CN107956121A - A kind of preparation method of wrinkle resistant hemp fabric - Google Patents
A kind of preparation method of wrinkle resistant hemp fabric Download PDFInfo
- Publication number
- CN107956121A CN107956121A CN201711238634.0A CN201711238634A CN107956121A CN 107956121 A CN107956121 A CN 107956121A CN 201711238634 A CN201711238634 A CN 201711238634A CN 107956121 A CN107956121 A CN 107956121A
- Authority
- CN
- China
- Prior art keywords
- parts
- hemp fabric
- preparation
- wrinkle resistant
- preliminary drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation method of wrinkle resistant hemp fabric, dipping：Hemp fabric is immersed in dressing liquid, dressing liquid bath raio is 1:20‑30；The hemp fabric after dipping is carried out two leachings two on car is padded to roll, the pick-up rate is 80 100%, and the temperature of padding is 30 40 DEG C；Hemp fabric after padding carries out preliminary drying, and the preliminary drying temperature is 60 70 DEG C, and the preliminary drying time is 3 5min；Hemp fabric after padding is baked, the baking temperature is 130 140 DEG C, and described to bake the time be 3 5min；Hemp fabric after baking is washed 35 times with 20 30 DEG C of clear water, is then dried.The present invention provides a kind of preparation method of wrinkle resistant hemp fabric, and compared with traditional chemical routes, treatment process energy consumption is low, efficient, pollution is few, is conducive to environmental protection.Anti-crease finishing for linen is processed, and crease recovery increased, and the mechanics mechanical performance and dyeability of fabric also have lifting, and washability is strong, soft.
Description
Technical field
The present invention relates to a kind of preparation method of wrinkle resistant hemp fabric, belong to textile processing field.
Technical background
Fabric final finishing is to improve appearance and feel, the enhancement wearability or tax of fabric by main method chemically or physically
The technical process of specific function is given, is the process of textile " making something perfect even more perfect ".The development court of present fabric final finishing technology
Product function, differential, superior, processing technology variation, depth direction are developed, and emphasize to improve taking for product
Performance, increases value-added content of product.In recent years, constantly introduced from other technologies field and use for reference various new technologies, added with improving
Work depth, obtains good running product.With mankind's environmental pollution and the concern destroyed, health is increasingly paid attention to, is carried
" low-carbon " economy is advocated, final finishing technical requirements carry out environmentally friendly " green " processing, production " cleaning ", the textile product of " low-carbon ".Face
The basic afterfinish method of material has：Stable dimensions, improve appearance method for sorting, improve feel optimization performance method for sorting,
The arrangement for making fabric obtain multi-functional, high added value method for sorting, make the advanced method for sorting of fabric, meet particular/special requirement
Method.
Fiber crops are one of fibers that the mankind utilize earliest, and such good hygroscopic fabric, moisture releasing is also fast, is not likely to produce electrostatic, wears
Nice and cool, flaxen fiber has the characteristics that antiseptic and inhibiting bacteria function, ventilative pleasant, but there is also in wearing process the problem of fold；Therefore
To improve this problem points, bast fiber fabrics noniron finish is particularly important；Because strength is poor under flaxen fiber dry state, in the past by anti-
Fabric after wrinkle method for sorting arrangement, ultimate strength is poor, and feel is coarse, and wearability index substantially reduces, so as to limit city
The popularization of field.And with environmental protection and the proposition of comprehensive utilization of energy problem, finishing agent is towards low energy consumption, free of contamination direction
Development.Since different finishing agents can produce different effects, suitable finishing agent and its addition agent aid etc., optimization are selected
Process conditions, are the keys for improving hemp fabric wrinkle proofing effect.Only by selecting suitable finishing agent and additive,
Process optimization is carried out, to hemp fabric wrinkle proofing, can just reach the requirement of advanced dress ornament.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to provide a kind of preparation method of wrinkle resistant hemp fabric.
The present invention is achieved by the following technical solutions：A kind of preparation method of wrinkle resistant hemp fabric, including it is following
Step：
（1）Dipping：Hemp fabric is immersed in dressing liquid, dressing liquid bath raio is 1:20-30, wherein, the finishing agent by
The component composition of following parts by weight：40-48 parts of deionized water, 3-10 parts of tricresyl phosphate (2- chloroethyls) ester, containing the poly- silicon of hydroxyl alkyl
3-6 parts of oxygen alkane, 12-16 parts of methacrylic resin, 4-12 parts of poly (sodium aspartate), 2-6 parts of octyl phenol polyoxyethylene ether, lemon
Sour sodium 10-14 parts, 4-8 parts of polyoxylethylene abietate, 2-9 parts of sorbitan monooleate, 1,2- benzisothiazoles -3-
5-10 parts of ketone；
（2）Two leachings two are rolled：The hemp fabric after dipping is carried out two leachings two on car is padded to roll, the pick-up rate is 80-
100%, the temperature of padding is 30-40 DEG C；
（3）Preliminary drying：Hemp fabric after padding carries out preliminary drying, and the preliminary drying temperature is 60-70 DEG C, the preliminary drying time
For 3-5min；
（4）Bake：Hemp fabric after padding is baked, the baking temperature is 130-140 DEG C, described when baking
Between be 3-5min；
（5）Washing drying：Hemp fabric after baking is washed 3-5 times with 20-30 DEG C of clear water, is then dried.
