CN107879678A - A kind of diatom ooze coating - Google Patents
A kind of diatom ooze coating Download PDFInfo
- Publication number
- CN107879678A CN107879678A CN201711116546.3A CN201711116546A CN107879678A CN 107879678 A CN107879678 A CN 107879678A CN 201711116546 A CN201711116546 A CN 201711116546A CN 107879678 A CN107879678 A CN 107879678A
- Authority
- CN
- China
- Prior art keywords
- parts
- dry powder
- diatom ooze
- peel dry
- mesh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of diatom ooze coating, and it belongs to paint field, and in particular to a kind of coating composition.The diatom ooze coating of the present invention includes according to mass fraction：10 60 parts of diatomite, high stick are recessed native 3 20 parts, suspending agent is recessed native 3 20 parts, 15 50 parts of bentonite, 2 30 parts of orange peel dry powder, 2 30 parts of pomelo peel dry powder, 2 30 parts of lemon peel dry powder, 2 30 parts of pineapple peel dry powder, 1 20 parts of tealeaves dry powder, 5 45 parts of activated carbon, 1 15 parts of formaldehyde lyase, 1 10 parts of nano titanium oxide and 1 10 parts of pigment.The diatom ooze coating production cost of the present invention is low, eliminates formaldehyde, purification air, deodorization and sterilization and other effects height.
Description
Technical field
The invention belongs to paint field, and in particular to a kind of coating composition.
Background technology
With the continuous enhancing of people's health consciousness, improve indoor environmental quality, reduce finishing pollution oneself through by increasingly
More people payes attention to.Various building materials are commonly used in house decoration, although single building materials formaldehyde examination is not exceeded, are built using a variety of
Easily formaldehydogenic overlying pollution is just produced after material.Diatom ooze is a kind of dry powder-shaped being formulated using diatomite as main raw material(s)
Inner wall decoration coating material, have elimination formaldehyde, purification air, regulation humidity, releasing negative oxygen ion, fire protection flame retarding, metope white
The functions such as clean, deodorization and sterilization.It is substitute wallpaper and emulsion paint new due to diatom ooze health environment-friendly and with ornamental very well
Generation house decorative material.Diatom ooze has the attribute of mud, chance water reducible into mud reuse, the flesh suitable for repairing, enriching
Reason pattern and color be adapted to all kinds of interior decoration projects using, be not easy to be infected with grey life the characteristics of, receive the extensive favor of people.
But the production cost for the diatom ooze sold on the market at present is high, substantial amounts of artificial conjunction is with the addition of in diatom ooze
Into additive so that diatom ooze easily produces harmful substance, its eliminate formaldehyde, purification air, deodorization and sterilization and other effects up for
Further improve.
The content of the invention
It is an object of the invention to provide a kind of diatom ooze coating of prosthetic synthetic additive, the coating can effectively disappear
Except formaldehyde, purification air, deodorization and sterilization.
To achieve the above object, the technical scheme is that a kind of diatom ooze coating, the diatom ooze coating is according to matter
Amount number includes：Diatomite 10-60 parts, the recessed native 3-20 parts of high stick, the recessed native 3-20 parts of suspending agent, bentonite 15-50 parts, orange
Skin dry powder 2-30 parts, pomelo peel dry powder 2-30 parts, lemon peel dry powder 2-30 parts, pineapple peel dry powder 2-30 parts, tealeaves dry powder 1-20
Part, activated carbon 5-45 parts, formaldehyde lyase 1-15 parts, nano titanium oxide 1-10 parts and pigment 1-10 parts.
Preferably, the diatom ooze coating includes according to mass fraction：Diatomite 20-50 parts, the recessed native 8-16 parts of high stick,
The recessed native 8-16 parts of suspending agent, bentonite 22-42 parts, orange peel dry powder 9-23 parts, pomelo peel dry powder 9-23 parts, lemon peel dry powder 9-
23 parts, pineapple peel dry powder 9-23 parts, tealeaves dry powder 5-15 parts, activated carbon 15-35 parts, formaldehyde lyase 4-12 parts, nano-silica
Change titanium 3-8 parts and pigment 3-8 parts.
