CN107955502A - A kind of corrosion-resistant blender - Google Patents
A kind of corrosion-resistant blender Download PDFInfo
- Publication number
- CN107955502A CN107955502A CN201711356804.5A CN201711356804A CN107955502A CN 107955502 A CN107955502 A CN 107955502A CN 201711356804 A CN201711356804 A CN 201711356804A CN 107955502 A CN107955502 A CN 107955502A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrosion
- oxide
- resistant
- earth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of corrosion-resistant blender, including agitator body, and in described one layer of corrosion-resistant finishes of agitator body surface spraying, which includes following components according to the mass fraction:Phenol formaldehyde epoxy vinyl ester resin:50 60 parts, furane resins:20 30 parts, polyacrylamide:35 parts, Oppanol:8 13 parts, filler:6 12 parts, hydroxypropyl methyl cellulose:13 15 parts, ethylene glycol ethyl ether:35 parts, trbasic zinc phosphate:38 parts, graphene:36 parts, pentaerythrite three (3 '-aziridino) propionic ester:48 parts, compound rare-earth:0.3 0.6 parts, sodium tetrapolyphosphate:24 parts, dioctyl phthalate:56 parts, sodium base bentonite:10 15 parts, polyaminoester emulsion:13 16 parts, aluminium hydroxide:24 parts;The present invention has good corrosion resistance, service life length.
Description
Technical field
The present invention relates to a kind of blender, is specifically a kind of corrosion-resistant blender.
Background technology
Blender is that a kind of axis with blade rotates in cylinder or groove, makes into required denseness to mix or rub up material
Machine, the utilization of present mixer is more and more extensive, and many blenders are chiefly used in the stirring of Corrosive Materia, but its is big
It is the agitating vane using metal mostly, is stirred in Corrosive Materia so that it easily corrodes, so that influencing it uses effect
Fruit, also shortens its service life.
The content of the invention
The technical problems to be solved by the invention are the shortcomings existing in the prior art for more than, there is provided a kind of corrosion-resistant
Blender.
The present invention solve above technical problem technical solution be:A kind of corrosion-resistant blender, including agitator body, its
It is characterized in that, in described one layer of corrosion-resistant finishes of agitator body surface spraying, which includes according to the mass fraction
Following components:Phenol formaldehyde epoxy vinyl ester resin:50-60 parts, furane resins:20-30 parts, polyacrylamide:3-5 parts, gather different
Butene rubber:8-13 parts, filler:6-12 parts, hydroxypropyl methyl cellulose:13-15 parts, ethylene glycol ethyl ether:3-5 parts, trbasic zinc phosphate:
3-8 parts, graphene:3-6 parts, pentaerythrite three-(3- '-aziridinos)-propionic ester:4-8 parts, compound rare-earth:0.3-0.6 parts, four
Polyphosphate sodium:2-4 parts, dioctyl phthalate:5-6 parts, sodium base bentonite:10-15 parts, polyaminoester emulsion:13-16 parts,
Aluminium hydroxide:2-4 parts;
The filler includes according to the mass fraction:Aluminium oxide:5-8 parts, nickel oxide:3-4 parts, potassium oxide:3-6 parts, barium sulfate:6-
9 parts, antimony oxide:1-2 parts, zinc oxide:2-3 parts, zirconium oxide:3-5 parts, carborundum:6-8 parts, titanium oxide:2-3 parts;
The compound rare-earth includes following component by mass percentage:Dysprosium:15-18%, cerium:25-28%, praseodymium:5-9%, neodymium:4-
7%, gadolinium:3-6%, remaining is that the sum of lanthanum element, above lanthanide rare each component is 100%.
