CN107815776A - Biaxially fabric and its manufacture method containing drawing and extruding bar - Google Patents
Biaxially fabric and its manufacture method containing drawing and extruding bar Download PDFInfo
- Publication number
- CN107815776A CN107815776A CN201711002840.1A CN201711002840A CN107815776A CN 107815776 A CN107815776 A CN 107815776A CN 201711002840 A CN201711002840 A CN 201711002840A CN 107815776 A CN107815776 A CN 107815776A
- Authority
- CN
- China
- Prior art keywords
- extruding
- weft yarns
- biaxially
- bars
- weft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of biaxially fabric and its manufacture method containing drawing and extruding bar.The fabric includes:﹢ N ° weft yarns, abreast arranged according to predetermined space in ﹢ N ° with broadwise;﹢ N ° drawing and extruding bars, abreast arrange according to predetermined space and ﹢ N ° weft yarns, be stacked with ﹢ N ° weft yarns each other;N ° of weft yarn, abreast arrange according to predetermined space in N ° with broadwise, be stacked with ﹢ N ° weft yarns;N ° of drawing and extruding bar, abreast arrange according to predetermined space and N ° of weft yarn, be stacked with N ° of weft yarn each other;Bundled yarn, abreast arrange, ﹢ N ° weft yarns, ﹢ N ° drawing and extruding bars, N ° of weft yarn and N ° of drawing and extruding bar bondage are integrally formed, quantity >=1 of ﹢ N ° drawing and extruding bars and N ° of drawing and extruding bar along warp-wise.According to the biaxially fabric containing drawing and extruding bar of the present invention, because drawing and extruding bar is played a supporting role in fabric, so fabric fold or bending in process of deployment can be reduced.
Description
Technical field
The present invention relates to a kind of fabric, more particularly to a kind of biaxially fabric containing drawing and extruding bar and its manufacture
Method.
Background technology
Wind energy is a kind of regenerative resource of cleaning, and storage capacity is huge, so as to which wind energy is increasingly by the weight of countries in the world
Depending on.
With the development of wind-power electricity generation, the installed capacity of wind-driven generator is stepped up MW class, wind-force by multikilowatt
Generator capacity is even up to more than 10MW, and the lifting of wind-driven generator capacity is necessarily accompanied with the blade of wind-driven generator not
Disconnected increase, the length of blade increase to tens meters by original more than ten meters, and most long blade is up to more than 80 meters at present.
Blade the more does the more big, and the weight of blade also becomes increasing, and the safety of blower fan faces more challenges challenge, blade one
The defects of a little small, is possible to produce very detrimental effect safely to blade.The upper-lower casing of blade is to wrap up core by interior exterior skin
What material and girder perfusion formed, interior exterior skin is usually by three axles and/or biaxially fabric is formed.Interior exterior skin is in laying
During fold, bending the defects of, may result in the stripping of covering and core or girder, in turn result in the failure of blade,
Threaten fan operation safety.In addition, biaxially fabric is additionally operable to the making of web, shearing resistance effect is played in web, it is double
If the defects of fold occurs in axial direction fibre fabric, the shearing resistance effect of web can be caused to have a greatly reduced quality.When making blade, typically pass through
The artificial method for catching up with cloth eliminates the laying defects such as fold, bending, because the process is completely dependent on manually, so inevitably
There is fabric laying defect.
At present, for prevent fabric fold or bending the defects of, mainly by the pre-setting powder craft of fabric come
Solve the above problems, the pre-setting powder craft of fabric is fixed adjacent two layers fabric using pre-setting powder, can be made
Fabric keeps fiber-wall-element model and flatness, reduces the defects of bulge, fold or fabric during laying are bent.
The existing limitation of aforesaid way is:Pre-setting powder may be to the fabric reinforced composites that ultimately form
Performance have an impact;In addition, pre-setting powder needs specific condition to store, storage life is shorter.
The content of the invention
In order to solve the above problems, a kind of biaxially fabric and its manufacture method containing drawing and extruding bar are proposed.
