CN107836766A - A kind of processing technology for emulating bark trunk - Google Patents
A kind of processing technology for emulating bark trunk Download PDFInfo
- Publication number
- CN107836766A CN107836766A CN201610858843.4A CN201610858843A CN107836766A CN 107836766 A CN107836766 A CN 107836766A CN 201610858843 A CN201610858843 A CN 201610858843A CN 107836766 A CN107836766 A CN 107836766A
- Authority
- CN
- China
- Prior art keywords
- bark
- trunk
- mould
- emulation
- emulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of processing technology for emulating bark trunk, comprises the following steps：Step 1, mold；Step 2, production material is selected：Production material includes resin 10~25%, color essence 1~5%, curing agent 0.25~5%, silica 0.25~15%, polyurethane list 5~10%, oxidized starch 10~25% and silica gel 25~40%；Step 3, produced in mould：Above-mentioned production material is put into emulation bark trunk mould and heats production definition；Step 4, paint：Coloured accordingly as requested by coloring agent；Compared with prior art, the present invention has following beneficial effect：The present invention compensate for natural tree " exposed section ", fidelity is good, plasticity is strong, it is Well-recovered, resistance to expose to wind and rain, usage time is long, stability and wearability are strong, not fugitive color, easy to operate, it is especially more perfect to irregular " exposed section " effect process, and it is easy construction, cheap, it can be widely used for the processing of natural tree decoration.
Description
Technical field
The present invention is a kind of processing technology for emulating bark trunk, belongs to emulation bark and preparation method thereof.
Background technology
Emulation is exactly a kind of real thing of imitation, and emulation plant is exactly technical staff's imitation phytomorph and developed
Thing is heeled in, as industry constantly develops, the progress of technology, emulation plant, the exploitation of preservative plant and carrying for art reprocessing
Rise, more emulation plants are harmonious by the perfection for annotating man and nature.
The advantages of emulation plant, is：
First, bionical landscape plant is emulated not restricted by natural conditions such as sunlight, air, moisture, seasons, can be according to existing
Need to follow one's inclinations from floristics, no matter northwest desert or bleak and desolate gobi can build the green generation that it's like spring all the year round
Boundary；
2nd, without watering, fertilising, withered and fallen without worrying that plant is withered, a large amount of expenses are save for management in the future.
In natural landscape, primary trees due to the natural causes such as thunder and lightning, insect pest, frost and mismanagement etc. it is artificial because
There is vacancy, breakage in element, bark, and people need to be repaired using bark is emulated.
The content of the invention
In view of the deficienciess of the prior art, it is an object of the present invention to provide it is a kind of emulate bark trunk processing technology, with
Solve the problems, such as to propose in above-mentioned background technology.
To achieve these goals, the present invention is to realize by the following technical solutions：A kind of emulation bark trunk
Processing technology, comprise the following steps：
Step 1, mold：To be cleaned up with the emulation bark trunk die surface of emulation Bark mark reason, wipes it is air-dried,
Then in emulation bark trunk mould texture face spray last layer oil-based release agent；
Step 2, production material is selected：Production material include resin 10~25%, color essence 1~5%, curing agent 0.25~
5%th, silica 0.25~15%, polyurethane list 5~10%, oxidized starch 10~25% and silica gel 25~40%；
Step 3, produced in mould：Above-mentioned production material is put into emulation bark trunk mould and heats production definition；
Step 4, paint：Coloured accordingly as requested by coloring agent.
Further, in step 1, the emulation bark trunk mould is the two-component mould of silicon rubber environment-friendly materials.
Further, in step 2, production material by resin 25%, color essence 5%, curing agent 5%, silica 1 5%,
Polyurethane list 5%, oxidized starch 20% and silica gel 25% are formed.
Further, in step 2, production material includes resin 10%, color essence 3%, curing agent 5%, silica
7%th, polyurethane list 5%, oxidized starch 20% and silica gel 50% are formed.