The technical solution that further limits of the present invention is:
Foregoing corrosion-resistant finishes includes following components according to the mass fraction:Phenol formaldehyde epoxy vinyl ester resin:53 parts, furans tree
Fat:24 parts, polyacrylamide:3 parts, Oppanol:8 parts, filler:8 parts, hydroxypropyl methyl cellulose:13 parts, ethylene glycol
Ether:3 parts, trbasic zinc phosphate:4 parts, graphene:3 parts, pentaerythrite three-(3- '-aziridinos)-propionic ester:5 parts, compound rare-earth:
0.3 part, sodium tetrapolyphosphate:2 parts, dioctyl phthalate:5 parts, sodium base bentonite:10 parts, polyaminoester emulsion:13 parts, hydrogen
Aluminium oxide:3 parts;
Filler includes according to the mass fraction:Aluminium oxide:5 parts, nickel oxide:3 parts, potassium oxide:3 parts, barium sulfate:7 parts, antimony oxide:1
Part, zinc oxide:2 parts, zirconium oxide:3 parts, carborundum:6 parts, titanium oxide:2 parts;
Compound rare-earth includes following component by mass percentage:Dysprosium:15%, cerium:25%, praseodymium:5%, neodymium:4%, gadolinium:3%, remaining is
The sum of lanthanum element, above lanthanide rare each component is 100%.
Foregoing corrosion-resistant finishes includes following components according to the mass fraction:Phenol formaldehyde epoxy vinyl ester resin:56 parts, furan
Furane resins:26 parts, polyacrylamide:5 parts, Oppanol:10 parts, filler:11 parts, hydroxypropyl methyl cellulose:14 parts,
Ethylene glycol ethyl ether:5 parts, trbasic zinc phosphate:6 parts, graphene:5 parts, pentaerythrite three-(3- '-aziridinos)-propionic ester:It is 6 parts, compound
Rare earth:0.4 part, sodium tetrapolyphosphate:3 parts, dioctyl phthalate:6 parts, sodium base bentonite:12 parts, polyaminoester emulsion:14
Part, aluminium hydroxide:3 parts;
The filler includes according to the mass fraction:Aluminium oxide:6 parts, nickel oxide:4 parts, potassium oxide:4 parts, barium sulfate:8 parts, oxidation
Antimony:1.5 parts, zinc oxide:3 parts, zirconium oxide:4 parts, carborundum:7 parts, titanium oxide:3 parts;
The compound rare-earth includes following component by mass percentage:Dysprosium:17%, cerium:27%, praseodymium:8%, neodymium:6%, gadolinium:5%, its
Remaining is that the sum of lanthanum element, above lanthanide rare each component is 100%.
Foregoing corrosion-resistant blender preparation method, specifically includes following steps:
Step 1:Phenol formaldehyde epoxy vinyl ester resin and furane resins are mixed to join in heating furnace, are heated to melting, then
Oppanol, polyaminoester emulsion, hydroxypropyl methyl cellulose and ethylene glycol ethyl ether are added, is stirred with 100-120r/min
10-15min;
Step 2:Trbasic zinc phosphate, graphene and sodium base bentonite are mixed 20-30min is stirred with 200-300r/min, add penta 4
Alcohol three-(3- '-aziridinos)-propionic ester, dioctyl phthalate, sodium tetrapolyphosphate and aluminium hydroxide, stirs 30-40min,
Temperature is heated to 70-78 DEG C, keeps the temperature 20-30min, it is spare:
Step 3:Step 1 and step 2 are mixed, high-speed stirred 40-50min, its speed is 500-560r/min
Step 4:Send after filler and compound rare-earth are mixed and be ground into ball mill, sieve, be then added to step 3
In, it is stirred continuously, time 1-2h, obtains corrosion resistant coating;
Step 5:First in one layer binder of agitator body surface spraying, then corrosion resistant coating is sprayed by flush coater
Apply, specific control parameter is:Spraying flow is 90-100ml/10s, and spraying number of turns control is enclosed in 20-24, sprays mist type pressure control
System is in 0.4-0.5MPa, spray distance control 20-30cm;
Step 6:The agitator body sprayed is placed in curing oven, temperature is 90-95 DEG C, time 40-50min.
The beneficial effects of the invention are as follows:The present invention has the advantages that intensity is high, corrosion resistant, is scribbled on agitator body surface
One layer of corrosion-resistant coating, improves the corrosion resistance of blender, and adding compound rare-earth has the excellent transparency, there is uniqueness
Plasticising, toughening effect, while there is excellent weather resistance and excellent electrical insulation capability, nontoxic, safety and sanitation, phenolic aldehyde ring
Ethylene oxide base ester resin has a higher heat endurance, and after resin solidification, crosslink density is big, its heat distortion temperature reaches 120-135
DEG C, it can prolong the service life and there is excellent corrosion resistance, especially to containing solutions of chlorine or organic solvent good corrosion resistance, hydrogen
Aluminium oxide can be used as fire retardant, can not only be fire-retardant, and can prevent smoke, not produce droppings, do not produce toxic gas, furan
Furane resins after hardening, has the erosion of resistance to strong acid, highly basic and organic solvent, still very stable at high temperature.