Preferably, the diatom ooze coating includes according to mass fraction：35 parts of diatomite, high stick are recessed native 12 parts, suspend
Agent is recessed native 12 parts, 32 parts of bentonite, 16 parts of orange peel dry powder, 16 parts of pomelo peel dry powder, 16 parts of lemon peel dry powder, pineapple peel dry powder
5 parts of 16 parts, 10 parts of tealeaves dry powder, 25 parts of activated carbon, 8 parts of formaldehyde lyase, 5 parts of nano titanium oxide and pigment.
Preferably, the diatomite is 200-10000 mesh.
Preferably, the recessed soil of the high stick is 200-600 mesh.
Preferably, the recessed soil of the suspending agent is 200-600 mesh.
Preferably, the bentonite is 200-2000 mesh.
Preferably, the orange peel dry powder, pomelo peel dry powder, lemon peel dry powder, pineapple peel dry powder are 100-800 mesh.
Preferably, the tealeaves dry powder is 100-1000 mesh.
Preferably, the activated carbon is 100-2000 mesh.
The occupation mode of the diatom ooze coating of the present invention is that stirring turns into fine and smooth paste after being mixed with water.
1st, diatomite of the invention has the characteristics that porosity is big, absorbability is strong, chemical property is stable, wear-resisting, heat-resisting, energy
Beneficial surface property is provided for coating (increase-volume, thickening memory improve adhesive force)；Because it has larger pore volume, not only
Film can be made to shorten drying time, the dosage of resin can be also reduced, reduce cost；Diatomite is free of harmful chemical, except
Have the characteristics that non-ignitable, sound insulation, waterproof, it is in light weight and heat-insulated outside, also dehumidifying, deodorization, the effect of purifying the air of a room etc..
2nd, the recessed soil of high stick that the present invention uses is a kind of natural hydration zeopan, and it has unique three-dimensional space
Between chain structure；It is by works such as immersion, grinding, dehydration, surface active, crushing parcel, allotments using Concave-convex clay rod
Skill is mainly used as suspending agent, the thickening agents of coating through a kind of high-viscosity products made of scientific formula and special processing process.
3rd, the recessed soil of suspending agent is that a kind of natural hydration alumina magnesia silicate is process through exquisiteness, and it has unique
Three dimensions chain structure, and special pin, rod fibrous crystal form, thus have together ordinary colloid and suspension.It is passed through
Cross that immersion, scattered, grinding, surface active, allotment etc. are refined to be formed, with spies such as excellent suspension, wetability, dispersivenesses
Point.
4th, bentonite of the invention has strong a hygroscopicity and dilatancy, the water of adsorbable 8~15 times of own vols,
Volumetric expansion is up to several times to 30 times；As a form of gel or suspension can be dispersed into aqueous medium, this medium solution has certain
Viscosity, variability and lubricity；There is stronger cation exchange capacity (CEC)；Have necessarily to various gases, liquid, organic substance
Adsorption capacity, maximal absorptive capacity is up to 5 times of weight of itself；The admixture of it and water, mud or fine sand has preferably plastic
Property and cohesiveness.
5th, orange peel dry powder, pomelo peel dry powder, lemon peel dry powder, pineapple peel dry powder, the tealeaves dry powder that the present invention uses：Inhale
Receive indoor formaldehyde residual peculiar smell.
6th, the activated carbon in the present invention is it is possessed and indoor harmful gas molecular size using advanced boring technique
The pore structure to match, it is exclusively used in swimming carefully in all harmful gases and air such as formaldehyde adsorption, ammonia, radon
Bacterium；With inhale taste, detoxification, deodorization, dry, it is mould proof, sterilization, purification etc. comprehensive function, applied to finishing pollution administer in can have
Effect removes indoor environmental pollution.
