CN107951545A - A kind of aseptic electric operation device - Google Patents
A kind of aseptic electric operation device Download PDFInfo
- Publication number
- CN107951545A CN107951545A CN201711416574.7A CN201711416574A CN107951545A CN 107951545 A CN107951545 A CN 107951545A CN 201711416574 A CN201711416574 A CN 201711416574A CN 107951545 A CN107951545 A CN 107951545A
- Authority
- CN
- China
- Prior art keywords
- handle
- operation device
- weight
- electric operation
- connecting rod
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aseptic electric operation device, include the handle of gun shaped(1), the handle(1)Inside it is provided with bull stick(4), the bull stick(4)Front end and connecting rod(2)One end be flexibly connected, the flexible connection is the connecting rod(2)On be provided with card slot, the bull stick(4)On be provided with and the matched card of the card slot(7), the handle(1)End be provided with pushing block(8), the pushing block(8)On to be connected with least two being arranged in parallel and penetrate the handle(1)Push rod(9), the push rod(9)Free end face described in connecting rod(2), the connecting rod(2)The other end and operating theater instruments(3)It is flexibly connected, the bull stick(4)With driving device(5)It is connected.The present invention makes handle avoid operating theater instruments from polluting handle away from operating theater instruments;The setting of nanometer antibacterium coating, makes the present invention be not easy to be contaminated, even if also allowing for sterilizing after contaminated, further prevents cross-patient contamination.
Description
Technical field
The present invention relates to a kind of aseptic electric operation device, belong to power tools technology field.
Background technology
The handle of current electric operation device is generally connected directly with operating theater instruments such as scalpels, and operating theater instruments is easy to pollute
Handle, after especially needing the electric handle of Reusability to be contaminated, since the high-temperature sterilization of electric handle inconvenience or use disappear
Venom thoroughly cleans, and thimerosal can only be used to clean electric handle surface and carried out disinfection, this makes the disinfection of electric handle very not
Thoroughly, the patient that easily infection next bit uses, infection will bring great pain once occurring to patient.
The content of the invention
The technical problem to be solved by the invention is to provide a kind of electric operation device of handle not easy to pollute;Further
Ground, the present invention provides a kind of handle and is provided outside antimicrobial coating, easy to sterilize, prevents the electric operation device of infection;More into one
Step ground, the present invention provide a kind of quick detachable aseptic electric operation device.
In order to solve the above technical problems, the technical solution adopted by the present invention is:
A kind of aseptic electric operation device, includes the handle of gun shaped, is provided with bull stick in the handle, before the bull stick
End is flexibly connected with one end of connecting rod, described to be flexibly connected to be provided with card slot in the connecting rod, is set on the bull stick
Have and the matched card of the card slot, the end of the handle are provided with pushing block, it is parallel to be connected with least two on the pushing block
Push rod that is setting and penetrating the handle, connecting rod described in the free end face of the push rod, the other end of the connecting rod
It is flexibly connected with operating theater instruments, the bull stick is connected with driving device.
It is to be connected through a screw thread between the connecting rod and operating theater instruments;The front end of the handle is provided with for accommodating institute
State the groove of connecting rod.
Set has elastic component outside the push rod, and the flexible member includes spring.
The operating theater instruments includes scalpel.
The driving device includes buncher or electric rotating machine.
The outer surface of the handle is provided with nanometer antibacterium coating.
The nanometer antibacterium coating includes zinc doping calcium silicates coating.
The preparation method of the zinc doping calcium silicates coating comprises the following steps:
S01, by appropriate drying to the zinc oxide of constant weight, silica, calcirm-fluoride, calcium silicates and titanium dioxide after mixing,
It is put into crucible, high temperature, which is processed, to burn to wire drawing without node;
S02, takes out crucible, and the solution in crucible is ground into powder after cooling rapidly;
S03,95% ethanol is added in powder is uniformly mixed it, and then the shell of the handle is placed in alcohol mixeding liquid, is taken
Go out rear high-temperature firing, be molded, obtain zinc doping calcium silicates coating.
