CN107878096A - A kind of jade fire forging inlaying gold surface treatment method - Google Patents
A kind of jade fire forging inlaying gold surface treatment method Download PDFInfo
- Publication number
- CN107878096A CN107878096A CN201711139926.9A CN201711139926A CN107878096A CN 107878096 A CN107878096 A CN 107878096A CN 201711139926 A CN201711139926 A CN 201711139926A CN 107878096 A CN107878096 A CN 107878096A
- Authority
- CN
- China
- Prior art keywords
- gold
- jade
- filamentary silver
- groove
- grooving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of jade fire forging inlaying gold surface treatment method, comprises the following steps：A：The pre- grooving of jade surface, B:Gold/filamentary silver inlaid jade groove, C：Gold/filamentary silver adaptability fire forging processing, D：Outer surface beauty post processing；The manufacture craft of present invention process method is simple, operating process control is easy, grooving is inlaid with gold/filamentary silver on the flaw of jade and crack path, after being removed to crackle and flaw, filled up by spun gold or filamentary silver, it not only avoid appearance effects of the groove defect to the art work, more improve the aesthetic feeling and art form of the art work, flaw and crackle are modified and blocked, the ornamental value of the art work is improved, resource is effectively utilized, and the step of this process easily operates, difficulty is low, there is great promotional value.
Description
Technical field
The invention belongs to handicraft decorative technical field, it is related to that a kind of flow is simple, easy to operate jade fire forging inlaying gold
Surface treatment method.
Background technology
Emerald is in the world（Especially East Asia）The jewel that each department are welcome extensively is classified.Commonly known as
Beautiful mineral are mainly jadeite and nephrite, and sensu lato jade not only includes jadeite and nephrite, also including serpentine, lapis lazuli, agate
Jewel in Nao, coral, marble and other meanings.Flaw, such as crackle all be present in the existing rare jade of major part.So
Precious material is just as such flaw can not produce the value that it should have, and the removal to flaw or crackle can be damaged
Bad jade itself, largely so rare material just waste, therefore, research and develop a kind of jade fire and forge inlaying gold silver process, according to
Jade flaw in itself and crackle, which carry, carries out the operation such as cut-away, and carries out blocking decoration having with ornament materials and improve outside works
Appearance quality, raising artistic value is significant, while the more conducively variation of mentality of designing.
The content of the invention
It is an object of the invention to provide a kind of simple jade fire forging inlaying gold surface treatment method of technique.
The object of the present invention is achieved like this, comprises the following steps A：The pre- grooving of jade surface, B:Gold/filamentary silver is inlayed
Jade groove, C：Gold/filamentary silver adaptability fire forging processing, D：Outer surface beauty post processing；
A：The pre- grooving of jade surface
Decorative pattern path is designed according to crackle and flaw in jade surface, and mark is carried out on decorative pattern path, utilizes special equipment
Along mark grooving；
B:Gold/filamentary silver inlaid jade groove
First proof gold filamentary silver is annealed, i.e., being warmed to blowtorch makes gold/filamentary silver soften, then gold/filamentary silver is placed on jade and dug in advance
Groove in, and shaping to groove be adapted width；
C：Gold/filamentary silver adaptability fire forging processing
The temperature of the softening above is heated to gold/filamentary silver in dovetail groove with spray gun, and is gently tapped with hammer is inlayed, is annealed repeatedly
3 ~ 5 times, 5 ~ 10min of interval time, make gold/filamentary silver substantially concordant with dovetail groove orifice plane；
D：Outer surface beauty post processing
It is trimmed to special file and white steel knife smooth, then with emerald or topaz polishing blade, is polished, then mended with diamond dust
Light, finally cleaned with supersonic wave cleaning machine；Work finishes.
The manufacture craft of present invention process method is simple, and operating process control is easy, in the flaw and crack path of jade
Upper grooving is inlaid with gold/filamentary silver, after being removed to crackle and flaw, is filled up by spun gold or filamentary silver, not only avoid groove and lack
The appearance effects to the art work are damaged, the aesthetic feeling and art form of the art work is more improved, flaw and crackle is modified and hidden
Gear, improves the ornamental value of the art work, resource is effectively utilized, and the step of this process easily operates, difficult
Spend low, there is great promotional value.
Brief description of the drawings
Fig. 1 is to take the jade for having many crackles before treatment method；
Fig. 2 is the jade after designing decorative pattern path with pen for jade surface；
Fig. 3 is the jade after grooving（Fig. 1 Local map）；
Fig. 4 is the jade of embedded spun gold（Fig. 1 Local map）；
Fig. 5 is to take the jade after treatment method（Fig. 1 Local map）.
Embodiment
The present invention is further illustrated below in conjunction with the accompanying drawings, but the present invention must not be any limitation as in any way,
Based on present invention teach that any changes and modifications made, belong to protection scope of the present invention.
As shown in the figure：The present invention comprises the following steps：A：The pre- grooving of jade surface, B:Gold/filamentary silver inlaid jade groove, C：
Gold/filamentary silver adaptability fire forging processing, D：Outer surface beauty post processing；
A：The pre- grooving of jade surface
Decorative pattern path is designed according to crackle and flaw in jade surface, and mark is carried out on decorative pattern path, utilizes special equipment
Along mark grooving；
B:Gold/filamentary silver inlaid jade groove
First proof gold filamentary silver is annealed, i.e., being warmed to blowtorch makes gold/filamentary silver soften, then gold/filamentary silver is placed on jade and dug in advance
Groove in, and shaping to groove be adapted width；
C：Gold/filamentary silver adaptability fire forging processing
The temperature of the softening above is heated to gold/filamentary silver in dovetail groove with spray gun, and is gently tapped with hammer is inlayed, is annealed repeatedly
3 ~ 5 times, 5 ~ 10min of interval time, make gold/filamentary silver substantially concordant with dovetail groove orifice plane；
D：Outer surface beauty post processing
It is trimmed to special file and white steel knife smooth, then with emerald or topaz polishing blade, is polished, then mended with diamond dust
Light, finally cleaned with supersonic wave cleaning machine；Work finishes.