7th, formaldehyde lyase of the invention can react under liquid, solid, gaseous state with free formaldehyde,
Rapid decompose removes formaldehyde pollutants in 3 hours, can strength quickly remove formaldehyde, have it is nontoxic, harmless, be not easily decomposed, no
The good characteristic of secondary pollution can be caused.
8th, the present invention adds nano titanium oxide in coating, and the coating produced has sterilization, antifouling, deodorization, self-cleaning
The characteristics of, it is capable of purifying air, anti-applied to the bacteriums such as hospital ward, operating room and family bathroom space are intensive, the place easily bred
Only infection, deodorization taste removal, effectively kill harmful bacteria.
Beneficial effects of the present invention are：
Suspending agent, thickener in the present invention by the use of the recessed soil of high stick and the recessed soil of suspending agent as coating, bentonite conduct
Binding agent, the days such as orange peel dry powder, pomelo peel dry powder, lemon peel dry powder, pineapple peel dry powder, tealeaves dry powder are with the addition of in coating
The assimilation effect of right composition enhancing formaldehyde, diatom is mixed coating and be not likely to produce harmful substance, eliminated so as to strengthen diatom ooze coating
First silicon, purification air, deodorization and sterilization and other effects；Activated carbon, the formaldehyde lyase added in the present invention greatly strengthen diatom ooze
Coating absorbs the effect of formaldehyde, and nano titanium oxide greatly strengthen the bacteria-eliminating efficacy of diatom ooze coating, substantially reduces indoor dirt
Dye, purification indoor environment, the living environment of health is built for people.The diatom ooze coating production cost of the present invention is low, eliminates first
Aldehyde, purification air, deodorization and sterilization and other effects height.
Embodiment
Following examples are used to illustrate the present invention, but are not limited to the scope of the present invention.
Embodiment 1
The diatom ooze coating of the present embodiment is by diatomite 10kg, the recessed native 8kg of high stick, the recessed native 12kg of suspending agent, swelling
Native 32kg, orange peel dry powder 16kg, pomelo peel dry powder 9kg, lemon peel dry powder 9kg, pineapple peel dry powder 2kg, tealeaves dry powder 1kg,
Activated carbon 15kg, formaldehyde lyase 12kg, nano titanium oxide 10kg and pigment 8kg are well mixed manufactured, wherein diatomite
For 1000-2000 mesh；The high recessed soil of stick is 200-400 mesh；The recessed soil of suspending agent is 200-600 mesh；Bentonite is 200-2000 mesh；
Orange peel dry powder, pomelo peel dry powder, lemon peel dry powder, pineapple peel dry powder are 100-800 mesh；Tealeaves dry powder is 100-1000
Mesh；Activated carbon is 1000-2000 mesh.
Embodiment 2
The diatom ooze coating of the present embodiment is by diatomite 20kg, the recessed native 12kg of high stick, the recessed native 3kg of suspending agent, swelling
Native 15kg, orange peel dry powder 23kg, pomelo peel dry powder 30kg, lemon peel dry powder 30kg, pineapple peel dry powder 23kg, tealeaves dry powder
5kg, activated carbon 25kg, formaldehyde lyase 4kg, nano titanium oxide 3kg and pigment 5kg are well mixed manufactured, wherein diatom
Soil is 2000-5000 mesh；The high recessed soil of stick is 400-600 mesh；The recessed soil of suspending agent is 200-600 mesh；Bentonite is 200-1500
Mesh；Orange peel dry powder, pomelo peel dry powder, lemon peel dry powder, pineapple peel dry powder are 100-800 mesh；Tealeaves dry powder is 100-300
Mesh；Activated carbon is 100-500 mesh.
