CN107964347A - A kind of environmental protection delustring white paint - Google Patents
A kind of environmental protection delustring white paint Download PDFInfo
- Publication number
- CN107964347A CN107964347A CN201710850796.3A CN201710850796A CN107964347A CN 107964347 A CN107964347 A CN 107964347A CN 201710850796 A CN201710850796 A CN 201710850796A CN 107964347 A CN107964347 A CN 107964347A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass fraction
- minutes
- reaction
- butanediol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of environmentally friendly delustring white paint, according to the mass fraction, specifically it is made by following component:45 60 parts of matting resin, 35 parts of calcium carbonate, 8 10 parts of paraffin, 20 25 parts of titanium dioxide, 0.4 0.48 parts of anti-settling agent, 0.2 0.4 parts of defoamer, 0.3 0.5 parts of levelling agent, 25 35 parts of white spirit.By experiment; a kind of environmentally friendly delustring white paint provided by the invention; compared to existing commercial like product; burst size of methanal substantially reduces, more health environment-friendly, while has extremely excellent extinction performance; paint film dumb light performance is good; more aobvious top grade, while help to protect user's vision health, the market competitiveness is extremely strong.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of environmental protection delustring white paint.
Background technology
Paint is that one kind can firmly be covered in body surface, and the chemistry for playing protection, decoration, mark and other specific uses mixes
Compound coating.Chinese coating circle is more authoritative《Coating process》What one book was defined as:" coating is a kind of material, this
Material can be coated in object surface with different construction technologies, and it is firm, thin with some strength, continuous solid-state to form adhesion
Film.The film common name film so formed, also known as paint film or coating." coating is generally by film forming matter, color stuffing, solvent, auxiliary agent etc.
Four parts form.According to performance requirement, composition can be slightly changed sometimes, as varnish does not have not having in color stuffing, powdery paints
Solvent.Paint belongs to organic chemical industry's macromolecular material, and the film formed belongs to high-molecular compound type.It is current according to the modern times
Chemical products classification, coating belongs to fine chemical product.Modern coating progressively becomes a kind of multi-functional work
Journey material, is an important industry in chemical industry.
In existing delustring white paint, addition delustring material is made typically in paint, if this manufacture craft delustring material
Stirring inequality may result in that paint face extinction effect is variant, seriously affects the aesthetics after product quality and japanning, makes at the same time
Paint film feel can be also influenced with delustring material, product competitiveness in the market is limited.
The content of the invention
To solve the above-mentioned problems, the present invention provides a kind of environmentally friendly delustring white paint.
The present invention is achieved through the following technical solutions:
A kind of environmental protection delustring white paint, according to the mass fraction, is specifically made by following component:45-60 parts of matting resin, calcium carbonate 3-
5 parts, 8-10 parts of paraffin, 20-25 parts of titanium dioxide, 0.4-0.48 parts of anti-settling agent, 0.2-0.4 parts of defoamer, levelling agent 0.3-0.5
Part, 25-35 parts of white spirit;
The matting resin, its preparation method, is specially following steps:
A according to the mass fraction, by 3-9 parts of micro crystal material, 10-15 parts of active carbon nanoparticles, 1-2 parts of lithia, potassium oxide 0.6-0.9
Part mixing, repeatedly ball milling sieve 80 mesh, until all raw materials can cross 80 mesh sieves, obtain powder;
B according to the mass fraction, by 12-17 parts of butanediol, 30-32 parts of polytetrahydrofuran diol, polypropylene glycol adipate glycol
5-15 parts, 8-10 parts of polycaprolactone glycol be transferred to after being mixed using high mixer in reaction kettle, add the 0.4-0.7 times of butanediol
The DMPA of the diisocyanate of mass fraction and the 0.8-1 times of butanediol mass fraction, prior to 110-112 DEG C insulation, fully
Reaction 20-25 minutes, is then cooled to 80-85 DEG C of insulation, adds the catalysis of the 0.01-0.012 times of butanediol mass fraction
Agent, the reaction was continued 30-40 minutes, and the method combined using high mild catalyst, is both reduced the reaction time, turn avoid reaction
During impurity generation;
(3)NCO content in reaction kettle is detected, when NCO content reaches theoretical value, is added after being cooled to 50-60 DEG C described in 1 times
The dimethylethanolamine of DMPA mass fractions, the reaction was continued 12-18 minutes, obtains performed polymer;
(4)The performed polymer is poured into No. two reaction kettles with deionized water, adds 0.3-0.4 times of described performed polymer quality part
Powder described in several sulfonate sodiums and step A, is sufficiently stirred 3-5 minutes under room temperature using 5000-6000r/min rotating speeds, then
Through chain extending reaction, up to the matting resin;It is anti-that chain extension is carried out after the performed polymer is mixed with the powder, sulfonate sodium again
Should, obtained matting resin extinction effect is good, while the delustring white paint made without adding delustring material, environment protection health again.