Groove in step A is dovetail groove, and the opening size of dovetail groove is 1 ~ 2mm.
Gold/filamentary silver is heated to 800 DEG C in step B.
The clearance control between gold/filamentary silver and jade groove in step B is 0.1mm.
It it is 1200 DEG C to the heating-up temperature of spun gold in step C, the heating-up temperature of filamentary silver is 800 DEG C.
Emerald or topaz polishing blade in step D for more than 7 degree of Mo Shi emerald or topaz polishing blade.
Diamond dust in step D is No. 1600 diamond dusts.
Embodiment
Embodiment 1：White jade pendant one, there is yellow cord flaw on size 35mmX25mmX10mm, surface, is set along striped
Annular silk ribbon knot is counted, and mark is carried out along silk ribbon knot shape, digs dovetail groove along mark, notch size is 1mm, and proof gold silk is heated
It is inlaid into after to 800 DEG C of softenings in dovetail groove, control gap is heated to 1200 DEG C with blowtorch and hammered into shape gently with inlaying in 0.1mm
Strike, 3 times repeatedly, be trimmed to special file and white steel knife it is smooth, then with more than 7 degree of Mo Shi emerald or topaz polishing blade,
It is polished, then with No. 1600 diamond dust light fillings, is finally cleaned with supersonic wave cleaning machine；Work finishes, attractive appearance association
Adjust, it is harmonious in colour.
Embodiment 2：The beautiful goods of furniture for display rather than for use one of green, there is crack flaw on size 100mmX60mmX25mm, surface, is set along crack
Meter rises shape flower, and carries out mark along shape flower-shape shape is risen, and digs dovetail groove along mark, notch size is 1.5mm, and silver-colored spun gold is heated to
It is inlaid into after 800 DEG C of softenings in dovetail groove, control gap is heated to 800 DEG C with blowtorch and rapped with hammer is inlayed in 0.1mm,
4 times repeatedly, it is trimmed to special file and white steel knife smooth, then with more than 7 degree of Mo Shi emerald or topaz polishing blade, is carried out
Polishing, then with No. 1600 diamond dust light fillings, finally cleaned with supersonic wave cleaning machine；Work finishes, and attractive appearance is coordinated, color
It is color harmonious.
Embodiment 3：White background jade goods of furniture for display rather than for use one, there is crack flaw on size 150mmX60mmX40mm, surface, along crack
Needle shape lace is designed, and mark is carried out along lace, digs dovetail groove along mark, notch size is 2mm, and spun gold is heated to
It is inlaid into after 800 DEG C of softenings in dovetail groove, control gap is heated to 1200 DEG C with blowtorch and rapped with hammer is inlayed in 0.1mm,
5 times repeatedly, it is trimmed to special file and white steel knife smooth, then with more than 7 degree of Mo Shi emerald or topaz polishing blade, is carried out
Polishing, then with No. 1600 diamond dust light fillings, finally cleaned with supersonic wave cleaning machine；Work finishes, and attractive appearance is coordinated, color
It is color harmonious.
Claims (7)
1. a kind of jade fire forging inlaying gold surface treatment method, it is characterized in that：Comprise the following steps：A：The pre- grooving of jade surface, B:
Gold/filamentary silver inlaid jade groove, C：Gold/filamentary silver adaptability fire forging processing, D：Outer surface beauty post processing；
A：The pre- grooving of jade surface
Decorative pattern path is designed according to crackle and flaw in jade surface, and mark is carried out on decorative pattern path, utilizes special equipment
Along mark grooving；
B:Gold/filamentary silver inlaid jade groove
First proof gold filamentary silver is annealed, i.e., being warmed to blowtorch makes gold/filamentary silver soften, then gold/filamentary silver is placed on jade and dug in advance
Groove in, and shaping to groove be adapted width；
C：Gold/filamentary silver adaptability fire forging processing
The temperature of the softening above is heated to gold/filamentary silver in dovetail groove with spray gun, and is gently tapped with hammer is inlayed, is annealed repeatedly
3 ~ 5 times, 5 ~ 10min of interval time, make gold/filamentary silver substantially concordant with dovetail groove orifice plane；
D：Outer surface beauty post processing
It is trimmed to special file and white steel knife smooth, then with emerald or topaz polishing blade, is polished, then mended with diamond dust
Light, finally cleaned with supersonic wave cleaning machine；Work finishes.
2. the method for microwave method reducing and decomposing phosphogypsum according to claim 1, it is characterised in that the groove in step A is swallow
Stern notch, the opening size of dovetail groove is 1 ~ 2mm.
3. the method for microwave method reducing and decomposing phosphogypsum according to claim 1, it is characterised in that by gold/silver in step B
Silk is heated to 800 DEG C.
4. technical method according to claim 1, it is characterised in that the gap between gold/filamentary silver and jade groove in step B
Control as 0.1mm.
5. technical method according to claim 1, it is characterised in that it is 1200 DEG C to the heating-up temperature of spun gold in step C,
The heating-up temperature of filamentary silver is 800 DEG C.
6. technical method according to claim 1, it is characterised in that emerald or topaz polishing blade in step D are Mo Shi 7
More than degree emerald or topaz polishing blade.
7. technical method according to claim 1, it is characterised in that the diamond dust in step D is No. 1600 diamond dusts.