CN107903531A - 一种建筑装饰用环保pvc材料及其制备方法 - Google Patents

一种建筑装饰用环保pvc材料及其制备方法 Download PDF

Info

Publication number
CN107903531A
CN107903531A CN201711101947.1A CN201711101947A CN107903531A CN 107903531 A CN107903531 A CN 107903531A CN 201711101947 A CN201711101947 A CN 201711101947A CN 107903531 A CN107903531 A CN 107903531A
Authority
CN
China
Prior art keywords
parts
pvc
architectural decoration
benzoate
antioxidant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711101947.1A
Other languages
English (en)
Inventor
张如才
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Jiaxing Metal Materials Co Ltd
Original Assignee
Anhui Jiaxing Metal Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Jiaxing Metal Materials Co Ltd filed Critical Anhui Jiaxing Metal Materials Co Ltd
Priority to CN201711101947.1A priority Critical patent/CN107903531A/zh
Publication of CN107903531A publication Critical patent/CN107903531A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种建筑装饰用环保PVC材料及其制备方法，包括由以下重量份的原料制备而成：聚氯乙烯30‑50份、无机填料10‑15份、顺式异戊橡胶5‑10份、PVC S700树脂粉8‑15份、废旧塑料12‑15份、硅酸纤维12‑18份、方解石15‑25份、苯甲酸盐4‑9份、细孔硅胶10‑20份、甲基丙烯酸甲酯11‑17份、纳米氧化铈2‑8份、发泡助剂3‑7份、抗氧剂1‑5份和钛酸铝偶联剂2‑6份。本发明采用聚氯乙烯、无机填料、顺式异戊橡胶、PVC S700树脂粉、废旧塑料、硅酸纤维、方解石、苯甲酸盐、细孔硅胶、甲基丙烯酸甲酯、纳米氧化铈有效配比，具有良好的防腐、隔热、防水和耐火等方面的性能；可以满足建材市场的绿色环保要求，还能保证该材料像原建材一样稳定。

Description

一种建筑装饰用环保PVC材料及其制备方法
技术领域
本发明涉及建筑材料制作技术领域，具体涉及一种建筑装饰用环保PVC材料及其制备方法。
背景技术
早在上世纪四十年代人们就发现废旧塑料与 pvc 并用技术进行了研究，废旧塑料具有一定的极性，与 pvc 的溶解度参数非常接近，他们都是非晶聚合物，两者之间具有很好的相容性，因此通常将他们共混，所制得的合金材料具有优异的耐候性、耐溶剂性以及较好的力学强度和加工性能，广泛应用于密封件、电线电缆护套、油管等领域。废旧塑料与聚氯乙烯的合金材料分为交联型和非交联型，交联型的合金不溶不熔，很难再生利用，对环境造成严重污染，而非交联的合金虽然加工性能较好，但力学性能不理想。