A kind of environmental protection delustring white paint, its preparation method, is specially following steps:
(1)The matting resin, calcium carbonate, paraffin, titanium dioxide are thoroughly mixed in 50-60 DEG C, 3000-4000r/min
8-10 minutes, then add the white spirit, ball milling sieves 80 mesh after 90-120 minutes, obtains centrotheca;
(2)The centrotheca is added into the anti-settling agent, defoamer, levelling agent, under the conditions of 30-32 DEG C, 800-1000r/min after
Continuous stirring 10-15 minutes, obtains secondary slurry;
(3)By the secondary slurry be placed in aging 1.5-2 in aging pond it is small when after get product.
Beneficial effects of the present invention:The present invention is preparing environmentally friendly delustring using raw material of the environmentally friendly matting resin as white paint
Powder described in adding step A in resin process, makes waterborne polyurethane resin carry excellent effect performance, to be produced on the basis of this
White paint, avoid the traditional delustring material of addition, i.e., it is environmentally friendly, paint film effects also more uniformly, beauty.By experiment, this hair
A kind of environmentally friendly delustring white paint of bright offer, compared to existing commercial like product, burst size of methanal substantially reduces, more healthy
Environmental protection, while there is extremely excellent extinction performance, paint film dumb light performance is good, more aobvious top grade, while helps to protect user to regard
Power health, the market competitiveness are extremely strong.
Embodiment
Embodiment 1
A kind of environmental protection delustring white paint, according to the mass fraction, is specifically made by following component:45 parts of matting resin, 3 parts of calcium carbonate,
8 parts of paraffin, 20 parts of titanium dioxide, 0.4 part of anti-settling agent, 0.2 part of defoamer, 0.3 part of levelling agent, 25 parts of white spirit;
The matting resin, its preparation method, is specially following steps:
A according to the mass fraction, 3 parts of micro crystal material, 10 parts of active carbon nanoparticles, 1 part of lithia, 0.6 part of potassium oxide is mixed, repeatedly
Ball milling sieves 80 mesh, until all raw materials can cross 80 mesh sieves, obtains powder;
B according to the mass fraction, by 12 parts of butanediol, 30 parts of polytetrahydrofuran diol, 5 parts of polypropylene glycol adipate glycol, poly-
8 parts of caprolactone diol is transferred in reaction kettle after being mixed using high mixer, adds two isocyanides of 0.4 times of butanediol mass fraction
The DMPA of acid esters and 0.8 times of butanediol mass fraction, fully prior to 110-112 DEG C insulation, reaction 20 minutes, then cools down
To 80-85 DEG C of insulation, the catalyst of 0.01 times of butanediol mass fraction is added, the reaction was continued 30 minutes;
(3)NCO content in reaction kettle is detected, when NCO content reaches theoretical value, is added after being cooled to 50-60 DEG C described in 1 times
The dimethylethanolamine of DMPA mass fractions, the reaction was continued 12 minutes, obtains performed polymer;
(4)The performed polymer is poured into No. two reaction kettles with deionized water, 0.3 times of performed polymer quality number of addition
Powder described in sulfonate sodium and step A, is sufficiently stirred 3 minutes under room temperature using 5000-6000r/min rotating speeds, then through chain extension
Reaction, up to the matting resin.
