A kind of preparation method of oxytolerant chemical industry armor band Download PDFInfo
- Publication number
- CN107828348A CN107828348A CN201711119955.9A CN201711119955A CN107828348A CN 107828348 A CN107828348 A CN 107828348A CN 201711119955 A CN201711119955 A CN 201711119955A CN 107828348 A CN107828348 A CN 107828348A
- Authority
- CN
- China
- Prior art keywords
- parts
- cleaning fluid
- oxytolerant
- chemical industry
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of oxytolerant chemical industry armor band, including following operating procedure：（1）Glass fibre ribbon is put into cleaning fluid, after cleaning, drying and processing, wherein cleaning fluid are made up of the component of following parts by weight：19 25 parts of decanedioic acid disodium salt, 13 16 parts of 1 sodium heptanesulfonate, 13 parts of citric acid stearoyl monoglyceride, 48 parts of ammonium pentaborate, 8 10 parts of sodium perborate, 250 300 parts of water；（2）Again on glass fibre ribbon external coating after binding agent, finished product.A kind of preparation method of oxytolerant chemical industry armor band provided by the invention, simple to operate, cost is cheap, green, and obtained industrial armor band, every excellent in mechanical performance, cohesive force is strong, and especially it has excellent oxidation resistent susceptibility.
Description
Technical field
The invention belongs to the preparing technical field of industrial armor band, and in particular to a kind of preparation of oxytolerant chemical industry armor band
Method.
Background technology
Armoring tape, also known as armor band, fiberglass adhesive tape, i.e. fiberglass adhesive tape, at home also known as industrial plate armour twine
Around band, winding band, armor band or belt armour.Armoring tape be special glass fibre is woven into high intensity, high-elastic structure is knitted
Thing, then braiding belt surface coating water cure high-molecular compound and a kind of manufactured fiberglass product.It has chance water quick
Solidification, easy to operate and the features such as have a wide range of application, the works bending strength and tensile strength that are formed after solidification be high, nontoxic nothing
Taste is non-stimulated, water-fast corrosion-resistant.Because its is easy to use, be easy to carry, and can random-shaping, in recent years more and more by
It is applied to the fields such as the cable accessory of power communication, chemical industry, ocean, mining industry, automobile making, shipbuilding, statue, medical treatment.Existing skill
Armor band in art, easily it is oxidized, and then fails during use.
The content of the invention
In order to solve the above-mentioned technical problem, the present invention provides a kind of preparation method of oxytolerant chemical industry armor band.
The present invention is achieved by the following technical solutions.
A kind of preparation method of oxytolerant chemical industry armor band, including following operating procedure：
（1）Glass fibre ribbon is put into cleaning fluid, clean after, drying and processing, wherein cleaning fluid by following parts by weight group
Divide and be made：Decanedioic acid disodium salt 19-25 parts, 1- sodium heptanesulfonate 13-16 parts, citric acid stearoyl monoglyceride 1-3 parts, five boron
Sour ammonium 4-8 parts, sodium perborate 8-10 parts, water 250-300 parts；
（2）Again on glass fibre ribbon external coating after binding agent, finished product, wherein binding agent by following parts by weight group
Divide and be made：Butyl acrylate 88-92 parts, acrylamide 3-6 parts, acrylic acid 8-10 parts, Morpholine fatty acid salt fruit wax 2-5 parts, Asia
Ethyl dioleoyl amine 1-4 parts, ammonium persulfate 0.6-0.9 parts, water 70-80 parts.
Specifically, above-mentioned steps（1）In, when cleaning fluid cleans, the temperature of cleaning fluid is 40-45 DEG C.
Specifically, above-mentioned steps（2）In, binding agent is made of following methods：By acrylamide, acrylic acid, morpholine fat
Fat hydrochlorate fruit wax, ethylene oleamide, ammonium persulfate are added into water, after heating the mixture to 88-92 DEG C, slowly to it
Middle addition butyl acrylate, after the completion of charging, it is incubated and continues after stirring 2-3 hours, binding agent is made.
Technical scheme more than, the beneficial effects of the invention are as follows：
A kind of preparation method of oxytolerant chemical industry armor band provided by the invention, simple to operate, cost is cheap, green, system
The industrial armor band obtained, every excellent in mechanical performance, cohesive force is strong, and especially it has excellent oxidation resistent susceptibility.The present invention
The cleaning fluid of offer, can effectively remove the greasy dirt on glass fibre ribbon surface, and and can strengthens the adhesion of remaining binding agent；
Binding agent provided by the invention, oxidation resistent susceptibility is excellent, effectively extends the service life of armor band.
Embodiment
Below by specific embodiment, the present invention is described in detail, but the purposes of these illustrative embodiments and
Purpose is only used for enumerating the present invention, not forms any type of any restriction to the real protection scope of the present invention, more non-to incite somebody to action
Protection scope of the present invention is confined to this.
Embodiment 1
A kind of preparation method of oxytolerant chemical industry armor band, including following operating procedure：
（1）Glass fibre ribbon is put into cleaning fluid, clean after, drying and processing, wherein cleaning fluid by following parts by weight group
Divide and be made：19 parts of decanedioic acid disodium salt, 13 parts of 1- sodium heptanesulfonates, 1 part of citric acid stearoyl monoglyceride, 4 parts of ammonium pentaborate,
8 parts of sodium perborate, 250 parts of water；
（2）Again on glass fibre ribbon external coating after binding agent, finished product, wherein binding agent by following parts by weight group
Divide and be made：88 parts of butyl acrylate, 3 parts of acrylamide, 8 parts of acrylic acid, 2 parts of Morpholine fatty acid salt fruit wax, ethylene oleoyl
1 part of amine, 0.6 part of ammonium persulfate, 70 parts of water.
