CN1078201A - 平版印刷腐蚀剂 - Google Patents
平版印刷腐蚀剂 Download PDFInfo
- Publication number
- CN1078201A CN1078201A CN 92103059 CN92103059A CN1078201A CN 1078201 A CN1078201 A CN 1078201A CN 92103059 CN92103059 CN 92103059 CN 92103059 A CN92103059 A CN 92103059A CN 1078201 A CN1078201 A CN 1078201A
- Authority
- CN
- China
- Prior art keywords
- printing
- agent
- corrosive
- ferrocyanide
- general formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种固体粉末状平版印刷腐蚀剂，主
要用作平版印刷氧化锌版的腐蚀及润版，解决了以往
腐蚀剂易变质不能长期保存的问题。由于加入非离
子表面活性剂，提高了腐蚀剂的亲水能力，印刷质量
显著改善。
Description
本发明是用在平版印刷氧化锌版上的腐蚀剂。
平版印刷氧化锌版是由氧化锌粉末和绝缘性树脂共同涂在纸基上形成的。制版后为了使图文部分亲油，空白部分亲水，必须擦上腐蚀液进行腐蚀，并且在印刷机的水斗中加入润版液，开机即可印刷，一般将腐蚀液稀释数倍即可成润版液。
以前的腐蚀液一般是以亚铁氰化物（昭52-101102）或植酸（平1-259995）为主剂的，亚铁氰化物亲水性好，但在水溶液中不稳定，Fe2+易在空气中氧化成Fe3+，Fe3+在亚铁氰化物水溶液中产生兰色沉淀，所以以亚铁氰化物为主剂的腐蚀液不易长期保存;植酸亲水性差，以植酸为主剂的腐蚀液和润版液在印刷中易使版上脏，发生印刷故障。
为了使含亚铁氰化物的腐蚀剂能长期保存，将腐蚀剂作成固体粉末，使用时加适量水即可成腐蚀液，稀释数倍即可成润版液。为了达到最佳印刷效果，加适量非离子表面活性剂，特别是加通式[Ⅰ]、[Ⅱ]、[Ⅲ]、[Ⅳ]所示的化合物最为有利。
通式[Ⅰ]：
通式[Ⅱ]：
通式[Ⅲ]：
通式[Ⅳ]：
在本发明所提供的固体平版印刷腐蚀剂中，亚铁氰化物主要指亚铁氰化钾、亚铁氰化钠等，亚铁氰化物所占重量百分比为30%至50%。小于30%时，亲水性太差，易使印版上脏;大于50%时，腐蚀剂加水后，由于Fe2+离子的浓度太高，在空气中很快氧化成Fe3+，产生兰色沉淀，使腐蚀液变质。
磷酸盐在腐蚀剂中主要起缓冲PH的作用，所占重量百分比为30%至50%。磷酸盐主要指磷酸氢二钠，磷酸二氢钠，磷酸二氢钾，磷酸氢二铵，磷酸二氢铵等。
亚硫酸盐在腐蚀剂中所占重量百分比为4%至10%，在腐蚀剂溶于水后起抗氧化作用，保护Fe2+不被氧化成Fe3+。小于4%时，抗氧化效果不好;大于10%时使腐蚀液的亲水性显著下降，出现印版上脏的现象。亚硫酸盐主要指亚硫酸钠，亚硫酸铵等。