A kind of environmental protection delustring white paint, its preparation method, is specially following steps:
(1)The matting resin, calcium carbonate, paraffin, titanium dioxide are thoroughly mixed 8 in 50-60 DEG C, 3000-4000r/min
Minute, then add the white spirit, ball milling sieves 80 mesh after 90 minutes, obtains centrotheca;
(2)The centrotheca is added into the anti-settling agent, defoamer, levelling agent, under the conditions of 30-32 DEG C, 800-1000r/min after
Continuous stirring 10 minutes, obtains secondary slurry;
(3)By it is described it is secondary slurry be placed in aging pond it is aging 1.5 it is small when after get product.
Embodiment 2
A kind of environmental protection delustring white paint, according to the mass fraction, is specifically made by following component:60 parts of matting resin, 5 parts of calcium carbonate,
10 parts of paraffin, 25 parts of titanium dioxide, 0.48 part of anti-settling agent, 0.4 part of defoamer, 0.5 part of levelling agent, 35 parts of white spirit;
The matting resin, its preparation method, is specially following steps:
A according to the mass fraction, 9 parts of micro crystal material, 15 parts of active carbon nanoparticles, 2 parts of lithia, 0.9 part of potassium oxide is mixed, repeatedly
Ball milling sieves 80 mesh, until all raw materials can cross 80 mesh sieves, obtains powder;
B according to the mass fraction, by 17 parts of butanediol, 32 parts of polytetrahydrofuran diol, 15 parts of polypropylene glycol adipate glycol, poly-
10 parts of caprolactone diol is transferred in reaction kettle after being mixed using high mixer, and add 0.7 times of butanediol mass fraction two are different
The DMPA of cyanate and 1 times of butanediol mass fraction, fully prior to 110-112 DEG C insulation, reaction 25 minutes, then cools down
To 80-85 DEG C of insulation, the catalyst of 0.012 times of butanediol mass fraction is added, the reaction was continued 40 minutes;
(3)NCO content in reaction kettle is detected, when NCO content reaches theoretical value, is added after being cooled to 50-60 DEG C described in 1 times
The dimethylethanolamine of DMPA mass fractions, the reaction was continued 18 minutes, obtains performed polymer;
(4)The performed polymer is poured into No. two reaction kettles with deionized water, 0.4 times of performed polymer quality number of addition
Powder described in sulfonate sodium and step A, is sufficiently stirred 5 minutes under room temperature using 5000-6000r/min rotating speeds, then through chain extension
Reaction, up to the matting resin.
A kind of environmental protection delustring white paint, its preparation method, is specially following steps:
(1)The matting resin, calcium carbonate, paraffin, titanium dioxide are thoroughly mixed in 50-60 DEG C, 3000-4000r/min
10 minutes, then add the white spirit, ball milling sieves 80 mesh after 120 minutes, obtains centrotheca;
(2)The centrotheca is added into the anti-settling agent, defoamer, levelling agent, under the conditions of 30-32 DEG C, 800-1000r/min after
Continuous stirring 15 minutes, obtains secondary slurry;
(3)By it is described it is secondary slurry be placed in aging pond it is aging 2 it is small when after get product.
