CN107815178A - A kind of preparation method of antirusting paint - Google Patents
A kind of preparation method of antirusting paint Download PDFInfo
- Publication number
- CN107815178A CN107815178A CN201710864375.6A CN201710864375A CN107815178A CN 107815178 A CN107815178 A CN 107815178A CN 201710864375 A CN201710864375 A CN 201710864375A CN 107815178 A CN107815178 A CN 107815178A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- mixing time
- preparation
- antirust agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of preparation method of antirusting paint of the present invention, it is characterised in that step is as follows：（1）Prepare antirust agent, 10 50 parts of 5 25 parts of 10 20 parts of 10 20 parts of 4 16 parts of 5 30 parts of 5 20 parts of citric acid, sodium metasilicate, ammonium nitrate, silicon dioxide microparticle, tri-n-butylamine, nitrilotriethanol amine, water according to the mass fraction is put into mixer stirring, mixing time 30min；（2）Prepare coating, 40 80 parts of 50 100 parts of vistanex according to the mass fraction and polyurethane resin are mixed, mixing time is 40min, the antirust agent prepared is added in step (1) after the completion of stirring to carry out continuing to stir, mixing time is 50min, and stirring is completed.The rustless property of the antirust agent of gained of the invention is splendid.
Description
Technical field
The present invention relates to a kind of preparation method of antirusting paint.
Background technology
In the environment such as seawater or high temperature/high humidity environment of saliferous, the rust of white can be formed by being coated with the surface of the steel of metal
Mark, cause the reduction of outward appearance that substrate surface substantially deteriorates or antirust ability.
Therefore, a kind of antirusting paint is developed to have been to be concerned by more and more people.
The content of the invention
The present invention proposes a kind of preparation method of antirusting paint regarding to the issue above.
Specific technical scheme is as follows：
A kind of preparation method of antirusting paint, it is characterised in that step is as follows：
（1）Antirust agent is prepared, by citric acid 5-20 parts according to the mass fraction, sodium metasilicate 5-30 parts, ammonium nitrate 4-16 parts, dioxy
SiClx particulate 10-20 parts, tri-n-butylamine 10-20 parts, nitrilotriethanol amine 5-25 parts, water 10-50 parts are put into mixer stirring,
Mixing time 30min；
（2）Coating is prepared, vistanex 50-100 parts according to the mass fraction and polyurethane resin 40-80 parts are entered
Row is mixed, mixing time 40min, and the antirust agent prepared is added in step (1) after the completion of stirring and carries out continuing to stir,
Mixing time is 50min, and stirring is completed.
The preparation method of above-mentioned a kind of antirusting paint, it is characterised in that the water is deionized water.
The preparation method of above-mentioned a kind of antirusting paint, it is characterised in that the particle diameter of silicon dioxide microparticle is 50-100nm.
The rustless property of the antirust agent of gained of the invention is splendid.
Embodiment
To make technical scheme become apparent from clearly, the present invention is described further below in conjunction with the accompanying drawings,
Any scheme drawn to the technical characteristic progress equivalencing of technical solution of the present invention and conventional reasoning each falls within guarantor of the present invention
Protect scope.
Embodiment 1
A kind of preparation method of antirusting paint, it is characterised in that step is as follows：
（1）Antirust agent is prepared, by 4 parts of 5 parts of 5 parts of citric acid, sodium metasilicate, ammonium nitrate, silicon dioxide microparticle according to the mass fraction
10 parts, 10 parts of tri-n-butylamine, 5 parts of nitrilotriethanol amine, 10 parts of water be put into mixer stirring, mixing time 30min；
（2）Coating is prepared, 40 parts of 50 parts of vistanex according to the mass fraction and polyurethane resin are mixed
Stirring, mixing time 40min, the antirust agent prepared is added in step (1) after the completion of stirring and carries out continuing to stir, during stirring
Between be 50min, stirring complete.
The particle diameter of silicon dioxide microparticle is 50nm.
Embodiment 2
A kind of preparation method of antirusting paint, it is characterised in that step is as follows：
（1）Antirust agent is prepared, 16 parts of 30 parts of 20 parts of citric acid, sodium metasilicate, ammonium nitrate, silica according to the mass fraction is micro-
20 parts of grain, 20 parts of tri-n-butylamine, 25 parts of nitrilotriethanol amine, 50 parts of water are put into mixer stirring, mixing time 30min；
（2）Coating is prepared, 80 parts of 100 parts of vistanex according to the mass fraction and polyurethane resin are mixed
Stirring, mixing time 40min, the antirust agent prepared is added in step (1) after the completion of stirring and carries out continuing to stir, during stirring
Between be 50min, stirring complete.
The particle diameter of silicon dioxide microparticle is 100nm.
Claims (3)
1. a kind of preparation method of antirusting paint, it is characterised in that step is as follows：
（1）Antirust agent is prepared, by citric acid 5-20 parts according to the mass fraction, sodium metasilicate 5-30 parts, ammonium nitrate 4-16 parts, dioxy
SiClx particulate 10-20 parts, tri-n-butylamine 10-20 parts, nitrilotriethanol amine 5-25 parts, water 10-50 parts are put into mixer stirring,
Mixing time 30min；
（2）Coating is prepared, vistanex 50-100 parts according to the mass fraction and polyurethane resin 40-80 parts are entered
Row is mixed, mixing time 40min, and the antirust agent prepared is added in step (1) after the completion of stirring and carries out continuing to stir,
Mixing time is 50min, and stirring is completed.
2. a kind of preparation method of antirusting paint as claimed in claim 1, it is characterised in that the water is deionized water.
3. a kind of preparation method of antirusting paint as claimed in claim 1, it is characterised in that the particle diameter of silicon dioxide microparticle is
50-100nm。