CN107746105A

CN107746105A - A kind of sewage-treating agent

Info

Publication number: CN107746105A
Application number: CN201711213474.4A
Authority: CN
Inventors: 唐毅
Original assignee: Individual
Current assignee: Individual
Priority date: 2017-11-28
Filing date: 2017-11-28
Publication date: 2018-03-02

Abstract

The invention provides a kind of sewage-treating agent, its preparation method are as follows：To TiO₂Dispersant is added in solution, regulation pH value is pre-dispersed to 9~10 progress, at 40~50 DEG C, adds TiO₂The SiO of quality 0.1~0.3%₂, pH value of solution is adjusted to 8.5~9.5 with sodium metasilicate, is aged 2~3h；Then dispersant is added again under heat-retaining condition, stirred evenly, add TiO₂The SiO of quality 0.01~0.03%₂, 2~3h is aged, is filtered, dries, produces.The additive of the present invention uses multilayer coating structure technique, der Pilz tentacle can be snarled layer by layer, greatly reduce der Pilz specific surface area, contain the competitive advantage of der Pilz and zoogloea, keep strong status of the zoogloea in substrate competition, efficiency of sludge treatment is improved, so as to effectively prevent and contain the outburst of sludge bulking.

Description

A kind of sewage-treating agent

Technical field

The invention belongs to technical field of sewage, and in particular to a kind of sewage-treating agent.

Background technology

City domestic sewage typically uses active sludge treatment process, if A/O techniques are wherein conventional one kind, many institutes It is well known that active sludge treatment process sludge bulking incidence is high, the incidence of even European and American developed countries is all up to 50~60%, the incidence of city domestic sewage treatment plants at different levels of China is just higher.Once occurring, it endangers pole for sludge bulking To be serious, not only make sludge loss, go out aqueous suspension (SS) severe overweight, and be also greatly reduced the place of sewage disposal system Reason ability, while need considerable time ability recovery system normal.Sewage disposal system for using activated sludge process, Active pollution index is made up of der Pilz and zoogloea, and der Pilz is attached on der Pilz as skeleton, zoogloea so that Sludge flco has preferably flocculation, sedimentation and concentration performance.When der Pilz amount reproduction, when its quantity is close to zoogloea, silk Shape bacterium stretches out from sludge flco, forms the activated sludge skeleton of " seta ball " shape, and these stretch to countless " tentacles " of outside, resistance Hindered the compression between flco, sludge bulking just there occurs, if not containing the further breeding of der Pilz, once the number of der Pilz Amount exceedes zoogloea, and stretching out the tentacle of zoogloea, to may be prevented from flco agglomerating so that and flco is loose, and settling property substantially reduces, Sludge bulking will break out.More than 90% sludge bulking is all relevant with the hyper-proliferative of der Pilz in activated sludge bulking, That is der Pilz hyper-proliferative is controlled with regard to the generation of sludge bulking can be controlled.

The content of the invention

The technical problem to be solved in the present invention is to provide one kind prevention and containment der Pilz excessive multiplication, caused dirt is avoided The sewage-treating agent of mud expansion, and can effectively improve effluent index.

Technical scheme provided by the invention is a kind of sewage-treating agent, and its preparation method is as follows：To TiO₂Added in solution Dispersant, sodium metasilicate regulation pH value is pre-dispersed to 9~10 progress, at 40~50 DEG C, adds TiO₂Quality 0.1~0.3% SiO₂, pH value of solution is adjusted to 8.5~9.5 with sodium metasilicate, is aged 2~3h；Then dispersant is added again under heat-retaining condition, stir It is even, add TiO₂The SiO of quality 0.01~0.03%₂, 2~3h is aged, is filtered, dries, produces.

During first time coated with silica, the addition of silica is few, only the 0.1 of titania weight~ 0.3%, temperature of plate is relatively low, only 40~50 DEG C, and now silica forms loose island cladding, bag in titanium dioxide surface Cover very sparse.Because first time covering amount is less, substantial amounts of titanium dioxide is there remains in solution, continues to add dispersant, Titanium dioxide is extremely easily adsorbed at the loose island of the titanium dioxide granule through coated with silica in the presence of dispersant On surface, add silica and carry out second of coated with silica, now temperature of plate is still maintained at 40~50 DEG C, because This, continues to form more sparse island cladding in titanium dioxide surface.Thin dioxy is coated on because silica is sparse Change on titanium surface, leave larger gap, and aperture diameter is more than der Pilz tentacle diameter, der Pilz tentacle can extend into processing Inside agent, and the grid system that titanium dioxide is unique, can snarl der Pilz tentacle is noisy, due to der Pilz tentacle typically compared with Long, the application uses multilayer coating structure, can make a noise and snarl der Pilz tentacle, greatly reduces der Pilz specific surface area, contains Der Pilz and the competitive advantage of zoogloea, strong status of the zoogloea in substrate competition is kept, improves efficiency of sludge treatment, from And effectively prevent and contain the outburst of sludge bulking.

TiO₂The mass concentration of solution is 20~30%.

Institute's dispersant is calgon.

The addition of calgon is TiO₂The 0.1~0.2% of weight.

The drying is that filter cake is baked into 12~24h at 105~120 DEG C.