Embodiment
Embodiment 1
The present embodiment provides a kind of corrosion-resistant blender, including agitator body, in one layer of corrosion resistant of agitator body surface spraying
Erosion resisting coating, the corrosion-resistant finishes include following components according to the mass fraction:Corrosion-resistant finishes includes with the following group according to the mass fraction
Point:Phenol formaldehyde epoxy vinyl ester resin:53 parts, furane resins:24 parts, polyacrylamide:3 parts, Oppanol:8 parts, fill out
Material:8 parts, hydroxypropyl methyl cellulose:13 parts, ethylene glycol ethyl ether:3 parts, trbasic zinc phosphate:4 parts, graphene:3 parts, pentaerythrite three-
(3- '-aziridinos)-propionic ester:5 parts, compound rare-earth:0.3 part, sodium tetrapolyphosphate:2 parts, dioctyl phthalate:5 parts, receive
Base bentonite:10 parts, polyaminoester emulsion:13 parts, aluminium hydroxide:3 parts;
Filler includes according to the mass fraction:Aluminium oxide:5 parts, nickel oxide:3 parts, potassium oxide:3 parts, barium sulfate:7 parts, antimony oxide:1
Part, zinc oxide:2 parts, zirconium oxide:3 parts, carborundum:6 parts, titanium oxide:2 parts;
Compound rare-earth includes following component by mass percentage:Dysprosium:15%, cerium:25%, praseodymium:5%, neodymium:4%, gadolinium:3%, remaining is
The sum of lanthanum element, above lanthanide rare each component is 100%.
A kind of corrosion-resistant blender preparation method of the present embodiment, specifically includes following steps:
Step 1:Phenol formaldehyde epoxy vinyl ester resin and furane resins are mixed to join in heating furnace, are heated to melting, then
Oppanol, polyaminoester emulsion, hydroxypropyl methyl cellulose and ethylene glycol ethyl ether are added, 15min is stirred with 100r/min;
Step 2:Trbasic zinc phosphate, graphene and sodium base bentonite are mixed 30min are stirred with 200r/min, add penta tetrol three-
(3- '-aziridinos)-propionic ester, dioctyl phthalate, sodium tetrapolyphosphate and aluminium hydroxide, stirs 35min, by temperature plus
Heat keeps the temperature 25min to 73 DEG C, spare:
Step 3:Step 1 and step 2 are mixed, high-speed stirred 45min, its speed is 530r/min
Step 4:Send after filler and compound rare-earth are mixed and be ground into ball mill, sieve, be then added to step 3
In, it is stirred continuously, time 1.5h, obtains corrosion resistant coating;
Step 5:First in one layer binder of agitator body surface spraying, then corrosion resistant coating is sprayed by flush coater
Apply, specific control parameter is:Spraying flow is 90ml/10s, and the control of the spraying number of turns exists in 22 circles, the pressure control of spraying mist type
0.4MPa, spray distance control 25cm;
Step 6:The agitator body sprayed is placed in curing oven, temperature is 92 DEG C, time 45min.
