CN107893227A - Intelligent air condition condenser liner, condenser - Google Patents

Intelligent air condition condenser liner, condenser Download PDF

Info

Publication number
CN107893227A
CN107893227A CN201711086907.4A CN201711086907A CN107893227A CN 107893227 A CN107893227 A CN 107893227A CN 201711086907 A CN201711086907 A CN 201711086907A CN 107893227 A CN107893227 A CN 107893227A
Authority
CN
China
Prior art keywords
condenser
parts
liner
air condition
intelligent air
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711086907.4A
Other languages
Chinese (zh)
Inventor
刘晓东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711086907.4A priority Critical patent/CN107893227A/en
Publication of CN107893227A publication Critical patent/CN107893227A/en
Pending legal-status Critical Current

Abstract

A kind of intelligent air condition condenser liner, compressor, the liner are made up of the raw material of following parts by weight：1.2 1.8 parts of graphite, 0.3 0.5 parts of carborundum, 0.6 0.8 parts of magnesia, 0.8 1.2 parts of iron suicide, 0.2 0.6 parts of boron carbide, 1.0 1.5 parts of copper powder, 15 20 parts of aluminium powder.The condenser includes condenser body and the liner.Liner provided by the invention can meet work requirements of the condenser under high/low temperature and high-low pressure environment, extend condenser service life；Simultaneously can be compatible with condenser well, make condenser that there is more preferable heat preservation and insulation.

