CN107936332A - A kind of wear resistant automobile cover tire formula and its preparation process - Google Patents
A kind of wear resistant automobile cover tire formula and its preparation process Download PDFInfo
- Publication number
- CN107936332A CN107936332A CN201711372240.4A CN201711372240A CN107936332A CN 107936332 A CN107936332 A CN 107936332A CN 201711372240 A CN201711372240 A CN 201711372240A CN 107936332 A CN107936332 A CN 107936332A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear resistant
- cover tire
- automobile cover
- resistant automobile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wear resistant automobile cover tire formula, the formula of its raw material by weight are as follows：60 80 parts of latex reclaimed rubber, 20 30 parts of neoprene, 20 30 parts of dioctyl phthalate, 12 16 parts of stearic acid carbon fiber, 12 16 parts of polyester fiber, 12 16 parts of aluminum fiber, 8 12 parts of N220 carbon blacks, 8 12 parts of precipitated calcium carbonate, 48 parts of activator, 48 parts of vulcanizing agent, 48 parts of antioxidant, 48 parts of binding agent, 25 parts of zinc oxide, 25 parts of aluminium powder, 25 parts of titanium valve.Present invention also offers a kind of preparation process of wear resistant automobile cover tire.The present invention enables to autotyre casing to have good wear-resisting property, and can also increase its anti-pressure ability and intensity, and can be used in cold season and hot season.
Description
Technical field
The present invention relates to auto parts preparing technical field, more particularly to a kind of wear resistant automobile cover tire formula and its preparation work
Skill.
Background technology
Automobile tire is one of important component of automobile, it is directly contacted with road surface, and automotive suspension relaxes vapour jointly
Car suffered impact when driving, ensures that automobile has good driving comfort and ride performance；Ensure that wheel and road surface have
Good adhesion；Improve traction property, braking and the passability of automobile；Subject the weight of automobile, tire institute on automobile
The important function risen is increasingly valued by people.And cover tire is then the carrier that tire is directly contacted with ground, therefore, cover tire
After prolonged use, easily easily wear, if serious, vehicle may be caused not travel, for this reason, we have proposed
A kind of wear resistant automobile cover tire formula and its preparation process.
The content of the invention
The present invention proposes a kind of wear resistant automobile cover tire formula and its preparation process, to solve to propose in above-mentioned background technology
The problem of.
The present invention proposes a kind of wear resistant automobile cover tire formula, and the formula of its raw material by weight is as follows：Latex reclaimed rubber 60-
80 parts, 20-30 parts of neoprene, 20-30 parts of dioctyl phthalate, 12-16 parts of stearic acid carbon fiber, polyester fiber 12-
16 parts, it is 12-16 parts of aluminum fiber, 8-12 parts of N220 carbon blacks, 8-12 parts of precipitated calcium carbonate, 4-8 parts of activator, 4-8 parts of vulcanizing agent, anti-
Old agent 4-8 parts, 4-8 parts of binding agent, 2-5 parts of zinc oxide, 2-5 parts of aluminium powder, 2-5 parts of titanium valve.
Preferably, latex reclaimed rubber, neoprene, the weight ratio of dioctyl phthalate are 65-75: 23-28: 23-
28。
Preferably, stearic acid carbon fiber, polyester fiber, the weight ratio of aluminum fiber are 13-15: 13-15: 13-15.
Preferably, N220 carbon blacks, the weight ratio of precipitated calcium carbonate are 9-11: 9-11.
Preferably, activator, vulcanizing agent, antioxidant, the weight ratio of binding agent are 5-7: 5-7: 5-7: 5-7.
Preferably, zinc oxide, aluminium powder, the weight ratio of titanium valve are 3-4: 3-4: 3-4.
Preferably, the formula of its raw material by weight is as follows：
65-75 parts of latex reclaimed rubber, 23-28 parts of neoprene, 23-28 parts of dioctyl phthalate, stearic acid carbon are fine
13-15 parts of dimension, 13-15 parts of polyester fiber, 13-15 parts of aluminum fiber, 9-11 parts of N220 carbon blacks, 9-11 parts of precipitated calcium carbonate, activation
5-7 parts of agent, 5-7 parts of vulcanizing agent, 5-7 parts of antioxidant, 5-7 parts of binding agent, 3-4 parts of zinc oxide, 3-4 parts of aluminium powder, 3-4 parts of titanium valve.