Specifically, above-mentioned steps（1）In, when cleaning fluid cleans, the temperature of cleaning fluid is 40 DEG C.
Specifically, above-mentioned steps（2）In, binding agent is made of following methods：By acrylamide, acrylic acid, morpholine fat
Fat hydrochlorate fruit wax, ethylene oleamide, ammonium persulfate are added into water, after heating the mixture to 88 DEG C, slowly thereto
Butyl acrylate is added, after the completion of charging, after being incubated and continuing stirring 2 hours, binding agent is made.
Embodiment 2
A kind of preparation method of oxytolerant chemical industry armor band, including following operating procedure：
（1）Glass fibre ribbon is put into cleaning fluid, clean after, drying and processing, wherein cleaning fluid by following parts by weight group
Divide and be made：22 parts of decanedioic acid disodium salt, 15 parts of 1- sodium heptanesulfonates, 2 parts of citric acid stearoyl monoglyceride, 6 parts of ammonium pentaborate,
9 parts of sodium perborate, 280 parts of water；
（2）Again on glass fibre ribbon external coating after binding agent, finished product, wherein binding agent by following parts by weight group
Divide and be made：90 parts of butyl acrylate, 5 parts of acrylamide, 9 parts of acrylic acid, 3 parts of Morpholine fatty acid salt fruit wax, ethylene oleoyl
2 parts of amine, 0.8 part of ammonium persulfate, 75 parts of water.
Specifically, above-mentioned steps（1）In, when cleaning fluid cleans, the temperature of cleaning fluid is 43 DEG C.
Specifically, above-mentioned steps（2）In, binding agent is made of following methods：By acrylamide, acrylic acid, morpholine fat
Fat hydrochlorate fruit wax, ethylene oleamide, ammonium persulfate are added into water, after heating the mixture to 90 DEG C, slowly thereto
Butyl acrylate is added, after the completion of charging, after being incubated and continuing stirring 2.5 hours, binding agent is made.
Embodiment 3
A kind of preparation method of oxytolerant chemical industry armor band, including following operating procedure：
（1）Glass fibre ribbon is put into cleaning fluid, clean after, drying and processing, wherein cleaning fluid by following parts by weight group
Divide and be made：25 parts of decanedioic acid disodium salt, 16 parts of 1- sodium heptanesulfonates, 3 parts of citric acid stearoyl monoglyceride, 8 parts of ammonium pentaborate,
10 parts of sodium perborate, 300 parts of water；
（2）Again on glass fibre ribbon external coating after binding agent, finished product, wherein binding agent by following parts by weight group
Divide and be made：92 parts of butyl acrylate, 6 parts of acrylamide, 10 parts of acrylic acid, 5 parts of Morpholine fatty acid salt fruit wax, ethylene oleoyl
4 parts of amine, 0.9 part of ammonium persulfate, 80 parts of water.
Specifically, above-mentioned steps（1）In, when cleaning fluid cleans, the temperature of cleaning fluid is 45 DEG C.
Specifically, above-mentioned steps（2）In, binding agent is made of following methods：By acrylamide, acrylic acid, morpholine fat
Fat hydrochlorate fruit wax, ethylene oleamide, ammonium persulfate are added into water, after heating the mixture to 92 DEG C, slowly thereto
Butyl acrylate is added, after the completion of charging, after being incubated and continuing stirring 3 hours, binding agent is made.
Claims (3)
1. a kind of preparation method of oxytolerant chemical industry armor band, it is characterised in that including following operating procedure：
（1）Glass fibre ribbon is put into cleaning fluid, clean after, drying and processing, wherein cleaning fluid by following parts by weight group
Divide and be made：Decanedioic acid disodium salt 19-25 parts, 1- sodium heptanesulfonate 13-16 parts, citric acid stearoyl monoglyceride 1-3 parts, five boron
Sour ammonium 4-8 parts, sodium perborate 8-10 parts, water 250-300 parts；
（2）Again on glass fibre ribbon external coating after binding agent, finished product, wherein binding agent by following parts by weight group
Divide and be made：Butyl acrylate 88-92 parts, acrylamide 3-6 parts, acrylic acid 8-10 parts, Morpholine fatty acid salt fruit wax 2-5 parts, Asia
Ethyl dioleoyl amine 1-4 parts, ammonium persulfate 0.6-0.9 parts, water 70-80 parts.
2. according to a kind of preparation method of oxytolerant chemical industry armor band described in claim 1, it is characterised in that above-mentioned steps
（1）In, when cleaning fluid cleans, the temperature of cleaning fluid is 40-45 DEG C.
3. according to a kind of preparation method of oxytolerant chemical industry armor band described in claim 1, it is characterised in that above-mentioned steps
（2）In, binding agent is made of following methods：By acrylamide, acrylic acid, Morpholine fatty acid salt fruit wax, ethylene oleoyl
Amine, ammonium persulfate are added into water, after heating the mixture to 88-92 DEG C, are slowly added butyl acrylate thereto, have been fed
Cheng Hou, it is incubated and continues after stirring 2-3 hours, binding agent is made.