有机酸采用固体结晶性的酸，主要有柠檬酸、琥珀酸、已二酸、富马酸、马来酸、草酸、酒石酸等，有机酸所占重量百分比为5%至15%，小于5%时，加水后的腐蚀液PH值太高，印版易上脏;大于15%时，PH值太低，酸度过大，使亚硫酸盐很快分解，抗氧化性下降，Fe2+在酸度太大时很快氧化成Fe3+，产生大量兰色沉淀，使腐蚀液失效。
前述通式[Ⅰ][Ⅱ][Ⅲ][Ⅳ]表示的非离子表面活性剂，在腐蚀剂中所占重量百分比为1%至5%，小于1%时活性太低，亲水性太差;大于5%时，活性太强，易将氧化锌版上的树脂擦掉，露出纸基，印版在印刷过程中易上脏，达不到理想的印刷效果。
消泡剂主要指有机硅消泡剂，用来抑制非离子表面活性剂的泡沫，加少量即可。
以下是本发明的实施例，下列举例可做为示范，但并不是对发明的局限。
实施例1：
按下列重量称取各化合物：
亚铁氰化钾 60g
磷酸二氢钾 60g
亚硫酸钠 12g
柠檬酸 16g
AEO-9 3g
有机硅消泡剂 少量
将称好的化合物放入烧杯中，AEO-9和有机硅消泡剂是液体，但相对于固体是很少的，搅拌均匀，固体将AEO-9和有机硅消泡剂吸附，真空喷雾干燥，形成能长期保存的固体粉末状的平版印刷腐蚀剂。将上述腐蚀剂加一公斤水溶解即成为氧化锌版腐蚀液。在理光小胶印印刷机的水斗中加入由腐蚀液稀释五倍的润版液，印刷两千张版不上脏，印刷品质量上乘。加水后的腐蚀液放置三个月后不见沉淀，效果如初。
比较例1：
亚铁氰化钾 60g
磷酸二氢钾 60g
亚硫酸钠 12g
柠檬酸 16g
水 1000g
在与实施例1完全相同的条件下印刷，印刷200张左右时印版上脏，印刷品空白部分上脏。
实施例2：
按下列重量称取化合物：
亚铁氰化钾 60g
磷酸二氢铵 20g
磷酸氢二铵 20g
亚硫酸钠 6g
马来酸 20g
OP-10 4g
有机硅消泡剂 少量
用与实施例1完全相同的方法配制腐蚀剂，用与实施例1完全相同的方法和设备印刷，印刷三千张印版不上脏，印刷品质量上乘。加水后的腐蚀液放置二个月，不见沉淀，印刷效果如初。
比较例2：
亚铁氰化钾 60g
磷酸二氢铵 20g
磷酸氢二铵 20g
柠檬酸 20g
水 1000g
用与实施例1完全相同的条件下印刷，印刷300张左右时印版上脏，将该液放置三天，溶液产生大量沉淀，上机试验，印刷50张印版就上脏，无法使用。
实施例3：
亚铁氰化钾 40g
磷酸二氢钠 60g
磷酸二氢钾 60g
亚硫酸钠 10g
柠檬酸 25g
尼纳尔 5g
有机硅消泡剂 少量
用与实施例1完全相同的方法配制腐蚀剂，用与实施例1完全相同的方法和设备印刷，印刷五千张印版不上脏，印刷品质量上乘。加水后的腐蚀液放置二个月不见沉淀，印刷效果如初。
实施例4：
亚铁氰化钠 60g
磷酸二氢钠 60g
亚硫酸钠 12g
马来酸 15g
油酸聚氧乙烯酯 5g
有机硅消泡剂 少许
用与实施例1完全相同的方法配制腐蚀剂，用与实施例1完全相同的方法和设备印刷，印刷二千张印版不上脏，印刷品质量上乘。加水后的腐蚀液放置三个月不见沉淀，印刷效果如初。
Claims (1)
1、本发明提供一种固体粉末状平版印刷腐蚀剂，其中含有亚铁氰化物、磷酸盐、亚硫酸盐、有机酸、消泡剂、还至少含有一种下列通式[Ⅰ][Ⅱ][Ⅲ][Ⅳ]表示的化合物。
通式[Ⅰ]：
通式[Ⅱ]：
(CH2CH2O)n·H(R是C8-18的烷基，n=8～30)
通式[Ⅲ]：
(CH2CH2OH)2(R是C8-18的烷基)
通式[Ⅳ]：