CN107915401A - A kind of shatter-resistant cell phone screen glass - Google Patents
A kind of shatter-resistant cell phone screen glass Download PDFInfo
- Publication number
- CN107915401A CN107915401A CN201711048722.4A CN201711048722A CN107915401A CN 107915401 A CN107915401 A CN 107915401A CN 201711048722 A CN201711048722 A CN 201711048722A CN 107915401 A CN107915401 A CN 107915401A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- shatter
- cell phone
- phone screen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of glass material, and in particular to a kind of shatter-resistant cell phone screen glass, belong to electronic equipment screen glass technology field.Shatter-resistant cell phone screen glass, include each component of following parts by weight：80 100 parts of silica, 10 20 parts of aluminium oxide, 2 10 parts of lithia, 1 15 parts of potassium oxide, 3 20 parts of cupric oxide, 5 10 parts of zinc oxide, 1 10 parts of selenium oxide, 28 parts of antimony oxide, 1 10 parts of platinum oxide.The present invention passes through silica, aluminium oxide, lithia, potassium oxide, cupric oxide, zinc oxide, selenium oxide, antimony oxide, the compounding of platinum oxide, so that handset touch panel strength of glass is high, with good shatter-resistant performance and anti-aging property, production cost is low, service life length, glass density is relatively low, meets lightweight requirements.
Description
Technical field
The present invention relates to a kind of glass material, and in particular to a kind of shatter-resistant cell phone screen glass, belong to electronic equipment screen
With glass technology field.
Background technology
With constantly advancing for the mankind, present electronic equipment has become the essential use of people's daily life
Product, liquid crystal display is typically equipped with these electronic equipments.Liquid crystal display is the physical characteristic using liquid crystal, during energization
Arrangement becomes orderly, makes light prevent light from passing through easily by fall into disarray during, no power.On the surface of liquid crystal display
Be generally adopted by glass, if but now electronic equipment glass in use, imprudence come off from user, cause
Mobile phone glass screen ruptures, and influences to use.
The content of the invention
The object of the present invention is to provide a kind of shatter-resistant cell phone screen glass, the present invention passes through silica, aluminium oxide, oxidation
Lithium, potassium oxide, cupric oxide, zinc oxide, selenium oxide, antimony oxide, the compounding of platinum oxide so that handset touch panel strength of glass is high,
With good shatter-resistant performance and anti-aging property, production cost is low, and service life length, glass density is relatively low, meets lightweight
It is required that the touch-screen especially suitable for making the mobile equipment such as mobile phone.
The purpose of the present invention is what is be achieved through the following technical solutions, a kind of shatter-resistant cell phone screen glass, it is characterized in that, institute
Stating shatter-resistant cell phone screen glass includes each component of following parts by weight：80-100 parts of silica, 10-20 parts of aluminium oxide, oxygen
Change 2-10 parts of lithium, 1-15 parts of potassium oxide, 3-20 parts of cupric oxide, 5-10 parts of zinc oxide, 1-10 parts of selenium oxide, antimony oxide 2-8
Part, 1-10 parts of platinum oxide.
Preferably, the shatter-resistant cell phone screen glass include each component of following parts by weight：83-97 parts of silica, oxygen
Change 10.7-19.1 parts of aluminium, 2.4-9.5 parts of lithia, 3.8-11.0 parts of potassium oxide, 6-18 parts of cupric oxide, zinc oxide 5.4-
9.2 parts, 1.9-8.8 parts of selenium oxide, 2.6-7.3 parts of antimony oxide, 1.7-9.4 parts of platinum oxide.
Preferably, the shatter-resistant cell phone screen glass include each component of following parts by weight：85-94 parts of silica, oxygen
Change 11.5-18.4 parts of aluminium, 3.6-8.3 parts of lithia, 4.7-10.6 parts of potassium oxide, 9-17 parts of cupric oxide, zinc oxide 6.2-
8.5 parts, 2.7-8.1 parts of selenium oxide, 3.1-6.6 parts of antimony oxide, 2.5-8.2 parts of platinum oxide.
Preferably, the shatter-resistant cell phone screen glass include each component of following parts by weight：87-92 parts of silica, oxygen
Change 12.7-17.3 parts of aluminium, 4.4-7.6 parts of lithia, 5.8-9.3 parts of potassium oxide, 11-15 parts of cupric oxide, zinc oxide 6.8-
7.8 parts, 3.9-7.0 parts of selenium oxide, 4.3-5.8 parts of antimony oxide, 3.7-7.0 parts of platinum oxide.
Preferably, the shatter-resistant cell phone screen glass include each component of following parts by weight：89-91 parts of silica, oxygen
Change 14.4-16.2 parts of aluminium, 5.7-6.4 parts of lithia, 7.6-8.2 parts of potassium oxide, 13.0-14.3 parts of cupric oxide, zinc oxide
7.2-7.6 parts, 5.1-6.4 parts of selenium oxide, 4.9-5.3 parts of antimony oxide, 4.3-5.9 parts of platinum oxide.
Compared with prior art, the invention has the advantages that：The present invention passes through silica, aluminium oxide, oxidation
Lithium, potassium oxide, cupric oxide, zinc oxide, selenium oxide, antimony oxide, the compounding of platinum oxide so that handset touch panel strength of glass is high,
With good shatter-resistant performance and anti-aging property, production cost is low, and service life length, glass density is relatively low, meets lightweight
It is required that the touch-screen especially suitable for making the mobile equipment such as mobile phone.Mobile phone screen of the present invention glass preparation technique method letter
Single, prepared product has more superior fire-retardant, acid and alkali-resistance, water-proof antibiotic performance, is adapted to use in multiple fields, improves
Properties of product.The glass transmission rate that the present invention obtains is good, and reflectance and glossiness are suitable, can effectively prevent user and exists
Big to eye injury during using mobile phone, TV, computer, eyeshield is effective.
