CN107916033A - A kind of coating on coil-winding circle - Google Patents

A kind of coating on coil-winding circle Download PDF

Info

Publication number
CN107916033A
CN107916033A CN201711239463.3A CN201711239463A CN107916033A CN 107916033 A CN107916033 A CN 107916033A CN 201711239463 A CN201711239463 A CN 201711239463A CN 107916033 A CN107916033 A CN 107916033A
Authority
CN
China
Prior art keywords
parts
coil
antioxidant
coating
hours
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711239463.3A
Other languages
Chinese (zh)
Inventor
梅和润
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Shang Qin Electronic Technology Co Ltd
Original Assignee
Anhui Shang Qin Electronic Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Shang Qin Electronic Technology Co Ltd filed Critical Anhui Shang Qin Electronic Technology Co Ltd
Priority to CN201711239463.3A priority Critical patent/CN107916033A/en
Publication of CN107916033A publication Critical patent/CN107916033A/en
Withdrawn legal-status Critical Current

Abstract

A kind of coating on coil-winding circle, is related to coil processing technical field, it is characterised in that：It is made up of the following materials in parts by weight, 11 17 parts of resin, 12 6 10 parts of nylon, 6 11 parts attapulgite modified, 25 parts of dihydromethyl propionic acid, 15 points of Aerosol OT, 25 parts of butyl acrylate, 4,14 parts of 4 di-2-ethylhexylphosphine oxides (2,6 DI-tert-butylphenol compounds), 14 parts of benzoin dimethylether, 26 parts of 2 benzylimidazoline, 16 parts of 4 tert-butyl phenol, 37 parts of pentaerythritol triacrylate, 8 15 parts of defoamer, 8 15 parts of antioxidant, 5 10 parts of biomass auxiliary material, 20 27 parts of deionized water.The method of the present invention is reasonable, easy to operate, wear-resisting, high temperature resistant.

