CN107972342A - A kind of heat insulation and wear resistance fenestrated membrane - Google Patents
A kind of heat insulation and wear resistance fenestrated membrane Download PDFInfo
- Publication number
- CN107972342A CN107972342A CN201610920101.XA CN201610920101A CN107972342A CN 107972342 A CN107972342 A CN 107972342A CN 201610920101 A CN201610920101 A CN 201610920101A CN 107972342 A CN107972342 A CN 107972342A
- Authority
- CN
- China
- Prior art keywords
- heat insulation
- wear resistance
- fenestrated membrane
- present
- fenestrated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat insulation and wear resistance fenestrated membrane, including substrate layer and heat insulation and wear resistance layer, heat insulation and wear resistance layer includes the component raw material of acrylate monomer, modified polyurethane, ultraviolet absorber, UV light-cured resins, nano-metal-oxide, photoinitiator, carborundum, defoamer and auxiliary agent, obtained fenestrated membrane has good wear-resisting, weather-proof and thermal insulation, can be widely used in the industries such as automobile and building.
Description
Technical field
The present invention relates to optics technical field of membrane, more particularly to a kind of heat insulation and wear resistance fenestrated membrane.
Background technology
Fenestrated membrane is a kind of energy conservation and environmental protection and has a vast market development prospect film product, is mainly used in automotive window
And building window, there are heat-insulating and energy-saving, uvioresistant, beautiful and comfortable, four fundamental characteristics of safety anti-explosive.According to application field
Difference, at present glass fenestrated membrane be roughly divided into three classes：Building glass fenestrated membrane, vehicle glass fenestrated membrane, safety glass fenestrated membrane, fenestrated membrane
Using more and more extensive, to after 2000, a large amount of use of thermal isolation film, antiknock film on automobile, safety diaphragm largely uses in silver
On row sales counter.
The fabrics such as furniture, carpet, artistic pictures, curtain in building or automotive trim shine in sunlight or strong artificial light
Lower meeting accelerated ageing, with being continuously increased for usage time, the appearance and physical property of fenestrated membrane can be also gradually reduced.In addition,
Under ultraviolet lighting, photooxidative degradation can be produced and cause to greatly shorten its service life, at present, most domestic fenestrated membrane product is deposited
Uv-shielding capacity difference and ageing-resistant performance it is bad the problems such as, i.e. rejection rate ＜ 90% of the fenestrated membrane to ultraviolet.It is meanwhile existing
Fenestrated membrane the problem of being faced with scratch resistance, resistance to ag(e)ing, wearability, poor thermal insulation.Therefore, be badly in need of developing a kind of wearability, every
Hot good fenestrated membrane.
Therefore, in view of the above-mentioned problems, being necessary to propose a kind of endurable barrier ultraviolet, and with excellent anti-zoned
Wound, ageing-resistant performance, heat-insulated fenestrated membrane.
The content of the invention
In view of this, the present invention provides a kind of heat insulation and wear resistance fenestrated membrane, to provide preferable wearability and thermal insulation.
In order to realize foregoing invention purpose, the present invention provides a kind of heat insulation and wear resistance fenestrated membrane, including：
Substrate layer and heat insulation and wear resistance layer, the heat insulation and wear resistance layer include the component raw material of following parts by weight：
As a further improvement on the present invention, the thickness of the heat insulation and wear resistance fenestrated membrane is 3~6 μm.
As a further improvement on the present invention, the photoinitiator is 2,4,6, the oxidation of-trimethylbenzoy-dipheny
Mixture more than one or both of phosphine, 1- hydroxycyclohexyl phenyl ketones or 2,4,6- triphenylimidazolyl base dimers.
As a further improvement on the present invention, the auxiliary agent is organic silicon modified by polyether analog assistant.
Compared with prior art, the beneficial effects of the invention are as follows：
Heat insulation and wear resistance fenestrated membrane in the present invention, wearability are greatly promoted with hardness, while its good heat-insulation effect, with glass
Fitting is close, and the feature of environmental protection is high.
Brief description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, below will be to embodiment or existing
There is attached drawing needed in technology description to be briefly described, it should be apparent that, drawings in the following description are only this
Some embodiments described in invention, for those of ordinary skill in the art, without creative efforts,
Other attached drawings can also be obtained according to these attached drawings.
Fig. 1 is the structure diagram of heat insulation and wear resistance fenestrated membrane in the present invention.
Embodiment
The technical solution in the embodiment of the present invention will be described in detail below, it is clear that described embodiment is only
Only it is part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, ordinary skill
Personnel's all other embodiments obtained on the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
Join shown in Fig. 1, the heat insulation and wear resistance fenestrated membrane in the present invention, including：
Substrate layer 1 and heat insulation and wear resistance layer 2, heat insulation and wear resistance layer 2 include the component raw material of following parts by weight：
The thickness of heat insulation and wear resistance fenestrated membrane in the present invention is 3~6 μm, has preferable frivolous property, can be close with window
Fitting.
Wherein, photoinitiator 2,4,6 ,-trimethylbenzoy-dipheny phosphine oxide, 1- hydroxycyclohexylphenyl first
Mixture more than one or both of ketone or 2,4,6- triphenylimidazolyl base dimers, realizes its good characteristic.
Auxiliary agent is organic silicon modified by polyether analog assistant.
Due to acrylate monomer of the heat insulation and wear resistance layer 2 including suitable number of heat insulation and wear resistance fenestrated membrane of the present invention, it is modified and gathers
The originals such as urethane, ultraviolet absorber, UV light-cured resins, nano-metal-oxide, photoinitiator, carborundum, defoamer and auxiliary agent
Material so that fenestrated membrane has good wear-resisting, weather-proof and thermal insulation, can be widely used in the industries such as automobile and building.
As can be seen from the above technical solutions, the setting of the invention by substrate layer 1 and heat insulation and wear resistance layer 2, and it is heat-insulated resistance to
Mill layer 2 selects specific component, can effectively realize good wear-resisting and thermal insulation.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.Any reference numeral in claim should not be considered as to the involved claim of limitation.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical solution, this narrating mode of specification is only that those skilled in the art should for clarity
Using specification as an entirety, the technical solution in each embodiment can also be closed through appropriate, and forming those skilled in the art can
With the other embodiment of understanding.
Claims (4)
- A kind of 1. heat insulation and wear resistance fenestrated membrane, it is characterised in that including substrate layer and heat insulation and wear resistance layer, the heat insulation and wear resistance layer include with The component raw material of lower parts by weight：
- 2. heat insulation and wear resistance fenestrated membrane according to claim 1, it is characterised in that the thickness of the heat insulation and wear resistance fenestrated membrane is 3~6 μm。
- 3. heat insulation and wear resistance fenestrated membrane according to claim 1, it is characterised in that the photoinitiator is 2,4,6 ,-trimethyl Benzoyl-diphenyl phosphine oxide, 1- hydroxycyclohexyl phenyl ketones or 2, one kind in 4,6- triphenylimidazolyl base dimers Or two or more mixture.
- 4. heat insulation and wear resistance fenestrated membrane according to claim 1, it is characterised in that the auxiliary agent helps for organic silicon modified by polyether class Agent.