Preferably, the optimization formula of its raw material by weight is as follows：
It is 70 parts of latex reclaimed rubber, 25 parts of neoprene, 25 parts of dioctyl phthalate, 14 parts of stearic acid carbon fiber, poly-
14 parts of ester fiber, 14 parts of aluminum fiber, 10 parts of N220 carbon blacks, 10 parts of precipitated calcium carbonate, 6 parts of activator, 6 parts of vulcanizing agent, antioxidant 6
Part, 6 parts of binding agent, 3.5 parts of zinc oxide, 3.5 parts of aluminium powder, 3.5 parts of titanium valve.
Present invention also offers a kind of preparation process of wear resistant automobile cover tire, include the following steps：
S1, in proportion insert latex reclaimed rubber, neoprene and dioctyl phthalate in smelting furnace, and
Melting is carried out under conditions of 200-300 degrees Celsius, after its thawing, adds stearic acid carbon fiber, polyester into smelting furnace again
Fiber, aluminum fiber, N220 carbon blacks and precipitated calcium carbonate, then carry out mixing 4-8min, and in the process of mixing
In add zinc oxide, aluminium powder and titanium valve thereto, finally activator, vulcanizing agent, antioxidant and binding agent are added to molten
In furnace, it being treated after mixing, being taken out, it is spare to form mixed solution；
Mixed solution, be poured into autotyre casing mould by S2, after its shaping, takes out, forms preliminary autotyre casing,
And cooled down under field conditions (factors), then to the processing on its surface and inside, up to wear resistant automobile cover tire.
A kind of wear resistant automobile cover tire provided by the present invention and its technique is prepared, had the beneficial effect that：The present invention passes through
The addition of plurality of raw materials, and rational proportion, enable to autotyre casing to have good wear-resisting property, and can also increase it
Anti-pressure ability and intensity, also improve the use scope of cover tire, it is used in cold season and hot season,
Effectively improve its service life.
Embodiment
With reference to specific embodiment, the present invention will be further described.
Embodiment 1
The present invention proposes a kind of wear resistant automobile cover tire formula, and the formula of its raw material by weight is as follows：Latex reclaimed rubber 60
Part, 20 parts of neoprene, 20 parts of dioctyl phthalate, 12 parts of stearic acid carbon fiber, 12 parts of polyester fiber, aluminum fiber 12
Part, 8 parts of N220 carbon blacks, 8 parts of precipitated calcium carbonate, 4 parts of activator, 4 parts of vulcanizing agent, 4 parts of antioxidant, 4 parts of binding agent, zinc oxide 2
Part, 2 parts of aluminium powder, 2 parts of titanium valve.
Present invention also offers a kind of preparation process of wear resistant automobile cover tire, include the following steps：
S1, in proportion insert latex reclaimed rubber, neoprene and dioctyl phthalate in smelting furnace, and
Melting is carried out under conditions of 200 degrees Celsius, after its thawing, added again into smelting furnace stearic acid carbon fiber, polyester fiber,
Aluminum fiber, N220 carbon blacks and precipitated calcium carbonate, then carry out mixing 4min, and during mixing thereto
Zinc oxide, aluminium powder and titanium valve are added, finally activator, vulcanizing agent, antioxidant and binding agent are added to smelting furnace, treated
It takes out after mixing, and it is spare to form mixed solution；
Mixed solution, be poured into autotyre casing mould by S2, after its shaping, takes out, forms preliminary autotyre casing,
And cooled down under field conditions (factors), then to the processing on its surface and inside, up to wear resistant automobile cover tire.
Embodiment 2
The present invention proposes a kind of wear resistant automobile cover tire formula, and the formula of its raw material by weight is as follows：Latex reclaimed rubber 65
Part, 23 parts of neoprene, 23 parts of dioctyl phthalate, 13 parts of stearic acid carbon fiber, 13 parts of polyester fiber, aluminum fiber 13
Part, 9 parts of N220 carbon blacks, 9 parts of precipitated calcium carbonate, 5 parts of activator, 5 parts of vulcanizing agent, 5 parts of antioxidant, 5 parts of binding agent, zinc oxide 3
Part, 3 parts of aluminium powder, 3 parts of titanium valve.
Present invention also offers a kind of preparation process of wear resistant automobile cover tire, include the following steps：
S1, in proportion insert latex reclaimed rubber, neoprene and dioctyl phthalate in smelting furnace, and
Melting is carried out under conditions of 230 degrees Celsius, after its thawing, added again into smelting furnace stearic acid carbon fiber, polyester fiber,
Aluminum fiber, N220 carbon blacks and precipitated calcium carbonate, then carry out mixing 5min, and during mixing thereto
Zinc oxide, aluminium powder and titanium valve are added, finally activator, vulcanizing agent, antioxidant and binding agent are added to smelting furnace, treated
It takes out after mixing, and it is spare to form mixed solution；
Mixed solution, be poured into autotyre casing mould by S2, after its shaping, takes out, forms preliminary autotyre casing,
And cooled down under field conditions (factors), then to the processing on its surface and inside, up to wear resistant automobile cover tire.