Embodiment 3
A kind of environmental protection delustring white paint, according to the mass fraction, is specifically made by following component:50 parts of matting resin, 4 parts of calcium carbonate,
9 parts of paraffin, 22 parts of titanium dioxide, 0.45 part of anti-settling agent, 0.3 part of defoamer, 0.4 part of levelling agent, 30 parts of white spirit;
The matting resin, its preparation method, is specially following steps:
A according to the mass fraction, 6 parts of micro crystal material, 12 parts of active carbon nanoparticles, 1.5 parts of lithia, 0.8 part of potassium oxide is mixed, instead
Multiple ball milling sieves 80 mesh, until all raw materials can cross 80 mesh sieves, obtains powder;
B according to the mass fraction, by 15 parts of butanediol, 31 parts of polytetrahydrofuran diol, 10 parts of polypropylene glycol adipate glycol, poly-
9 parts of caprolactone diol is transferred in reaction kettle after being mixed using high mixer, adds two isocyanides of 0.5 times of butanediol mass fraction
The DMPA of acid esters and 0.9 times of butanediol mass fraction, fully prior to 110-112 DEG C insulation, reaction 22 minutes, then cools down
To 80-85 DEG C of insulation, the catalyst of 0.011 times of butanediol mass fraction is added, the reaction was continued 35 minutes;
(3)NCO content in reaction kettle is detected, when NCO content reaches theoretical value, is added after being cooled to 50-60 DEG C described in 1 times
The dimethylethanolamine of DMPA mass fractions, the reaction was continued 16 minutes, obtains performed polymer;
(4)The performed polymer is poured into No. two reaction kettles with deionized water, adds 0.35 times of performed polymer quality number
Sulfonate sodium and step A described in powder, be sufficiently stirred 4 minutes using 5000-6000r/min rotating speeds under room temperature, then through expand
Chain reaction, up to the matting resin.
A kind of environmental protection delustring white paint, its preparation method, is specially following steps:
(1)The matting resin, calcium carbonate, paraffin, titanium dioxide are thoroughly mixed 9 in 50-60 DEG C, 3000-4000r/min
Minute, then add the white spirit, ball milling sieves 80 mesh after 100 minutes, obtains centrotheca;
(2)The centrotheca is added into the anti-settling agent, defoamer, levelling agent, under the conditions of 30-32 DEG C, 800-1000r/min after
Continuous stirring 12 minutes, obtains secondary slurry;
(3)By it is described it is secondary slurry be placed in aging pond it is aging 2 it is small when after get product.
Comparative example
This comparative example compared with Example 1, without using the matting resin, using only standard aqueous polyurethane resin, in addition
Method and step all same.
Control group
Commercially available white paint.
Be applied as the paint film of 100 μ m-thicks using above-mentioned 5 kinds environmentally friendly delustring white paints respectively, and to the burst size of methanal of paint film into
Row measure, as a result such as table 1, is measured the extinction performance of paint film, the results are shown in Table 2:
Table 1
Burst size of methanal(mg/m³) | |
Embodiment 1 | 0.09 |
Embodiment 2 | 0.09 |
Embodiment 3 | 0.10 |
Comparative example | 0.13 |
Control group | 0.16 |
Table 2
45 ° of glossiness(%) | Mist degree(%) | |
Embodiment 1 | 2.9 | 76.8 |
Embodiment 2 | 3.4 | 78.1 |
Embodiment 3 | 3.6 | 77.5 |
Comparative example | 10.8 | 40.3 |
Control group | 12.5 | 32.2 |
From table 1, table 2, a kind of environmentally friendly delustring white paint provided by the invention, compared to existing commercial like product, formaldehyde
Burst size substantially reduces, more health environment-friendly, while has extremely excellent extinction performance, and paint film dumb light performance is good, more aobvious height
Shelves, while help to protect user's vision health, the market competitiveness is extremely strong.