目前，PVC 管材因具有耐腐蚀性强、强度高、刚性好等特点，被广泛应用在给水、建筑、排水、排污、化工等技术领域，是一种适用范围仅次于聚乙烯的塑料管材，但由于 PVC管材的耐磨性能较差，且不可以在恶劣的环境下使用，在很大程度上制约了 PVC 管材的使用，现有技术中有加耐腐蚀性成分的 PVC 管材，但效果较差，不能满足需求。
因此，为解决上述问题，特提供一种新的技术方案。
发明内容
为解决上述问题，本发明提供了一种建筑装饰用环保PVC材料及其制备方法。
为实现上述目的，本发明采取的技术方案为：
一种建筑装饰用环保PVC材料及其制备方法，包括由以下重量份的原料制备而成：聚氯乙烯30-50份、无机填料10-15份、顺式异戊橡胶5-10份、PVC S700树脂粉8-15份、废旧塑料12-15份、硅酸纤维12-18份、方解石15-25份、苯甲酸盐4-9份、细孔硅胶10-20份、甲基丙烯酸甲酯11-17份、纳米氧化铈2-8份、发泡助剂3-7份、抗氧剂1-5份和钛酸铝偶联剂2-6份。
一种建筑装饰用环保PVC材料，包括由以下重量份的原料制备而成：聚氯乙烯31-49份、无机填料11-14份、顺式异戊橡胶6-9份、PVC S700树脂粉9-14份、废旧塑料13-15份、硅酸纤维13-17份、方解石16-24份、苯甲酸盐5-8份、细孔硅胶12-19份、甲基丙烯酸甲酯12-16份、纳米氧化铈3-7份、发泡助剂4-6份、抗氧剂2-4份和钛酸铝偶联剂3-5份。
进一步地，一种建筑装饰用环保PVC材料，包括由以下重量份的原料制备而成：聚氯乙烯40份、无机填料12份、顺式异戊橡胶8份、PVC S700树脂粉11份、废旧塑料14份、硅酸纤维16份、方解石18份、苯甲酸盐6份、细孔硅胶16份、甲基丙烯酸甲酯13份、纳米氧化铈5份、发泡助剂5份、抗氧剂3份和钛酸铝偶联剂4份。
进一步地，所述发泡助剂为偶氮二甲酰胺或十二水硫酸铝钾；所述抗氧剂为 2，6-三级丁基 -4- 甲基苯酚、双（3，5- 三级丁基 -4- 羟基苯基）硫醚；所述钛酸铝偶联剂为邻苯二甲酸二 (2- 乙基己 ) 酯或邻苯二甲酸酯。
进一步地，一种建筑装饰用环保PVC材料的制备方法，包括如下步骤：
S1、将聚氯乙烯30-50份、PVC S700树脂粉8-15份、硅酸纤维12-18份、方解石15-25份、苯甲酸盐4-9份、细孔硅胶10-20份加入粉碎机粉碎均匀后，倒入到搅拌机中搅拌5-8min，得到混合物；
S2、将步骤S1所得的混合物中加入无机填料10-15份、顺式异戊橡胶5-10份、废旧塑料12-15份、甲基丙烯酸甲酯11-17份、发泡助剂3-7份、抗氧剂1-5份和钛酸铝偶联剂2-6份，在80-100℃下高速搅拌3-6min混合均匀，冷却之后得混合物料；
S3、将步骤S2所得的混合物料加入螺杆挤出机中，转速为50-90r/min，挤出温度为150-200℃挤出成型得到建筑装饰用环保PVC材料。
本发明采用聚氯乙烯、无机填料、顺式异戊橡胶、PVC S700树脂粉、废旧塑料、硅酸纤维、方解石、苯甲酸盐、细孔硅胶、甲基丙烯酸甲酯、纳米氧化铈有效配比，具有良好的防腐、隔热、防水和耐火等方面的性能；可以满足建材市场的绿色环保要求，还能保证该材料像原建材一样稳定，市场前景巨大。
具体实施方式
为了使本发明的目的及优点更加清楚明白，以下结合实施例对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
