, 3.9-7.2 parts of tungsten oxide.
Embodiment 4
A kind of mobile phone screen protective glass, includes each component of following percentage by weight：64-76 parts of silica, calcium oxide
27.8-33.1 parts, 14.4-15.7 parts of barium monoxide, 3.6-6.4 parts of titanium oxide, 4.3-7.6 parts of vanadium oxide, manganese oxide 9.3-
12.0 parts, 8.4-11.3 parts of cobalt oxide, 3.0-3.8 parts of niobium oxide, 1.9-2.2 parts of zirconium oxide, 4.4-6.7 parts of tungsten oxide.
Embodiment 5
A kind of mobile phone screen protective glass, includes each component of following percentage by weight：67 parts of silica, calcium oxide 31.8
Part, 14.8 parts of barium monoxide, 5.7 parts of titanium oxide, 5.6 parts of vanadium oxide, 11.6 parts of manganese oxide, 9.2 parts of cobalt oxide, niobium oxide
3.5 parts, 2.0 parts of zirconium oxide, 6.2 parts of tungsten oxide.
Embodiment 6
A kind of mobile phone screen protective glass, includes each component of following percentage by weight：72 parts of silica, calcium oxide 29.2
Part, 15.2 parts of barium monoxide, 4.8 parts of titanium oxide, 6.9 parts of vanadium oxide, 10.7 parts of manganese oxide, 10.7 parts of cobalt oxide, niobium oxide
3.2 parts, 2.1 parts of zirconium oxide, 5.1 parts of tungsten oxide.
Claims (5)
1. a kind of mobile phone screen protective glass, it is characterized in that, the mobile phone screen protective glass includes each group of following parts by weight
Point：50-90 parts of silica, 20-40 parts of calcium oxide, 10-20 parts of barium monoxide, 1-9 parts of titanium oxide, 2-10 parts of vanadium oxide,
6-15 parts of manganese oxide, 3-18 parts of cobalt oxide, 2-5 parts of niobium oxide, 1-3 parts of zirconium oxide, 2-9 parts of tungsten oxide.
2. a kind of mobile phone screen protective glass according to claim 1, it is characterized in that, the mobile phone screen protective glass bag
Include each component of following parts by weight：56-85 parts of silica, 23-37 parts of calcium oxide, 12-18 parts of barium monoxide, titanium oxide
1.9-8.0 parts, 2.4-9.5 parts of vanadium oxide, 6.8-14.1 parts of manganese oxide, 7-13 parts of cobalt oxide, 2.3-4.6 parts of niobium oxide,
1.3-2.6 parts of zirconium oxide, 2.4-8.7 parts of tungsten oxide.
3. a kind of mobile phone screen protective glass according to claim 1, it is characterized in that, the mobile phone screen protective glass bag
Include each component of following parts by weight：60-81 parts of silica, 27-34 parts of calcium oxide, 14-16 parts of barium monoxide, titanium oxide
2.7-7.3 parts, 3.6-8.4 parts of vanadium oxide, 7.9-12.8 parts of manganese oxide, 7.7-12.4 parts of cobalt oxide, niobium oxide 2.7-4.1
Part, 1.6-2.4 parts of zirconium oxide, 3.9-7.2 parts of tungsten oxide.
4. a kind of mobile phone screen protective glass according to claim 1, it is characterized in that, the mobile phone screen protective glass bag
Include each component of following parts by weight：64-76 parts of silica, 27.8-33.1 parts of calcium oxide, 14.4-15.7 parts of barium monoxide,
3.6-6.4 parts of titanium oxide, 4.3-7.6 parts of vanadium oxide, 9.3-12.0 parts of manganese oxide, 8.4-11.3 parts of cobalt oxide, niobium oxide
3.0-3.8 parts, 1.9-2.2 parts of zirconium oxide, 4.4-6.7 parts of tungsten oxide.
5. a kind of mobile phone screen protective glass according to claim 1, it is characterized in that, the mobile phone screen protective glass bag
Include each component of following parts by weight：67-72 parts of silica, 29.2-31.8 parts of calcium oxide, 14.8-15.2 parts of barium monoxide,
4.8-5.7 parts of titanium oxide, 5.6-6.9 parts of vanadium oxide, 10.7-11.6 parts of manganese oxide, 9.2-10.7 parts of cobalt oxide, niobium oxide
3.2-3.5 parts, 2.0-2.1 parts of zirconium oxide, 5.1-6.2 parts of tungsten oxide.