According to the exemplary embodiment of the present invention, there is provided a kind of biaxially fabric containing drawing and extruding bar, it is described to contain
The biaxially fabric of drawing and extruding bar includes:﹢ N ° weft yarns, abreast arranged according to predetermined space in ﹢ N ° with weft direction;﹢ N °
Drawing and extruding bar, abreast arrange according to predetermined space and the ﹢ N ° weft yarns, and be stacked with the ﹢ N ° weft yarns each other;- N ° of latitudes
Yarn, abreast arrange according to predetermined space in-N ° with weft direction, and be stacked with the ﹢ N ° weft yarns;- N ° of drawing and extruding bars, each other it
Between abreast arranged according to predetermined space and the-N ° of weft yarns, and be stacked with-N ° of the weft yarns;Bundled yarn, along warp direction
Abreast arrange, the ﹢ N ° weft yarns, the ﹢ N ° the drawing and extruding bars ,-N ° of weft yarns and the-N ° of drawing and extruding bars bondage are woven into
It is integrated, wherein, quantity >=1 of the ﹢ N ° drawing and extruding bars and the-N ° of drawing and extruding bars.
According to the exemplary embodiment of the present invention, N scope can be:0 < N < 90.
According to the exemplary embodiment of the present invention, N can be 45.
According to the exemplary embodiment of the present invention, the diameter of the ﹢ N ° drawing and extruding bars and the-N ° of drawing and extruding bars can be
In the range of 0.1mm to 10mm.
According to the exemplary embodiment of the present invention, the shape of the cross section of the ﹢ N ° drawing and extruding bars and the-N ° of drawing and extruding bars can
Think circular, ellipse or rectangle.
According to the exemplary embodiment of the present invention, the quality of the biaxially fabric unit area containing drawing and extruding bar
Can be 100 to 3000g/m2In the range of, breadth can be in the range of 300mm to 3000mm.
According to the exemplary embodiment of the present invention, the ﹢ N ° weft yarns and the-N ° of weft yarns can by glass fibre, carbon fiber,
A kind of or more kinds of being made in aramid fiber, basalt fibre, Fypro and polyimide fiber composition.
According to the exemplary embodiment of the present invention, the line density of the ﹢ N ° weft yarns and the-N ° of weft yarns can be in 100tex
To 4800tex.
According to the exemplary embodiment of the present invention, the ﹢ N ° drawing and extruding bars and the-N ° of drawing and extruding bars can be by fibers and resin-made
Into the fiber can be glass fibre, carbon fiber, aramid fiber, basalt fibre, Fypro and polyimide fiber
In it is a kind of or more kinds of, the resin can be epoxy resin, polyurethane resin, vinyl epoxy resin, unsaturated poly-
It is a kind of or more kinds of in ester resin and acrylate.
According to the exemplary embodiment of the present invention, the bundled yarn and the ﹢ N ° weft yarns, the ﹢ N ° drawing and extruding bars, it is described-
Can have angle between N ° of weft yarn and the-N ° of drawing and extruding bars.
According to the exemplary embodiment of the present invention, a kind of manufacturer of the biaxially fabric containing drawing and extruding bar is improved
Method, the manufacture method include:﹢ N ° weft yarns are abreast arranged according to predetermined space in ﹢ N ° with weft direction;Each other according to
Predetermined space abreast arranges ﹢ N ° drawing and extruding bars with the ﹢ N ° weft yarns, and is stacked with the ﹢ N ° weft yarns;It it is in-N ° with weft direction
- N ° of weft yarns are abreast arranged according to predetermined space, to be stacked with the ﹢ N ° weft yarns;Each other according to predetermined space with it is described-
N ° of weft yarn abreast arranges-N ° of drawing and extruding bars, and is stacked with-N ° of the weft yarns;Abreast arranged along warp direction bundled yarn with
By the bundled yarn by the ﹢ N ° weft yarns, the ﹢ N ° the drawing and extruding bars ,-N ° of weft yarns and the-N ° of drawing and extruding bars bondage loop bonding
It is integrally formed, wherein, quantity >=1 of the ﹢ N ° drawing and extruding bars and the-N ° of drawing and extruding bars.
According to the exemplary embodiment of the present invention, wherein, N scope can be:0 < N < 90.
