CN107866523A - It is exclusively used in the pressure ceroplastic of essence casting Ludox - Google Patents
It is exclusively used in the pressure ceroplastic of essence casting Ludox Download PDFInfo
- Publication number
- CN107866523A CN107866523A CN201711095203.3A CN201711095203A CN107866523A CN 107866523 A CN107866523 A CN 107866523A CN 201711095203 A CN201711095203 A CN 201711095203A CN 107866523 A CN107866523 A CN 107866523A
- Authority
- CN
- China
- Prior art keywords
- wax
- mould
- cooling water
- pressure
- ceroplastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of pressure ceroplastic for being exclusively used in essence casting Ludox, comprise the following steps：Wax injector oil pressure, holding temperature, operation button are checked, it is handled normal condition, and ready cooling water；Wax cylinder is taken out from incubator, on wax injector, squeezes the wax material that net top is mixed with air；Mould is placed on wax injector work top, adjustment workbench makes mould casting mouth with penetrating the highly consistent of hawfinch, all fuse loose piece positions of mould are checked in correct position, the smooth opening mould of mould open/close, spray releasing agent, hawfinch is penetrated into the alignment of mould casting mouth after matched moulds；Play button is pressed, suppresses wax-pattern；By dismounting order, fuse is extracted out, open mould, it is careful to take out wax part, it is put into cooling water and cools down；Wax bits, the releasing agent on mold parting surface and fuse are removed with compressed air；Wax part is gently taken out from cooling water after 25 hours, blows off wax bits and the globule with compressed air, and qualified wax part is properly placed in tray by self-test.
Description
Technical field
The present invention relates to a kind of essence casting Ludox technique, and in particular to a kind of pressure ceroplastic for being exclusively used in essence casting Ludox.
Background technology
Ludox technique belongs to precision-investment casting, is a kind of few cutting or the casting technique without cutting.It is to cast at present
One of most classical technology of industry, and hardware casting, stainless cast steel part, sewing casting and weaving casting guaranteed quality exquisiteness compared with
Strong technique.At present, the pressure ceroplastic in existing essence casting Ludox technique, due to penetrate wax pressure is big, penetrate hawfinch temperature for it is low,
Dwell time is grown, and causes wax part the shortcomings that not wear-resisting, service life is short, hardness is low to be present.
The content of the invention
It is an object of the invention to provide a kind of pressure ceroplastic for being exclusively used in essence casting Ludox, after the pressure ceroplastic,
Wax part has the characteristics of wearability is strong, service life is long, hardness is high.
In order to achieve the above object, the pressure ceroplastic for being exclusively used in essence casting Ludox of the invention, comprises the following steps：
A checks wax injector oil pressure, holding temperature, operation button, it is handled normal condition, and the wax pressure of penetrating for adjusting wax injector is
0.25-0.40Mpa, hawfinch temperature is penetrated as 56-60 DEG C, dwell time ＞ 8 hours, and ready cooling water；
B takes out wax cylinder from incubator, on wax injector, squeezes the wax material that net top is mixed with air；
By through examining qualified mould to be placed on wax injector work top, adjustment workbench makes mould casting mouth and penetrates hawfinch c
It is highly consistent, check that all fuse loose piece positions of mould are smooth in correct position, mould open/close；
D opens mould, sprays releasing agent, is directed at mould casting mouth after matched moulds and penetrates hawfinch；
E both hands press play button, suppress wax-pattern；
F presses dismounting order, extracts fuse out, opens mould, careful to take out wax part by using compressed air, and will be selected after wax
Part is put into cooling water and cooled down；
G removes wax bits, the releasing agent on mold parting surface and fuse by using compressed air or special bamboo knife；
After h wax parts cool down 2-5 hours in cooling water, wax part is gently taken out from cooling water, blowing off wax with compressed air considers to be worth doing
And the globule, and self-test is carried out, qualified wax part is properly placed in tray.
Further, the temperature of the cooling water in described step a is less than 10 DEG C.
Further, after the wax cylinder in described step b shoots away wax, incubator inside holding is sent back in time.
Further, selected in described step f have including scrapping serious bubble the unsharp wax part of wax part, corner angle,
Deform the wax part that can not be repaired, size wax part against regulation.
Further, the cooling water in described step f need to be changed once daily.
In the above-mentioned technical solutions, due to by the way that the wax pressure of penetrating for adjusting wax injector to be 0.25-0.40Mpa, penetrate hawfinch
Temperature is 56-60 DEG C, dwell time ＞ 8 hours, both ensure that the toughness of wax part, resistance to corrosion, abrasive resistance and had born to rush
The ability of load is hit, and effectively extends the service life of wax part.
Embodiment
The pressure ceroplastic for being exclusively used in essence casting Ludox of the present invention is described further with reference to specific implementation；
Implementation column 1
The pressure ceroplastic for being exclusively used in essence casting Ludox of the present invention, comprises the following steps：
A checks wax injector oil pressure, holding temperature, operation button, it is handled normal condition, and the wax pressure of penetrating for adjusting wax injector is
0.25Mpa, penetrate hawfinch temperature be 56 DEG C, the dwell time be 9 hours, and ready cooling water；
B takes out wax cylinder from incubator, on wax injector, squeezes the wax material that net top is mixed with air；
By through examining qualified mould to be placed on wax injector work top, adjustment workbench makes mould casting mouth and penetrates hawfinch c
It is highly consistent, check that all fuse loose piece positions of mould are smooth in correct position, mould open/close；
D opens mould, sprays releasing agent, is directed at mould casting mouth after matched moulds and penetrates hawfinch；
E both hands press play button, suppress wax-pattern；
F presses dismounting order, extracts fuse out, opens mould, careful to take out wax part by using compressed air, and will be selected after wax
Part is put into cooling water and cooled down；
G removes wax bits, the releasing agent on mold parting surface and fuse by using compressed air or special bamboo knife；
After h wax parts cool down 2 hours in cooling water, wax part is gently taken out from cooling water, with compressed air blow off wax bits and
The globule, and self-test is carried out, qualified wax part is properly placed in tray.