Description

A kind of coating on coil-winding circle
Technical field
The present invention relates to coil to process technical field, and in particular to the coating on a kind of coil-winding circle.
Background technology
Coil is often referred to wire winding in a ring, and most common coil application has:Motor, inductance, transformer and annular Antenna etc..
Coil in circuit refers to inductor.It is that guide line one piece one is wound up, conducting wire insulate each other, and insulate Pipe can be hollow, can also include iron core or powder core, abbreviation inductance.Inductance can be divided into fixed inductance and can power transformation again Sense, fixed inductance coil abbreviation inductance or coil.Represented with L, unit has Henry (H), millihenry (mH), microhenry (uH), 1H =10^3mH=10^6uH.
Inductance is classified：
By inductance formal classification:Fixed inductance, variable inductance.
By magnetizer qualitative classification:Hollow coil, ferrite coil, iron-core coil, copper core coil.
Classify by job specification:Aerial coil, oscillator coil, choking-winding, trap coil, deflection coil.
Classify by winding structure:Single layer coil, lattice coil, honeycomb coil.
And coil is typically all by filament to be wrapped in what is used on wire turn, but some around wire turn because of using one The appearance for the problems such as easily occurring wearing after the section time or causing outer surface cracking because of long-term heating, come off, so It is easy for causing damage and can not uses, or even the generation for the big problem burned occurs.
The content of the invention
The technical problems to be solved by the invention be to overcome existing technological deficiency provide a kind of method rationally, operation side Just the coating on a kind of, wear-resisting, heat safe coil-winding circle.
The technical problems to be solved by the invention are realized using following technical solution：
A kind of coating on coil-winding circle, it is characterised in that：It is made up of the following materials in parts by weight,
11-17 parts of resin, 126-10 parts of nylon, 6-11 parts attapulgite modified, 2-5 parts of dihydromethyl propionic acid, butanedioic acid 1-5 points of di-isooctyl sodium sulfonate, 2-5 parts of butyl acrylate, 1-4 parts of 4,4- methylene-bis(2,6-di-t-butyl phenol)s, rest in peace Fragrant double 1-4 parts of methyl ether, 2-6 parts of 2- benzylimidazolines, 1-6 parts of 4-TBP, 3-7 parts of pentaerythritol triacrylate, disappear 8-15 parts of infusion, 8-15 parts of antioxidant, 5-10 parts of biomass auxiliary material, 20-27 parts of deionized water；
The resin is polyvinyl resin, one kind in alkyd resin, epoxy resin, Lauxite, polyamide；
The antioxidant is antioxidant A W, one kind in anti-aging agent RD, antioxidant A, antioxidant D, antioxidant CPPD；
The defoamer for silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene pentaerythrite ether, One kind in polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether；
The attapulgite modified preparation method is to grind attapulgite and cross 400-500 mesh sieves, be then placed on 70 Toasted 40 minutes at a temperature of DEG C, then add the pure water of 0.73 times of its quality, 30 are stirred under 90 DEG C of temperature constant state Minute, tributyl phosphate is then added, and 70 DEG C are cooled to, 1.8 hours are then stirred, re-dry, re-grind, and obtains It is attapulgite modified；
The mass ratio of the tributyl phosphate and attapulgite is 1：2.9；
The biology auxiliary material is made up of the following materials in parts by weight,
1 part of blue stone, 2 parts of realgar, 3 parts of honeycomb, 4 parts of garlic, 5 parts of Chinese prickly ash, 6 parts of the tuber of stemona, 7 parts of betel nut, 1 part of Chinese honey locust, cnidium monnieri 2 parts of son, 3 parts of chaulmoogra, 4 parts of corter pseudolaricis, 5 parts of Fructus meliae toosendan, 6 parts of hairyvein agrimony, 7 parts of calamine；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant 4-5 hour of middle baking, is then placed in equipment and grinds and cross 400-500 mesh sieves, the clear water for adding 0.7 times of quality of materials stirs 1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
The preparation method of coating on a kind of coil-winding circle is,
I by resin, nylon 12, attapulgite modified, dihydromethyl propionic acid, Aerosol OT, acrylic acid Butyl ester, 4,4- methylene-bis(2,6-di-t-butyl phenol)s, benzoin dimethylether, defoamer, deionized water are put into stirring In the reaction kettle of device, 160 DEG C are being uniformly heated to always from 40, is continuing 6.5 hours；
During 2- benzylimidazolines, 4-TBP, pentaerythritol triacrylate, antioxidant are added to I by II, and rise Warm 25-35 DEG C, continue to mix 4 hours；
70-80 DEG C is cooled to after the completion of III mixing and adds biomass auxiliary material, 45-55 DEG C is cooled to after mixing 1 hour, Continue to mix 2 hours.
Beneficial effects of the present invention are：Above-mentioned material is combined mixing, react, heat up, by way of mold And processing, the performance of product have obtained more powerful optimization and release, and it is almost non-toxic pollution-free, for environment, human body All it is not injure and destroy, and with the addition of the material of biomass, is also one very good with biological coating now Selection, nontoxic and pollution-free and of low cost, product has good water proof, moisture-proof, insulation, measuring body effect, and uses the longevity Life adds.The method of the present invention is reasonable, easy to operate, wear-resisting, high temperature resistant.
Embodiment
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention easy to understand, below into One step illustrates the present invention.
Embodiment 1
A kind of coating on coil-winding circle, it is characterised in that：It is made up of the following materials in parts by weight,
11 parts of resin, 126 parts of nylon, 6 parts attapulgite modified, 2 parts of dihydromethyl propionic acid, butanedioic acid di-isooctyl sulfonic acid Sodium 1 divides, 2 parts of butyl acrylate, 1 part of 4,4- methylene-bis(2,6-di-t-butyl phenol)s, 1 part of benzoin dimethylether, 2- phenyl 2 parts of imidazoline, 1 part of 4-TBP, 3 parts of pentaerythritol triacrylate, 8 parts of defoamer, 8 parts of antioxidant, biomass are auxiliary Expect 5 parts, 20 parts of deionized water；
The resin is polyvinyl resin, one kind in alkyd resin, epoxy resin, Lauxite, polyamide；
The antioxidant is antioxidant A W, one kind in anti-aging agent RD, antioxidant A, antioxidant D, antioxidant CPPD；
The defoamer for silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene pentaerythrite ether, One kind in polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether；
The attapulgite modified preparation method is to grind attapulgite and cross 400-500 mesh sieves, be then placed on 70 Toasted 40 minutes at a temperature of DEG C, then add the pure water of 0.73 times of its quality, 30 are stirred under 90 DEG C of temperature constant state Minute, tributyl phosphate is then added, and 70 DEG C are cooled to, 1.8 hours are then stirred, re-dry, re-grind, and obtains It is attapulgite modified；
The mass ratio of the tributyl phosphate and attapulgite is 1：2.9；
The biology auxiliary material is made up of the following materials in parts by weight,
1 part of blue stone, 2 parts of realgar, 3 parts of honeycomb, 4 parts of garlic, 5 parts of Chinese prickly ash, 6 parts of the tuber of stemona, 7 parts of betel nut, 1 part of Chinese honey locust, cnidium monnieri 2 parts of son, 3 parts of chaulmoogra, 4 parts of corter pseudolaricis, 5 parts of Fructus meliae toosendan, 6 parts of hairyvein agrimony, 7 parts of calamine；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant 4-5 hour of middle baking, is then placed in equipment and grinds and cross 400-500 mesh sieves, the clear water for adding 0.7 times of quality of materials stirs 1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