Further, in step 3, silica gel 25~40% and color essence 1~5% are put into container first, in environment
Temperature stirs 20-30min in the environment of being 25-30 °, stirs, and after completion of stirring, adds resin 10~25% and consolidates
Agent 0.25~5%, 60-70min is stirred in the environment of being 25-30 ° in environment temperature, stirs, then adds in container
Enter silica 0.25~15%, polyurethane list 5~10% and oxidized starch 10~25%, a semifused is equably fallen
With hairbrush the mixture on die surface fully brushed in emulation bark trunk mould texture aspect, in 5~20 minutes it is even, in ring
At a temperature of border temperature is 27-32 °, 5-15min is placed, then another semifused is equably poured on to emulation bark trunk mould
Have texture aspect, with hairbrush the mixture on die surface fully brushed in 5~20 minutes it is even, in the environment that temperature is 25-30 °
Heat cure shaping in lower 120~180 minutes, the demoulding, obtain emulation bark.
Further, in step 4, after obtaining emulation bark, using coloring agent by spraying or smearing colouring.
Beneficial effects of the present invention：A kind of processing technology of emulation bark trunk of the present invention, the present invention compensate for naturally
Trees " exposed section ", fidelity is good, plasticity is strong, it is Well-recovered, resistance to expose to wind and rain, usage time is long, stability and wearability
By force, not fugitive color, easy to operate, it is especially more perfect to irregular " exposed section " effect process and easy construction, cheap, can
It is widely used in the processing of natural tree decoration.
Embodiment
To be easy to understand the technical means, the inventive features, the objects and the advantages of the present invention, with reference to
Embodiment, the present invention is expanded on further.
The present invention provides a kind of technical scheme：A kind of processing technology for emulating bark trunk, comprises the following steps：
Step 1, mold：To be cleaned up with the emulation bark trunk die surface of emulation Bark mark reason, wipes it is air-dried,
Then in emulation bark trunk mould texture face spray last layer oil-based release agent；
Step 2, production material is selected：Production material include resin 10~25%, color essence 1~5%, curing agent 0.25~
5%th, silica 0.25~15%, oxidized starch 10~25% and silica gel 25~40%；
Step 3, produced in mould：Above-mentioned production material is put into emulation bark trunk mould and heats production definition；
Step 4, paint：Coloured accordingly as requested by coloring agent.
In step 1, the emulation bark trunk mould is the two-component mould of silicon rubber environment-friendly materials.
In step 2, production material is by resin 25%, color essence 5%, curing agent 5%, silica 1 5%, polyurethane list
5%th, oxidized starch 20% and silica gel 25% are formed.
In step 2, production material includes resin 10%, color essence 3%, curing agent 5%, silica 7%, polyurethane list
5%th, oxidized starch 20% and silica gel 50% are formed.
In step 3, silica gel 25~40% and color essence 1~5% are put into container first, are 25- in environment temperature
20-30min is stirred in the environment of 30 °, is stirred, after completion of stirring, adds resin 10~25% and curing agent 0.25
~5%, 60-70min is stirred in the environment of being 25-30 ° in environment temperature, stirs, titanium dioxide is then added in container
Silicon 0.25~15%, polyurethane list 5~10% and oxidized starch 10~25%, a semifused is equably poured on artificial tree
Skin trunk mould texture aspect, with hairbrush is fully brushed the mixture on die surface even in 5~20 minutes, be in environment temperature
At a temperature of 27-32 °, 5-15min is placed, then another semifused is equably poured on to emulation bark trunk mould texture layer
Face, with hairbrush the mixture on die surface fully brushed in 5~20 minutes it is even, 120 in the environment of being 25-30 ° in temperature~
Heat cure is molded in 180 minutes, the demoulding, obtains emulation bark.
In step 4, after obtaining emulation bark, using coloring agent by spraying or smearing colouring.
As one embodiment of the present of invention：The present invention compensate for natural tree " exposed section ", and fidelity is good, plasticity
By force, it is Well-recovered, resistance to expose to wind and rain, usage time is long, stability and wearability are strong, not fugitive color, easy to operate, especially to not advising
Then " exposed section " effect process is more perfect, and easy construction, cheap, can be widely used for the processing of natural tree decoration.