Embodiment 3
The diatom ooze coating of the present embodiment is by diatomite 50kg, the recessed native 16kg of high stick, the recessed native 16kg of suspending agent, swelling
Native 50kg, orange peel dry powder 2kg, pomelo peel dry powder 2kg, lemon peel dry powder 16kg, pineapple peel dry powder 30kg, tealeaves dry powder
15kg, activated carbon 45kg, formaldehyde lyase 8kg, nano titanium oxide 1kg and pigment 10kg are well mixed manufactured, wherein silicon
Diatomaceous earth is 400-800 mesh；The high recessed soil of stick is 200-600 mesh；The recessed soil of suspending agent is 400-600 mesh；Bentonite is 200-2000
Mesh；Orange peel dry powder, pomelo peel dry powder, lemon peel dry powder, pineapple peel dry powder are 100-800 mesh；Tealeaves dry powder is 100-
1000 mesh；Activated carbon is 200-800 mesh.
Embodiment 4
The diatom ooze coating of the present embodiment is by diatomite 60kg, the recessed native 20kg of high stick, the recessed native 8kg of suspending agent, swelling
Native 22kg, orange peel dry powder 30kg, pomelo peel dry powder 22kg, lemon peel dry powder 2kg, pineapple peel dry powder 9kg, tealeaves dry powder
20kg, activated carbon 35kg, formaldehyde lyase 15kg, nano titanium oxide 5kg and pigment 3kg are well mixed manufactured, wherein silicon
Diatomaceous earth is 8000-10000 mesh；The high recessed soil of stick is 200-600 mesh；The recessed soil of suspending agent is 200-400 mesh；Bentonite is 1000-
2000 mesh；Orange peel dry powder, pomelo peel dry powder, lemon peel dry powder, pineapple peel dry powder are 100-800 mesh；Tealeaves dry powder is
100-500 mesh；Activated carbon is 1500-2000 mesh.
Embodiment 5
The diatom ooze coating of the present embodiment is by diatomite 35kg, the recessed native 3kg of high stick, the recessed native 20kg of suspending agent, swelling
Native 42kg, orange peel dry powder 9kg, pomelo peel dry powder 16kg, lemon peel dry powder 23kg, pineapple peel dry powder 16kg, tealeaves dry powder
10kg, activated carbon 5kg, formaldehyde lyase 1kg, nano titanium oxide 8kg and pigment 1kg are well mixed manufactured, wherein diatom
Soil is 200-400 mesh；The high recessed soil of stick is 200-600 mesh；The recessed soil of suspending agent is 200-600 mesh；Bentonite is 200-800 mesh；
Orange peel dry powder, pomelo peel dry powder, lemon peel dry powder, pineapple peel dry powder are 100-800 mesh；Tealeaves dry powder is 600-1000
Mesh；Activated carbon is 100-2000 mesh.
The high recessed soil of stick is the concave convex rod binder product of Mingguang City Guo Xingaotu Co., Ltds in above example.
The recessed soil of suspending agent is the concave-convex stick suspending agent product of Xuyi Boyto Ao Tu limited companies.
Checking test
Stirring is tested as fine and smooth paste as coating for wall surface after obtained product in embodiment 1-5 is mixed with water
The fundamental property of obtained product in embodiment 1-5 is demonstrate,proved, it is as a result as follows：
It is water-fast, hold color, life-span：Respectively after coating completes 6 months and 12 months, with giant to scribbling embodiment 1-
The wall of diatom ooze coating coating continuously sprays 1000L water in 5, does not occur wall and fades, ftractures, peeling phenomenon.
Purify air performance：(space is 20m in the closing space of obtained coating in inwall coating embodiment 1-53),
It is 0.2mg/m to adjust initial concentration of formaldehyde3, tested again after 24h, concentration of formaldehyde point in the closing space of 5 embodiments
0.03mg/m is not down to it3、0.03mg/m3、0.02mg/m3、0.03mg/m3、0.02mg/m3, illustrating the product of the present invention can have
Harmful substance formaldehyde in effect absorption air.