Embodiment 2
The present embodiment provides a kind of corrosion-resistant blender, including agitator body, in one layer of corrosion resistant of agitator body surface spraying
Erosion resisting coating, the corrosion-resistant finishes include following components according to the mass fraction:Phenol formaldehyde epoxy vinyl ester resin:56 parts, furans tree
Fat:26 parts, polyacrylamide:5 parts, Oppanol:10 parts, filler:11 parts, hydroxypropyl methyl cellulose:14 parts, second two
Alcohol ether:5 parts, trbasic zinc phosphate:6 parts, graphene:5 parts, pentaerythrite three-(3- '-aziridinos)-propionic ester:6 parts, compound rare-earth:
0.4 part, sodium tetrapolyphosphate:3 parts, dioctyl phthalate:6 parts, sodium base bentonite:12 parts, polyaminoester emulsion:14 parts, hydrogen
Aluminium oxide:3 parts;
The filler includes according to the mass fraction:Aluminium oxide:6 parts, nickel oxide:4 parts, potassium oxide:4 parts, barium sulfate:8 parts, oxidation
Antimony:1.5 parts, zinc oxide:3 parts, zirconium oxide:4 parts, carborundum:7 parts, titanium oxide:3 parts;
The compound rare-earth includes following component by mass percentage:Dysprosium:17%, cerium:27%, praseodymium:8%, neodymium:6%, gadolinium:5%, its
Remaining is that the sum of lanthanum element, above lanthanide rare each component is 100%.
A kind of corrosion-resistant blender preparation method of the present embodiment, specifically includes following steps:
Step 1:Phenol formaldehyde epoxy vinyl ester resin and furane resins are mixed to join in heating furnace, are heated to melting, then
Oppanol, polyaminoester emulsion, hydroxypropyl methyl cellulose and ethylene glycol ethyl ether are added, 10min is stirred with 120r/min;
Step 2:Trbasic zinc phosphate, graphene and sodium base bentonite are mixed 20min are stirred with 300r/min, add penta tetrol three-
(3- '-aziridinos)-propionic ester, dioctyl phthalate, sodium tetrapolyphosphate and aluminium hydroxide, stirs 37min, by temperature plus
Heat keeps the temperature 23min to 76 DEG C, spare:
Step 3:Step 1 and step 2 are mixed, high-speed stirred 40min, its speed is 560r/min
Step 4:Send after filler and compound rare-earth are mixed and be ground into ball mill, sieve, be then added to step 3
In, it is stirred continuously, time 2h, obtains corrosion resistant coating;
Step 5:First in one layer binder of agitator body surface spraying, then corrosion resistant coating is sprayed by flush coater
Apply, specific control parameter is:Spraying flow is 100ml/10s, and the control of the spraying number of turns exists in 24 circles, the pressure control of spraying mist type
0.45MPa, spray distance control 30cm;
Step 6:The agitator body sprayed is placed in curing oven, temperature is 95 DEG C, time 40min.
In addition to the implementation, the present invention can also have other embodiment.It is all to use equivalent substitution or equivalent transformation shape
Into technical solution, all fall within the protection domains of application claims.
Claims (4)
1. a kind of corrosion-resistant blender, including agitator body, it is characterised in that in one layer of the agitator body surface spraying
Corrosion-resistant finishes, the corrosion-resistant finishes include following components according to the mass fraction:Phenol formaldehyde epoxy vinyl ester resin:50-60 parts,
Furane resins:20-30 parts, polyacrylamide:3-5 parts, Oppanol:8-13 parts, filler:6-12 parts, hydroxypropyl methyl
Cellulose:13-15 parts, ethylene glycol ethyl ether:3-5 parts, trbasic zinc phosphate:3-8 parts, graphene:3-6 parts, pentaerythrite three-(3- nitrogen third
Piperidinyl)-propionic ester:4-8 parts, compound rare-earth:0.3-0.6 parts, sodium tetrapolyphosphate:2-4 parts, dioctyl phthalate:5-6
Part, sodium base bentonite:10-15 parts, polyaminoester emulsion:13-16 parts, aluminium hydroxide:2-4 parts;
The filler includes according to the mass fraction:Aluminium oxide:5-8 parts, nickel oxide:3-4 parts, potassium oxide:3-6 parts, barium sulfate:6-
9 parts, antimony oxide:1-2 parts, zinc oxide:2-3 parts, zirconium oxide:3-5 parts, carborundum:6-8 parts, titanium oxide:2-3 parts;
The compound rare-earth includes following component by mass percentage:Dysprosium:15-18%, cerium:25-28%, praseodymium:5-9%, neodymium:4-
7%, gadolinium:3-6%, remaining is that the sum of lanthanum element, above lanthanide rare each component is 100%.