Embodiment 3
The present invention proposes a kind of wear resistant automobile cover tire formula, and the formula of its raw material by weight is as follows：Latex reclaimed rubber 70
Part, 25 parts of neoprene, 25 parts of dioctyl phthalate, 14 parts of stearic acid carbon fiber, 14 parts of polyester fiber, aluminum fiber 14
Part, 10 parts of N220 carbon blacks, 10 parts of precipitated calcium carbonate, 6 parts of activator, 6 parts of vulcanizing agent, 6 parts of antioxidant, 6 parts of binding agent, zinc oxide
3.5 parts, 3.5 parts of aluminium powder, 3.5 parts of titanium valve.
Present invention also offers a kind of preparation process of wear resistant automobile cover tire, include the following steps：
S1, in proportion insert latex reclaimed rubber, neoprene and dioctyl phthalate in smelting furnace, and
Melting is carried out under conditions of 250 degrees Celsius, after its thawing, added again into smelting furnace stearic acid carbon fiber, polyester fiber,
Aluminum fiber, N220 carbon blacks and precipitated calcium carbonate, then carry out mixing 6min, and during mixing thereto
Zinc oxide, aluminium powder and titanium valve are added, finally activator, vulcanizing agent, antioxidant and binding agent are added to smelting furnace, treated
It takes out after mixing, and it is spare to form mixed solution；
Mixed solution, be poured into autotyre casing mould by S2, after its shaping, takes out, forms preliminary autotyre casing,
And cooled down under field conditions (factors), then to the processing on its surface and inside, up to wear resistant automobile cover tire.
Embodiment 4
The present invention proposes a kind of wear resistant automobile cover tire formula, and the formula of its raw material by weight is as follows：Latex reclaimed rubber 75
Part, 28 parts of neoprene, 28 parts of dioctyl phthalate, 15 parts of stearic acid carbon fiber, 15 parts of polyester fiber, aluminum fiber 15
Part, 11 parts of N220 carbon blacks, 11 parts of precipitated calcium carbonate, 7 parts of activator, 7 parts of vulcanizing agent, 7 parts of antioxidant, 7 parts of binding agent, zinc oxide
4 parts, 4 parts of aluminium powder, 4 parts of titanium valve.
Present invention also offers a kind of preparation process of wear resistant automobile cover tire, include the following steps：
S1, in proportion insert latex reclaimed rubber, neoprene and dioctyl phthalate in smelting furnace, and
Melting is carried out under conditions of 270 degrees Celsius, after its thawing, added again into smelting furnace stearic acid carbon fiber, polyester fiber,
Aluminum fiber, N220 carbon blacks and precipitated calcium carbonate, then carry out mixing 7min, and during mixing thereto
Zinc oxide, aluminium powder and titanium valve are added, finally activator, vulcanizing agent, antioxidant and binding agent are added to smelting furnace, treated
It takes out after mixing, and it is spare to form mixed solution；
Mixed solution, be poured into autotyre casing mould by S2, after its shaping, takes out, forms preliminary autotyre casing,
And cooled down under field conditions (factors), then to the processing on its surface and inside, up to wear resistant automobile cover tire.
Embodiment 5
The present invention proposes a kind of wear resistant automobile cover tire formula, and the formula of its raw material by weight is as follows：Latex reclaimed rubber 80
Part, 30 parts of neoprene, 30 parts of dioctyl phthalate, 16 parts of stearic acid carbon fiber, 16 parts of polyester fiber, aluminum fiber 16
Part, 12 parts of N220 carbon blacks, 12 parts of precipitated calcium carbonate, 8 parts of activator, 8 parts of vulcanizing agent, 8 parts of antioxidant, 8 parts of binding agent, zinc oxide
5 parts, 5 parts of aluminium powder, 5 parts of titanium valve.