According to the exemplary embodiment of the present invention, N can be 45.
According to the exemplary embodiment of the present invention, the bundled yarn and the ﹢ N ° weft yarns, the ﹢ N ° drawing and extruding bars, it is described-
Can have angle between N ° of weft yarn and the-N ° of drawing and extruding bars.
According to the biaxially fabric containing drawing and extruding bar of the present invention, because drawing and extruding bar plays necessarily in fabric
Supporting role, it is possible to reduce fabric in process of deployment the defects of layer of cloth fold, bulge or fiber bending, so as to
Ensure the performance of paving quality and fabric reinforced composites;Due to the fiber-wall-element model of fabric can be kept, so
After laying perfusion, be advantageous to keep the proper property of fabric reinforced composites.
According to the present invention the biaxially fabric containing drawing and extruding bar, because drawing and extruding bar degree of orientation is higher, thus with
Fabric after conventional perfusion is compared, and is had higher mechanical property, is knitted so as to improve final fiber to a certain extent
Thing strengthens the mechanical property of composite.
Brief description of the drawings
Fig. 1 is the signal for the biaxially fabric containing drawing and extruding bar for showing the exemplary embodiment according to the present invention
Figure.
Embodiment
The exemplary embodiment of the present invention is described in detail below in conjunction with accompanying drawing.Throughout the specification, it is identical
Label indicate identical part all the time.
Generally, the length and width of fabric is defined below:The length parallel with selvedge is referred to as coupe, the direction of coupe
It is exactly the warp-wise of fabric;Perpendicular length is referred to as breadth with selvedge, and the direction of breadth is the broadwise of fabric.
Fig. 1 is the signal for the biaxially fabric containing drawing and extruding bar for showing the exemplary embodiment according to the present invention
Figure.In Fig. 1, horizontal direction is the warp direction of biaxially fabric, and vertical direction is the broadwise of biaxially fabric
Direction;The angle obtained from weft direction along rotate counterclockwise is positive-angle, correspondingly, from weft direction along dextrorotation
The angle for turning to obtain is negative angle.
As shown in figure 1, included according to the biaxially fabric containing drawing and extruding bar of the exemplary embodiment of the present invention:﹢
N ° of weft yarn 31, abreast arranged according to predetermined space in ﹢ N ° with weft direction;﹢ N ° drawing and extruding bars 41, each other according between predetermined
Abreast arranged every with ﹢ N ° weft yarns 31, and it is stacked with ﹢ N ° weft yarns 31;- N ° of weft yarns 51, with weft direction in-N ° according between predetermined
Every abreast arranging, and it is stacked with ﹢ N ° weft yarns 31;- N ° of drawing and extruding bars 61 are flat according to predetermined space and-N ° of weft yarns 51 each other
Arrange capablely, and it is stacked with-N ° of weft yarns 51;Bundled yarn 71, abreast arranged along warp direction, by ﹢ N ° weft yarns 31, ﹢ N °
Drawing and extruding bar 41 ,-N ° of weft yarns 51 and the-N ° of bondage loop bondings of drawing and extruding bar 61 are integrally formed, wherein, the drawing and extruding bars of ﹢ N ° 41 and-N ° of drawing and extruding bars 61
Quantity >=1.
Here, ﹢ N ° drawing and extruding bars 41 are making the mistake of the biaxially fabric containing drawing and extruding bar with stacked refer to of ﹢ N ° weft yarns 31
N ° of drawing and extruding bar of Cheng Zhong, ﹢ 41 be placed on one layer of ﹢ N ° weft yarn 31 or under., can be by ﹢ N ° drawing and extruding bars 41 in bondage loop bonding
With the Split Down of ﹢ N ° weft yarns 31, then loop bonding;﹢ N ° drawing and extruding bars 41 can not also be directly woven into the Split Down of ﹢ N ° weft yarns 31.It is similar
Ground, with the stacked finger of-N ° of weft yarns 51 during the biaxially fabric containing drawing and extruding bar is made ,-N ° are drawn-N ° of drawing and extruding bars 61
Squeeze rod 61 be placed on one layer of-N ° of weft yarn 51 or under., can be by-N ° of drawing and extruding bars 61 and-N ° of weft yarns 51 in bondage loop bonding
Split Down, then loop bonding;- N ° of drawing and extruding bars 61 can not also be directly woven into-N ° of the Split Down of weft yarn 51.