2. corrosion-resistant blender according to claim 1, it is characterised in that:The corrosion-resistant finishes includes according to the mass fraction
Following components:Phenol formaldehyde epoxy vinyl ester resin:53 parts, furane resins:24 parts, polyacrylamide:3 parts, Oppanol:
8 parts, filler:8 parts, hydroxypropyl methyl cellulose:13 parts, ethylene glycol ethyl ether:3 parts, trbasic zinc phosphate:4 parts, graphene:3 parts, season penta
Tetrol three-(3- '-aziridinos)-propionic ester:5 parts, compound rare-earth:0.3 part, sodium tetrapolyphosphate:2 parts, phthalic acid two is pungent
Ester:5 parts, sodium base bentonite:10 parts, polyaminoester emulsion:13 parts, aluminium hydroxide:3 parts;
The filler includes according to the mass fraction:Aluminium oxide:5 parts, nickel oxide:3 parts, potassium oxide:3 parts, barium sulfate:7 parts, oxidation
Antimony:1 part, zinc oxide:2 parts, zirconium oxide:3 parts, carborundum:6 parts, titanium oxide:2 parts;
The compound rare-earth includes following component by mass percentage:Dysprosium:15%, cerium:25%, praseodymium:5%, neodymium:4%, gadolinium:3%, its
Remaining is that the sum of lanthanum element, above lanthanide rare each component is 100%.
3. corrosion-resistant blender according to claim 1, it is characterised in that:The corrosion-resistant finishes includes according to the mass fraction
Following components:Phenol formaldehyde epoxy vinyl ester resin:56 parts, furane resins:26 parts, polyacrylamide:5 parts, Oppanol:
10 parts, filler:11 parts, hydroxypropyl methyl cellulose:14 parts, ethylene glycol ethyl ether:5 parts, trbasic zinc phosphate:6 parts, graphene:5 parts, season
Penta tetrol, three-(3- '-aziridinos)-propionic ester:6 parts, compound rare-earth:0.4 part, sodium tetrapolyphosphate:3 parts, phthalic acid two is pungent
Ester:6 parts, sodium base bentonite:12 parts, polyaminoester emulsion:14 parts, aluminium hydroxide:3 parts;
The filler includes according to the mass fraction:Aluminium oxide:6 parts, nickel oxide:4 parts, potassium oxide:4 parts, barium sulfate:8 parts, oxidation
Antimony:1.5 parts, zinc oxide:3 parts, zirconium oxide:4 parts, carborundum:7 parts, titanium oxide:3 parts;
The compound rare-earth includes following component by mass percentage:Dysprosium:17%, cerium:27%, praseodymium:8%, neodymium:6%, gadolinium:5%, its
Remaining is that the sum of lanthanum element, above lanthanide rare each component is 100%.
4. according to any corrosion-resistant blender preparation methods of claim 1-3, it is characterised in that specifically include following step
Suddenly:
Step 1:Phenol formaldehyde epoxy vinyl ester resin and furane resins are mixed to join in heating furnace, are heated to melting, then
Oppanol, polyaminoester emulsion, hydroxypropyl methyl cellulose and ethylene glycol ethyl ether are added, is stirred with 100-120r/min
10-15min;
Step 2:Trbasic zinc phosphate, graphene and sodium base bentonite are mixed 20-30min is stirred with 200-300r/min, add penta 4
Alcohol three-(3- '-aziridinos)-propionic ester, dioctyl phthalate, sodium tetrapolyphosphate and aluminium hydroxide, stirs 30-40min,
Temperature is heated to 70-78 DEG C, keeps the temperature 20-30min, it is spare:
Step 3:Step 1 and step 2 are mixed, high-speed stirred 40-50min, its speed is 500-560r/min
Step 4:Send after filler and compound rare-earth are mixed and be ground into ball mill, sieve, be then added to step 3
In, it is stirred continuously, time 1-2h, obtains corrosion resistant coating;
Step 5:First in one layer binder of agitator body surface spraying, then corrosion resistant coating is sprayed by flush coater
Apply, specific control parameter is:Spraying flow is 90-100ml/10s, and spraying number of turns control is enclosed in 20-24, sprays mist type pressure control
System is in 0.4-0.5MPa, spray distance control 20-30cm;
Step 6:The agitator body sprayed is placed in curing oven, temperature is 90-95 DEG C, time 40-50min.