Further, the step（1）Middle dip time is 30-45min.
Further, the step（2）Middle first time soaking time is 1-3min, and second of soaking time is 3-6min.
Further, the step（5）Middle drying temperature is 60-100 DEG C, time 5-10min.
Further, the finishing agent is made of the component of following parts by weight：44 parts of deionized water, tricresyl phosphate (2- chlorine
Ethyl) 6.5 parts of ester, 4.5 parts of polysiloxanes containing hydroxyl alkyl, 14 parts of methacrylic resin, 8 parts of poly (sodium aspartate), octyl phenol
4 parts of polyoxyethylene ether, 12 parts of sodium citrate, 6 parts of polyoxylethylene abietate, 5.5 parts of sorbitan monooleate, 1,2- benzene
And 7.5 parts of isothiazoline -3- ketone.
Beneficial effect：The present invention provides a kind of preparation method of wrinkle resistant hemp fabric, compared with traditional chemical routes,
Treatment process energy consumption is low, efficient, pollution is few, is conducive to environmental protection.Anti-crease finishing for linen is processed, crease recovery
Property increased, and the mechanics mechanical performance and dyeability of fabric also have lifting, and washability is strong, soft.
Embodiment
Example of the present invention is the description of the invention and cannot limit the present invention, in the implication suitable with the present invention
Any change and adjustment with scope, are all considered as within the scope of the invention.
Embodiment 1
A kind of preparation method of wrinkle resistant hemp fabric, comprises the following steps：
（1）Dipping：Hemp fabric is immersed in dressing liquid, dressing liquid bath raio is 1:20-30, wherein, the finishing agent by
The component composition of following parts by weight：40 parts of deionized water, 3 parts of tricresyl phosphate (2- chloroethyls) ester, polysiloxanes containing hydroxyl alkyl 3
Part, 12 parts of methacrylic resin, 4 parts of poly (sodium aspartate), 2 parts of octyl phenol polyoxyethylene ether, 10 parts of sodium citrate, rosin acid
4 parts of polyoxyethylene ester, 2 parts of sorbitan monooleate, 5 parts of 1,2- benzisothiazole-3-ketones；
（2）Two leachings two are rolled：The hemp fabric after dipping is carried out two leachings two on car is padded to roll, the pick-up rate is 80-
100%, the temperature of padding is 30-40 DEG C；
（3）Preliminary drying：Hemp fabric after padding carries out preliminary drying, and the preliminary drying temperature is 60-70 DEG C, the preliminary drying time
For 3-5min；
（4）Bake：Hemp fabric after padding is baked, the baking temperature is 130-140 DEG C, described when baking
Between be 3-5min；
（5）Washing drying：Hemp fabric after baking is washed 3-5 times with 20-30 DEG C of clear water, is then dried.
The step（1）Middle dip time is 30-45min.The step（2）Middle first time soaking time is 1-3min,
Second of soaking time is 3-6min.The step（5）Middle drying temperature is 60-100 DEG C, time 5-10min.
Embodiment 2
A kind of preparation method of wrinkle resistant hemp fabric, comprises the following steps：
（1）Dipping：Hemp fabric is immersed in dressing liquid, dressing liquid bath raio is 1:20-30, wherein, the finishing agent by
The component composition of following parts by weight：48 parts of deionized water, 10 parts of tricresyl phosphate (2- chloroethyls) ester, polysiloxanes containing hydroxyl alkyl 6
Part, 16 parts of methacrylic resin, 12 parts of poly (sodium aspartate), 6 parts of octyl phenol polyoxyethylene ether, 14 parts of sodium citrate, rosin
Sour 8 parts of polyoxyethylene ester, 9 parts of sorbitan monooleate, 10 parts of 1,2- benzisothiazole-3-ketones；
（2）Two leachings two are rolled：The hemp fabric after dipping is carried out two leachings two on car is padded to roll, the pick-up rate is 80-
100%, the temperature of padding is 30-40 DEG C；
（3）Preliminary drying：Hemp fabric after padding carries out preliminary drying, and the preliminary drying temperature is 60-70 DEG C, the preliminary drying time
For 3-5min；
（4）Bake：Hemp fabric after padding is baked, the baking temperature is 130-140 DEG C, described when baking
Between be 3-5min；
（5）Washing drying：Hemp fabric after baking is washed 3-5 times with 20-30 DEG C of clear water, is then dried.