Alternatively, N span can be 0 < N < 90, it is preferable that can be 60,90 etc., N is preferably 45.
Alternatively, the diameter of ﹢ N ° drawing and extruding bars 41 and-N ° of drawing and extruding bars 61 can be in the range of 0.1mm to 10mm.
Alternatively, ﹢ N ° drawing and extruding bars 41 and circular, the oval or rectangle that is shaped as of the cross section of-N ° of drawing and extruding bars 61, but
According to the exemplary embodiment not limited to this of the present invention, the cross section of ﹢ N ° drawing and extruding bars 41 and-N ° of drawing and extruding bars 61 can also be other
Suitable shape.
Alternatively, ﹢ N ° drawing and extruding bars 41 and-N ° of drawing and extruding bars 61 can be solid bar or hollow bar.
Alternatively, the quality of the biaxially fabric unit area containing drawing and extruding bar can be 100 to 3000g/m2Model
In enclosing, breadth can be in the range of 300mm to 3000mm.
Alternatively, ﹢ N ° weft yarns 31 and-N ° of weft yarns 51 can be fine by glass fibre, carbon fiber, aramid fiber, basalt
A kind of or more kinds of in dimension, Fypro and polyimide fiber is made, but according to the exemplary embodiment of the present invention
Not limited to this, ﹢ N ° weft yarns 31 and-N ° of weft yarns 51 can also be made up of other suitable fibers.
Alternatively, the line density of ﹢ N ° weft yarns 31 and-N ° of weft yarns 51 can be in the range of 100tex to 4800tex.Here solve
Tex, Tex (Tekes) are released, it is referred to as special, public branch is once called as, is a kind of line density unit.Symbol is tex, also known as " number ",
Refer to the grams of 1000 meters of long yarn weight under official regain, tex=g/L*1000, wherein g are the weight of yarn (or silk)
(gram), L are the length (rice) of yarn (or silk).It is direct system unit, and grammes per square metre is bigger, and yarn is thicker, is commonly used to represent silvalin
Line.Alternatively, ﹢ N ° drawing and extruding bars 41 and-N ° of drawing and extruding bars 61 can be made up of fiber and resin, and fiber can be glass fibre, carbon
It is a kind of or more kinds of in fiber, aramid fiber, basalt fibre, Fypro and polyimide fiber.Resin can be with
It is a kind of in epoxy resin, polyurethane resin, vinyl epoxy resin, unsaturated polyester resin and acrylate or more
It is a variety of, but according to the exemplary embodiment not limited to this of the present invention, ﹢ N ° drawing and extruding bars 41 and-N ° of drawing and extruding bars 61 can also be by other
Suitable fiber and resin are made.
Alternatively, between bundled yarn 71 and ﹢ N ° weft yarns 31, ﹢ N ° drawing and extruding bars 41 ,-N ° of weft yarns 51 and-N ° of drawing and extruding bars 61
With angle.
Referring to Fig. 1 descriptions according to the biaxially fabric containing drawing and extruding bar of the exemplary embodiment of the present invention
Manufacture method.
The step of reference picture the 1, the 1st, ﹢ N ° weft yarns 31 are abreast arranged according to predetermined space in ﹢ N ° with weft direction.2nd step, that
﹢ N ° drawing and extruding bars 41 are abreast arranged according to predetermined space and ﹢ N ° weft yarns 31 between this, and it is stacked with ﹢ N ° weft yarns 31.3rd step, with
Weft direction abreast arranges-N ° of weft yarns 51 according to predetermined space in-N °, with stacked with ﹢ N ° weft yarns 31.4th step, each other
According to predetermined space and-N ° of weft yarns 51 abreast-N ° of drawing and extruding bars of arrangement 61, and stacked with-N ° of weft yarns 51.5th step, along warp-wise
Bundled yarn 71 is abreast arranged to draw ﹢ N ° weft yarns 31, ﹢ N ° drawing and extruding bars 41 ,-N ° of weft yarns 51 and-N ° by bundled yarn 71 in direction
The bondage loop bonding of rod 61 is squeezed to be integrally formed, wherein, quantity >=1 of ﹢ N ° drawing and extruding bars 41 and-N ° of drawing and extruding bars 61.