The zinc oxide, silica, calcirm-fluoride, the weight of calcium silicates and titanium dioxide are:1 ~ 2 parts by weight of zinc oxide,
0 ~ 20 parts by weight of silica 1,3 ~ 5 parts by weight of 5 ~ 8 parts by weight of calcirm-fluoride, 5 ~ 10 parts by weight of calcium silicates and titanium dioxide;High temperature
Bright temperature is processed as 800 ~ 1000 DEG C;It is rapid to be cooled to cool down using ice-water bath.
The dosage of 95% ethanol is 2 ~ 5 times of parts by weight of powder;The temperature of high-temperature firing is to be fired at 650 ~ 700 DEG C
10 ~ 15 minutes.
A kind of aseptic electric operation device provided by the invention, the setting of connecting rod, makes handle away from operating theater instruments,
Operating theater instruments is avoided to pollute handle;The setting of nanometer antibacterium coating, makes the present invention be not easy to be contaminated, even if being also allowed for after contaminated
Disinfection, further prevents cross-patient contamination;The preparation method of zinc doping calcium silicates coating makes nanometer antibacterium coating and handle
Shell strong bonded, it is not easily to fall off, there is the antibacterial effect of long acting antibiotic;The combination settings of pushing block, push rod, are easy to connecting rod
Disassembled from handle, prevent connecting rod from polluting handle, clean rank is high, further prevents cross-patient contamination.
Brief description of the drawings
Fig. 1 is the structure diagram of the present invention.
Embodiment
The present invention is further described below in conjunction with the accompanying drawings.
Embodiment 1
As shown in Figure 1, a kind of aseptic electric operation device, include the handle 1 of gun shaped, bull stick is provided with the handle 1
4, the front end of the bull stick 4 is flexibly connected with one end of connecting rod 2, described to be flexibly connected to be provided with card in the connecting rod 2
Groove, is provided with card 7 matched with the card slot on the bull stick 4, the end of the handle 1 is provided with pushing block 8, described to push away
At least two push rods 9 that are being arranged in parallel and penetrating the handle 1 are connected with block 8, are connected described in the free end face of the push rod 9
Extension bar 2, the other end of the connecting rod 2 are flexibly connected with operating theater instruments 3, and the bull stick 4 is connected with driving device 5.
It is to be connected through a screw thread between the connecting rod 2 and operating theater instruments 3;The front end of the handle 1 is provided with for holding
Receive the groove 6 of the connecting rod 2.
The outside of push rod 9 set has elastic component, and the flexible member includes spring.
The operating theater instruments 3 includes scalpel.
The driving device 5 includes buncher or electric rotating machine.
The outer surface of the handle 1 is provided with nanometer antibacterium coating.
The nanometer antibacterium coating includes zinc doping calcium silicates coating.
The preparation method of the zinc doping calcium silicates coating comprises the following steps:
S01, by appropriate drying to the zinc oxide of constant weight, silica, calcirm-fluoride, calcium silicates and titanium dioxide after mixing,
It is put into crucible, high temperature, which is processed, to burn to wire drawing without node;
S02, takes out crucible, and the solution in crucible is ground into powder after cooling rapidly;
S03,95% ethanol is added in powder is uniformly mixed it, and then the shell of the handle 1 is placed in alcohol mixeding liquid,
High-temperature firing after taking-up, shaping, obtains zinc doping calcium silicates coating.
The zinc oxide, silica, calcirm-fluoride, the weight of calcium silicates and titanium dioxide are:1 ~ 2 parts by weight of zinc oxide,
0 ~ 20 parts by weight of silica 1,3 ~ 5 parts by weight of 5 ~ 8 parts by weight of calcirm-fluoride, 5 ~ 10 parts by weight of calcium silicates and titanium dioxide;High temperature
Bright temperature is processed as 800 ~ 1000 DEG C;It is rapid to be cooled to cool down using ice-water bath.
The dosage of 95% ethanol is 2 ~ 5 times of parts by weight of powder;The temperature of high-temperature firing is to be fired at 650 ~ 700 DEG C
10 ~ 15 minutes.
Embodiment 2
The present embodiment is differed only in embodiment 1:The zinc oxide, silica, calcirm-fluoride, calcium silicates and titanium dioxide
Weight be:1 parts by weight of zinc oxide, 0 parts by weight of silica 1,5 parts by weight of calcirm-fluoride, 5 parts by weight of calcium silicates and titanium dioxide
3 parts by weight;High temperature processs bright temperature as 800 DEG C;It is rapid to be cooled to cool down using ice-water bath.