Embodiment
Embodiment 1
A kind of shatter-resistant cell phone screen glass, include each component of following percentage by weight：80-100 parts of silica, aluminium oxide
10-20 parts, 2-10 parts of lithia, 1-15 parts of potassium oxide, 3-20 parts of cupric oxide, 5-10 parts of zinc oxide, 1-10 parts of selenium oxide,
2-8 parts of antimony oxide, 1-10 parts of platinum oxide.
Embodiment 2
A kind of shatter-resistant cell phone screen glass, include each component of following percentage by weight：83-97 parts of silica, aluminium oxide
10.7-19.1 parts, 2.4-9.5 parts of lithia, 3.8-11.0 parts of potassium oxide, 6-18 parts of cupric oxide, zinc oxide 5.4-9.2
Part, 1.9-8.8 parts of selenium oxide, 2.6-7.3 parts of antimony oxide, 1.7-9.4 parts of platinum oxide.
Embodiment 3
A kind of shatter-resistant cell phone screen glass, include each component of following percentage by weight：85-94 parts of silica, aluminium oxide
11.5-18.4 parts, 3.6-8.3 parts of lithia, 4.7-10.6 parts of potassium oxide, 9-17 parts of cupric oxide, 6.2-8.5 parts of zinc oxide,
2.7-8.1 parts of selenium oxide, 3.1-6.6 parts of antimony oxide, 2.5-8.2 parts of platinum oxide.
Embodiment 4
A kind of shatter-resistant cell phone screen glass, include each component of following percentage by weight：87-92 parts of silica, aluminium oxide
12.7-17.3 parts, 4.4-7.6 parts of lithia, 5.8-9.3 parts of potassium oxide, 11-15 parts of cupric oxide, 6.8-7.8 parts of zinc oxide,
3.9-7.0 parts of selenium oxide, 4.3-5.8 parts of antimony oxide, 3.7-7.0 parts of platinum oxide.
Embodiment 5
A kind of shatter-resistant cell phone screen glass, include each component of following percentage by weight：89 parts of silica, aluminium oxide 16.2
Part, 5.7 parts of lithia, 8.2 parts of potassium oxide, 13.0 parts of cupric oxide, 7.6 parts of zinc oxide, 5.1 parts of selenium oxide, antimony oxide 5.3
Part, 4.3 parts of platinum oxide.
Embodiment 6
A kind of shatter-resistant cell phone screen glass, include each component of following percentage by weight：91 parts of silica, aluminium oxide 14.4
Part, 6.4 parts of lithia, 7.6 parts of potassium oxide, 14.3 parts of cupric oxide, 7.2 parts of zinc oxide, 6.4 parts of selenium oxide, antimony oxide 4.9
Part, 5.9 parts of platinum oxide.
Claims (5)
1. a kind of shatter-resistant cell phone screen glass, it is characterized in that, the shatter-resistant cell phone screen glass include each group of following parts by weight
Point：80-100 parts of silica, 10-20 parts of aluminium oxide, 2-10 parts of lithia, 1-15 parts of potassium oxide, cupric oxide 3-20
Part, 5-10 parts of zinc oxide, 1-10 parts of selenium oxide, 2-8 parts of antimony oxide, 1-10 parts of platinum oxide.
2. a kind of shatter-resistant cell phone screen glass according to claim 1, it is characterized in that, the shatter-resistant cell phone screen glass bag
Include each component of following parts by weight：83-97 parts of silica, 10.7-19.1 parts of aluminium oxide, 2.4-9.5 parts of lithia, oxygen
Change 3.8-11.0 parts of potassium, 6-18 parts of cupric oxide, 5.4-9.2 parts of zinc oxide, 1.9-8.8 parts of selenium oxide, antimony oxide 2.6-7.3
Part, 1.7-9.4 parts of platinum oxide.
3. a kind of shatter-resistant cell phone screen glass according to claim 1, it is characterized in that, the shatter-resistant cell phone screen glass bag
Include each component of following parts by weight：85-94 parts of silica, 11.5-18.4 parts of aluminium oxide, 3.6-8.3 parts of lithia, oxidation
4.7-10.6 parts of potassium, 9-17 parts of cupric oxide, 6.2-8.5 parts of zinc oxide, 2.7-8.1 parts of selenium oxide, antimony oxide 3.1-6.6
Part, 2.5-8.2 parts of platinum oxide.
4. a kind of shatter-resistant cell phone screen glass according to claim 1, it is characterized in that, the shatter-resistant cell phone screen glass bag
Include each component of following parts by weight：87-92 parts of silica, 12.7-17.3 parts of aluminium oxide, 4.4-7.6 parts of lithia, oxidation
5.8-9.3 parts of potassium, 11-15 parts of cupric oxide, 6.8-7.8 parts of zinc oxide, 3.9-7.0 parts of selenium oxide, antimony oxide 4.3-5.8
Part, 3.7-7.0 parts of platinum oxide.
5. a kind of shatter-resistant cell phone screen glass according to claim 1, it is characterized in that, the shatter-resistant cell phone screen glass bag
Include each component of following parts by weight：89-91 parts of silica, 14.4-16.2 parts of aluminium oxide, 5.7-6.4 parts of lithia, oxidation
7.6-8.2 parts of potassium, 13.0-14.3 parts of cupric oxide, 7.2-7.6 parts of zinc oxide, 5.1-6.4 parts of selenium oxide, antimony oxide 4.9-
5.3 parts, 4.3-5.9 parts of platinum oxide.