CN107825074A - A kind of notebook bonnet processing method - Google Patents
A kind of notebook bonnet processing method Download PDFInfo
- Publication number
- CN107825074A CN107825074A CN201711090313.0A CN201711090313A CN107825074A CN 107825074 A CN107825074 A CN 107825074A CN 201711090313 A CN201711090313 A CN 201711090313A CN 107825074 A CN107825074 A CN 107825074A
- Authority
- CN
- China
- Prior art keywords
- notebook
- processing method
- bonnet
- plate
- notebook bonnet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of notebook bonnet processing method, the aluminum alloy plate materials matched with notebook bonnet dimensions are chosen first, aluminum alloy plate materials raw material is cut then according to the detailed design size of notebook bonnet, punching press is carried out to plate using punch press afterwards, the surrounding of plate is processed into the curved edge of bending, next the burr and overlap of plate are removed, sandblasting polishing then is carried out to surface；Anodized and emanation spraying paint；Finally paint vehicle is dried.The present invention is integrally formed by the way of punching press, is saved the plenty of time with respect to CNC processing, is improved production efficiency and reduce production cost, while punch process also enhances the overall intensity of bonnet.On the other hand, the present invention carries out blasting treatment, anodized in aluminum alloy surface and coats three-proofing coating so that product is overall more attractive in appearance and practical.
Description
Technical field
The present invention relates to notebook computer to produce and process field, more particularly to a kind of notebook bonnet processing method.
Background technology
With advances in technology, notebook computer also gradually spreads to huge numbers of families.The size of notebook also constantly towards
Miniaturization, become more and more frivolous, portable.Traditional notebook computer typically uses plastic casing, to ensure entirety
It is light and.But as expanding economy, the living standard of people improve, profile and material to notebook there has also been higher
Requirement.Meanwhile the lightening of notebook computer also proposes higher requirement to heat dispersion.Therefore, increasing factory
Family starts to give birth to metalliferous notebook bonnet.In the prior art, the processing of notebook bonnet mostly using CNC be molded, technique compared with
For complexity, long processing time, difficulty is big and cost is higher.
The content of the invention
In order to solve the above problems, the invention provides a kind of notebook bonnet processing method.
The present invention is realized using following scheme：
A kind of notebook bonnet processing method, comprises the following steps：
Step 1, choose the aluminum alloy plate materials matched with notebook bonnet dimensions；
Step 2, aluminum alloy plate materials raw material is cut according to the detailed design size of notebook bonnet；
Step 3, punching press is carried out to plate using punch press, the surrounding of plate is processed into the curved edge of bending；
Step 4, remove the burr and overlap of plate；
Step 5, to going to the surface after flash removed and overlap to carry out sandblasting polishing；
Step 6, the surface after polishing sandblasting carry out anodized；
Step 7, to the surface spraying paint vehicle after blasting treatment；
Step 8, paint vehicle is dried.
Further, the step 3 punching press frequency is 150-180 beats/min.
Further, the step 5 blasting treatment uses 250#~280# beades.
Further, the step 5 blast time is the 70-100 seconds.
Further, the paint vehicle is three-proofing coating.
Further, the thickness of the three-proofing coating is 50-80um.
Existing technology is compareed, the invention has the advantages that：
The present invention is integrally formed by the way of punching press, is saved the plenty of time with respect to CNC processing, is improved production efficiency and drop
Low production cost, while punch process also enhances the overall intensity of bonnet.On the other hand, the present invention enters in aluminum alloy surface
Row blasting treatment, anodized simultaneously coat three-proofing coating so that product is overall more attractive in appearance and practical.
Embodiment
For ease of skilled artisan understands that the present invention, makees further detailed below in conjunction with specific embodiment to the present invention
Thin description
The invention provides a kind of notebook bonnet processing method, comprise the following steps：
Step 1, choose the aluminum alloy plate materials matched with notebook bonnet dimensions；
Step 2, aluminum alloy plate materials raw material is cut according to the detailed design size of notebook bonnet；
Step 3, punching press is carried out to plate using punch press, the surrounding of plate is processed into the curved edge of bending；
Step 4, remove the burr and overlap of plate；
Step 5, to going to the surface after flash removed and overlap to carry out sandblasting polishing；
Step 6, the surface after polishing sandblasting carry out anodized；
Step 7, to the surface spraying paint vehicle after blasting treatment；
Step 8, paint vehicle is dried.
Wherein, the punching press frequency of step 3 is 150 beats/min.Step 5 blasting treatment uses 250# beades, during sandblasting
Between be 100 seconds.Paint vehicle employs three-proofing coating, and the thickness of three-proofing coating is 50um.When it is implemented, the punching press frequency of step 3 can
For any value between 150-180 beats/min, such as 160 times, 170 inferior.Step 5 blasting treatment bead can use 250#
Any value between~280#, such as 260#, 270#, blast time can be any value between the 70-100 seconds, such as 70 seconds, 80
Second etc..The thickness of three-proofing coating any value between 50-80um, such as 60um, 70um.
The present invention is integrally formed by the way of punching press, is saved the plenty of time with respect to CNC processing, is improved production efficiency
And production cost is reduced, while punch process also enhances the overall intensity of bonnet.On the other hand, the present invention is in aluminium alloy table
Face carries out blasting treatment, anodized and coats three-proofing coating so that product is overall more attractive in appearance and practical.
Although description of this invention combination embodiments above is carried out, those skilled in the art
Many replacements, modifications and variations can be carried out according to above-mentioned content, be obvious.Therefore, it is all such to substitute, change
Enter and change is included in scope of the appended claims.
Claims (6)
1. a kind of notebook bonnet processing method, it is characterised in that comprise the following steps：
Step 1, choose the aluminum alloy plate materials matched with notebook bonnet dimensions；
Step 2, aluminum alloy plate materials raw material is cut according to the detailed design size of notebook bonnet；
Step 3, punching press is carried out to plate using punch press, the surrounding of plate is processed into the curved edge of bending；
Step 4, remove the burr and overlap of plate；
Step 5, to going to the surface after flash removed and overlap to carry out sandblasting polishing；
Step 6, the surface after polishing sandblasting carry out anodized；
Step 7, to the surface spraying paint vehicle after blasting treatment；
Step 8, paint vehicle is dried.
2. notebook bonnet processing method according to claim 1, it is characterised in that the step 3 punching press frequency is
150-180 beats/min.
3. notebook bonnet processing method according to claim 2, it is characterised in that the step 5 blasting treatment uses
250#~280# beades.
4. notebook bonnet processing method according to claim 3, it is characterised in that the step 5 blast time is
The 70-100 seconds.
5. notebook bonnet processing method according to claim 4, it is characterised in that the paint vehicle is three-proofing coating.
6. notebook bonnet processing method according to claim 5, it is characterised in that the thickness of the three-proofing coating is 50-
80um。