CN107879697A - A kind of dry-mixed mortar containing cellulose ether - Google Patents
A kind of dry-mixed mortar containing cellulose ether Download PDFInfo
- Publication number
- CN107879697A CN107879697A CN201711370568.2A CN201711370568A CN107879697A CN 107879697 A CN107879697 A CN 107879697A CN 201711370568 A CN201711370568 A CN 201711370568A CN 107879697 A CN107879697 A CN 107879697A
- Authority
- CN
- China
- Prior art keywords
- dry
- parts
- cellulose ether
- mixed mortar
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Present invention is generally directed to the problem of the poor water retention property of dry-mixed mortar and rheological characteristic difference, the water-retaining property and rheological characteristic of cellulose ether reinforced mortar are added in dry-mixed mortar, so that dry-mixed mortar is more convenient for using and constructed.Present invention generally provides a kind of dry-mixed mortar containing cellulose ether, it is intended to which the problem of changing traditional mortar water-retaining property and poor rheological characteristic, it is made up of following raw material：10 ~ 25 parts of cement, middle 10 ~ 50 parts of sand, 10 ~ 40 parts of fine sand, 10 ~ 20 parts of flyash, 0.2 ~ 0.4 part of cellulose ether, 0.05 ~ 0.15 part of water reducer, 0.05 ~ 0.15 part of air entraining agent.
Description
Technical field
The invention belongs to building material field, more particularly to a kind of dry-mixed mortar containing cellulose ether.
Background technology
Dry-mixed mortar is generally hydraulic cement mixed mortar, refers to the aggregate through drying screening process（Such as quartz sand）、
Inorganic coagulation material（Such as cement）And additive（Such as polymer）Deng a kind of particle that progress physical mixed forms by a certain percentage
Shape or powdery, building site is transported in the form of packed or be in bulk, the material for adding water to can be used directly after mixing and stirring.Also referred to as mortar is done
Powder, dry blend, dry mixing powder etc..Dry powder and mortar plays bonding, pad, protection and decoration function in construction industry with thin layer, builds
Build with fitting-out work using extremely wide.As the continuous improvement of construction quality, environmental requirement and civilized construction requirement, construction are existing
The shortcomings that field mixing mortar and limitation are more and more prominent, and predominantly dry-mixed mortar needs secondary mix and stir after being transported to job site
Wasting manpower and material resources, secondly poor for the water holding capacity of dry-mixed mortar, rheological characteristic is poor, is not easy to construct.Present invention is generally directed to dry
The problem of poor water retention property and rheological characteristic difference of mortar, the water-retaining property and stream of cellulose ether reinforced mortar are added in dry-mixed mortar
Denaturation, so that dry-mixed mortar is more convenient for using and constructed.
The content of the invention
Present invention generally provides a kind of dry-mixed mortar containing cellulose ether, it is intended to changes traditional mortar water-retaining property and rheology
The problem of property is poor, it is made up of following raw material：
10 ~ 25 parts of cement, middle 10 ~ 50 parts of sand, 10 ~ 40 parts of fine sand, 10 ~ 20 parts of flyash, 0.2 ~ 0.4 part of cellulose ether, diminishing
0.05 ~ 0.15 part of agent, 0.05 ~ 0.15 part of air entraining agent；
The cement is Portland cement, grade strength 32.5；
The middle sand is continuous grading Machine-made Sand, and content of stone powder is 2 ~ 8%；
The fine sand is continuous grading Machine-made Sand, and content of stone powder is 2 ~ 8%；
The flyash is two level ordinary fly ash；
The cellulose ether is TYLOSE 30000, and viscosity is 300 ~ 1200；
The water reducer is naphthalene series high-efficiency powder water reducer, and diminishing efficiency is 20 ~ 30%；
The air entraining agent is common rosin class air entraining agent.
Case is embodied：
Matched according to above-mentioned technical proposal of the present invention, now carry out two implementation columns and tested and studied.
Embodiment 1：
15 parts of cement, middle 20 parts of sand, 25 parts of fine sand, 15 parts of flyash, 0.2 part of cellulose ether, 0.1 part of water reducer, air entraining agent 0.1
Part.
Embodiment 2：
15 parts of cement, middle 20 parts of sand, 25 parts of fine sand, 15 parts of flyash, 0.4 part of cellulose ether, 0.1 part of water reducer, air entraining agent 0.1
Part.
Dry-mixed mortar of the present invention mix and stir and form of construction work and mixing and stirring for common dry-mixed mortar it is identical with form of construction work, add water
Can construction usage after mixing and stirring.
Experiment measuring study, measurement result now are carried out to the water-retaining property and rheological characteristic of the cellulose ether dry-mixed mortar after mixing and stirring
It is as shown in the table：
| Embodiment | Water retention | Setting time | Denseness loss late | Condense compression strength |
| 1 | 89% | 6h | 34% | 12.4MPa |
| 2 | 85% | 7h | 27% | 11.7MPa |
The increase with cellulose ether is can be seen that from the data of experiment detection, the water-retaining property of dry-mixed mortar strengthens therewith, rheology
Performance is also improved well, so as to change some drawbacks of current dry-mixed mortar.
It should be noted that the foregoing description of the disclosed embodiments, a variety of modifications to these embodiments are to ability
It will be apparent for the professional and technical personnel in domain, generic principles defined herein can not depart from the present invention's
In the case of spirit or scope, realize in other embodiments.Therefore, the present invention be not intended to be limited to it is shown in this article these
Embodiment, and it is to fit to the most wide scope consistent with principles disclosed herein and features of novelty.
Claims (1)
1. a kind of dry-mixed mortar containing cellulose ether, is characterised by, it is made up of following raw material：
10 ~ 25 parts of cement, middle 10 ~ 50 parts of sand, 10 ~ 40 parts of fine sand, 10 ~ 20 parts of flyash, 0.2 ~ 0.4 part of cellulose ether, diminishing
0.05 ~ 0.15 part of agent, 0.05 ~ 0.15 part of air entraining agent；
The cement is Portland cement, grade strength 32.5；
The middle sand is continuous grading Machine-made Sand, and content of stone powder is 2 ~ 8%；
The fine sand is continuous grading Machine-made Sand, and content of stone powder is 2 ~ 8%；
The flyash is two level ordinary fly ash；
The cellulose ether is TYLOSE 30000, and viscosity is 300 ~ 1200；
The water reducer is naphthalene series high-efficiency powder water reducer, and diminishing efficiency is 20 ~ 30%；
The air entraining agent is common rosin class air entraining agent.