According to the exemplary embodiment of the present invention, during bondage loop bonding, then drawing and extruding bar can stitch again first with yarn Split Down
Compile, can also be woven into drawing and extruding bar during bondage loop bonding.
According to the exemplary embodiment of the present invention, during bondage loop bonding, then drawing and extruding bar can stitch again first with yarn Split Down
Compile, can also be woven into drawing and extruding bar during bondage loop bonding.For example, can be by ﹢ N ° drawing and extruding bars 41 and ﹢ N ° weft yarns 31 simultaneously
﹢ N ° drawing and extruding bars 41, then loop bonding again, can also be woven into by stock during bondage loop bonding.Similarly, can be by-N ° of pultrusions
- N ° of drawing and extruding bars 61, then loop bonding again, can also be woven into by rod 61 and the-N ° of Split Down of weft yarn 51 during bondage loop bonding.
Although according to present embodiment illustrates the biaxially fabric containing drawing and extruding bar, basis
The fabric not limited to this of the exemplary embodiment of the present invention, can also three axially, four axially or more axial direction fibres are knitted
Thing.
According to the mode such as exemplary embodiment, diameter, cross sectional shape, thickness that can be by changing drawing and extruding bar of the present invention
It to change the intensity of the biaxially fabric containing drawing and extruding bar, may apply to the biaxially fabric containing drawing and extruding bar
Different operating modes and field, for example, can be applied to the fields such as wind-powered electricity generation, automobile, ship.
According to the biaxially fabric containing drawing and extruding bar of the exemplary embodiment of the present invention due to containing drawing and extruding bar, institute
So that in process of deployment, the flatness of fabric can be effectively improved and keep fiber-wall-element model, so as to keep fabric to strengthen
The performance of composite.Further, since drawing and extruding bar fiber-wall-element model itself is good, it is possible to further lifting fabric enhancing
The performance of composite.
The biaxially fabric containing drawing and extruding bar using the exemplary embodiment according to the present invention can effectively change
The defects of being apt to fabric gauffer, bulge problem, so as to improve the performance of fabric reinforced composites and quality.
Although the exemplary embodiment of the present invention is described in detail above, it will be understood by those skilled in the art that
Without departing from the principles and spirit of the present invention, various modifications and variations can be made to embodiments of the invention.But
It should be appreciated that in the opinion of those skilled in the art, these modifications and variations will fall into claim limited it is of the invention
In the range of.
Claims (14)
1. a kind of biaxially fabric containing drawing and extruding bar, it is characterised in that the biaxially fiber containing drawing and extruding bar is knitted
Thing includes:
﹢ N ° weft yarns (31), abreast arranged according to predetermined space in ﹢ N ° with weft direction;
﹢ N ° drawing and extruding bars (41), abreast arranged according to predetermined space and the ﹢ N ° weft yarns (31) each other, and with the ﹢ N °
Weft yarn (31) is stacked;
- N ° of weft yarns (51), abreast arranged according to predetermined space in-N ° with weft direction, and it is folded with the ﹢ N ° weft yarns (31)
Put;
- N ° of drawing and extruding bars (61), abreast arranged according to predetermined space and the-N ° of weft yarns (51) each other, and with described-N °
Weft yarn (51) is stacked;
Bundled yarn (71), abreast arranged along warp direction, by the ﹢ N ° weft yarns (31), the ﹢ N ° drawing and extruding bars (41),
- N ° of the weft yarns (51) and-N ° of drawing and extruding bars (61) bondage loop bonding are integrally formed,
Wherein, quantity >=1 of ﹢ N ° (41) drawing and extruding bars and the-N ° of drawing and extruding bars (61).
2. the biaxially fabric according to claim 1 containing drawing and extruding bar, it is characterised in that 0 < N < 90.