本发明包括由以下重量份的原料制备而成：聚氯乙烯30-50份、无机填料10-15份、顺式异戊橡胶5-10份、PVC S700树脂粉8-15份、废旧塑料12-15份、硅酸纤维12-18份、方解石15-25份、苯甲酸盐4-9份、细孔硅胶10-20份、甲基丙烯酸甲酯11-17份、纳米氧化铈2-8份、发泡助剂3-7份、抗氧剂1-5份和钛酸铝偶联剂2-6份。
一种建筑装饰用环保PVC材料，包括由以下重量份的原料制备而成：聚氯乙烯31-49份、无机填料11-14份、顺式异戊橡胶6-9份、PVC S700树脂粉9-14份、废旧塑料13-15份、硅酸纤维13-17份、方解石16-24份、苯甲酸盐5-8份、细孔硅胶12-19份、甲基丙烯酸甲酯12-16份、纳米氧化铈3-7份、发泡助剂4-6份、抗氧剂2-4份和钛酸铝偶联剂3-5份。
一种建筑装饰用环保PVC材料，包括由以下重量份的原料制备而成：聚氯乙烯40份、无机填料12份、顺式异戊橡胶8份、PVC S700树脂粉11份、废旧塑料14份、硅酸纤维16份、方解石18份、苯甲酸盐6份、细孔硅胶16份、甲基丙烯酸甲酯13份、纳米氧化铈5份、发泡助剂5份、抗氧剂3份和钛酸铝偶联剂4份。
所述发泡助剂为偶氮二甲酰胺或十二水硫酸铝钾；所述抗氧剂为 2，6- 三级丁基-4- 甲基苯酚、双（3，5- 三级丁基 -4- 羟基苯基）硫醚；所述钛酸铝偶联剂为邻苯二甲酸二 (2- 乙基己 ) 酯或邻苯二甲酸酯。
一种建筑装饰用环保PVC材料的制备方法，包括如下步骤：
S1、将聚氯乙烯30-50份、PVC S700树脂粉8-15份、硅酸纤维12-18份、方解石15-25份、苯甲酸盐4-9份、细孔硅胶10-20份加入粉碎机粉碎均匀后，倒入到搅拌机中搅拌5-8min，得到混合物；
S2、将步骤S1所得的混合物中加入无机填料10-15份、顺式异戊橡胶5-10份、废旧塑料12-15份、甲基丙烯酸甲酯11-17份、发泡助剂3-7份、抗氧剂1-5份和钛酸铝偶联剂2-6份，在80-100℃下高速搅拌3-6min混合均匀，冷却之后得混合物料；
S3、将步骤S2所得的混合物料加入螺杆挤出机中，转速为50-90r/min，挤出温度为150-200℃挤出成型得到建筑装饰用环保PVC材料。
实施例1：
一种建筑装饰用环保PVC材料的制备方法，包括如下步骤：
S1、将聚氯乙烯40份、PVC S700树脂粉11份、硅酸纤维16份、方解石18份、苯甲酸盐6份、细孔硅胶16份加入粉碎机粉碎均匀后，倒入到搅拌机中搅拌8min，得到混合物；
S2、将步骤S1所得的混合物中加入无机填料12份、顺式异戊橡胶8份、废旧塑料14份、甲基丙烯酸甲酯13份、发泡助剂5份、抗氧剂3份和钛酸铝偶联剂4份，在90℃下高速搅拌35min混合均匀，冷却之后得混合物料；
S3、将步骤S2所得的混合物料加入螺杆挤出机中，转速为60r/min，挤出温度为180℃挤出成型得到建筑装饰用环保PVC材料。
实施例2：
一种建筑装饰用环保PVC材料的制备方法，包括如下步骤：
S1、将聚氯乙烯30份、PVC S700树脂粉8份、硅酸纤维12份、方解石15份、苯甲酸盐4份、细孔硅胶10份加入粉碎机粉碎均匀后，倒入到搅拌机中搅拌5min，得到混合物；
S2、将步骤S1所得的混合物中加入无机填料10份、顺式异戊橡胶5份、废旧塑料12份、甲基丙烯酸甲酯11份、发泡助剂3份、抗氧剂1份和钛酸铝偶联剂2份，在80℃下高速搅拌3min混合均匀，冷却之后得混合物料；
S3、将步骤S2所得的混合物料加入螺杆挤出机中，转速为80r/min，挤出温度为150℃挤出成型得到建筑装饰用环保PVC材料。
实施例3：
一种建筑装饰用环保PVC材料的制备方法，包括如下步骤：
S1、将聚氯乙烯50份、PVC S700树脂粉15份、硅酸纤维18份、方解石25份、苯甲酸盐9份、细孔硅胶20份加入粉碎机粉碎均匀后，倒入到搅拌机中搅拌8min，得到混合物；