The step（1）Middle dip time is 30-45min.The step（2）Middle first time soaking time is 1-3min,
Second of soaking time is 3-6min.The step（5）Middle drying temperature is 60-100 DEG C, time 5-10min.
Embodiment 3
A kind of preparation method of wrinkle resistant hemp fabric, comprises the following steps：
（1）Dipping：Hemp fabric is immersed in dressing liquid, dressing liquid bath raio is 1:20-30, wherein, the finishing agent by
The component composition of following parts by weight：44 parts of deionized water, 6.5 parts of tricresyl phosphate (2- chloroethyls) ester, polysiloxanes containing hydroxyl alkyl
4.5 parts, 14 parts of methacrylic resin, 8 parts of poly (sodium aspartate), 4 parts of octyl phenol polyoxyethylene ether, 12 parts of sodium citrate, pine
Fragrant 6 parts of polyoxyethylene ester of acid, 5.5 parts of sorbitan monooleate, 7.5 parts of 1,2- benzisothiazole-3-ketones；
（2）Two leachings two are rolled：The hemp fabric after dipping is carried out two leachings two on car is padded to roll, the pick-up rate is 80-
100%, the temperature of padding is 30-40 DEG C；
（3）Preliminary drying：Hemp fabric after padding carries out preliminary drying, and the preliminary drying temperature is 60-70 DEG C, the preliminary drying time
For 3-5min；
（4）Bake：Hemp fabric after padding is baked, the baking temperature is 130-140 DEG C, described when baking
Between be 3-5min；
（5）Washing drying：Hemp fabric after baking is washed 3-5 times with 20-30 DEG C of clear water, is then dried.
The step（1）Middle dip time is 30-45min.The step（2）Middle first time soaking time is 1-3min,
Second of soaking time is 3-6min.The step（5）Middle drying temperature is 60-100 DEG C, time 5-10min.
Claims (5)
1. a kind of preparation method of wrinkle resistant hemp fabric, it is characterised in that the described method comprises the following steps：
（1）Dipping：Hemp fabric is immersed in dressing liquid, dressing liquid bath raio is 1:20-30, wherein, the finishing agent by
The component composition of following parts by weight：40-48 parts of deionized water, 3-10 parts of tricresyl phosphate (2- chloroethyls) ester, containing the poly- silicon of hydroxyl alkyl
3-6 parts of oxygen alkane, 12-16 parts of methacrylic resin, 4-12 parts of poly (sodium aspartate), 2-6 parts of octyl phenol polyoxyethylene ether, lemon
Sour sodium 10-14 parts, 4-8 parts of polyoxylethylene abietate, 2-9 parts of sorbitan monooleate, 1,2- benzisothiazoles -3-
5-10 parts of ketone；
（2）Two leachings two are rolled：The hemp fabric after dipping is carried out two leachings two on car is padded to roll, the pick-up rate is 80-
100%, the temperature of padding is 30-40 DEG C；
（3）Preliminary drying：Hemp fabric after padding carries out preliminary drying, and the preliminary drying temperature is 60-70 DEG C, the preliminary drying time
For 3-5min；
（4）Bake：Hemp fabric after padding is baked, the baking temperature is 130-140 DEG C, described when baking
Between be 3-5min；
（5）Washing drying：Hemp fabric after baking is washed 3-5 times with 20-30 DEG C of clear water, is then dried.
A kind of 2. preparation method of wrinkle resistant hemp fabric according to claim 1, it is characterised in that：The step（1）
Middle dip time is 30-45min.
A kind of 3. preparation method of wrinkle resistant hemp fabric according to claim 1, it is characterised in that：The step（2）
Middle first time soaking time is 1-3min, and second of soaking time is 3-6min.
A kind of 4. preparation method of wrinkle resistant hemp fabric according to claim 1, it is characterised in that：The step（5）
Middle drying temperature is 60-100 DEG C, time 5-10min.
A kind of 5. preparation method of wrinkle resistant hemp fabric according to claim 1, it is characterised in that：The finishing agent by
The component composition of following parts by weight：44 parts of deionized water, 6.5 parts of tricresyl phosphate (2- chloroethyls) ester, polysiloxanes containing hydroxyl alkyl
4.5 parts, 14 parts of methacrylic resin, 8 parts of poly (sodium aspartate), 4 parts of octyl phenol polyoxyethylene ether, 12 parts of sodium citrate, pine
Fragrant 6 parts of polyoxyethylene ester of acid, 5.5 parts of sorbitan monooleate, 7.5 parts of 1,2- benzisothiazole-3-ketones.