Present invention also offers a kind of preparation process of wear resistant automobile cover tire, include the following steps：
S1, in proportion insert latex reclaimed rubber, neoprene and dioctyl phthalate in smelting furnace, and
Melting is carried out under conditions of 300 degrees Celsius, after its thawing, added again into smelting furnace stearic acid carbon fiber, polyester fiber,
Aluminum fiber, N220 carbon blacks and precipitated calcium carbonate, then carry out mixing 8min, and during mixing thereto
Zinc oxide, aluminium powder and titanium valve are added, finally activator, vulcanizing agent, antioxidant and binding agent are added to smelting furnace, treated
It takes out after mixing, and it is spare to form mixed solution；
Mixed solution, be poured into autotyre casing mould by S2, after its shaping, takes out, forms preliminary autotyre casing,
And cooled down under field conditions (factors), then to the processing on its surface and inside, up to wear resistant automobile cover tire.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (9)
1. a kind of wear resistant automobile cover tire formula, it is characterised in that the formula of its raw material by weight is as follows：Latex reclaimed rubber 60-80
Part, 20-30 parts of neoprene, 20-30 parts of dioctyl phthalate, 12-16 parts of stearic acid carbon fiber, polyester fiber 12-16
Part, 12-16 parts of aluminum fiber, 8-12 parts of N220 carbon blacks, 8-12 parts of precipitated calcium carbonate, 4-8 parts of activator, 4-8 parts of vulcanizing agent, prevent always
4-8 parts of agent, 4-8 parts of binding agent, 2-5 parts of zinc oxide, 2-5 parts of aluminium powder, 2-5 parts of titanium valve.
2. wear resistant automobile cover tire formula according to claim 1, it is characterised in that latex reclaimed rubber, neoprene, adjacent benzene
The weight ratio of diformazan dioctyl phthalate is 65-75: 23-28: 23-28.
3. wear resistant automobile cover tire formula according to claim 1, it is characterised in that stearic acid carbon fiber, polyester fiber, aluminium
The weight ratio of fiber is 13-15: 13-15: 13-15.
4. wear resistant automobile cover tire formula according to claim 1, it is characterised in that N220 carbon blacks, the weight of precipitated calcium carbonate
Amount is than being 9-11: 9-11.
5. wear resistant automobile cover tire formula according to claim 1, it is characterised in that activator, vulcanizing agent, antioxidant, viscous
The weight ratio for tying agent is 5-7: 5-7: 5-7: 5-7.
6. wear resistant automobile cover tire formula according to claim 1, it is characterised in that zinc oxide, aluminium powder, the weight ratio of titanium valve
For 3-4: 3-4: 3-4.
7. the wear resistant automobile cover tire formula according to claim 2-6, it is characterised in that the formula of its raw material by weight is such as
Under：
65-75 parts of latex reclaimed rubber, 23-28 parts of neoprene, 23-28 parts of dioctyl phthalate, stearic acid carbon fiber 13-
15 parts, 13-15 parts of polyester fiber, 13-15 parts of aluminum fiber, 9-11 parts of N220 carbon blacks, 9-11 parts of precipitated calcium carbonate, activator 5-7
Part, 5-7 parts of vulcanizing agent, 5-7 parts of antioxidant, 5-7 parts of binding agent, 3-4 parts of zinc oxide, 3-4 parts of aluminium powder, 3-4 parts of titanium valve.
8. wear resistant automobile cover tire formula according to claim 1, it is characterised in that the optimization formula of its raw material by weight is such as
Under：
70 parts of latex reclaimed rubber, 25 parts of neoprene, 25 parts of dioctyl phthalate, 14 parts of stearic acid carbon fiber, polyester are fine
Dimension 14 parts, 14 parts of aluminum fiber, 10 parts of N220 carbon blacks, 10 parts of precipitated calcium carbonate, 6 parts of activator, 6 parts of vulcanizing agent, 6 parts of antioxidant,
6 parts of binding agent, 3.5 parts of zinc oxide, 3.5 parts of aluminium powder, 3.5 parts of titanium valve.
9. a kind of preparation process of wear resistant automobile cover tire according to claim 1, it is characterised in that include the following steps：
S1, in proportion insert latex reclaimed rubber, neoprene and dioctyl phthalate in smelting furnace, and in 200-
Melting is carried out under conditions of 300 degrees Celsius, after its thawing, added again into smelting furnace stearic acid carbon fiber, polyester fiber,
Aluminum fiber, N220 carbon blacks and precipitated calcium carbonate, then carry out mixing 4-8min, and to it during mixing
Middle addition zinc oxide, aluminium powder and titanium valve, finally add activator, vulcanizing agent, antioxidant and binding agent to smelting furnace,
Treat it after mixing, take out, it is spare to form mixed solution；
Mixed solution, be poured into autotyre casing mould by S2, after its shaping, takes out, and forms preliminary autotyre casing, and
Cooled down under natural conditions, then to the processing on its surface and inside, up to wear resistant automobile cover tire.