Suspending agent, thickener in the present invention by the use of the recessed soil of high stick and the recessed soil of suspending agent as coating, bentonite conduct
Binding agent, the days such as orange peel dry powder, pomelo peel dry powder, lemon peel dry powder, pineapple peel dry powder, tealeaves dry powder are with the addition of in coating
The assimilation effect of right composition enhancing formaldehyde, diatom is mixed coating and be not likely to produce harmful substance, eliminated so as to strengthen diatom ooze coating
First silicon, purification air, deodorization and sterilization and other effects；Activated carbon, the formaldehyde lyase added in the present invention greatly strengthen diatom ooze
Coating absorbs the effect of formaldehyde, and nano titanium oxide greatly strengthen the bacteria-eliminating efficacy of diatom ooze coating, substantially reduces indoor dirt
Dye, purification indoor environment, the living environment of health is built for people.Production cost of the present invention is low, eliminate formaldehyde, purification air,
Deodorization and sterilization and other effects height.
Although above with general explanation and specific embodiment, the present invention is described in detail, at this
On the basis of invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Therefore,
These modifications or improvements without departing from theon the basis of the spirit of the present invention, belong to the scope of protection of present invention.
Claims (10)
- A kind of 1. diatom ooze coating, it is characterised in that：The diatom ooze coating includes according to mass fraction：Diatomite 10-60 parts, The recessed native 3-20 parts of high stick, the recessed native 3-20 parts of suspending agent, bentonite 15-50 parts, orange peel dry powder 2-30 parts, pomelo peel dry powder 2- 30 parts, lemon peel dry powder 2-30 parts, pineapple peel dry powder 2-30 parts, tealeaves dry powder 1-20 parts, activated carbon 5-45 parts, formaldehyde lyase 1-15 parts, nano titanium oxide 1-10 parts and pigment 1-10 parts.
- 2. diatom ooze coating according to claim 1, it is characterised in that：The diatom ooze coating is according to mass fraction bag Include：Diatomite 20-50 parts, the recessed native 8-16 parts of high stick, the recessed native 8-16 parts of suspending agent, bentonite 22-42 parts, orange peel dry powder 9- 23 parts, pomelo peel dry powder 9-23 parts, lemon peel dry powder 9-23 parts, pineapple peel dry powder 9-23 parts, tealeaves dry powder 5-15 parts, activated carbon 15-35 parts, formaldehyde lyase 4-12 parts, nano titanium oxide 3-8 parts and pigment 3-8 parts.
- 3. diatom ooze coating according to claim 2, it is characterised in that：The diatom ooze coating is according to mass fraction bag Include：35 parts of diatomite, high stick are recessed native 12 parts, suspending agent is recessed native 12 parts, 32 parts of bentonite, 16 parts of orange peel dry powder, pomelo peel 16 parts of dry powder, 16 parts of lemon peel dry powder, 16 parts of pineapple peel dry powder, 10 parts of tealeaves dry powder, 25 parts of activated carbon, 8 parts of formaldehyde lyase, 5 parts of 5 parts of nano titanium oxide and pigment.
- 4. according to the diatom ooze coating described in any one of claim 1-3 claim, it is characterised in that：The diatomite is 200-10000 mesh.
- 5. according to the diatom ooze coating described in any one of claim 1-3 claim, it is characterised in that：The high stick is recessed Soil is 200-600 mesh.
- 6. according to the diatom ooze coating described in any one of claim 1-3 claim, it is characterised in that：The suspending agent is recessed Soil is 200-600 mesh.
- 7. according to the diatom ooze coating described in any one of claim 1-3 claim, it is characterised in that：The bentonite is 200-2000 mesh.
- 8. according to the diatom ooze coating described in any one of claim 1-3 claim, it is characterised in that：The orange peel is done Powder, pomelo peel dry powder, lemon peel dry powder, pineapple peel dry powder are 100-800 mesh.
- 9. according to the diatom ooze coating described in any one of claim 1-3 claim, it is characterised in that：The tealeaves dry powder For 100-1000 mesh.
- 10. according to the diatom ooze coating described in any one of claim 1-3 claim, it is characterised in that：The activated carbon For 100-2000 mesh.