3. the biaxially fabric according to claim 2 containing drawing and extruding bar, it is characterised in that N 45.
4. the biaxially fabric according to claim 2 containing drawing and extruding bar, it is characterised in that the ﹢ N ° drawing and extruding bars
(41) and-N ° of drawing and extruding bars (61) diameter in the range of 0.1mm to 10mm.
5. the biaxially fabric according to claim 4 containing drawing and extruding bar, it is characterised in that the ﹢ N ° drawing and extruding bars
(41) and the cross section of-N ° of drawing and extruding bars (61) is shaped as circular, ellipse or rectangle.
6. the biaxially fabric according to claim 5 containing drawing and extruding bar, it is characterised in that described to contain drawing and extruding bar
Biaxially fabric unit area quality 100 to 3000g/m2In the range of, breadth is in 300mm to 3000mm scopes
It is interior.
7. the biaxially fabric according to any one of claim 1 to 6 containing drawing and extruding bar, it is characterised in that institute
It is fine by glass fibre, carbon fiber, aramid fiber, basalt fibre, polyamide to state ﹢ N ° weft yarns (31) and-N ° of weft yarns (51)
A kind of or more kinds of in peacekeeping polyimide fiber is made.
8. the biaxially fabric according to claim 7 containing drawing and extruding bar, it is characterised in that the ﹢ N ° weft yarns
(31) and-N ° of weft yarns (51) line density in the range of 100tex to 4800tex.
9. the biaxially fabric according to claim 8 containing drawing and extruding bar, it is characterised in that the ﹢ N ° drawing and extruding bars
(41) it is made up with-N ° of the drawing and extruding bars (61) of fiber and resin, the fiber is glass fibre, carbon fiber, aramid fiber, profound
A kind of or more kinds of in military rock fiber, Fypro and polyimide fiber, the resin is epoxy resin, polyurethane
It is a kind of or more kinds of in resin, vinyl epoxy resin, unsaturated polyester resin and acrylate.
10. the biaxially fabric according to claim 9 containing drawing and extruding bar, it is characterised in that the bundled yarn
(71) with the ﹢ N ° weft yarns (31), the ﹢ N ° drawing and extruding bars (41) ,-N ° of weft yarns (51) and-N ° of drawing and extruding bars (61)
Between be respectively provided with angle.
11. a kind of manufacture method of the biaxially fabric containing drawing and extruding bar, it is characterised in that the manufacture method includes:
﹢ N ° weft yarns (31) are abreast arranged according to predetermined space in ﹢ N ° with weft direction;
Abreast arrange ﹢ N ° drawing and extruding bars (41) according to predetermined space and the ﹢ N ° weft yarns (31) each other, and with the ﹢ N °
Weft yarn (31) is stacked;
- N ° of weft yarns (51) are abreast arranged according to predetermined space in-N ° with weft direction, with stacked with the ﹢ N ° weft yarns (31);
Each other according to predetermined space and the-N ° of weft yarns (51) abreast-N ° of drawing and extruding bars of arrangement (61), and with described-N °
Weft yarn (51) is stacked;
Abreast arranged along warp direction bundled yarn (71) with by the bundled yarn (71) by the ﹢ N ° weft yarns (31), institute
﹢ N ° drawing and extruding bars (41) ,-N ° of weft yarns (51) and-N ° of drawing and extruding bars (61) bondage loop bonding is stated to be integrally formed,
Wherein, quantity >=1 of the ﹢ N ° drawing and extruding bars (41) and-N ° of drawing and extruding bars (61).
12. the manufacture method of the biaxially fabric according to claim 11 containing drawing and extruding bar, wherein, 0 < N <
90。
13. the manufacture method of the biaxially fabric according to claim 12 containing drawing and extruding bar, it is characterised in that N
For 45.
14. the manufacture method of the biaxially fabric according to claim 11 containing drawing and extruding bar, it is characterised in that institute
State bundled yarn (71) and the ﹢ N ° weft yarns (31), the ﹢ N ° drawing and extruding bars (41) ,-N ° of weft yarns (51) and-N ° of drawings
Angle is respectively provided between crowded rod (61).