S2、将步骤S1所得的混合物中加入无机填料10份、顺式异戊橡胶5份、废旧塑料12份、甲基丙烯酸甲酯11份、发泡助剂3份、抗氧剂1份和钛酸铝偶联剂2份，在80℃下高速搅拌3min混合均匀，冷却之后得混合物料；
S3、将步骤S2所得的混合物料加入螺杆挤出机中，转速为60r/min，挤出温度为150℃挤出成型得到建筑装饰用环保PVC材料。
本发明采用聚氯乙烯、无机填料、顺式异戊橡胶、PVC S700树脂粉、废旧塑料、硅酸纤维、方解石、苯甲酸盐、细孔硅胶、甲基丙烯酸甲酯、纳米氧化铈有效配比，具有良好的防腐、隔热、防水和耐火等方面的性能；可以满足建材市场的绿色环保要求，还能保证该材料像原建材一样稳定，市场前景巨大。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以作出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (5)

1.一种建筑装饰用环保PVC材料，其特征在于，包括由以下重量份的原料制备而成：聚氯乙烯30-50份、无机填料10-15份、顺式异戊橡胶5-10份、PVC S700树脂粉8-15份、废旧塑料12-15份、硅酸纤维12-18份、方解石15-25份、苯甲酸盐4-9份、细孔硅胶10-20份、甲基丙烯酸甲酯11-17份、纳米氧化铈2-8份、发泡助剂3-7份、抗氧剂1-5份和钛酸铝偶联剂2-6份。
2.根据权利要求1所述的一种建筑装饰用环保PVC材料，其特征在于，包括由以下重量份的原料制备而成：聚氯乙烯31-49份、无机填料11-14份、顺式异戊橡胶6-9份、PVC S700树脂粉9-14份、废旧塑料13-15份、硅酸纤维13-17份、方解石16-24份、苯甲酸盐5-8份、细孔硅胶12-19份、甲基丙烯酸甲酯12-16份、纳米氧化铈3-7份、发泡助剂4-6份、抗氧剂2-4份和钛酸铝偶联剂3-5份。
3.根据权利要求1所述的一种建筑装饰用环保PVC材料，其特征在于，包括由以下重量份的原料制备而成：聚氯乙烯40份、无机填料12份、顺式异戊橡胶8份、PVC S700树脂粉11份、废旧塑料14份、硅酸纤维16份、方解石18份、苯甲酸盐6份、细孔硅胶16份、甲基丙烯酸甲酯13份、纳米氧化铈5份、发泡助剂5份、抗氧剂3份和钛酸铝偶联剂4份。
4.根据权利要求1所述的一种建筑装饰用环保PVC材料，其特征在于，所述发泡助剂为偶氮二甲酰胺或十二水硫酸铝钾；所述抗氧剂为 2，6- 三级丁基 -4- 甲基苯酚、双（3，5-三级丁基 -4- 羟基苯基）硫醚；所述钛酸铝偶联剂为邻苯二甲酸二 (2- 乙基己 ) 酯或邻苯二甲酸酯。
5.根据权利要求1所述的一种建筑装饰用环保PVC材料的制备方法，其特征在于，包括如下步骤：
S1、将聚氯乙烯30-50份、PVC S700树脂粉8-15份、硅酸纤维12-18份、方解石15-25份、苯甲酸盐4-9份、细孔硅胶10-20份加入粉碎机粉碎均匀后，倒入到搅拌机中搅拌5-8min，得到混合物；
S2、将步骤S1所得的混合物中加入无机填料10-15份、顺式异戊橡胶5-10份、废旧塑料12-15份、甲基丙烯酸甲酯11-17份、发泡助剂3-7份、抗氧剂1-5份和钛酸铝偶联剂2-6份，在80-100℃下高速搅拌3-6min混合均匀，冷却之后得混合物料；
S3、将步骤S2所得的混合物料加入螺杆挤出机中，转速为50-90r/min，挤出温度为150-200℃挤出成型得到建筑装饰用环保PVC材料。
CN201711101947.1A 2017-11-10 2017-11-10 一种建筑装饰用环保pvc材料及其制备方法 Pending CN107903531A (zh)