CN107935160A - A kind of polyacrylamide sewage water inorganic agent - Google Patents
A kind of polyacrylamide sewage water inorganic agent Download PDFInfo
- Publication number
- CN107935160A CN107935160A CN201711213482.9A CN201711213482A CN107935160A CN 107935160 A CN107935160 A CN 107935160A CN 201711213482 A CN201711213482 A CN 201711213482A CN 107935160 A CN107935160 A CN 107935160A
- Authority
- CN
- China
- Prior art keywords
- tio
- polyacrylamide
- inorganic agent
- parts
- sewage water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of polyacrylamide sewage water inorganic agent, it is made of the raw material of following parts by weight:10~15 parts of polyacrylamide, 2~3 parts of medical stone, 4~7 parts of titanium dioxide multilayer coating structure thing;The preparation method of titanium dioxide multilayer coating structure thing is as follows:To TiO2Dispersant is added in solution, adjusting pH value is pre-dispersed to 9~10 progress, at 40~50 DEG C, adds TiO2The Al2O3 of quality 0.1~0.3%, adjusts pH value of solution to 8.5~9.5 with aluminum sulfate, is aged 2~3h;Then dispersant is added again under heat-retaining condition, stirred evenly, add TiO2The Al2O3 of quality 0.01~0.03%, is aged 2~3h, filters, dry, to obtain the final product.The additive of the present invention can improve efficiency of sludge treatment, so as to effectively prevent and contain the outburst of sludge bulking.
Description
Technical field
The invention belongs to technical field of sewage, and in particular to a kind of polyacrylamide sewage water inorganic agent.
Background technology
City domestic sewage generally uses active sludge treatment process, if A/O techniques are wherein common one kind, many institutes
It is well known that active sludge treatment process sludge bulking incidence is high, the incidence of even European and American developed countries is all up to
50~60%, the incidence of city domestic sewage treatment plants at different levels of China is with regard to higher.Once occurring, it endangers pole for sludge bulking
To be serious, not only make sludge loss, go out aqueous suspension (SS) severe overweight, but also be also greatly reduced the place of sewage disposal system
Reason ability, while need considerable time ability recovery system normal.Sewage disposal system for using activated sludge process,
Active pollution index is made of der Pilz and zoogloea, and der Pilz is attached on der Pilz as skeleton, zoogloea so that
Sludge flco has preferable flocculation, sedimentation and concentration performance.When der Pilz amount reproduction, when its quantity is close to zoogloea, silk
Shape bacterium stretches out from sludge flco, forms the activated sludge skeleton of " seta ball " shape, these stretch to countless " tentacles " of outside, resistance
Hindered the compression between flco, sludge bulking just there occurs, if not containing the further breeding of der Pilz, once the number of der Pilz
Amount exceedes zoogloea, and stretching out the tentacle of zoogloea, to may be prevented from flco agglomerating so that and flco is loose, and settling property substantially reduces,
Sludge bulking will be broken out.More than 90% sludge bulking is all related with the hyper-proliferative of der Pilz in activated sludge bulking,
That is der Pilz hyper-proliferative is controlled with regard to the generation of sludge bulking can be controlled.
The content of the invention
The technical problem to be solved in the present invention is to provide one kind prevention and containment der Pilz excessive multiplication, caused dirt is avoided
The sewage-treating agent of mud expansion, and can effectively improve effluent index.
Technical solution provided by the invention is a kind of polyacrylamide sewage water inorganic agent, by the raw material group of following parts by weight
Into:10~15 parts of polyacrylamide, 2~3 parts of medical stone, 4~7 parts of titanium dioxide multilayer coating structure thing;
The preparation method of titanium dioxide multilayer coating structure thing is as follows:To TiO2Dispersant is added in solution, aluminum sulfate adjusts pH
Value is pre-dispersed to 9~10 progress, at 40~50 DEG C, adds TiO2The Al2O3 of quality 0.1~0.3%, is adjusted molten with aluminum sulfate
Liquid pH to 8.5~9.5, is aged 2~3h;Then dispersant is added again under heat-retaining condition, stirred evenly, add TiO2Quality 0.01
~0.03% Al2O3, is aged 2~3h, filters, dry, to obtain the final product.