As an alternative embodiment of the invention：Comprise the following steps：
Step 1, mold：To be cleaned up with the emulation bark trunk die surface of emulation Bark mark reason, wipes it is air-dried,
Then in emulation bark trunk mould texture face spray last layer oil-based release agent, emulation bark trunk mould is silicon rubber environmental protection material
The two-component mould of material；
Step 2, production material is selected：Production material includes resin 25%, color essence 3%, curing agent 3%, silica
14%th, polyurethane list 5%, oxidized starch 20% and silica gel 30%；
Step 3, produced in mould：Above-mentioned production material is put into emulation bark trunk mould and heats production definition, it is first
First silica gel 30% and color essence 3% are put into container, 20-30min is stirred in the environment of being 25-30 ° in environment temperature, stirs
Uniformly, after completion of stirring, resin 25% and curing agent 3% are added, 60- is stirred in the environment of being 25-30 ° in environment temperature
70min, stir, silica 1 4%, polyurethane list 5% and oxidized starch 20% are then added in container, by one
Semifused is equably poured on emulation bark trunk mould texture aspect, will be mixed on die surface with hairbrush in 5~20 minutes
Compound fully brush it is even, environment temperature be 27-32 ° at a temperature of, place 5-15min, then by another semifused equably
Be poured on emulation bark trunk mould texture aspect, with hairbrush the mixture on die surface fully brushed in 5~20 minutes it is even,
Heat cure shaping in 120~180 minutes in the environment of temperature is 25-30 °, the demoulding, obtains emulation bark；
Step 4, paint：After obtaining emulation bark, using coloring agent by spraying or smearing colouring.
As an alternative embodiment of the invention：Comprise the following steps：
Step 1, mold：To be cleaned up with the emulation bark trunk die surface of emulation Bark mark reason, wipes it is air-dried,
Then in emulation bark trunk mould texture face spray last layer oil-based release agent, emulation bark trunk mould is silicon rubber environmental protection material
The two-component mould of material；
Step 2, production material is selected：Production material includes resin 10%, color essence 3%, curing agent 5%, silica
7%th, polyurethane list 5%, oxidized starch 20% and silica gel 50% are formed；
Step 3, produced in mould：Above-mentioned production material is put into emulation bark trunk mould and heats production definition, it is first
First silica gel 50% and color essence 3% are put into container, 20-30min is stirred in the environment of being 25-30 ° in environment temperature, stirs
Uniformly, after completion of stirring, resin 10% and curing agent 5% are added, 60- is stirred in the environment of being 25-30 ° in environment temperature
70min, stir, silica 1 5%, polyurethane list 5% and oxidized starch 20% are then added in container, by one
Semifused is equably poured on emulation bark trunk mould texture aspect, will be mixed on die surface with hairbrush in 5~20 minutes
Compound fully brush it is even, environment temperature be 27-32 ° at a temperature of, place 5-15min, then by another semifused equably
Be poured on emulation bark trunk mould texture aspect, with hairbrush the mixture on die surface fully brushed in 5~20 minutes it is even,
Heat cure shaping in 120~180 minutes in the environment of temperature is 25-30 °, the demoulding, obtains emulation bark；
Step 4, paint：After obtaining emulation bark, using coloring agent by spraying or smearing colouring.