The preparation method of coating on a kind of coil-winding circle is,
I by resin, nylon 12, attapulgite modified, dihydromethyl propionic acid, Aerosol OT, acrylic acid Butyl ester, 4,4- methylene-bis(2,6-di-t-butyl phenol)s, benzoin dimethylether, defoamer, deionized water are put into stirring In the reaction kettle of device, 160 DEG C are being uniformly heated to always from 40, is continuing 6.5 hours；
During 2- benzylimidazolines, 4-TBP, pentaerythritol triacrylate, antioxidant are added to I by II, and rise Warm 25-35 DEG C, continue to mix 4 hours；
70-80 DEG C is cooled to after the completion of III mixing and adds biomass auxiliary material, 45-55 DEG C is cooled to after mixing 1 hour, Continue to mix 2 hours.
Embodiment 2
A kind of coating on coil-winding circle, it is characterised in that：It is made up of the following materials in parts by weight,
17 parts of resin, 1210 parts of nylon, 11 parts attapulgite modified, 5 parts of dihydromethyl propionic acid, butanedioic acid di-isooctyl sulphur Sour sodium 5 divides, 5 parts of butyl acrylate, 4 parts of 4,4- methylene-bis(2,6-di-t-butyl phenol)s, 4 parts of benzoin dimethylether, 2- benzene 6 parts of base imidazoline, 6 parts of 4-TBP, 7 parts of pentaerythritol triacrylate, 15 parts of defoamer, 15 parts of antioxidant, biology 10 parts of matter auxiliary material, 27 parts of deionized water；
The resin is polyvinyl resin, one kind in alkyd resin, epoxy resin, Lauxite, polyamide；
The antioxidant is antioxidant A W, one kind in anti-aging agent RD, antioxidant A, antioxidant D, antioxidant CPPD；
The defoamer for silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene pentaerythrite ether, One kind in polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether；
The attapulgite modified preparation method is to grind attapulgite and cross 400-500 mesh sieves, be then placed on 70 Toasted 40 minutes at a temperature of DEG C, then add the pure water of 0.73 times of its quality, 30 are stirred under 90 DEG C of temperature constant state Minute, tributyl phosphate is then added, and 70 DEG C are cooled to, 1.8 hours are then stirred, re-dry, re-grind, and obtains It is attapulgite modified；
The mass ratio of the tributyl phosphate and attapulgite is 1：2.9；
The biology auxiliary material is made up of the following materials in parts by weight,
1 part of blue stone, 2 parts of realgar, 3 parts of honeycomb, 4 parts of garlic, 5 parts of Chinese prickly ash, 6 parts of the tuber of stemona, 7 parts of betel nut, 1 part of Chinese honey locust, cnidium monnieri 2 parts of son, 3 parts of chaulmoogra, 4 parts of corter pseudolaricis, 5 parts of Fructus meliae toosendan, 6 parts of hairyvein agrimony, 7 parts of calamine；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant 4-5 hour of middle baking, is then placed in equipment and grinds and cross 400-500 mesh sieves, the clear water for adding 0.7 times of quality of materials stirs 1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
The preparation method of coating on a kind of coil-winding circle is,
I by resin, nylon 12, attapulgite modified, dihydromethyl propionic acid, Aerosol OT, acrylic acid Butyl ester, 4,4- methylene-bis(2,6-di-t-butyl phenol)s, benzoin dimethylether, defoamer, deionized water are put into stirring In the reaction kettle of device, 160 DEG C are being uniformly heated to always from 40, is continuing 6.5 hours；
During 2- benzylimidazolines, 4-TBP, pentaerythritol triacrylate, antioxidant are added to I by II, and rise Warm 25-35 DEG C, continue to mix 4 hours；
70-80 DEG C is cooled to after the completion of III mixing and adds biomass auxiliary material, 45-55 DEG C is cooled to after mixing 1 hour, Continue to mix 2 hours.
Embodiment 3
A kind of coating on coil-winding circle, it is characterised in that：It is made up of the following materials in parts by weight,
13 parts of resin, 128 parts of nylon, 9 parts attapulgite modified, 3 parts of dihydromethyl propionic acid, butanedioic acid di-isooctyl sulfonic acid Sodium 4 divides, 3 parts of butyl acrylate, 2 parts of 4,4- methylene-bis(2,6-di-t-butyl phenol)s, 3 parts of benzoin dimethylether, 2- phenyl 4 parts of imidazoline, 5 parts of 4-TBP, 6 parts of pentaerythritol triacrylate, 12 parts of defoamer, 13 parts of antioxidant, biomass 8 parts of auxiliary material, 25 parts of deionized water；
The resin is polyvinyl resin, one kind in alkyd resin, epoxy resin, Lauxite, polyamide；
The antioxidant is antioxidant A W, one kind in anti-aging agent RD, antioxidant A, antioxidant D, antioxidant CPPD；
The defoamer for silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene pentaerythrite ether, One kind in polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether；
The attapulgite modified preparation method is to grind attapulgite and cross 400-500 mesh sieves, be then placed on 70 Toasted 40 minutes at a temperature of DEG C, then add the pure water of 0.73 times of its quality, 30 are stirred under 90 DEG C of temperature constant state Minute, tributyl phosphate is then added, and 70 DEG C are cooled to, 1.8 hours are then stirred, re-dry, re-grind, and obtains It is attapulgite modified；
The mass ratio of the tributyl phosphate and attapulgite is 1：2.9；
The biology auxiliary material is made up of the following materials in parts by weight,
1 part of blue stone, 2 parts of realgar, 3 parts of honeycomb, 4 parts of garlic, 5 parts of Chinese prickly ash, 6 parts of the tuber of stemona, 7 parts of betel nut, 1 part of Chinese honey locust, cnidium monnieri 2 parts of son, 3 parts of chaulmoogra, 4 parts of corter pseudolaricis, 5 parts of Fructus meliae toosendan, 6 parts of hairyvein agrimony, 7 parts of calamine；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant 4-5 hour of middle baking, is then placed in equipment and grinds and cross 400-500 mesh sieves, the clear water for adding 0.7 times of quality of materials stirs 1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
The preparation method of coating on a kind of coil-winding circle is,
I by resin, nylon 12, attapulgite modified, dihydromethyl propionic acid, Aerosol OT, acrylic acid Butyl ester, 4,4- methylene-bis(2,6-di-t-butyl phenol)s, benzoin dimethylether, defoamer, deionized water are put into stirring In the reaction kettle of device, 160 DEG C are being uniformly heated to always from 40, is continuing 6.5 hours；
During 2- benzylimidazolines, 4-TBP, pentaerythritol triacrylate, antioxidant are added to I by II, and rise Warm 25-35 DEG C, continue to mix 4 hours；
70-80 DEG C is cooled to after the completion of III mixing and adds biomass auxiliary material, 45-55 DEG C is cooled to after mixing 1 hour, Continue to mix 2 hours.
A kind of coating of motor, is made up of the following materials in parts by weight,
10 parts of polyvinyl resin, 8 parts of nylon 11,5 parts of activated carbon, 3 parts of calcium propionate, 2 parts of styrene, sebacic dihydrazide 4 Part, 2 parts of anilinomethyl triethoxysilane, 3 parts of polyethyl acrylate, 3 parts of polyoxylethylene abietate, 13 parts of antioxidant A, water 20 parts；
Preparation method：Above-mentioned material is put into reaction kettle and prepares 6-8 hour in a conventional manner.
By experiment, measure 1-3 of the embodiment of the present invention and comparative example performance and effect, such as following table：
The basic principles, main features and the advantages of the invention have been shown and described above.The technology of the industry Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its Equivalent thereof.