During first time alumina-coated, the additive amount of aluminium oxide is few, is only the 0.1~0.3% of titania weight, bag
It is relatively low to cover temperature, is only 40~50 DEG C, aluminium oxide forms loose island cladding in titanium dioxide surface at this time, coats very dilute
Dredge.Since first time covering amount is less, substantial amounts of titanium dioxide is there remains in solution, continues to add dispersant, titanium dioxide exists
Extremely it is easily adsorbed on the loose island surface of the titanium dioxide granule of oxidized aluminium cladding, adds under the action of dispersant
Aluminium oxide carries out second of alumina-coated, and temperature of plate is still maintained at 40~50 DEG C at this time, therefore, continues in titanium dioxide
Surface forms more sparse island cladding.It is coated on titanium dioxide surface, leaves larger since aluminium oxide is sparse thin
Gap, and aperture diameter is more than der Pilz tentacle diameter, and der Pilz tentacle can be extend into inside inorganic agent, and titanium dioxide is only
Special grid system, der Pilz tentacle can be made a noise and snarled, since der Pilz tentacle is generally longer, the application uses multilayer coating structure
Structure, can make a noise and snarl der Pilz tentacle, greatly reduce der Pilz specific surface area, contain that the competition of der Pilz and zoogloea is excellent
Gesture, keeps strong status of the zoogloea in substrate competition, improves efficiency of sludge treatment, so as to effectively prevent and contain that sludge is swollen
Swollen outburst.
TiO2The mass concentration of solution is 20~30%.
Institute's dispersant is calgon.
The additive amount of calgon is TiO2The 0.1~0.2% of weight.
The drying is that filter cake is baked 12~24h at 105~120 DEG C.
The preparation method of additive of the present invention is:Polyacrylamide, medical stone, titanium dioxide multilayer coating structure thing are mixed
Close, crush, to obtain the final product.
The application method of this product:Launched in the water inlet of sewage treatment plants (using active sludge treatment process) dirty
Water treatment agent, as wastewater influent COD > 100mg/L, 5~10kg is launched by sewage per ton;When wastewater influent COD concentration is 50
During~100mg/L, 2~5kg is launched by sewage per ton;When wastewater influent COD concentration is 30~50mg/L, thrown by sewage per ton
Put 0.5~2kg.
Compared with prior art, additive of the invention uses multilayer coating structure technique, can snarl der Pilz tentacle layer by layer, greatly
It is big to reduce der Pilz specific surface area, contain the competitive advantage of der Pilz and zoogloea, keep zoogloea having in substrate competition
Power status, improves efficiency of sludge treatment, so as to effectively prevent and contain the outburst of sludge bulking.
Embodiment
The present invention is further elaborated for specific examples below, but not as a limitation of the invention.
Embodiment 1
1) to the TiO that mass concentration is 20%2Calgon is added in solution, the additive amount of calgon is TiO2
The 0.1% of weight, aluminum sulfate adjusting pH value is pre-dispersed to 9 progress, at 40 DEG C, adds TiO2The Al2O3 of quality 0.1%, is used
Aluminum sulfate adjusts pH value of solution to 8.5, is aged 2h;Then calgon is added again under heat-retaining condition, calgon
Additive amount is TiO2The 0.1% of weight, stirs evenly, and adds TiO2The AL2O3 of quality 0.01%, is aged 2h, filtering, dries at 105 DEG C
12h processed, up to titanium dioxide multilayer coating structure thing.
2) by polyacrylamide 10kg, medical stone 2kg, titanium dioxide multilayer coating structure thing 4kg co-grindings, to obtain the final product.
Embodiment 2
1) to the TiO that mass concentration is 30%2Calgon is added in solution, the additive amount of calgon is TiO2
The 0.2% of weight, aluminum sulfate adjusting pH value is pre-dispersed to 10 progress, at 50 DEG C, adds TiO2The Al2O3 of quality 0.3%, is used
Aluminum sulfate adjusts pH value of solution to 9.5, is aged 3h;Then calgon is added again under heat-retaining condition, calgon
Additive amount is TiO2The 0.2% of weight, stirs evenly, and adds TiO2The AL2O3 of quality 0.03%, is aged 3h, filtering, dries at 120 DEG C
24h processed, up to titanium dioxide multilayer coating structure thing.