The application method of this product：Launched in the water inlet of sewage treatment plants (using active sludge treatment process) dirty Water treatment agent, as wastewater influent COD ＞ 100mg/L, 5~10kg is launched by sewage per ton；When wastewater influent COD concentration is 50 During~100mg/L, 2~5kg is launched by sewage per ton；When wastewater influent COD concentration is 30~50mg/L, thrown by sewage per ton Put 0.5~2kg.

Compared with prior art, additive of the invention uses multilayer coating structure technique, can snarl der Pilz tentacle layer by layer, greatly It is big to reduce der Pilz specific surface area, contain the competitive advantage of der Pilz and zoogloea, keep zoogloea having in substrate competition Power status, efficiency of sludge treatment is improved, so as to effectively prevent and contain the outburst of sludge bulking.

Embodiment

The present invention is further elaborated for specific examples below, but not as a limitation of the invention.

Embodiment 1

To the TiO that mass concentration is 20%₂Calgon is added in solution, the addition of calgon is TiO₂Weight The 0.1% of amount, sodium metasilicate regulation pH value is pre-dispersed to 9 progress, at 40 DEG C, adds TiO₂The SiO of quality 0.1%₂, use silicic acid Sodium adjusts pH value of solution to 8.5, is aged 2h；Then calgon, the addition of calgon are added again under heat-retaining condition Measure as TiO₂The 0.1% of weight, is stirred evenly, and adds TiO₂The SiO of quality 0.01%₂, 2h is aged, filtering, is baked at 105 DEG C 12h, produce.

Embodiment 2

To the TiO that mass concentration is 30%₂Calgon is added in solution, the addition of calgon is TiO₂Weight The 0.2% of amount, sodium metasilicate regulation pH value is pre-dispersed to 10 progress, at 50 DEG C, adds TiO₂The SiO of quality 0.3%₂, use silicic acid Sodium adjusts pH value of solution to 9.5, is aged 3h；Then calgon, the addition of calgon are added again under heat-retaining condition Measure as TiO₂The 0.2% of weight, is stirred evenly, and adds TiO₂The SiO of quality 0.03%₂, 3h is aged, filtering, is baked at 120 DEG C 24h, produce.

Embodiment 3

To the TiO that mass concentration is 25%₂Calgon is added in solution, the addition of calgon is TiO₂Weight The 0.15% of amount, sodium metasilicate regulation pH value is pre-dispersed to 9.5 progress, at 45 DEG C, adds TiO₂The SiO of quality 0.2%₂, use silicon Sour sodium adjusts pH value of solution to 9, is aged 2.5h；Then calgon is added again under heat-retaining condition, calgon adds Dosage is TiO₂The 0.15% of weight, is stirred evenly, and adds TiO₂The SiO of quality 0.02%₂, 2.5h is aged, filtering, is dried at 115 DEG C 18h processed, is produced.

Embodiment 4

To the TiO that mass concentration is 20%₂Calgon is added in solution, the addition of calgon is TiO₂Weight The 0.2% of amount, sodium metasilicate regulation pH value is pre-dispersed to 9 progress, at 50 DEG C, adds TiO₂The SiO of quality 0.1%₂, use silicic acid Sodium adjusts pH value of solution to 9.5, is aged 2h；Then calgon, the addition of calgon are added again under heat-retaining condition Measure as TiO₂The 0.1% of weight, is stirred evenly, and adds TiO₂The SiO of quality 0.03%₂, 2h is aged, filtering, is baked at 120 DEG C 12h, produce.

Experimental example

By taking certain municipal sewage plant as an example, using A/O handling process, table 1 is that the factory 2017 year connects in April, 1~2017 Continuous four months actual operating data, its water outlet reach《Urban wastewater treatment firm pollutant emission standard》(GB18918-2002) Middle secondary standard.Applicant carried out launching the experiment of sewage-treating agent continuous four days of April 1~4 in 2017, and this four days respectively The sewage-treating agent of the embodiment of the present invention 1~4 is added in water inlet, and is adjusted according to same day inflow and inlet COD concentration Injected volume, detection water outlet are fully achieved《Urban wastewater treatment firm pollutant emission standard》(GB18918-2002) one-level A is marked in Standard, refer to and be shown in Table 2.

Table 1

Table 2

Claims

A kind of 1. sewage-treating agent, it is characterised in that：Its preparation method is as follows：To TiO₂Dispersant is added in solution, sodium metasilicate is adjusted It is pre-dispersed to 9~10 progress to save pH value, at 40~50 DEG C, adds TiO₂The SiO of quality 0.1~0.3%₂, adjusted with sodium metasilicate PH value of solution is aged 2~3h to 8.5~9.5；Then dispersant is added again under heat-retaining condition, stirred evenly, add TiO₂Quality 0.01~0.03% SiO₂, 2~3h is aged, is filtered, dries, produces.
2. sewage-treating agent according to claim 1, it is characterised in that：TiO₂The mass concentration of solution is 20~30%.
3. sewage-treating agent according to claim 1, it is characterised in that：Institute's dispersant is calgon.
4. sewage-treating agent according to claim 3, it is characterised in that：The each addition of calgon is TiO₂Weight The 0.1~0.2% of amount.
5. sewage-treating agent according to claim 1, it is characterised in that：The drying be by filter cake at 105~120 DEG C Bake 12~24h.