The dosage of 95% ethanol is 2 times of parts by weight of powder;The temperature of high-temperature firing is to be fired 10 minutes at 650 DEG C.
Embodiment 3
The present embodiment is differed only in embodiment 1:The zinc oxide, silica, calcirm-fluoride, calcium silicates and titanium dioxide
Weight be:2 parts by weight of zinc oxide, 20 parts by weight of silica, 8 parts by weight of calcirm-fluoride, 10 parts by weight of calcium silicates and titanium dioxide
5 parts by weight of titanium;High temperature processs bright temperature as 1000 DEG C;It is rapid to be cooled to cool down using ice-water bath.
The dosage of 95% ethanol is 5 times of parts by weight of powder;The temperature of high-temperature firing is to be fired 15 minutes at 700 DEG C.
The above is only the preferred embodiment of the present invention, it should be pointed out that:For the ordinary skill people of the art
For member, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (10)
- A kind of 1. aseptic electric operation device, it is characterised in that:Handle including gun shaped(1), the handle(1)Interior setting There is bull stick(4), the bull stick(4)Front end and connecting rod(2)One end be flexibly connected, the flexible connection is the connecting rod (2)On be provided with card slot, the bull stick(4)On be provided with and the matched card of the card slot(7), the handle(1)End End is provided with pushing block(8), the pushing block(8)On to be connected with least two being arranged in parallel and penetrate the handle(1)Push rod (9), the push rod(9)Free end face described in connecting rod(2), the connecting rod(2)The other end and operating theater instruments(3)It is living Dynamic connection, the bull stick(4)With driving device(5)It is connected.
- A kind of 2. aseptic electric operation device according to claim 1, it is characterised in that:The connecting rod(2)With Operating theater instruments(3)Between to be connected through a screw thread;The handle(1)Front end be provided with for accommodating the connecting rod(2)'s Groove(6).
- A kind of 3. aseptic electric operation device according to claim 1, it is characterised in that:The push rod(9)Outside Set has elastic component, and the flexible member includes spring.
- A kind of 4. aseptic electric operation device according to claim 1, it is characterised in that:The operating theater instruments(3) Including scalpel.
- A kind of 5. aseptic electric operation device according to claim 1, it is characterised in that:The driving device(5) Including buncher or electric rotating machine.
- A kind of 6. aseptic electric operation device according to claim 1, it is characterised in that:The handle(1)It is outer Surface is provided with nanometer antibacterium coating.
- A kind of 7. aseptic electric operation device according to claim 6, it is characterised in that:The nanometer antibacterium coating Including zinc doping calcium silicates coating.
- A kind of 8. aseptic electric operation device according to claim 7, it is characterised in that:The zinc doping calcium silicates The preparation method of coating comprises the following steps:S01, by appropriate drying to the zinc oxide of constant weight, silica, calcirm-fluoride, calcium silicates and titanium dioxide after mixing, It is put into crucible, high temperature, which is processed, to burn to wire drawing without node;S02, takes out crucible, and the solution in crucible is ground into powder after cooling rapidly;S03,95% ethanol is added in powder is uniformly mixed it, then by the handle(1)Shell be placed in alcohol mixeding liquid In, high-temperature firing after taking-up, shaping, obtains zinc doping calcium silicates coating.
- A kind of 9. aseptic electric operation device according to claim 8, it is characterised in that:The zinc oxide, dioxy SiClx, calcirm-fluoride, the weight of calcium silicates and titanium dioxide are:1 ~ 2 parts by weight of zinc oxide, 0 ~ 20 parts by weight of silica 1, fluorination 3 ~ 5 parts by weight of 5 ~ 8 parts by weight of calcium, 5 ~ 10 parts by weight of calcium silicates and titanium dioxide;High temperature processs bright temperature as 800 ~ 1000 DEG C;It is fast Speed is cooled to cool down using ice-water bath.
- A kind of 10. aseptic electric operation device according to claim 8, it is characterised in that:The use of 95% ethanol Measure 2 ~ 5 times of parts by weight for powder;The temperature of high-temperature firing is to be fired 10 ~ 15 minutes at 650 ~ 700 DEG C.