As an alternative embodiment of the invention：Comprise the following steps：
Step 1, mold：To be cleaned up with the emulation bark trunk die surface of emulation Bark mark reason, wipes it is air-dried,
Then in emulation bark trunk mould texture face spray last layer oil-based release agent, emulation bark trunk mould is silicon rubber environmental protection material
The two-component mould of material；
Step 2, production material is selected：Production material includes resin 10%, color essence 3%, curing agent 5%, silica
7%th, polyurethane list 5%, oxidized starch 20% and silica gel 50% are formed；
Step 3, produced in mould：Above-mentioned production material is put into emulation bark trunk mould and heats production definition, it is first
First silica gel 50% and color essence 3% are put into container, 20-30min is stirred in the environment of being 25-30 ° in environment temperature, stirs
Uniformly, after completion of stirring, resin 10% and curing agent 5% are added, 60- is stirred in the environment of being 25-30 ° in environment temperature
70min, stir, silica 1 5%, polyurethane list 5% and oxidized starch 20% are then added in container, by one
Semifused is equably poured on emulation bark trunk mould texture aspect, will be mixed on die surface with hairbrush in 5~20 minutes
Compound fully brush it is even, environment temperature be 27-32 ° at a temperature of, place 5-15min, then by another semifused equably
Be poured on emulation bark trunk mould texture aspect, with hairbrush the mixture on die surface fully brushed in 5~20 minutes it is even,
Heat cure shaping in 120~180 minutes in the environment of temperature is 25-30 °, the demoulding, obtains emulation bark；
Step 4, paint：After obtaining emulation bark, using coloring agent by spraying or smearing colouring.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above, for this area skill
For art personnel, it is clear that the invention is not restricted to the details of above-mentioned one exemplary embodiment, and without departing substantially from the present invention spirit or
In the case of essential characteristic, the present invention can be realized in other specific forms.Which point therefore, no matter from the point of view of, all should incite somebody to action
Embodiment regards exemplary as, and be it is nonrestrictive, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that all changes fallen in the implication and scope of the equivalency of claim are included in the present invention
It is interior.Any reference in claim should not be considered as to the involved claim of limitation.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that those skilled in the art should for clarity
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It is appreciated that other embodiment.
Claims (6)
- A kind of 1. processing technology for emulating bark trunk, it is characterised in that：Comprise the following steps：Step 1, mold：By the trunk from true bark unity and coherence in writing, by cat scanner and making, it is made with emulation Bark mark The emulation bark trunk mould of reason, the emulation bark trunk die surface with emulation Bark mark reason is cleaned up, wipes wind It is dry, then in emulation bark trunk mould texture face spray last layer oil-based release agent；Step 2, production material is selected：Production material includes resin 10~25%, color essence 1~5%, curing agent 0.25~5%, two Silica 0.25~15%, polyurethane list 5~10%, oxidized starch 10~25% and silica gel 25~40%；Step 3, produced in mould：Above-mentioned production material is put into emulation bark trunk mould and heats production definition；Step 4, paint：Coloured accordingly as requested by coloring agent.
- A kind of 2. processing technology for emulating bark trunk according to claim 1, it is characterised in that：In step 1, it is described Emulate the two-component mould that bark trunk mould is silicon rubber environment-friendly materials.
- A kind of 3. processing technology for emulating bark trunk according to claim 1, it is characterised in that：In step 2, produce Material is by resin 25%, color essence 5%, curing agent 5%, silica 1 5%, polyurethane list 5%, oxidized starch 20% and silicon Glue 25% is formed.
- A kind of 4. processing technology for emulating bark trunk according to claim 1, it is characterised in that：In step 2, produce Material includes resin 10%, color essence 3%, curing agent 5%, silica 7%, polyurethane list 5%, oxidized starch 20% and silicon Glue 50% is formed.
- A kind of 5. processing technology for emulating bark trunk according to claim 1, it is characterised in that：In step 3, first Silica gel 25~40% and color essence 1~5% are put into container, 20- is stirred in the environment of being 25-30 ° in environment temperature 30min, stir, after completion of stirring, add resin 10~25% and curing agent 0.25~5%, be in environment temperature 60-70min is stirred in the environment of 25-30 °, is stirred, silica 0.25~15%, polyurethane are then added in container List 5~10% and oxidized starch 10~25%, a semifused is equably poured on to emulation bark trunk mould texture aspect, With hairbrush the mixture on die surface fully brushed even in 5~20 minutes, at a temperature of environment temperature is 27-32 °, placed 5-15min, then another semifused is equably poured on to emulation bark trunk mould texture aspect, hair is used in 5~20 minutes Brush fully brushes the mixture on die surface even, thermosetting chemical conversion in 120~180 minutes in the environment of being 25-30 ° in temperature Type, the demoulding, obtain emulation bark.
- A kind of 6. processing technology for emulating bark trunk according to claim 1, it is characterised in that：In step 4, obtain After emulating bark, using coloring agent by spraying or smearing colouring.