Implementation column 2
1st, the pressure ceroplastic for being exclusively used in essence casting Ludox of the invention, comprises the following steps：
A checks wax injector oil pressure, holding temperature, operation button, it is handled normal condition, and the wax pressure of penetrating for adjusting wax injector is
0.30Mpa, penetrate hawfinch temperature be 58 DEG C, the dwell time be 10 hours, and ready cooling water；
B takes out wax cylinder from incubator, on wax injector, squeezes the wax material that net top is mixed with air；
By through examining qualified mould to be placed on wax injector work top, adjustment workbench makes mould casting mouth and penetrates hawfinch c
It is highly consistent, check that all fuse loose piece positions of mould are smooth in correct position, mould open/close；
D opens mould, sprays releasing agent, is directed at mould casting mouth after matched moulds and penetrates hawfinch；
E both hands press play button, suppress wax-pattern；
F presses dismounting order, extracts fuse out, opens mould, careful to take out wax part by using compressed air, and will be selected after wax
Part is put into cooling water and cooled down；
G removes wax bits, the releasing agent on mold parting surface and fuse by using compressed air or special bamboo knife；
After h wax parts cool down 4 hours in cooling water, wax part is gently taken out from cooling water, with compressed air blow off wax bits and
The globule, and self-test is carried out, qualified wax part is properly placed in tray.
Embodiment 3
The pressure ceroplastic for being exclusively used in essence casting Ludox of the present invention, comprises the following steps：
A checks wax injector oil pressure, holding temperature, operation button, it is handled normal condition, and the wax pressure of penetrating for adjusting wax injector is
0.40Mpa, penetrate hawfinch temperature be 60 DEG C, the dwell time be 12 hours, and ready cooling water；
B takes out wax cylinder from incubator, on wax injector, squeezes the wax material that net top is mixed with air；
By through examining qualified mould to be placed on wax injector work top, adjustment workbench makes mould casting mouth and penetrates hawfinch c
It is highly consistent, check that all fuse loose piece positions of mould are smooth in correct position, mould open/close；
D opens mould, sprays releasing agent, is directed at mould casting mouth after matched moulds and penetrates hawfinch；
E both hands press play button, suppress wax-pattern；
F presses dismounting order, extracts fuse out, opens mould, careful to take out wax part by using compressed air, and will be selected after wax
Part is put into cooling water and cooled down；
G removes wax bits, the releasing agent on mold parting surface and fuse by using compressed air or special bamboo knife；
After h wax parts cool down 5 hours in cooling water, wax part is gently taken out from cooling water, with compressed air blow off wax bits and
The globule, and self-test is carried out, qualified wax part is properly placed in tray.
In the various embodiments described above, the temperature of the cooling water in described step a is less than 10 DEG C；In described step b
Wax cylinder shoot away wax after, to send incubator inside holding back in time；Selected in described step f has serious bubble including scrapping
The unsharp wax part of wax part, corner angle, deform the wax part that can not be repaired, size wax part against regulation；In described step f
Cooling water need to be changed once daily.
Claims (5)
1. a kind of pressure ceroplastic for being exclusively used in essence casting Ludox, comprises the following steps：
A checks wax injector oil pressure, holding temperature, operation button, it is handled normal condition, and the wax pressure of penetrating for adjusting wax injector is
0.25-0.40Mpa, hawfinch temperature is penetrated as 56-60 DEG C, dwell time ＞ 8 hours, and ready cooling water；
B takes out wax cylinder from incubator, on wax injector, squeezes the wax material that net top is mixed with air；
By through examining qualified mould to be placed on wax injector work top, adjustment workbench makes mould casting mouth and penetrates hawfinch c
It is highly consistent, check that all fuse loose piece positions of mould are smooth in correct position, mould open/close；
D opens mould, sprays releasing agent, is directed at mould casting mouth after matched moulds and penetrates hawfinch；
E both hands press play button, suppress wax-pattern；
F presses dismounting order, extracts fuse out, opens mould, careful to take out wax part by using compressed air, and will be selected after wax
Part is put into cooling water and cooled down；
G removes wax bits, the releasing agent on mold parting surface and fuse by using compressed air or special bamboo knife；
After h wax parts cool down 2-5 hours in cooling water, wax part is gently taken out from cooling water, blowing off wax with compressed air considers to be worth doing
And the globule, and self-test is carried out, qualified wax part is properly placed in tray.
2. the kind according to claim into 1 is exclusively used in the pressure ceroplastic of essence casting Ludox, it is characterised in that：Described step
The temperature of cooling water in a is less than 10 DEG C.
3. the kind according to claim into 1 is exclusively used in the pressure ceroplastic of essence casting Ludox, it is characterised in that：Described step
After wax cylinder in b shoots away wax, incubator inside holding is sent back in time.
4. the kind according to claim into 1 is exclusively used in the pressure ceroplastic of essence casting Ludox, it is characterised in that：Described step
The selected wax part for having the unsharp wax part of wax part, corner angle of serious bubble, deformation to repair including scrapping, size in f are not
Wax part as defined in meeting.
5. the kind according to claim into 1 is exclusively used in the pressure ceroplastic of essence casting Ludox, it is characterised in that：Described step
Cooling water in f need to be changed once daily.