2) by polyacrylamide 15kg, medical stone 3kg, titanium dioxide multilayer coating structure thing 7kg co-grindings, to obtain the final product.
Embodiment 3
1) to the TiO that mass concentration is 25%2Calgon is added in solution, the additive amount of calgon is TiO2
The 0.15% of weight, aluminum sulfate adjusting pH value is pre-dispersed to 9.5 progress, at 45 DEG C, adds TiO2The Al2O3 of quality 0.2%,
PH value of solution is adjusted to 9 with aluminum sulfate, is aged 2.5h;Then calgon, calgon are added again under heat-retaining condition
Additive amount be TiO2The 0.15% of weight, stirs evenly, and adds TiO2The AL2O3 of quality 0.02%, is aged 2.5h, filtering, 115
18h is baked at DEG C, up to titanium dioxide multilayer coating structure thing.
2) by polyacrylamide 13kg, medical stone 2.5kg, titanium dioxide multilayer coating structure thing 6kg co-grindings, to obtain the final product.
Embodiment 4
1) to the TiO that mass concentration is 20%2Calgon is added in solution, the additive amount of calgon is TiO2
The 0.2% of weight, aluminum sulfate adjusting pH value is pre-dispersed to 9 progress, at 50 DEG C, adds TiO2The Al2O3 of quality 0.1%, is used
Aluminum sulfate adjusts pH value of solution to 9.5, is aged 2h;Then calgon is added again under heat-retaining condition, calgon
Additive amount is TiO2The 0.1% of weight, stirs evenly, and adds TiO2The AL2O3 of quality 0.03%, is aged 2h, filtering, dries at 120 DEG C
12h processed, up to titanium dioxide multilayer coating structure thing.
2) by polyacrylamide 10kg, medical stone 3kg, titanium dioxide multilayer coating structure thing 4kg co-grindings, to obtain the final product.
Experimental example
By taking certain municipal sewage plant as an example, using A/O treatment process, table 1 connects in April, 1~2017 for the factory 2017 year
Actual operating data four months continuous, its water outlet reach《Urban wastewater treatment firm pollutant emission standard》(GB18918-2002)
Middle secondary standard.Applicant carried out launching the experiment of sewage-treating agent continuous four days of April 1~4 in 2017, this four days respectively
The sewage-treating agent of the embodiment of the present invention 1~4 is added in water inlet, and is adjusted according to same day inflow and inlet COD concentration
Injected volume, detection water outlet are fully achieved《Urban wastewater treatment firm pollutant emission standard》(GB18918-2002) level-one A is marked in
Standard, refers to and is shown in Table 2.
Table 1
Table 2
Claims (5)
- A kind of 1. polyacrylamide sewage water inorganic agent, it is characterised in that:It is made of the raw material of following parts by weight:Polyacrylamide 10 ~15 parts, 2~3 parts of medical stone, 4~7 parts of titanium dioxide multilayer coating structure thing;The preparation method of titanium dioxide multilayer coating structure thing is as follows:To TiO2Dispersant is added in solution, aluminum sulfate adjusts pH value to 9 ~10 progress are pre-dispersed, at 40~50 DEG C, add TiO2The Al2O3 of quality 0.1~0.3%, pH value of solution is adjusted with aluminum sulfate To 8.5~9.5,2~3h is aged;Then dispersant is added again under heat-retaining condition, stirred evenly, add TiO2Quality 0.01~ 0.03% Al2O3, is aged 2~3h, filters, dry, to obtain the final product.
- 2. polyacrylamide sewage water inorganic agent according to claim 1, it is characterised in that:TiO2The mass concentration of solution is 20~30%.
- 3. polyacrylamide sewage water inorganic agent according to claim 1, it is characterised in that:Institute's dispersant is six inclined phosphorus Sour sodium.
- 4. polyacrylamide sewage water inorganic agent according to claim 3, it is characterised in that:The each addition of calgon Measure as TiO2The 0.1~0.2% of weight.
- 5. polyacrylamide sewage water inorganic agent according to claim 1, it is characterised in that:The drying is that filter cake exists 12~24h is baked at 105~120 DEG C.