Claims (2)

  1. A kind of 1. coating on coil-winding circle, it is characterised in that：It is made up of the following materials in parts by weight, 11-17 parts of resin, 126-10 parts of nylon, 6-11 parts attapulgite modified, 2-5 parts of dihydromethyl propionic acid, Aerosol OT 1-5 points, 2-5 parts of butyl acrylate, 1-4 parts of 4,4- methylene-bis(2,6-di-t-butyl phenol)s, 1-4 parts of benzoin dimethylether, 2- phenyl 2-6 parts of imidazoline, 1-6 parts of 4-TBP, 3-7 parts of pentaerythritol triacrylate, 8-15 parts of defoamer, antioxidant 8-15 Part, 5-10 parts of biomass auxiliary material, 20-27 parts of deionized water.
  2. 2. the coating on a kind of coil-winding circle according to claim 1, it is characterised in that：A kind of coil-winding The preparation method of coating on circle is,
    I by resin, nylon 12, attapulgite modified, dihydromethyl propionic acid, Aerosol OT, butyl acrylate, 4,4- methylene-bis(2,6-di-t-butyl phenol)s, benzoin dimethylether, defoamer, deionized water are put into the anti-of blender Answer in kettle, be uniformly heated to 160 DEG C always from 40, continuing 6.5 hours；
    During 2- benzylimidazolines, 4-TBP, pentaerythritol triacrylate, antioxidant are added to I by II, and heat up 25-35 DEG C, continue to mix 4 hours；
    70-80 DEG C is cooled to after the completion of III mixing and adds biomass auxiliary material, 45-55 DEG C is cooled to after mixing 1 hour, continues Mix 2 hours.
CN201711239463.3A 2017-11-30 2017-11-30 A kind of coating on coil-winding circle Withdrawn CN107916033A (en)