Claims (4)
1. a kind of environmental protection delustring white paint, it is characterised in that according to the mass fraction, be specifically made by following component:Matting resin 45-
60 parts, 3-5 parts of calcium carbonate, 8-10 parts of paraffin, 20-25 parts of titanium dioxide, 0.4-0.48 parts of anti-settling agent, 0.2-0.4 parts of defoamer, stream
Flat agent 0.3-0.5 parts, 25-35 parts of white spirit;
The matting resin, its preparation method, is specially following steps:
A according to the mass fraction, by 3-9 parts of micro crystal material, 10-15 parts of active carbon nanoparticles, 1-2 parts of lithia, potassium oxide 0.6-0.9
Part mixing, repeatedly ball milling sieve 80 mesh, until all raw materials can cross 80 mesh sieves, obtain powder;
B according to the mass fraction, by 12-17 parts of butanediol, 30-32 parts of polytetrahydrofuran diol, polypropylene glycol adipate glycol
5-15 parts, 8-10 parts of polycaprolactone glycol be transferred to after being mixed using high mixer in reaction kettle, add the 0.4-0.7 times of butanediol
The DMPA of the diisocyanate of mass fraction and the 0.8-1 times of butanediol mass fraction, prior to 110-112 DEG C insulation, fully
Reaction 20-25 minutes, is then cooled to 80-85 DEG C of insulation, adds the catalysis of the 0.01-0.012 times of butanediol mass fraction
Agent, the reaction was continued 30-40 minutes;
(3)NCO content in reaction kettle is detected, when NCO content reaches theoretical value, is added after being cooled to 50-60 DEG C described in 1 times
The dimethylethanolamine of DMPA mass fractions, the reaction was continued 12-18 minutes, obtains performed polymer;
(4)The performed polymer is poured into No. two reaction kettles with deionized water, adds 0.3-0.4 times of described performed polymer quality part
Powder described in several sulfonate sodiums and step A, is sufficiently stirred 3-5 minutes under room temperature using 5000-6000r/min rotating speeds, then
Through chain extending reaction, up to the matting resin.
2. a kind of environmentally friendly delustring white paint according to claim 1, it is characterised in that according to the mass fraction, specifically by as follows
Component is made:50 parts of matting resin, 4 parts of calcium carbonate, 9 parts of paraffin, 22 parts of titanium dioxide, 0.45 part of anti-settling agent, 0.3 part of defoamer,
0.4 part of levelling agent, 30 parts of white spirit.
3. a kind of environmentally friendly delustring white paint according to claim 1 or 2, it is characterised in that the matting resin, its preparation side
Method, is specially following steps:
A according to the mass fraction, 6 parts of micro crystal material, 12 parts of active carbon nanoparticles, 1.5 parts of lithia, 0.8 part of potassium oxide is mixed, instead
Multiple ball milling sieves 80 mesh, until all raw materials can cross 80 mesh sieves, obtains powder;
B according to the mass fraction, by 15 parts of butanediol, 31 parts of polytetrahydrofuran diol, 10 parts of polypropylene glycol adipate glycol, poly-
9 parts of caprolactone diol is transferred in reaction kettle after being mixed using high mixer, adds two isocyanides of 0.5 times of butanediol mass fraction
The DMPA of acid esters and 0.9 times of butanediol mass fraction, fully prior to 110-112 DEG C insulation, reaction 22 minutes, then cools down
To 80-85 DEG C of insulation, the catalyst of 0.011 times of butanediol mass fraction is added, the reaction was continued 35 minutes;
(3)NCO content in reaction kettle is detected, when NCO content reaches theoretical value, is added after being cooled to 50-60 DEG C described in 1 times
The dimethylethanolamine of DMPA mass fractions, the reaction was continued 16 minutes, obtains performed polymer;
(4)The performed polymer is poured into No. two reaction kettles with deionized water, adds 0.35 times of performed polymer quality number
Sulfonate sodium and step A described in powder, be sufficiently stirred 4 minutes using 5000-6000r/min rotating speeds under room temperature, then through expand
Chain reaction, up to the matting resin.
4. a kind of preparation method of environmentally friendly delustring white paint according to claim 1, is specially following steps:
(1)The matting resin, calcium carbonate, paraffin, titanium dioxide are thoroughly mixed in 50-60 DEG C, 3000-4000r/min
8-10 minutes, then add the white spirit, ball milling sieves 80 mesh after 90-120 minutes, obtains centrotheca;
(2)The centrotheca is added into the anti-settling agent, defoamer, levelling agent, under the conditions of 30-32 DEG C, 800-1000r/min after
Continuous stirring 10-15 minutes, obtains secondary slurry;
(3)By the secondary slurry be placed in aging 1.5-2 in aging pond it is small when after get product.