Description

Intelligent air condition condenser liner, condenser
Technical field
The present invention relates to air-conditioning technical field, and in particular to a kind of intelligent air condition condenser liner, condenser.
Background technology
Liquid refrigerant of the hanging air conditioner compressor by gaseous refrigerant compression for HTHP, is then delivered to condenser Turn into the liquid refrigerant of normal temperature high voltage after (outdoor unit) radiating, so what outdoor unit produced by boasting is hot blast.Then capillary is arrived, Into evaporator (indoor set), due to refrigerant from capillary reach evaporator after space increase suddenly, pressure reduces, liquid Refrigerant will vaporize, and become the refrigerant of gaseous state low temperature, and so as to absorb substantial amounts of heat, evaporator will turn cold, indoor set Fan the air of interior is blown over from evaporator, so what indoor set produced by boasting is exactly cold wind；Water vapour in air is met Water droplet will be condensed into after to cold evaporator, is spilt out along water pipe, here it is the reason for air-conditioning meeting water outlet.Then it is gaseous Refrigerant, which returns to compressor, to be continued to compress, and is continued cycling through.There is a part for being four-way valve when heating, make refrigerant cold On the contrary, so what is blown when heating outside room is cold wind when the flow direction and refrigeration of condenser and evaporator, what indoor set blew is Hot blast.It will discharge heat when being substantially exactly and utilize liquefaction (being changed into liquid from gas) in physics and vaporization (is changed into from liquid Gas) when to absorb the principle of heat.
Compressor, condenser as air-conditioning critical component, it is necessary to bear high/low temperature and high-low pressure environment, common metal It is difficult to meet to require, is required typically on compressor, the inside and outside wall of condenser coated with the inside and outside satisfaction that is lined with.
The content of the invention
The present invention is to solve the above problems, provide a kind of intelligent air condition condenser liner, condenser.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of intelligent air condition condenser liner, the liner are made up of the raw material of following parts by weight：
Graphite 1.2-1.8 parts, carborundum 0.3-0.5 parts, magnesia 0.6-0.8 parts, iron suicide 0.8-1.2 parts, boron carbide 0.2-0.6 parts, copper powder 1.0-1.5 parts, aluminium powder 15-20 parts.
Preferably, the liner is made up of the raw material of following parts by weight：
1.5 parts of graphite, 0.4 part of carborundum, 0.7 part of magnesia, 1.0 parts of iron suicide, 0.4 part of boron carbide, 1.3 parts of copper powder, 18 parts of aluminium powder.
A kind of condenser for being coated with the liner, including condenser body and the liner.
The liner is by spraying coating process coated on condenser body.
The condenser body includes following raw material：
Zinc 0.13%-0.15%, manganese 0.08%-0.12%, titanium 0.03%-0.10%, nickel 1.20%-1.80%, carbon 2.20%-2.60%, chromium 2.30%-2.50%, cobalt 0.03%-0.08%, cadmium 0.02%-0.07%, surplus are iron.
Preferably, the condenser body is made up of the raw material of following parts by weight：
Zinc 0.14%, manganese 0.10%, titanium 0.06%, nickel 1.50%, carbon 2.40%, chromium 2.40%, cobalt 0.05%, cadmium 0.04%, surplus is iron.
The condenser body, thickness of inner lining ratio are (20~30):1.
Preferably, the condenser body, thickness of inner lining are respectively 25mm, 1mm.
Beneficial effects of the present invention are：Liner provided by the invention can meet condenser in high/low temperature and high-low pressure environment Under work requirements, extend condenser service life；Simultaneously can be compatible with condenser well, make condenser with preferably every Hot heat-insulating property.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below Embodiment is closed, the present invention is expanded on further.
Embodiment 1
A kind of intelligent air condition condenser liner, the liner are made up of the raw material of following parts by weight：
1.2 parts of graphite, 0.3 part of carborundum, 0.6 part of magnesia, 0.8 part of iron suicide, 0.2 part of boron carbide, 1.0 parts of copper powder, 15 parts of aluminium powder.
A kind of condenser for being coated with the liner, including condenser body and the liner.
The liner is by spraying coating process coated on condenser body.
The condenser body includes following raw material：
Zinc 0.13%, manganese 0.08%, titanium 0.03%, nickel 1.20%, carbon 2.20%, chromium 2.30%, cobalt 0.03%, cadmium 0.02%, surplus is iron.
The condenser body, thickness of inner lining ratio are (20~30):1.
Preferably, the condenser body, thickness of inner lining are respectively 25mm, 1mm.
Embodiment 2
A kind of intelligent air condition condenser liner, the liner are made up of the raw material of following parts by weight：
1.5 parts of graphite, 0.4 part of carborundum, 0.7 part of magnesia, 1.0 parts of iron suicide, 0.4 part of boron carbide, 1.3 parts of copper powder, 18 parts of aluminium powder.
A kind of condenser for being coated with the liner, including condenser body and the liner.
The liner is by spraying coating process coated on condenser body.
The condenser body includes following raw material：
Zinc 0.13%, manganese 0.08%, titanium 0.03%, nickel 1.20%, carbon 2.20%, chromium 2.30%, cobalt 0.03%, cadmium 0.02%, surplus is iron.
The condenser body, thickness of inner lining ratio are (20~30):1.
Preferably, the condenser body, thickness of inner lining are respectively 25mm, 1mm.
Embodiment 3
A kind of intelligent air condition condenser liner, the liner are made up of the raw material of following parts by weight：
1.8 parts of graphite, 0.5 part of carborundum, 0.8 part of magnesia, 1.2 parts of iron suicide, 0.6 part of boron carbide, 1.5 parts of copper powder, 20 parts of aluminium powder.
A kind of condenser for being coated with the liner, including condenser body and the liner.
The liner is by spraying coating process coated on condenser body.
The condenser body includes following raw material：
Zinc 0.13%, manganese 0.08%, titanium 0.03%, nickel 1.20%, carbon 2.20%, chromium 2.30%, cobalt 0.03%, cadmium 0.02%, surplus is iron.
The condenser body, thickness of inner lining ratio are (20~30):1.
Preferably, the condenser body, thickness of inner lining are respectively 25mm, 1mm.
Embodiment 4
A kind of intelligent air condition condenser liner, the liner are made up of the raw material of following parts by weight：
1.5 parts of graphite, 0.4 part of carborundum, 0.7 part of magnesia, 1.0 parts of iron suicide, 0.4 part of boron carbide, 1.3 parts of copper powder, 18 parts of aluminium powder.
A kind of condenser for being coated with the liner, including condenser body and the liner.
The liner is by spraying coating process coated on condenser body.
The condenser body includes following raw material：
Zinc 0.14%, manganese 0.10%, titanium 0.06%, nickel 1.50%, carbon 2.40%, chromium 2.40%, cobalt 0.05%, cadmium 0.04%, surplus is iron.
The condenser body, thickness of inner lining ratio are (20~30):1.
Preferably, the condenser body, thickness of inner lining are respectively 25mm, 1mm.
Embodiment 5
A kind of intelligent air condition condenser liner, the liner are made up of the raw material of following parts by weight：
1.5 parts of graphite, 0.4 part of carborundum, 0.7 part of magnesia, 1.0 parts of iron suicide, 0.4 part of boron carbide, 1.3 parts of copper powder, 18 parts of aluminium powder.
A kind of condenser for being coated with the liner, including condenser body and the liner.
The liner is by spraying coating process coated on condenser body.
The condenser body includes following raw material：
Zinc 0.15%, manganese 0.12%, titanium 0.10%, nickel 1.80%, carbon 2.60%, chromium 2.50%, cobalt 0.08%, cadmium 0.07%, surplus is iron.
The condenser body, thickness of inner lining ratio are (20~30):1.
Preferably, the condenser body, thickness of inner lining are respectively 25mm, 1mm.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry For personnel it should be appreciated that the present invention is not limited to the above embodiments, that described in above-described embodiment and specification is only the present invention Preference, be not intended to limit the present invention, without departing from the spirit and scope of the present invention, the present invention also have it is various Changes and improvements, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by institute Attached claims and its equivalent thereof.

Claims (8)

1. a kind of intelligent air condition condenser liner, it is characterised in that the liner is made up of the raw material of following parts by weight：
Graphite 1.2-1.8 parts, carborundum 0.3-0.5 parts, magnesia 0.6-0.8 parts, iron suicide 0.8-1.2 parts, boron carbide 0.2- 0.6 part, copper powder 1.0-1.5 parts, aluminium powder 15-20 parts.
2. intelligent air condition condenser liner as claimed in claim 1, it is characterised in that the liner by following parts by weight original Material composition：
1.5 parts of graphite, 0.4 part of carborundum, 0.7 part of magnesia, 1.0 parts of iron suicide, 0.4 part of boron carbide, 1.3 parts of copper powder, aluminium powder 18 parts.
3. a kind of condenser for being coated with liner as claimed in claim 1, it is characterised in that including condenser body and described interior Lining.
4. intelligent air condition condenser as claimed in claim 3, it is characterised in that the liner is by spraying coating process coated in cold On condenser body.
5. intelligent air condition condenser as claimed in claim 3, it is characterised in that the condenser body includes following parts by weight Raw material：
Zinc 0.13%-0.15%, manganese 0.08%-0.12%, titanium 0.03%-0.10%, nickel 1.20%-1.80%, carbon 2.20%- 2.60%, chromium 2.30%-2.50%, cobalt 0.03%-0.08%, cadmium 0.02%-0.07%, surplus are iron.
6. intelligent air condition condenser as claimed in claim 3, it is characterised in that the condenser body is by following parts by weight Raw material forms：
Zinc 0.14%, manganese 0.10%, titanium 0.06%, nickel 1.50%, carbon 2.40%, chromium 2.40%, cobalt 0.05%, cadmium 0.04%, Surplus is iron.
7. intelligent air condition condenser as claimed in claim 3, it is characterised in that the condenser body, thickness of inner lining ratio are (20~30):1.
8. intelligent air condition condenser as claimed in claim 3, it is characterised in that the condenser body, thickness of inner lining difference For 25mm, 1mm.
CN201711086907.4A 2017-11-07 2017-11-07 Intelligent air condition condenser liner, condenser Pending CN107893227A (en)